Process for the chemical recycling of polycarbonates

Abstract

The invention relates to a process for the chemical recycling of polycarbonates by catalyzed reaction with diaryl carbonates to oligocarbonates which are crystallized, purified and then polycondensed back to polycarbonates, insoluble constituents optionally being removed before the crystallization step.

Description

Claims

1. A process for the chemical recycling of thermoplastic aromatic polycarbonates comprising degrading said polycarbonates having molecular weights Mw from 15,000 to 80,000, with diaryl carbonates, in a molar ratio of polycarbonate to diaryl carbonate between 1:0.05 and 1:3.5, at temperatures of 120.degree. C. to 320.degree. C. to oligocarbonates having a Mw from about 500 to 10,000 in the presence of catalysts, in quantities of 0.00005 to 10% by weight, based on the total quantity by weight of polycarbonate to be degraded, and crystallizing the oligocarbonates, purifying them and then polycondensing them back to thermoplastic polycarbonates, the polycondensation of the oligocarbonates to the polycarbonates being carried out at 100.degree. to 400.degree. C.

2. A process according to claim 1, characterized in that the catalysts are used in quantities of 0.0001 to 5% by weight, based on the total quantity by weight of polycarbonate to be degraded.

3. A process according to claim 1, characterized in that for promoting the polycondensation reaction the terminal OH to aryl carbonate group ratio of the reactants is of >25% OH:<75% aryl carbonate to <50% OH:>50% aryl carbonate.

4. A process according to claim 1, wherein the insoluble constituents are removed before the crystallization step.

5. A process according to claim 1, wherein the Mw of the oligocarbonates is in the range of about 1,000 to 7,000.