Patent Application
20190309389
The subject application relates generally to processing of metal ores or concentrates, and in particular to a process for separation of at least one metal sulfide from such ores or concentrates.
Metallurgical processes are applied to metal ore deposits and such processes can be categorized into three general areas: leaching, solution concentration and purification, and metal recovery.
Such processes have been previously described. For example, U.S. Pat. No. 3,709,680 to Holmes et al. (1973) is directed to leaching a copper concentrate prepared by flotation using a hot concentrated caustic solution.
U.S. Pat. No. 3,911,078 to Nadkami et al. (1975) is directed to a method for removing chemically bonded arsenic and antimony from copper sulfide ores.
U.S. Pat. No. 4,017,369 to Lindstrom (1977) is directed to the recovery of the antimony, arsenic, mercury and tin from alkaline leach solutions by electrowinning.
U.S. Pat. No. 4,051,220 to Coltrinari (1977) is directed to a process for treating mixed metal sulfides containing trivalent antimony sulfide. The process involves leaching with sodium sulfide to isolate copper sulfide as an insoluble solid. Following leaching, antimony and arsenic values are oxidized.
U.S. Pat. No. 5,137,640 to Poncha (1992) is directed to a process for reducing arsenic levels in a solution containing sulfuric acid, water, and arsenic acid by adding copper or a copper-containing compound to the solution to form dissolved copper arsenate, adding alkali solution to precipitate the copper arsenate and to neutralize arsenic and sulfuric acid.
U.S. Pat. No. 5,290,338 to Anderson et al. (1994) is directed to an antimony recovery process in which an antimony-containing material is leached in a solvent including elemental sulfur and caustic.
U.S. Pat. No. 5,750,019 to Olper (1998) is directed to a hydrometallurgical and electrochemical process for processing sulfur antimony ores and residues, the end products from which are electrolytic antimony and elemental sulfur.
Most of the economically significant base metal ore deposits worldwide contain mixed sulfides. Several types of mixed sulfide ores and concentrates may contain relatively large quantities of lead sulfide together with sulfides of other metals, such as copper, antimony and arsenic. Known metallurgical processes do not provide satisfactory metal sulfide separation from such ores and concentrates. It is desirable that certain metal sulfides be separated and recovered from ores and concentrates and converted, if necessary, to a form suitable for commercial sale, while other more deleterious elements (e.g. other metals/metal compounds) may be removed. Deleterious elements are understood to mean elements that are considered commercially deleterious and therefore, can vary widely depending on the commercial application. It is also desirable that the cost of separation of at least one metal sulfide and/or removing deleterious elements from the concentrate at or near the mine be kept low.
Accordingly, there is a need for an improved process for separation of at least one metal sulfide from a mixed sulfide ore or concentrate.
Accordingly, in one aspect there is provided a process for separation of at least one metal sulfide from a mixed sulfide concentrate, the mixed sulfide concentrate having at least one sulfide comprising antimony, arsenic and at least two metals, the at least two metals comprising a first metal and a second metal, the process comprising: subjecting the mixed sulfide concentrate to flotation in which at least one sulfide comprising antimony, arsenic and the first metal is floated and at least one sulfide comprising the second metal is depressed, the flotation yielding a first metal concentrate and a second metal concentrate, the first metal concentrate having the at least one sulfide comprising antimony, arsenic and the first metal, and the second metal concentrate having the at least one sulfide comprising the second metal; leaching the first metal concentrate to yield a further metal concentrate and a leach solution, the further metal concentrate comprising the first metal and the leach solution comprising soluble antimony and soluble arsenic; and one of: (i) oxidizing the leach solution to yield an antimony precipitate and an arsenic solution; (ii) forming a stable arsenic compound from the leach solution; and (iii) oxidizing the leach solution to yield an antimony precipitate and an arsenic solution, and forming a stable arsenic compound from the arsenic solution.
The leach solution may be oxidized to yield the antimony precipitate and the arsenic solution, and the stable arsenic compound is formed from the arsenic solution. The antimony and arsenic may be present in the mixed sulfide concentrate in a molar ratio of about 0.5:1 to about 1.5:1. The antimony and arsenic may be present in the mixed sulfide concentrate in a molar ratio of about 1:1.
The mixed sulfide concentrate may comprise the at least two metals, and a major amount of arsenic relative to antimony. The mixed sulfide concentrate may comprise the at least two metals, and a major amount of antimony relative to arsenic.
The arsenic solution may have an As:Sb concentration ratio of about 10:1 to about 500:1, typically about 20:1 to about 200:1, and more typically about 50:1 to about 100:1.
The first metal and the second metal may be different metals. The first metal and the second metal may be the same metal. The first metal and the second metal may be selected from the group consisting of copper, lead, silver, iron, mercury, zinc, and vanadium. The first metal may be copper and the second metal may be lead.
Subjecting the mixed sulfide concentrate to flotation may comprise using one or more of a sulfite salt and a caustic starch solution.
The second metal concentrate may have at least about 50% of the original antimony, the arsenic, and the first metal content of the mixed sulfide concentrate removed. The second metal concentrate may have about 60% to about 90% of the original antimony, arsenic, and the first metal content of the mixed sulfide concentrate removed. The first metal concentrate may have at least about 50% of the original second metal content of the mixed sulfide concentrate removed. The first metal concentrate may have about 65% to about 98% of the original second metal content of the mixed sulfide concentrate removed. The further metal concentrate may have at least about 75% of the original antimony and arsenic content of the mixed sulfide concentrate removed. The further metal concentrate may have about 80% to about 95% of the original antimony and arsenic content of the mixed sulfide concentrate removed.
The process may further comprise: washing solids remaining after the leaching to yield a first wash solution. The process may further comprise: acidifying the first wash solution to form a precipitate and to yield a first wash slurry; and separating the precipitate from the first wash slurry to yield a second wash solution. The process may further comprise: acidifying the second wash solution to precipitate arsenic and antimony species as a slurry; separating the precipitated arsenic and antimony species; and leaching the precipitated arsenic and antimony species with the first metal concentrate during the leaching. The process may further comprise: prior to the acidifying, oxidizing the first wash solution so as to oxidize As3+ to As5+ and Sb3+ to Sb5+. The process may further comprise: leaching the precipitate with the first metal concentrate during the leaching.
The oxidizing the leach solution may comprise oxidizing the soluble arsenic and antimony in the leach solution to yield soluble antimony and arsenic thiosalts. The oxidizing the soluble antimony and arsenic in the leach solution may comprise oxidizing with elemental sulfur. The process may further comprise determining an oxidation end point by at least one of wavelength monitoring and oxidation reduction potential (ORP) monitoring. The process may further comprise removing the soluble antimony and arsenic thiosalts from the leach solution by crystallization. The process may further comprise recovering the leach solution for recycling. The removing may comprise cooling the leach solution to induce the crystallization. The cooling may be controlled to avoid crystallization of alkali metal sulfide. The crystallization may comprise forming thioarsenate and thioantimonate salts. The process may further comprise dissolving crystals formed by the crystallization to yield the soluble antimony and arsenic thiosalts. The further metal concentrate may be washed to yield a wash solution, the dissolving comprises dissolving the crystals in the wash solution.
The process may further comprise oxidizing the soluble antimony and arsenic thiosalts to yield the antimony precipitate and the arsenic solution. The oxidizing the soluble antimony and arsenic thiosalts may comprise using an oxidizing agent. The oxidizing agent may be hydrogen peroxide and/or a metal catalyzed hydroquinone. The oxidizing the soluble antimony and arsenic thiosalts may be carried out at about atmospheric pressure. The process may further comprise: prior to the oxidizing the soluble antimony and arsenic thiosalts, acidifying a solution comprising the soluble antimony and arsenic thiosalts to precipitate arsenic and antimony species as a slurry; and dissolving the precipitated arsenic and antimony species through addition of base to the slurry, wherein the oxidizing comprises oxidizing the dissolved arsenic and antimony species. The process may further comprise: prior to the oxidizing the soluble antimony and arsenic thiosalts, acidifying a solution comprising the soluble antimony and arsenic thiosalts to precipitate an additional antimony sulfide product as a slurry; separating the additional antimony sulfide product from the slurry; acidifying the slurry to precipitate arsenic and antimony species; and dissolving the precipitated arsenic and antimony species through addition of base to the slurry, wherein the oxidizing comprises oxidizing the dissolved arsenic and antimony species. The additional antimony sulfide product may comprise antimony pentasulfide. Hydrogen sulfide gas may be produced, and the hydrogen sulfide gas be passed through a caustic scrubber. A sodium sulfide product or a sodium hydrosulfide product may be formed. The process may further comprise combining the sodium sulfide product or the sodium hydrosulfide product with leach reagents during the leaching.
The antimony precipitate may comprise sodium antimony hydroxide.
The arsenic solution may comprise soluble arsenate.
The forming further comprises returning a portion of the stable arsenic compound to the forming to act as precipitation seed material during the forming.
The process may further comprise, prior to the forming: acidifying the arsenic solution to decompose thiosulfates, to yield an acidified solution; oxidizing the acidified solution to oxidize residual As3+ to As5+ and reduced sulfur species to sulfates, to yield a slurry comprising elemental sulfur; separating elemental sulfur from the slurry to yield a liquid; and oxidizing the liquid to oxidize residual reduced sulfur species, to yield an oxidized solution, wherein the forming comprises forming the stable arsenic compound from the oxidized solution. The process may further comprise using the elemental sulfur as an oxidizing agent for the oxidizing of the leach solution.
The process may further comprise, prior to the forming: oxidizing the arsenic solution to oxidize residual As3+ to As5+ and reduced sulfur species to sulfates, to yield an oxidized solution; and acidifying the oxidized solution to yield an acidified oxidized solution, wherein forming comprises forming the stable arsenic compound from the acidified oxidized solution.
The stable arsenic compound may comprise ferric arsenate. The stable arsenic compound may be compliant with toxic characteristic leaching procedure (TCLP) standards.
The at least one sulfide comprising antimony, arsenic and at least two metals may comprise sulfosalts. The sulfosalts may comprise at least one of sulfarsenites, sulfarsenates, sulfantimonites, sulfantimonates and sulfosalts of SnS archetype. The sulfosalts may comprise at least one of: tetrahedrite, tennantite, enargite, bournonite, famatinite, and jamesonite.
The second metal concentrate may be substantially free of antimony, arsenic and the first metal. The further metal concentrate may be substantially free of antimony and arsenic.
In another aspect, there is provided a process for separation of at least one metal sulfide from a mixed sulfide concentrate, the mixed sulfide concentrate having at least one sulfide comprising antimony, arsenic, and at least two metals, the at least two metals comprising a first metal and a second metal, the process comprising: subjecting the mixed sulfide concentrate to flotation using one or more of a sulfite salt and a caustic starch solution in which at least one sulfide comprising antimony, arsenic, and the first metal is floated and at least one sulfide comprising the second metal is depressed, the flotation yielding a first metal concentrate and a second metal concentrate, the first metal concentrate having the at least one sulfide comprising antimony, arsenic, and the first metal, and the second metal concentrate having the at least one sulfide comprising the second metal.
Antimony and arsenic may be present in the mixed sulfide concentrate in a molar ratio of about 0.5:1 to about 1.5:1. Antimony and arsenic may be present in the mixed sulfide concentrate in a molar ratio of about 1:1.
The mixed sulfide concentrate may comprise the at least two metals, and a major amount of arsenic relative to antimony. The mixed sulfide concentrate may comprise the at least two metals, and a major amount of antimony relative to arsenic. The first metal and the second metal may be different metals. The first metal and the second metal may be the same metal. The first metal and the second metal may be selected from the group consisting of copper, lead, silver, iron, mercury, zinc, and vanadium. The first metal may be copper and the second metal may be lead.
The subjecting the mixed sulfide concentrate to flotation further comprises using at least one of a frother and a collector.
The second metal concentrate may have at least about 50% of the original antimony, arsenic, and the first metal content of the mixed sulfide concentrate removed. The second metal concentrate may have about 60% to about 90% of the original antimony, arsenic, and the first metal content of the mixed sulfide concentrate removed. The first metal concentrate may have at least about 50% of the original second metal content of the mixed sulfide concentrate removed. The first metal concentrate may have about 65% to about 98% of the original second metal content of the mixed sulfide concentrate removed. The further metal concentrate may have at least about 75% of the original antimony and arsenic content of the mixed sulfide concentrate removed. The further metal concentrate may have about 80% to about 95% of the original antimony and arsenic content of the mixed sulfide concentrate removed.
The process may further comprise leaching the first metal concentrate to yield a further metal concentrate and a leach solution, the further metal concentrate comprising the first metal and the leach solution comprising soluble arsenic and soluble antimony. The process may further comprise washing solids remaining after the leaching with to yield a first wash solution. The process may further comprise: acidifying the first wash solution to form a precipitate and yield a first wash slurry; and separating the precipitate from the first wash slurry to yield a second wash solution. The process may further comprise: acidifying the second wash solution to precipitate arsenic and antimony species as a slurry; separating the precipitated arsenic and antimony species; and leaching the precipitated arsenic and antimony species with the first metal concentrate during the leaching. The process may further comprise prior to the acidifying, oxidizing the first wash solution so as to oxidize As3+ to As5+ and Sb3+ to Sb5+. The process may further comprise: leaching the precipitate with the first metal concentrate during the leaching.
The sulfides may comprise antimony, arsenic and at least two metals comprise sulfosalts. The sulfosalts may comprise at least one of sulfarsenites, sulfarsenates, sulfantimonites, sulfantimonates and sulfosalts of SnS archetype. The sulfosalts may comprise at least one of tetrahedrite, tennantite, enargite, boumonite, famatinite, and jamesonite.
The second metal concentrate may be substantially free of antimony, arsenic and the first metal. The further metal concentrate may be substantially free of antimony and arsenic.
In another aspect, there is provides a process for leaching a first metal concentrate having at least one sulfide comprising antimony, arsenic, and at least one metal, the process comprising: leaching the first metal concentrate to yield a further metal concentrate and a leach solution, the leach solution comprising soluble arsenic and soluble antimony; removing the soluble antimony and soluble arsenic from the leach solution by crystallization; and recovering the leach solution for recycling.
Antimony and arsenic may be present in the at least one sulfide comprising antimony, arsenic and the at least one metal in a molar ratio of about 0.5:1 to about 1.5:1. Antimony and arsenic may be present in the at least one sulfide comprising antimony, arsenic and the at least one metal in a molar ratio of about 1:1. The mixed sulfide concentrate may comprise the at least one metal, and a major amount of arsenic relative to antimony. The mixed sulfide concentrate may comprise the at least one metal, and a major amount of antimony relative to arsenic.
The at least one sulfide may comprise at least two sulfides comprising different metals. The at least one sulfide may comprise at least two sulfides comprising the same metal.
The at least one metal may be selected from the group consisting of copper, lead, silver, iron, mercury, zinc, and vanadium. The at least one metal may comprise copper. The process may further comprise, prior to the removing: oxidizing the soluble arsenic and antimony in the leach solution to yield soluble antimony and arsenic thiosalts. The oxidizing the soluble antimony and arsenic in the leach solution may comprise oxidizing with elemental sulfur. The process may further comprise determining an oxidation end point by at least one of wavelength monitoring and oxidation reduction potential (ORP) monitoring. The process may further comprise removing the soluble antimony and arsenic thiosalts from the leach solution by crystallization.
The removing may comprise cooling the leach solution to induce the crystallization. The crystallization may comprise forming thioarsenate and thioantimonate salts.
The process may further comprise dissolving crystals formed by the crystallization to yield soluble antimony and arsenic thiosalts. The further metal concentrate may be washed to yield an wash solution, the dissolving comprising dissolving the crystals in the wash solution.
The process may further comprise oxidizing the soluble antimony and arsenic thiosalts to yield an antimony precipitate and an arsenic solution. The oxidizing the soluble antimony and arsenic thiosalts may comprise using an oxidizing agent. The oxidizing agent may be hydrogen peroxide and/or a metal catalyzed hydroquinone. The oxidizing the soluble antimony and arsenic thiosalts may be carried out at about atmospheric pressure. The process may further comprise: prior to the oxidizing the soluble antimony and arsenic thiosalts, acidifying a solution comprising the soluble antimony and arsenic thiosalts to precipitate arsenic and antimony species as a slurry; and dissolving the precipitated arsenic and antimony species through addition of base to the slurry, wherein the oxidizing comprises oxidizing the dissolved arsenic and antimony species. The process may further comprise: prior to the oxidizing the soluble antimony and arsenic thiosalts, acidifying a solution comprising the soluble antimony and arsenic thiosalts to precipitate an additional antimony sulfide product as a slurry; separating the additional antimony sulfide product from the slurry; acidifying the slurry to precipitate arsenic and antimony species; and dissolving the precipitated arsenic and antimony species through addition of base to the slurry, wherein the oxidizing comprises oxidizing the dissolved arsenic and antimony species. The additional antimony sulfide product may comprise antimony pentasulfide. Hydrogen sulfide gas may be produced, and the hydrogen sulfide gas may be passed through a caustic scrubber. A sodium sulfide product or a sodium hydrosulfide product may be formed. The process may further comprise combining the sodium sulfide product or the sodium hydrosulfide product with leach reagents during the leaching. The antimony precipitate may comprise sodium antimony hydroxide.
The arsenic solution may comprise soluble arsenate. The process may further comprise forming a stable arsenic compound from the arsenic solution. The forming further comprises returning a portion of the stable arsenic compound to the forming to act as precipitation seed material during the forming. The process may further comprise, prior to the forming: acidifying the arsenic solution to decompose thiosulfates, to yield an acidified solution; oxidizing the acidified solution to oxidize residual As3+ to As5+ and reduced sulfur species to sulfates, to yield a slurry comprising elemental sulfur; separating elemental sulfur from the slurry to yield a liquid; and oxidizing the liquid to oxidize residual reduced sulfur species, to yield an oxidized solution, wherein the forming comprises forming the stable arsenic compound from the oxidized solution. The process may further comprise using the elemental sulfur for use as an oxidizing agent for the oxidizing of the leach solution. The process may further comprise, prior to the forming: oxidizing the arsenic solution to oxidize residual As3+ to As5+ and reduced sulfur species to sulfates, to yield an oxidized solution; and acidifying the oxidized solution to yield an acidified oxidized solution, wherein forming comprises forming the stable arsenic compound from the acidified oxidized solution. The stable arsenic compound may comprise ferric arsenate. The stable arsenic compound may be compliant with toxic characteristic leaching procedure (TCLP) standards.
The at least one sulfide comprising antimony, arsenic and the at least one metal may comprise one or more sulfosalts. The one or more sulfosalts may comprise at least one of sulfarsenites, sulfarsenates, sulfantimonites, sulfantimonates and sulfosalts of SnS archetype. The one or more sulfosalts may comprise at least one of tetrahedrite, tennantite, enargite, boumrnonite, famatinite, and jamesonite.
The further metal concentrate may be substantially free of antimony and arsenic.
In another aspect, there is provided a process for separation of antimony and arsenic from a leach solution comprising soluble antimony and arsenic, the process comprising: oxidizing the soluble antimony and arsenic in the leach solution so as to reach an oxidation end point determined by at least one of wavelength monitoring and oxidation reduction potential (ORP) monitoring, to yield soluble antimony and arsenic thiosalts; and oxidizing the soluble antimony and arsenic thiosalts to yield an antimony precipitate and an arsenic solution.
Antimony and arsenic may be in the leach solution in a molar ratio of about 0.5:1 to about 1.5:1. Antimony and arsenic may be present in the leach solution in a molar ratio of about 1:1. The leach solution may comprise a major amount of arsenic relative to antimony. The leach solution may comprise a major amount of antimony relative to arsenic.
The oxidizing the soluble antimony and arsenic in the leach solution may comprise oxidizing with elemental sulfur.
The process may further comprise removing the soluble antimony and arsenic thiosalts from the leach solution by crystallization. The process may further comprise recovering the leach solution for recycling. The removing may comprise cooling the leach solution to induce the crystallization. The cooling may be controlled to avoid crystallization of alkali metal sulfide. The crystallization may comprise forming thioarsenate and thioantimonate salts. The process may further comprise dissolving crystals formed by the crystallization to yield the soluble antimony and arsenic thiosalts.
The oxidizing the soluble antimony and arsenic thiosalts may comprise using an oxidizing agent. The oxidizing agent may be hydrogen peroxide and/or a metal catalyzed hydroquinone.
The oxidizing the soluble antimony and arsenic thiosalts may be carried out at about atmospheric pressure.
The process may further comprise: prior to the oxidizing the soluble antimony and arsenic thiosalts, acidifying a solution comprising the soluble antimony and arsenic thiosalts to precipitate arsenic and antimony species as a slurry; and dissolving the precipitated arsenic and antimony species through addition of base to the slurry, wherein the oxidizing comprises oxidizing the dissolved arsenic and antimony species.
The process may further comprise: prior to the oxidizing the soluble antimony and arsenic thiosalts, acidifying a solution comprising the soluble antimony and arsenic thiosalts to precipitate an additional antimony sulfide product as a slurry; separating the additional antimony sulfide product from the slurry; acidifying the slurry to precipitate arsenic and antimony species; and dissolving the precipitated arsenic and antimony species through addition of base to the slurry, wherein the oxidizing comprises oxidizing the dissolved arsenic and antimony species. The additional antimony sulfide product comprises antimony pentasulfide. Hydrogen sulfide gas may be produced and the hydrogen sulfide gas may be passed through a caustic scrubber. A sodium sulfide product or a sodium hydrosulfide product may be formed.
The antimony precipitate may comprise sodium antimony hydroxide.
The arsenic solution may comprise soluble arsenate.
The process may further comprise forming a stable arsenic compound from the arsenic solution. The forming further comprises returning a portion of the stable arsenic compound to the forming to act as precipitation seed material during the forming. The process may further comprise, prior to the forming: acidifying the arsenic solution to decompose thiosulfates, to yield an acidified solution; oxidizing the acidified solution to oxidize residual As3+ to As5+ and reduced sulfur species to sulfates, to yield a slurry comprising elemental sulfur; separating elemental sulfur from the slurry to yield a liquid; and oxidizing the liquid to oxidize residual reduced sulfur species, to yield an oxidized solution, wherein the forming comprises forming the stable arsenic compound from the oxidized solution. The process may further comprise using the elemental sulfur for use as an oxidizing agent for the oxidizing of the leach solution. The process may further comprise, prior to the forming: oxidizing the arsenic solution to oxidize residual As3+ to As5+ and reduced sulfur species to sulfates, to yield an oxidized solution; and acidifying the oxidized solution to yield an acidified oxidized solution, wherein forming comprises forming the stable arsenic compound from the acidified oxidized solution. The stable arsenic compound may comprise ferric arsenate. The stable arsenic compound may be compliant with toxic characteristic leaching procedure (TCLP) standards.
In another aspect, there is provided a stabilization process for an arsenic solution derived from a mixed sulfide concentrate, the mixed sulfide concentrate having at least one sulfide comprising antimony, arsenic and at least one metal, the process comprising: forming a stable arsenic compound from the arsenic solution, at about atmospheric pressure.
Antimony and arsenic may be present in the mixed sulfide concentrate in a molar ratio of about 0.5:1 to about 1.5:1. Antimony and arsenic may be present in the mixed sulfide concentrate in a molar ratio of about 1:1.
The mixed sulfide concentrate may comprise the at least one metal, and a major amount of arsenic relative to antimony. The mixed sulfide concentrate may comprise the at least one metal, and a major amount of antimony relative to arsenic.
The arsenic solution may have an As:Sb concentration (g/L) ratio of about 10:1 to about 500:1, typically about 20:1 to about 200:1, and more typically about 50:1 to about 100:1.
The at least one metal may be selected from the group consisting of copper, lead, silver, iron, mercury, zinc, and vanadium. The at least one metal may comprise copper.
The arsenic solution may comprise soluble arsenate.
The process may further comprise forming a stable arsenic compound from the arsenic solution for disposal. The forming further comprises returning a portion of the stable arsenic compound to the forming to act as precipitation seed material during the forming. The process may further comprise, prior to the forming: acidifying the arsenic solution to decompose thiosulfates, to yield an acidified solution; oxidizing the acidified solution to oxidize residual As3+ to As5+ and reduced sulfur species to sulfates, to yield a slurry comprising elemental sulfur; separating elemental sulfur from the slurry to yield a liquid; and oxidizing the liquid to oxidize residual reduced sulfur species, to yield an oxidized solution, wherein the forming comprises forming the stable arsenic compound from the oxidized solution. The process may further comprise using the elemental sulfur for use as an oxidizing agent for the oxidizing of the leach solution. The process may further comprise, prior to the forming: oxidizing the arsenic solution to oxidize residual As3+ to As5+ and reduced sulfur species to sulfates, to yield an oxidized solution; and acidifying the oxidized solution to yield an acidified oxidized solution, wherein forming comprises forming the stable arsenic compound from the acidified oxidized solution. The stable arsenic compound may comprise ferric arsenate. The stable arsenic compound may be compliant with toxic characteristic leaching procedure (TCLP) standards.
In another aspect, there is provided a stabilization process for an arsenic solution comprising thiosulfates, the process comprising: acidifying the arsenic solution to decompose the thiosulfates, to yield an acidified solution; oxidizing the acidified solution to oxidize residual As3+ to As5+ and reduced sulfur species to sulfates, to yield a slurry comprising elemental sulfur; separating elemental sulfur from the slurry to yield a liquid; oxidizing the liquid to oxidize residual reduced sulfur species, to yield an oxidized solution; and forming a stable arsenic compound from the oxidized solution.
The process may further comprise forming a stable arsenic compound from the oxidized solution, at about atmospheric pressure. The stable arsenic compound may comprise ferric arsenate. The stable arsenic compound may be compliant with toxic characteristic leaching procedure (TCLP) standards.
The arsenic solution may be derived from a mixed sulfide concentrate, the mixed sulfide concentrate having at least one sulfide comprising antimony, arsenic and at least one metal. Antimony and arsenic may be present in the mixed sulfide concentrate in a molar ratio of about 0.5:1 to about 1.5:1. Antimony and arsenic may be present in the mixed sulfide concentrate in a molar ratio of about 1:1. The mixed sulfide concentrate may comprise the at least one metal, and a major amount of arsenic relative to antimony. The mixed sulfide concentrate may comprise the at least one metal, and a major amount of antimony relative to arsenic. The at least one metal may be selected from the group consisting of copper, lead, silver, iron, mercury, zinc, and vanadium.
In still another aspect, there is provided a stabilization process for an arsenic solution, the process comprising: oxidizing the arsenic solution to oxidize As3+ to As5+ and reduced sulfur species to sulfates, to yield an oxidized solution; and acidifying the oxidized solution to yield an acidified oxidized solution; and forming a stable arsenic compound from the acidified oxidized solution.
The process may further comprise forming the stable arsenic compound from the oxidized solution at about atmospheric pressure. The stable arsenic compound may comprise ferric arsenate. The stable arsenic compound may be compliant with toxic characteristic leaching procedure (TCLP) standards.
The arsenic solution may be derived from a mixed sulfide concentrate, the mixed sulfide concentrate having at least one sulfide comprising antimony, arsenic and at least one metal. Antimony and arsenic may be present in the mixed sulfide concentrate in a molar ratio of about 0.5:1 to about 1.5:1. Antimony and arsenic may be present in the mixed sulfide concentrate in a molar ratio of about 1:1. The mixed sulfide concentrate may comprise the at least one metal, and a major amount of arsenic relative to antimony. The mixed sulfide concentrate may comprise the at least one metal, and a major amount of antimony relative to arsenic. The at least one metal may be selected from the group consisting of copper, lead, silver, iron, mercury, zinc, and vanadium.
In accordance with the above aspects, the sodium concentration of the oxidized solution may be at least about 10 g/L. The sodium concentration of the oxidized solution may be about 30 g/L to about 70 g/L. The sodium concentration of the oxidized solution may be about 50 g/L to about 60 g/L.
In accordance with the above aspects, the process may further comprise extracting at least one precious metal. The extracting may comprise utilizing at least one of an ion exchange resin and a precipitation process. The precious metal may be gold.
In accordance with the above aspects, the wavelength monitoring may be colorimetry.
Embodiments will now be described more fully with reference to the accompanying drawings in which:
In embodiments, a process is provided for separation of at least one metal sulfide from a mixed sulfide ore or concentrate.
The mixed sulfide concentrate comprises at least one sulfide having at least one metal and/or at least one semi-metal. It is understood, when used herein, that at least one sulfide having at least one metal and/or at least one semi-metal may be selected from, for example, any sulfur-bearing compound of one or more metals; any sulfur-bearing compound of one or more semi-metals; any sulfur-bearing compound of one or more metals and one or more semi-metals, such as, and without being limited thereto, sulfosalts; and mixtures thereof. The one or more metals may be selected from, for example, copper, lead, silver, iron, mercury, zinc, or vanadium. The one or more semi-metals may be selected from, for example, arsenic, antimony, bismuth or germanium. As will be understood, sulfosalts comprise one or more metals, one or more semi-metals, and sulfur. Sulfosalts containing arsenic include sulfarsenites, such as tennantite, and sulfarsenates, such as enargite. Sulfosalts containing antimony include sulfantimonites, such as tetrahedrite and boumrnonite, sulfantimonates, such as famatinite, and sulfosalts of SnS archetype, such as jamesonite. It is known to be difficult to recover certain metals from such minerals. It is desirable to be able to recover, for example, metals, such as copper, from concentrates containing metal arsenic sulfosalt minerals and metal antimony sulfosalt minerals using an economically viable, hydrometallurgical process, while converting deleterious elements into one or more environmentally stable products.
In another embodiment, there is provided a process for separation of at least one metal sulfide from a mixed sulfide concentrate, where the mixed sulfide concentrate has at least one sulfide comprising antimony, arsenic and at least two metals, and the at least two metals comprise a first metal and a second metal. The process comprises: subjecting the mixed sulfide concentrate to flotation in which at least one sulfide comprising antimony, arsenic and the first metal is floated and at least one sulfide comprising the second metal is depressed, the flotation yielding a first metal concentrate and a second metal concentrate, the first metal concentrate having the at least one sulfide comprising antimony, arsenic and the first metal, and the second metal concentrate having the at least one sulfide comprising the second metal; leaching the first metal concentrate to yield a further metal concentrate and a leach solution, the further metal concentrate comprising the first metal and the leach solution comprising soluble antimony and soluble arsenic; and one of: (i) oxidizing the leach solution to yield an antimony precipitate and an arsenic solution; (ii) forming a stable arsenic compound from the leach solution; and (iii) oxidizing the leach solution to yield an antimony precipitate and an arsenic solution, and forming a stable arsenic compound from the arsenic solution.
In an embodiment of the process, the mixed sulfide concentrate is subjected to flotation in which copper, antimony, and arsenic sulfides are floated and lead sulfide is depressed. The flotation yields a lead concentrate comprising the lead sulfide and a first copper concentrate comprising the copper, antimony, and arsenic sulfides. The first copper concentrate is then leached to yield a second copper concentrate comprising the copper sulfide, and a leach solution comprising soluble arsenic and antimony. The leach solution is oxidized to yield an antimony precipitate and an arsenic solution. In other embodiments, a stable arsenic compound is formed from the arsenic solution for disposal. In additional embodiments, the lead concentrate is, substantially free of the copper, arsenic and antimony sulfides and/or the second copper concentrate is substantially free of the arsenic and antimony.
In still other embodiments, a specific flotation process is provided. A mixed sulfide concentrate comprising lead, copper, antimony and arsenic sulfide is subjected to flotation. The process comprises subjecting the mixed sulfide concentrate to flotation using one or more of a sulfite salt and a caustic starch solution in which lead sulfide (e.g. galena) is depressed in comparison to the copper, antimony and arsenic sulfides. The flotation provides a lead concentrate separate from a first copper concentrate. The lead concentrate comprises the lead sulfide and the first copper concentrate comprises the copper, arsenic and antimony sulfides (e.g. copper sulfosalts). In additional embodiments, the lead concentrate is substantially free of the copper, arsenic and antimony sulfides.
In another embodiment, there is provided a process for separation of at least one metal sulfide from a mixed sulfide concentrate, the mixed sulfide concentrate having at least one sulfide comprising antimony, arsenic, and at least two metals, the at least two metals comprising a first metal and a second metal. The process comprises: subjecting the mixed sulfide concentrate to flotation using one or more of a sulfite salt and a caustic starch solution in which at least one sulfide comprising antimony, arsenic, and the first metal is floated and at least one sulfide comprising the second metal is depressed, the flotation yielding a first metal concentrate and a second metal concentrate, the first metal concentrate having the at least one sulfide comprising antimony, arsenic, and the first metal, and the second metal concentrate having the at least one sulfide comprising the second metal.
In still other embodiments, a process for leaching a first copper concentrate comprising copper, antimony and arsenic sulfides (e.g. copper sulfosalts) is provided. The first copper concentrate is leached in an alkaline environment to yield a second copper concentrate, and a first leach solution comprising soluble arsenic and antimony. The soluble antimony and arsenic are removed from the leach solution by crystallization. The leach solution is recovered for recycling. In other embodiments, the second copper concentrate is substantially free of the arsenic and antimony sulfides.
In another embodiment, there is provided a process for leaching a first metal concentrate having at least one sulfide comprising antimony, arsenic, and at least one metal. The process comprises: leaching the first metal concentrate to yield a further metal concentrate and a leach solution, the further metal concentrate comprising the first metal and the leach solution comprising soluble arsenic and soluble antimony; removing the soluble antimony and soluble arsenic from the leach solution by crystallization; and recovering the leach solution for recycling.
In still other embodiments, a process for separation of antimony and arsenic from a leach solution comprising soluble antimony and arsenic is provided. The soluble antimony and arsenic in the leach solution are oxidized to reach an oxidation endpoint determined by at least one of wavelength monitoring and oxidation reduction potential (ORP) monitoring, to yield soluble antimony and arsenic thiosalts. The soluble antimony and arsenic thiosalts are oxidized to yield an antimony precipitate and an arsenic solution.
In another embodiment, there is provided a process for separation of antimony and arsenic from a leach solution comprising soluble antimony and arsenic, the process comprising: oxidizing the soluble antimony and arsenic in the leach solution so as to reach an oxidation end point determined by at least one of wavelength monitoring and oxidation reduction potential (ORP) monitoring, to yield soluble antimony and arsenic thiosalts; and oxidizing the soluble antimony and arsenic thiosalts to yield an antimony precipitate and an arsenic solution.
In further embodiments, a stabilization process for an arsenic solution derived from a mixed sulfide concentrate is provided, where the mixed sulfide concentrate comprises lead, copper, antimony and arsenic sulfides. The process comprises forming a stable arsenic compound from the arsenic solution, at about atmospheric pressure (e.g. about standard atmospheric pressure), optionally, for disposal. Therefore, the stabilization process does not take place in an autoclave.
In another embodiment, there is provided a stabilization process for an arsenic solution derived from a mixed sulfide concentrate, the mixed sulfide concentrate having at least one sulfide comprising antimony, arsenic and at least one metal. The process comprises: forming a stable arsenic compound from the arsenic solution, at about atmospheric pressure.
In another embodiment, there is provided a stabilization process for an arsenic solution comprising thiosulfates. The process comprises: acidifying the arsenic solution to decompose the thiosulfates, to yield an acidified solution; oxidizing the acidified solution to oxidize residual As3+ to As5+ and reduced sulfur species to sulfates, to yield a slurry comprising elemental sulfur; separating elemental sulfur from the slurry to yield a liquid; oxidizing the liquid to oxidize residual reduced sulfur species, to yield an oxidized solution; and forming a stable arsenic compound from the oxidized solution.
In another embodiment, there is provided a stabilization process for an arsenic solution. The process comprises: oxidizing the arsenic solution to oxidize As3+ to As5+ and reduced sulfur species to sulfates, to yield an oxidized solution; and acidifying the oxidized solution to yield an acidified oxidized solution; and forming a stable arsenic compound from the acidified oxidized solution.
It is understood that, when used herein, that an autoclave is a pressurized vessel used for chemical reactions and other processes.
Turning now to
Process 20 comprises a plurality of sub-processes that are carried out generally in sequence to process a mixed-sulfide concentrate 22 for separating and recovering metal sulfides therefrom. The mixed-sulfide concentrate 22 is formed from ore using one or more processes known to those skilled in the art, and comprises lead, copper, antimony and arsenic sulfides, as well as other minerals and precious metals. More specifically, the mixed-sulfide concentrate 22 is lead-rich and predominantly comprises galena (PbS) and copper sulfosalts, with antimony and arsenic being present in the mixed-sulfide concentrate 22 in any molar ratio. Typically, the antimony and arsenic are present in the mixed-sulfide concentrate 22 in a molar ratio of about 0.5:1 to about 1.5:1, and more typically in a molar ratio of about 1:1. In the embodiment shown, the sub-processes include a concentrate enrichment flotation process 24, a concentrate enrichment leaching process 26, a leach solution recovery process 28, and a leach tails stabilization process 30.
Certain embodiments of the sub-processes are outlined below with respect to
In the cleaning conditioner 44, conditioning reagents are combined with the lead-deficient concentrates 42, 54 and 76 to form a secondary conditioner pulp 62 having a solids content of about 10% to about 20%, and having a pH of about 5.5 to about 7.5. The secondary conditioner pulp 62 is subjected to a cleaning process 64, where it undergoes further flotation. The cleaning process 64 may comprise a single cleaning flotation bank, or may comprise two or more cleaning flotation banks (not shown) connected in series, such that concentrate from each upstream bank is collected and transferred to the next bank downstream in the series, and tailings from each downstream bank are fed to the previous bank upstream in the series. As is known in the art, each flotation bank includes one or more flotation cells connected in series. Concentrate 66 from the cleaning process 64 is collected and subjected to solid-liquid separation 68 so as to yield a solid, first copper concentrate 70 (e.g. a “dirty” copper concentrate). The first copper concentrate 70 is substantially free of lead sulfide(s). Typically, at least about 50% of the original lead sulfide content of the mixed sulfide concentrate 22 has been removed, more typically, about 65% to about 98%; about 75% to about 96%, or about 85% to about 95% has been removed.
Tailings 72 from the cleaning process 64 are fed to a cleaner scavenger 74 where they undergo further flotation. The cleaner scavenger 74 yields a lead-deficient cleaner scavenger concentrate 76, which is collected and transferred to the cleaning conditioner 44 with the lead-deficient concentrates 42 and 54. The cleaner scavenger 74 also yields lead-rich rougher tailings 78, which are subjected to the solid-liquid separation 58 to remove liquid so as to yield the solid, clean lead concentrate 60.
The conditioning reagents used for the concentrate enrichment flotation process 24 comprise a collector, a frother, a depressant, and a dispersant. In this embodiment, the collector is a thionocarbamate, which is a poor collector for galena and is therefore suitable for selective flotation of copper sulfosalts in copper-lead concentrates. In this embodiment, the frother is methyl isobutyl carbinol, and the depressant is an ammonium bisulfite solution. The depressant is added to depress lead sulfide flotation, and the method of addition of the depressant is based on achieving a target pH in the pulp. In this embodiment, a caustic starch solution is used as the dispersant. The collector is added to the rougher and cleaning process 64, and may also be added to the scavenger conditioner 48 and the cleaner scavenger 74. The frother is added to the scavenger 52 and the cleaning process 64, and may also be added to the rougher. The depressant and the dispersant are added to the first conditioner 36, the cleaning conditioner 44, and to the cleaning process 64. The dispersant may also be added to the scavenger conditioner 48 and to the cleaner scavenger 74.
In this embodiment, the wash solution 114 from the filtrate wash process 110 is then subjected to an oxidation process 118, in which elemental sulfur (S0) is added to the wash solution 114 at an elevated temperature in order to oxidize (As3+) and (Sb3+) to (As5+) and (Sb5+), respectively, so as to yield an oxidized wash solution 120. The oxidation process 118 is carried out under about atmospheric pressure at a temperature of about 65° C. to about 75° C., as required for dissolution of elemental sulfur, and for a time of about 0.1 hours to about 1 hour. The oxidized wash solution 120 is then acidified in a first acidification process 122, in which silicon, aluminum and copper are precipitated to yield an acidified wash slurry 124. In this embodiment, during the first acidification process 122, sulfuric acid is added to the oxidized wash solution 120 to reduce the pH to about 9.0 to about 10.0, in order to induce precipitation of the silicon, aluminum and copper. The acidified wash slurry 124 is then subjected to solid-liquid separation 126 to yield a mixed silicon, aluminum and copper precipitate 130 and a solution 132. The solution 132 is then subjected to a gold recovery process 134, during which the solution 132 is passed through a strong base ion exchange resin for extraction of gold and/or other precious metals. Solution 138, which remains after gold recovery process 134, is then acidified in a second acidification process 140, in which arsenic and antimony are precipitated as their respective sulfides, and any remaining gold copper, selenium, mercury and other impurities are also precipitated, and in which hydrogen sulfide (H2S) gas 144 is evolved. In this embodiment, during the second acidification process 140, sulfuric acid is added to the solution 138 to reduce the pH to about 3.0 to about 4.0, in order to ensure precipitation of the arsenic and antimony sulfides. The H2S gas 144 evolved during the second acidification process 140 is passed through a caustic scrubber (not shown) to yield a sodium sulfide (Na2S) or sodium hydrosulfide (NaHS) product, which in the embodiment shown, is combined with leach reagents 88 in the repulp/solution preparation process 92, for recycling. As will be appreciated, the recycling of reagents reduces the cost of supplying reagents, and/or the cost of destruction of used reagents. The second acidification process 140 yields a slurry 142, which is subjected to solid-liquid separation 146 to yield the solids 96 and an acidified wash solution 148. The acidified wash solution 148 is advanced to crystal dissolution 164 where the remaining acid is neutralized, and the solids 96 are combined with the leach feed pulp 94 during the leaching process 98 to releach the contained arsenic and antimony sulfides.
The solids 162 remaining after the solid-liquid separation 160 are dissolved in water and the acidified wash solution 148 (or wash solution 114, acidified wash solution 432, acidified wash solution 538, acidified wash solution 634 or acidified wash solution 750, from process 326, 426, 526, 626 or 727, respectively, described below) during a dissolution process 164 to yield a solution 166 comprising dissolved sodium thioantimonate (Na3SbS4) and dissolved sodium thioarsenate (Na3AsS4). The solution 166 has a combined antimony and arsenic concentration of about 50 g/L to about 100 g/L, depending on water addition. The solution 166 is then transferred to a gold recovery process 168 in which gold and/or other precious metals are recovered. In this embodiment, during the gold recovery process 168, the solution 166 is passed through a filter to recover insoluble gold from the dissolution process 164. Solution 170 remaining after the gold recovery process 168 is then acidified in a first acidification process 172, in which an antimony sulfide product containing predominantly antimony pentasulfide (Sb2S5) is precipitated to yield a slurry 174 and to evolve hydrogen sulfide (H2S) gas 176. In this embodiment, during the first acidification process 172, sufficient sulfuric acid is added to the solution 170 to reduce the pH to about 13 to about 7, in order to induce precipitation of typically about 60% to about 80% of the contained antimony as antimony sulfide. After addition of the sulfuric acid, the slurry 174 is passed through a gas stripping tower (not shown), counter current to air, to remove any dissolved H2S gas. The H2S gas recovered from the solution is combined with the H2S gas 176 evolved during the first acidification process 172. The slurry 174 is then subjected to solid-liquid separation 178 to yield an antimony sulfide precipitate 180 and a solution 182. The solution 182 is then acidified in a second acidification process 184 to precipitate arsenic and antimony species, which may include generally all of the arsenic and antimony species, so as to yield an acidified slurry 186 and to evolve hydrogen sulfide (H2S) gas 188. In this embodiment, during the second acidification process 184, sulfuric acid is added to the solution 182 to reduce the pH to about 4.0. The evolved H2S gas 188 (which may be combined with the H2S gas 176 above) is passed through a caustic scrubber (not shown) to yield a sodium sulfide (Na2S) or sodium hydrosulfide (NaHS) product solution, which is combined with leach reagents 88 in the repulp/solution preparation process 92, for recycling. The acidified slurry 186 is passed through a gas stripping tower, counter current to air, to remove any dissolved H2S gas. The H2S gas recovered from the solution is combined with the H2S gas 188 evolved during the second acidification process 172. The acidified slurry 186 is then subjected to a sulfide oxidation process 190, in which the solution is made more basic through the addition of NaOH to dissolve the arsenic and antimony sulfide precipitate in slurry 186. Hydrogen peroxide (H2O2) is then added to oxidize the dissolved thiosalts. Any suitable oxidizing agent may be used. In this embodiment, sodium hydroxide having a concentration of typically 50 wt % is added until an endpoint pH of from about 10.0 to about 12.0 is reached, after which hydrogen peroxide having a concentration of 30% to 70% is added slowly over a time sufficient to oxidize the dissolved thiosalts completely or nearly completely, typically about 3 hours to about 6 hours. During the sulfide oxidation process 190, more sodium hydroxide is added to maintain the pH from about 10.0 to about 12.0 to prevent or reduce the formation of elemental sulfur. The sulfide oxidation process 190 is carried out at about atmospheric pressure, and advantageously does not require use of an autoclave. The sulfide oxidation process 190 yields a slurry 192 containing predominantly solid sodium antimony hydroxide (NaSb(OH)6) and soluble arsenate (AsO4−3). The slurry 192 is then subjected to solid-liquid separation 194 to remove solids using any combination of thickeners, filters, or other commercially available solid-liquid separation technologies, so as to yield a solid sodium antimony hydroxide product 196 and a residual solution 198. The sodium antimony hydroxide product 196 may undergo further processing to produce an antimony-containing product of suitable grade for commercial sale.
Other configurations are possible. For example,
In a related embodiment, the oxidation process 118 may alternatively be omitted from the process 426, in which case the wash solution 114 from the filtrate wash process 110 may alternatively be acidified in the acidification process 422.
In a related embodiment, the oxidation process 118 may alternatively be omitted from the process 526, in which case the wash solution 114 from the filtrate wash process 110 may alternatively be acidified in the acidification process 522.
In a related embodiment, the solids 632 may alternatively be advanced to the sulfide oxidation process 190, for example.
In a related embodiment, the oxidation process 118 may alternatively be omitted from the process 726, in which case the wash solution 114 from the filtrate wash process 110 may alternatively be acidified in the first acidification process 722.
As will be appreciated, the process for separation of metal sulfides is not limited to that described above, and in other embodiments the process may comprise one or more of the following sub processes: the concentrate enrichment flotation process 24, the concentrate enrichment leaching process 26, the leach solution recovery process 28, and the leach tails stabilization process 30.
For example, the process comprises the concentrate enrichment flotation process 24 described above, together with one or more other sub processes for processing and/or removal of copper, antimony and/or arsenic sulfides. In another related embodiment, the process comprises the concentrate enrichment flotation process 24 and the concentrate enrichment leaching process 26 described above, together with other sub processes for processing and/or removal of antimony and/or arsenic sulfides. In another related embodiment, the process comprises the concentrate enrichment flotation process 24 and the leach solution recovery process 28 described above, together with other sub processes for processing and/or removal of copper, antimony and/or arsenic sulfides. In another related embodiment, the process comprises the concentrate enrichment flotation process 24 and the leach tails stabilization process 30 described above, together with other sub processes for processing and/or removal of copper, antimony and/or arsenic sulfides. In another related embodiment, the process comprises the concentrate enrichment flotation process 24 and any two (2) of the concentrate enrichment leaching process 26, the leach solution recovery process 28, and the leach tails stabilization process 30 described above, together with one or more other sub processes for processing and/or removal of copper, antimony and/or arsenic sulfides.
In other embodiments, the process comprises the concentrate enrichment leaching process 26 described above, together with one or more other sub processes for processing and/or removal of lead, antimony and/or arsenic sulfides. In one related embodiment, the process comprises the concentrate enrichment leaching process 26 and the leach solution recovery process 28 described above, together with other sub processes for processing and/or removal of lead, antimony and/or arsenic sulfides. In another related embodiment, the process comprises the concentrate enrichment leaching process 26 and the leach tails stabilization process 30 described above, together with other sub processes for processing and/or removal of lead, copper, antimony and/or arsenic sulfides. In another related embodiment, the process comprises the concentrate enrichment leaching process 26 and any two (2) of the concentrate enrichment flotation process 24, the leach solution recovery process 28, and the leach tails stabilization process 30 described above, together with one or more other sub processes for processing and/or removal of lead, antimony and/or arsenic sulfides.
In other embodiments, the process comprises the leach solution recovery process 28 described above, together with one or more other sub processes for processing and/or removal of lead, copper, antimony and/or arsenic sulfides. In one related embodiment, the process comprises the leach solution recovery process 28 and the leach tails stabilization process 30 described above, together with other sub processes for processing and/or removal of lead, copper, antimony and/or arsenic sulfides. In another related embodiment, the process comprises the leach solution recovery process 28 and any two (2) of the concentrate enrichment flotation process 24, the concentrate enrichment leaching process 26 and the leach tails stabilization process 30 described above, together with one or more other sub processes for processing and/or removal of lead, copper, antimony and/or arsenic sulfides.
In other embodiments, the process comprises the leach tails stabilization process 30 described above, together with one or more other sub processes for processing and/or removal of lead, copper, antimony and/or arsenic sulfides.
As will be appreciated, the process for separation of metal sulfides is not limited to the specific metal sulfide embodiments described herein, but may be applied to any suitable separation of metal sulfide(s), including at least one sulfide having at least one metal and/or at least one semi-metal with use of the suitable process step(s) described herein.
Although various conditions and reagents (e.g. acids, bases, oxidizing agents etc.) are used, various changes and modifications may be made.
For example, although in embodiments described above, hydrogen peroxide is used as an oxidizing agent, in other embodiments, other oxidizing agents may alternatively be used, such as metal catalyzed quinones, including metal catalyzed hydroquinones and any other precursors that may generate hydrogen peroxide. As an example, copper catalyzed hydroquinone may alternatively be used as an oxidizing agent instead of, or in combination with, hydrogen peroxide. Those skilled in the art will appreciate that still other oxidizing agents may be used.
Although in the embodiments described above, the leach solution is monitored during the oxidation process by colorimetry to determine the endpoint of oxidation, in other embodiments, the leach solution may alternatively be monitored by another suitable method to determine the endpoint of oxidation.
Although in the embodiments described above, the frother is methyl isobutyl carbinol, in other embodiments, any frother(s) that are known in the art, which give(s) the recovery of the desired minerals, may alternatively be used. Furthermore, blends of such frothers may also be used.
Although in the embodiments described above, the collector is a thionocarbamate, in other embodiments, any collector that provides sulfosalt (e.g. copper sulfosalt) flotation may alternatively be used. For example, alkyl thionocarbamates and/or allyl alkyl thionocarbamates, including short- and long-chained alkyl thionocarbamates and allyl alkyl thionocarbamates, may be used.
Although in the embodiments described above, the depressant is an ammonium bisulfite solution, in other embodiments, any agent that depresses the flotation of galena in the presence of sulfosalts (e.g. copper sulfosalts) may alternatively be used. Suitable depressants include sulfite salts, such as sulfites, bisulfites, and metabisulfites.
Although in the embodiments described above, the dispersant is a caustic starch solution, in other embodiments, any agent that disperses sulfides may alternatively be used. It is understood that a caustic starch solution may include naturally occurring starch and/or synthetic starch, combined with any suitable base, such as sodium hydroxide.
Although in the embodiments described above, the gold recovery process comprises using a strong base ion exchange resin for extraction of gold and/or other precious metals, in other embodiments, the gold recovery process may alternatively comprise use of a precipitation process for extraction of gold and/or other precious metals. Other known precious metal recovery processes may also be used.
Although in the embodiments described above, the solids filtered by the filtration process are subjected to a sodium hydroxide (NaOH) filtrate wash process so as to yield a wash solution, in other embodiments, the solids filtered by the filtration process may alternatively be washed with another solution or with water, so as to yield the wash solution.
In understanding the scope of the present application, the term “comprising” and its derivatives, as used herein, are intended to be open ended terms that specify the presence of the stated features, elements, components, groups, integers, and/or steps, but do not exclude the presence of other unstated features, elements, components, groups, integers and/or steps. The foregoing also applies to words having similar meanings such as the terms, “including”, “having” and their derivatives. It will be understood that any aspects described as “comprising” certain components may also “consist of” or “consist essentially of,” wherein “consisting of” has a closed-ended or restrictive meaning and “consisting essentially of” means including the components specified but excluding other components except for materials present as impurities, unavoidable materials present as a result of processes used to provide the components, and components added for a purpose other than achieving the technical effect of the invention.
Terms of degree such as “about” and “approximately” as used herein mean a reasonable amount of deviation of the modified term such that the end result is not significantly changed. These terms of degree should be construed as including a deviation of at least ±5% of the modified term if this deviation would not negate the meaning of the word it modifies.
When introducing elements disclosed herein, the articles “a”, “an” and “the” are intended to mean that there are one or more of the elements.
The above disclosure generally describes the present invention. A more complete understanding can be obtained by reference to the following specific Examples. The Examples are described solely for purposes of illustration and are not intended to limit the scope of the invention. Changes in form and substitution of equivalents are contemplated as circumstances may suggest or render expedient. Although specific terms have been employed herein, such terms are intended in a descriptive sense and not for purposes of limitation.
In Examples 1 to 3, “locked cycle” flotation tests were performed to evaluate the removal and separation efficiency of arsenic and antimony containing sulfosalts from the mixed sulfide concentrate.
In this example, the test was performed on a high copper feed concentrate using four locked cycles with a rougher and three stages of cleaning. The collector was a thiocarbamate (Aero A5100), the depressant was sodium metabisulfite (SMBS), and the dispersant was a caustic starch solution.
The results of the test are shown in Table 1. About 89% of the lead reported to the lead concentrate, while about 80% of the copper, about 82% of the arsenic and about 91% of the antimony reported to the copper concentrate.
In this example, a “locked cycle” flotation test was performed on a lower copper feed concentrate than the concentrate of Example 1, using six locked cycles with a rougher and three stages of cleaning. In this example, the collector was Aero A5100, the depressant was SMBS, and the dispersant was a caustic starch solution.
The results of this test are shown in Table 2. About 99% of the lead reported to the lead concentrate, while about 78% of the copper, about 84% of the arsenic and about 74% of the antimony reported to the copper concentrate.
In this example, a “locked cycle” flotation test was performed on a similar feed material to Example 2, using six locked cycles with a rougher and three stages of cleaning. In this example, the collector was Aero A5100, the depressant was ammonium bisulfite, and the dispersant was a caustic starch solution.
The results of this test are shown in Table 3. About 97% of the lead reported to the lead concentrate, while about 84% of the copper, about 86% of the arsenic and about 81% of the antimony reported to the copper concentrate.
In Examples 4 and 5, a locked cycle test was performed using repulp/solution preparation process 92, leaching process 98, filtration process 104, filtrate wash process 110, oxidation process 152, crystallization process 156, and solid-liquid separation 160, and with solution 90 being returned to the repulp/solution preparation process 92 for the next cycle. Twenty six cycles were performed in total. Two concentrate samples were used in this test, namely Concentrate 1 (cycles 1 to 18) and Concentrate 2 (cycles 19 to 26), with each concentrate sample comprising 1 kg of first copper concentrate from the concentrate enrichment flotation process 24. More specifically, Concentrate 1 was a composite sample of twelve (12) individual concentrates. The twelve (12) individual concentrates used to generate Concentrate 1 were determined to contain arsenic and antimony primarily as tetrahedrite and tennantite, with minor amounts of bournonite, freibergite, boulangerite and enargite being present. The compositions of Concentrate 1 and Concentrate 2 are provided in Table 4.
During repulp/solution preparation process 92, each concentrate was combined with about 4 kg of leach solution (specifically, fresh leach solution for the first cycle, and recycled leach solution from solid-liquid separation 160 for the subsequent cycles), to make a slurry with about 20 wt % solids. The leach solution recycled from solid-liquid separation 160 was analyzed and weighed, and the required amounts of sodium sulfide (Na2S.3H2O), sodium hydroxide (NaOH) and water were added to yield a solution containing about 120 g/L sulfide and about 40 g/L sodium hydroxide.
The slurry was then heated to about 100° C. and held at that temperature for about six hours to carry out leaching process 98. After the six hours, the slurry was filtered, and the primary filtrate was recovered and kept above about 70° C. prior to oxidation process 152. The solids were washed, during filtrate wash process 110, with about 1.5 L of water containing about 0.05 M NaOH using a two stage counter current wash procedure.
Chemical analysis results of the two composite concentrate samples are shown in Table 4. About 98% of the arsenic and about 96% of the antimony was leached from the concentrate samples.
In this example, the primary filtrate (leach solution 106) recovered after each leach cycle in Example 4 and kept at above about 70° C., was subjected to oxidation process 152, during which elemental sulfur was added until the color changed from yellow-green to orange-red. ORP values were observed to increase by about 150 mV, which indicated that ORP could have readily been used to measure the endpoint of oxidation.
Following oxidation, the solution was cooled to about 40° C. and held at that temperature for about 30 to about 60 minutes during crystallization process 156, to allow crystallization of the soluble arsenic and antimony as sodium thioarsenate and sodium thioantimonate. For the 26 cycles performed in the test, about 19.15 kg of wet crystals were recovered assaying about 6.2 wt % arsenic and about 12.1 wt % antimony. After crystallization, the solution 90 typically assayed about 30 to about 40 g/L arsenic and about 5 to about 15 g/L antimony.
In this example, a test was carried out in which about 200 g of crystals was dissolved in about 600 g of water, in order to determine the ability to selectively precipitate antimony sulfide (Sb2S5) from the dissolved crystals. Acid was added until precipitation was observed, at which point the solution was filtered and the precipitate analyzed. A further about 5 mL of acid was then added to the filtrate and, after a short equilibration period, the solids were again removed by filtration; this procedure was repeated until the pH dropped below about 5.0.
The results of this test are shown in Table 5. About 63% of the antimony was precipitated at an arsenic grade of about 0.5 wt %, while about 92% of the antimony was precipitated at an arsenic grade of about 1.0 wt %.
In this example, the crystals generated in the locked cycle test of Examples 4 and 5 were subjected to first acidification process 172 to generate a sulfide precipitate containing predominantly antimony sulfide (Sb2S5). Here, about five (5) kg of wet crystal was dissolved in about 15 L of water, and the resulting solution was filtered and acidified with concentrated sulfuric acid. After completing acid addition, the slurry was sparged for about 30 minutes to remove dissolved hydrogen sulfide gas. Throughout the test, air was pulled through the reactor headspace and was released to atmosphere via a single stage scrubber filled with about 50% sodium hydroxide solution.
As the antimony started to precipitate, the pH and ORP were observed to become stable. As will be understood, the system was buffered at this pH by the NaHS/H2S equilibrium and the slow rate of acid addition. After acid had been added, the pH moved back towards about pH 7 as the system returned to equilibrium.
Following acidification, the slurry was subjected to filtration. Solids recovered after the filtration assayed about 40 wt % antimony, about 33.5 wt % sulfur, and about 1.6 wt % arsenic. Approximately 65% of the antimony and approximately 5% of the arsenic was recovered from the feed solution.
In this example, about 200 g of crystal was dissolved in about 600 mL of water. After filtration, the solution was subjected to sulfide oxidation process 990, in which about 30% hydrogen peroxide was added to the solution until the target ORP was reached. The sulfide oxidation process was carried out both with pH control at pH of about 10, and without any pH control. The precipitate formed during each test was separated from the solution, washed and analyzed. The results are shown in Table 6. The results indicate that pH control was important in limiting elemental sulfur precipitation into the product.
Prior to arsenic stabilization, the arsenic solution (solution 198) is conditioned to ensure all of the arsenic and sulfur species are fully oxidized. In this example, an arsenic solution was acidified to a pH less than about 2.0 at about 80° C. The acidification generated elemental sulfur from decomposition of thiosulfate in the solution. Hydrogen peroxide was then added to increase the ORP to above approximately 600 mV, at which point oxidation of the solution was essentially complete, and therefore that the oxidized solution was a suitable feed for the arsenic stabilization process 220.
In this example, a continuous arsenic stabilization test was run on a solution generated by processing dissolved crystal from the locked cycle test of Examples 4 and 5 through first acidification process 172, sulfide oxidation process 190 and arsenic solution conditioning 1002. Ferric sulfate was then added to the acidified oxidized solution 1004 (hereafter the “feed solution”, in this example) to achieve a ferric to arsenic molar ratio of about 1.05. Analysis of the feed solution showed about 11 g/L arsenic, about 9 g/L iron, and about 60 g/L sodium. In this example, the sodium concentration in the solution was much higher than in conventional feed solutions for conventional arsenic stabilization processes due to the existence of sodium in the crystals, and due to the further addition of sodium hydroxide throughout the process.
The test was run continuously for about 26 hours, and included three stages of arsenic precipitation followed by one stage of arsenic polish. Each stage was carried out in a respective reactor. The operating conditions were as follows:
During the test, about 6.3 L of feed solution was treated. The polish slurry discharge was collected and combined with contents of the polish reactor at the end of the test, to constitute a discharge composite sample.
Solution profile sampling was conducted every two hours. The results showed consistent operation once equilibrium had been established, with the arsenic concentration being reduced from about 11 g/L in the feed solution to about 2.5 g/L in the first reactor, to about 0.9 g/L in the second reactor, to about 0.5 g/L in the third reactor. The arsenic concentration in the polish slurry discharge was less than about 2 mg/L. At the end of the test, the discharge composite sample was assayed and was found to contain about 6.4 wt % arsenic, about 6.0 wt % iron, and only about 0.2 wt % sodium. The solids passed TCLP for arsenic with an assay of less than 1.0 mg/L (target: less than about 5 mg/L).
Although embodiments have been described above with reference to the accompanying drawings, those of skill in the art will appreciate that variations and modifications may be made without departing from the scope thereof as defined by the appended claims.
The description as set forth is not intended to be exhaustive or to limit the scope of the invention. Many modifications and variations are possible in light of the above teaching without departing from the spirit and scope of the following claims. It is intended that the scope of the present invention be defined by the claims appended hereto, giving full cognizance to equivalents in all respects.
The present application is a divisional application of U.S. patent application Ser. No. 15/850,849, filed on Dec. 21, 2017, which a divisional application of U.S. patent application Ser. No. 15/115,142, filed on Jul. 28, 2016, which is a national stage application of PCT Patent Application No. PCT/CA2015/000050, filed Jan. 30, 2015, which claims priority to U.S. Provisional Patent Application Ser. No. 61/934,193, filed Jan. 31, 2014, the contents of each of which are hereby incorporated by reference in their entireties.
| Number | Date | Country | |
|---|---|---|---|
| 61934193 | Jan 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15850849 | Dec 2017 | US |
| Child | 16448226 | US | |
| Parent | 15115142 | Jul 2016 | US |
| Child | 15850849 | US |