Claims
- 1. A method of reinforcing structurally fragile inorganic fabrics with non-wettable, thermally stable, chemically inert fluoroplastics to provide gas permeable, wettable, chemically resistant, thermally stable composites having good mechanical strength comprising the steps of:
- (a) providing a fabric comprised of inorganic fibers whose surfaces are substantially free of contaminants and surfactants;
- (b) applying a minor coating of fluoroplastic particles to said fiber surfaces; and
- (c) controllably sintering said particles employing a temperature profile defined as a heating rate to and duration at a maximum temperature which causes said fluoroplastic particles to soften to the point where they partially fuse, or coalesce, but not to the point where they begin to flow, thereby causing said particles to permanently adhere to said fibers and provide a discontinuous fluoroplastic matrix which reinforces and strengthens said fabric.
- 2. The method of claim 1 wherein said fluoroplastic particles are selected from the group consisting of tetrafluoroethylene, chlorotrifluoroethylene, fluorinated ethylene propylene, polyvinylidene fluoride and polyvinyl fluoride.
- 3. The method of claim 1 wherein said fluoroplastic is tetrafluoroethylene and where said particles are applied to said fiber surfaces by immersing said fabric in an aqueous suspension of tetrafluoroethylene particles and subsequently removing excess particles from said fabric by sequentially draining and blotting said fabric.
- 4. A process of reinforcing a fragile inorganic substrate with non-wettable, chemically resistant, thermally stable polytetrafluoroethylene to form a wettable, chemically resistant, thermally stable composite having improved mechanical strength comprising the steps of immersing said substrate in a dilute suspension of polytetrafluoroethylene particles whereby said particles are evenly dispersed throughout the interstices of said substrate; removing said substrate from said dilute suspension and sequentially draining, blotting, and evaporating the carrier fluid from said suspension in an air oven or vacuum oven, thereby leaving a substrate evenly coated with discontinuous particles of polytetrafluoroethylene and thereafter sintering said discontinuous particles at a selected temperature ranging from 330.degree. to 450.degree. C. for 3-5 minutes to form a semicontinuous network of polytetrafluoroethylene particles which reinforce said inorganic substrate, thereby increasing the mechanical strength of said substrate.
Parent Case Info
This is a division of application Ser. No. 135,608, filed Mar. 31, 1980, now U.S. Pat. No. 4,308,325, patented Dec. 29, 1981.