The present invention relates to methods for producing aligned carbon nanotubes, and more particularly to methods and apparatus for continuous production of aligned carbon nanotubes. The invention further relates to methods and apparatus for continuous production of aligned carbon nanotubes which do not require patterned substrates, and which further produce quantities of high quality, homogenous populations of aligned nanotubes.
Aligned carbon nanotubes have application in numerous areas of composite materials, such as for use in separation media, as catalysts, as catalyst supports, in energy storage and transfer, in electronics applications such as in electron guns for use, e.g., in flat panel television picture technology, for EMI and RF shielding such as in the cellular telephone industry, as sensors or sensor components, and for use in electronically conductive plastics. Currently utilized technologies for production of aligned carbon nanotubes are labor intensive, costly, inefficient, and are not amenable to scale-up for industrial applicability.
The synthesis of aligned carbon nanotubes, such as multi-walled carbon nanotubes, via catalytic pyrolysis of hydrocarbons is known. Most of the known methodology for such synthesis requires use of patterned or preformed substrates to provide support to the growing nanotubes, allowing growth in an aligned pattern. Further, the presently utilized methods for synthesis of aligned carbon nanotubes rely on batch processes. While effective, batch processing methods for production of carbon nanotubes, particularly aligned carbon nanotubes, are labor intensive, costly, inefficient, and generally limited in production capacity at the industrial scale. Further, batch processing techniques may result in significant batch to batch variation in the quality of the nanotubes produced.
Accordingly, there is a need in the art for methods of production of carbon nanotubes which result in a high quality, homogenous population of aligned nanotubes. There is further a need in the art for such methods, and for apparatus for conducting the methods, which do not require specialized patterned substrates. The methods should reduce the labor required, and be amenable to scale-up for use in industrial applications requiring reproducibility, low cost, high volume, and a high quality product.
In accordance with the purposes of the present invention as described herein, a novel method for continuous production of aligned carbon nanotubes is described, beginning with dissolving a metal catalyst in a liquid hydrocarbon source to form a feed solution and dispersing the feed solution into a stream of an inert carrier gas. Metal catalyst may be admixed with said liquid hydrocarbon to yield a metal to carbon ratio of from about 0.075 atomic percent to about 1.25 atomic percent. In one embodiment, metal catalyst is admixed with said liquid hydrocarbon to yield a metal to carbon ratio of 0.75 atomic percent. Suitable metal catalysts include the group consisting of ferrocene, nickelocene, cobaltocene, manganocene, ruthenocene, iron napthenate, nickel napthenate, cobalt napthenate and any mixture thereof.
Any liquid hydrocarbon capable of being vaporized at a temperature of up to about 600 C and having a solubility of at least 0.5 weight percent for the metal catalyst selected may be used in the method of the present invention. This includes aromatic hydrocarbons, aliphatic hydrocarbons, substituted hydrocarbons, and nitrogen-containing hydrocarbons. The liquid hydrocarbon may be selected from the group consisting of xylene, toluene, benzene, hexane, pyridine, acetonitrile, or any combination thereof. Any known inert carrier gas is suitable, including the noble (Group VIII) gases, nitrogen, or mixtures thereof. Specific examples include argon, helium, nitrogen, and any combination. In a preferred embodiment, hydrogen is included in the inert carrier gas at a concentration of up to 30 volume percent. In a particularly preferred embodiment, the inert carrier gas stream contains hydrogen in a concentration of 10 volume percent.
The dispersed feed solution is then volatilized in a reactor. The reactor may be maintained at a temperature of from about 500 C to about 1000 C In one embodiment, the reactor is maintained at a temperature of from about 650 C to about 850 C Of course, those of skill in the art will realize that the optimal reactor temperature will depend on the volatilization temperature of the metal catalyst/liquid hydrocarbon feed solution of choice.
The rate at which the feed solution is delivered into the reactor is dependant on the metal catalyst concentration, reactor temperature, and gas flow rate. However, for optimal production of aligned carbon nanotubes, it is desirable to deliver the feed solution below the partial pressure (carbon) that elicits the co-generation of amorphous or pyrolytic carbon. The feed solution dispersed in inert carrier gas may be delivered into the reactor at a partial pressure (carbon) of from about 4 millibar to about 400 millibar. In one embodiment, the feed solution is delivered into the reactor to maintain a partial pressure of carbon of from about 48 millibar to about 380 millibar. Preferably, an oxygen- and ambient air-free environment is maintained within the reactor. This may be accomplished by any known means, such as for example a nitrogen purge box or a gas curtain placed at an opening of the reactor.
Concurrently therewith, a suitable substrate is continuously passed through the reactor to allow growth of aligned carbon nanotubes thereon. Substrate materials which do not have substantial carbon solubility at temperatures below 900 C are preferred. Any suitable substrate for promoting the growth of carbon nanotubes may be employed, preferably an inert glass or metal with thermal stability at a temperature of from about 500 C to about 900 C Suitable substrates include quartz, stainless steel, silicon, n-doped silicon, p-doped silicon, titanium nitride, and any mixture thereof. In a preferred embodiment of the present invention, the residence time of the substrate within the reactor is from about 10 minutes to about 180 minutes.
In another aspect of the method of the present invention, a method for continuous production of aligned carbon nanotubes with a tightly controlled range of external diameters is disclosed. Surprisingly, it has been discovered that the external diameter of aligned carbon nanotubes produced in accordance with the method of the present invention may be controlled by passing the metal catalyst/liquid hydrocarbon feed solution dispersed in the inert carrier gas through tubing of a particular inner diameter, followed by passing the feed solution through an inert, porous medium prior to delivery into the reactor. The inert, porous medium may be fabricated from any suitable inert powdered metal or ceramic, including any of the transition element metals or alloys thereof, as well as alumina, zirconia, silicon carbide, or silica ceramics. Specific examples include, but are not limited to, ceramic, alumina, steel, stainless steel, nickel, titanium, nickel-chromium alloys, or mixtures thereof. In a preferred embodiment, the inert, porous medium contains pores of from about 0.1 μm to about 1 μm in diameter. The final step is to mechanically recover the aligned carbon nanotubes from the substrate, for example by scraping, brushing, or ultrasonic cleaning. Process gases may be vented, or in a preferred embodiment are recycled through the reactor to preserve the concentration of hydrogen in the carrier gas.
In yet another aspect of the present invention, an apparatus for continuous production of aligned carbon nanotubes is taught, comprising a reactor, an injector for delivering a feed solution dispersed in an inert carrier gas into the hollow interior of the reactor, and a conveyor for continuously passing a substrate through the reactor at a controlled speed. It is preferred to exclude ambient air from the interior of the reactor during the reaction process. Those of skill in the art will appreciate that the reactor and conveyor may be fabricated from any suitably inert material which substantially prevents carbon nanotube growth thereon. In that way, nanotube growth is concentrated on the substrate passing through the reactor. Any suitably non-reactive metal or ceramic may be utilized, such as alumina, silicon carbide, Nichrome, and any combination. In accordance with the method of the present invention already disclosed, it will be appreciated that the conveyor is configured to pass the substrate through the reactor at a speed which provides a substrate residence time of from about 10 minutes to about 180 minutes.
The injector of the present invention comprises a tube-within-a-tube design configured for improved flow characteristics and feed consistency of the feed solution/carrier gas stream entering the reactor. In a presently preferred embodiment, the injector comprises a first hollow tube for delivering the feed solution as described supra and a second hollow tube for delivering the inert carrier gas. The first hollow tube is disposed in the interior of the second hollow tube, thereby defining an annulus between the first and second hollow tubes through which the inert carrier gas may be delivered. The end of the second tube extends beyond the corresponding end of the first tube, thereby defining a dispersion chamber wherein the feed solution is dispersed into the inert carrier gas prior to entry into the reactor.
Preferably, the first hollow tube has an outer cross-sectional area of from about 50 percent to about 90 percent of the internal cross-sectional area of the second hollow tube. In a preferred embodiment, the carrier gas is delivered through the annulus between the tubes at a Reynold's number of between about 1 and about 2000. In a particularly preferred embodiment, the carrier gas is delivered through the annulus at a Reynold's number of between about 50 and about 200. The dimensions of the first and second tubes, and their orientation relative to one another, may be configured such that the dispersion chamber formed thereby preferably has a length of from about 1 to about 15 times its diameter. In one embodiment, the length of the dispersion chamber is from about 8 to about 10 times its diameter.
As noted above, in one aspect of the method of this invention the catalyst/hydrocarbon/carrier gas dispersion may be passed through an inert, porous medium prior to entry into the reactor to control the external diameter of nanotubes formed thereby. Accordingly, the apparatus of the present invention preferably includes such an inert, porous medium terminal to the injector, in the form of a sinter fabricated from materials including, but not limited to, transition metals and their alloys, alumina, zirconia, silicon carbide, or silica ceramics. Specific examples include ceramic, alumina, steel, stainless steel, titanium, and any combination thereof. The sinter is selected to include a poresize of from about 0.1 μm to about 1 μm in diameter.
The injector of the present invention may be adapted for displacement within the reactor. As will be appreciated by those skilled in the art and as is further described below, this feature obviates the need for multiple reactors of different temperatures, such as for example a preheater followed by a reactor providing the desired temperature. Rather, the displaceable injector of the present design allows use of a single reactor, in which the feed solution/carrier gas may be delivered to any desired temperature zone. Thus, if the injector is displaced to a lower temperature zone of the reactor, a preheating step may be accomplished. Displacing the injector to a higher temperature zone of the reactor will allow the desired volatilization and nanotube-growing steps to occur. Accordingly, an actuator for displacing the injector within the reactor may be included in the apparatus of this invention. In one embodiment, an actuator is selected which allows displacing the injector along a longitudinal axis of the reactor. It will be appreciated that any suitable actuator capable of displacing the injector in a controlled fashion may be employed, such as a hydraulic or pneumatic cylinder, a rod-type electric cylinder, a belt-driven actuator, a ball screw-driven actuator, a robotic arm, or the like. The actuator may be coupled to a controller for remote operation. The injector may be supported by any suitable support, such as for example a linear guide having rollers.
It is known that the reaction by which carbon nanotubes are formed are preferably conducted in the absence of ambient air and oxygen. Accordingly, the apparatus of the present invention may include a means for excluding ambient air from the interior of the reactor. This feature may be accomplished by known devices, such as a nitrogen purge box or gas curtain adjacent an opening to the interior of the reactor.
In still yet another aspect of the present invention, a novel injector for use in continuous production of aligned carbon nanotubes is taught. As noted above, the injector is a tube-within-a-tube design including a first hollow tube for delivering the feed solution disposed within a second hollow tube for delivering the carrier gas, an annulus between the tubes through which the inert carrier gas is delivered. An end of the second tube extends beyond the corresponding end of the first tube, thereby defining a dispersion chamber wherein the feed solution is dispersed into the inert carrier gas prior to exiting the injector. The injector may further include an inert, porous medium terminal to the dispersion chamber for restricting the external diameter range of nanotubes formed thereby as described above. The preferred dimensions and suitable materials for fabrication of the components of the injector have been described above. While the injector as described is suitable for accomplishing the methods of the present invention as disclosed, it will be appreciated that the injector is also suitable for growth of aligned carbon nanotubes by other procedures, such as traditional batch processes.
In still yet another aspect of the present invention, a method of controlling the external diameter of carbon nanotubes produced by chemical vapor deposition is disclosed, comprising the steps of dissolving a metal catalyst in a liquid hydrocarbon source to form a feed solution, dispersing the feed solution in an inert carrier gas in a dispersion chamber, passing the feed solution/inert carrier gas dispersion through injector tubing of a desired inner diameter, and passing the feed solution through an inert, porous medium. The next step is to volatilize the feed solution in a reactor, while concurrently continuously passing a substrate through the reactor to allow growth of aligned carbon nanotubes thereon, and recovering the aligned carbon nanotubes from the substrate.
Suitable dimensions and materials for fabrication of components necessary for accomplishing the method for restricting external diameter of aligned carbon nanotubes grown thereby are as disclosed supra. It will be appreciated that the method as described is also suitable for restricting external diameter of carbon nanotubes grown in traditional batch procedures. In accordance with the injector tubing and pore size of the porous medium selected, growth of aligned carbon nanotubes having external diameters of from about 4 nm to about 300 nm is possible by the method herein disclosed.
Other objects and applications of the present invention will become apparent to those skilled in this art from the following description wherein there is shown and described a preferred embodiment of this invention, simply by way of illustration of the modes currently best suited to carry out the invention. As it will be realized, the invention is capable of other different embodiments and its several details are capable of modification in various, obvious aspects all without departing from the invention. Accordingly, the drawings and descriptions will be regarded as illustrative in nature and not as restrictive.
The accompanying drawing incorporated in and forming a part of the specification illustrates several aspects of the present invention and, together with the description, serves to explain the principles of the invention. In the drawing:
a and 3b are scanning electron micrograph (SEM) images showing aligned carbon nanotubes produced by the method of the present invention;
a and 5b are scanning electron micrograph (SEM) images showing aligned carbon nanotubes produced by the method of the present invention, at a feed solution delivery rate (partial pressure of carbon) of 250 mbar (
Reference will now be made in detail to the presently preferred embodiments of the invention, examples of which are illustrated in the accompanying drawing.
As summarized above, the present invention relates to novel methods and apparatus for continuous production of aligned carbon nanotubes. The methods and compositions of the present invention may be accomplished by various means which are illustrated in the examples below. These examples are intended to be illustrative only, as numerous modifications and variations will be apparent to those skilled in the art.
In one aspect, a novel method for continuous production of aligned carbon nanotubes is described, beginning with dissolving a metal catalyst in a liquid hydrocarbon source to form a feed solution and dispersing the feed solution into a stream of an inert carrier gas. In a preferred embodiment, metal catalyst is admixed with said liquid hydrocarbon to yield a metal to carbon ratio of from about 0.075 atomic percent to about 1.25 atomic percent. In an especially preferred embodiment, metal catalyst is admixed with said liquid hydrocarbon to yield a metal to carbon ratio of 0.75 atomic percent. Suitable metal catalysts include the group consisting of ferrocene, nickelocene, cobaltocene, manganocene, ruthenocene, iron napthenate, nickel napthenate, cobalt napthenate and any mixture thereof. In a preferred embodiment of the method of this invention, ferrocene is selected as the metal catalyst.
Any liquid hydrocarbon capable of being vaporized at a temperature of up to about 600 C and having a solubility of at least 0.5 weight percent for the metal catalyst selected may be used in the method of the present invention. Accordingly, it will be appreciated that the method for producing aligned carbon nanotubes of the present invention may be conducted at relatively moderate temperatures, and at atmospheric pressure, thereby reducing energy consumption and production costs and further enhancing the commercial utility thereof. Suitable liquid hydrocarbons include aromatic hydrocarbons, aliphatic hydrocarbons, substituted hydrocarbons such as halides, light elements, oxygen, and the like, nitrogen-containing hydrocarbons, or combinations or admixtures thereof. In one embodiment, the liquid hydrocarbon may be xylene, toluene, benzene, hexane, pyridine, acetonitrile, or any combination thereof. The carrier gas may be selected from the noble (Group VIII) gases, nitrogen, or mixtures thereof. Typical examples include argon, helium, nitrogen, and any combination thereof. It is preferred to include hydrogen in the inert carrier gas at a concentration of up to 30 volume percent. In a particularly preferred embodiment, hydrogen is included in the carrier gas stream at a concentration of 10 volume percent.
The dispersed feed solution is then volatilized in a reactor. Suitable reactor designs for producing carbon nanotubes are known in the art. The reactor may be maintained at a temperature of from about 500 C to about 100 C In one embodiment, the reactor is maintained at a temperature of from about 650 C to about 850 C. Those of skill in the art will realize that the optimal reactor temperature selected will depend on the temperature required to volatilize the particular metal catalyst/liquid hydrocarbon dispersion selected. The relatively moderate temperature at which the reaction may be conducted contributes to the commercial desirability of this method.
The rate at which the feed solution is delivered into the reactor is dependant on the reactor dimensions, metal catalyst concentration, and reaction conditions such as the reactor temperature and gas flow rate. Desirably, the feed solution is delivered into the reactor at a flow rate below the partial pressure (carbon) that elicits the co-generation of amorphous or pyrolytic carbon under the particular run conditions of choice. The feed solution dispersed in inert carrier gas may be delivered into the reactor at a partial pressure (carbon) of from about 4 millibar to about 400 millibar. In one embodiment, the feed solution may be delivered at a partial pressure (carbon) of from about 48 millibar to about 380 millibar. An oxygen- and ambient air-free environment may be maintained within the reactor by any desired means, such as a nitrogen purge box or a gas curtain placed at an opening of the reactor.
In the next step, suitable substrate materials may be continuously passed through the reactor to allow growth of aligned carbon nanotubes thereon. Any suitable substrate for promoting the growth of carbon nanotubes may be employed, preferably materials not having substantial carbon solubility at temperatures below 900 C It is preferred to utilize an inert glass or metal exhibiting thermal stability at a temperature of from about 500 C to about 900 C in accordance with the temperature range achievable by the reactor. Suitable substrates include quartz, stainless steel, silicon, n-doped silicon, p-doped silicon, titanium nitride, or combinations thereof. To allow the desired level of nanotube growth, the residence time of the substrate within the reactor may be set at from about 10 minutes to about 180 minutes, in accordance with the physical dimensions of the reactor. The final step is to mechanically recover the aligned carbon nanotubes from the substrate for subsequent processing and/or use. Process gases may be vented, or in a preferred embodiment are recycled through the reactor while preserving the concentration of hydrogen in the carrier gas.
Referring now to
In accordance with the method of the present invention already disclosed, it will be appreciated that the conveyor 28 is configured to pass the substrate 30 through the reactor 20 at a speed which provides a substrate residence time of from about 10 minutes to about 180 minutes, thereby optimizing growth conditions. The optimal substrate residence time, of course, will depend on variables such as the physical dimensions and temperature of the reactor 20, the volatilization characteristics of the feed solution of choice, and the like.
An insert (not shown), generally having the shape of an inverted “D”, may be included within the hollow interior 26 of the reactor 20 to provide support for the conveyor 28. However, it will be appreciated that any support means for the conveyor 28 may be adapted, such as a roller and track system (not shown) attached to the interior 26 of the reactor 20, or alternatively rollers 33 exterior of the reactor 20 as depicted in
The injector 21 of the present invention, as best seen in
Preferably, the first hollow tube 36 has an outer cross-sectional area of from about 50 percent to about 90 percent of the internal cross-sectional area of the second hollow tube 38. To assure laminar flow characteristics of the feed solution 22/carrier gas 24 entering the reactor 20, the carrier gas 24 is delivered through the annulus 40 at a flow rate resulting in a Reynold's number of between about 1 and about 2000. In a particularly preferred embodiment, the carrier gas is delivered through the annulus 40 to provide a Reynold's number of between about 50 and about 200.
The dimensions of the first and second tubes 36, 38, and their relative orientation, will primarily be determined by the size of reactor 20 employed. In general, the dimensions of the first and second tubes 36, 38, and their relative orientation are configured such that the dispersion chamber 42 formed thereby has a length of from about 1 to about 15 times its diameter. In one embodiment, the length of the dispersion 42 chamber is from about 8 to about 10 times its diameter. While the injector 21 as described is suitable for accomplishing the method of continuous production of aligned carbon nanotubes of the present invention as described, it will be appreciated that the injector 21 is also suitable for traditional batch processes for the growth of carbon nanotubes.
It is known to provide internal temperature zones having differing temperatures in standard reactors for use in production of carbon nanotubes by chemical vapor deposition. To provide such temperature zones, a single temperature controller 31 may be provided as shown in
An apparatus 10 for continuous production of aligned carbon nanotubes was constructed in accordance with the foregoing disclosure, and is schematically depicted in
Argon/hydrogen carrier gas 24 flow was initiated and brought to 1200 sccm (1080 sccm Ar, 120 sccm H2). Feed solution 22 was delivered into the reaction zone at a flow rate of 2.70 ml/h−1. A conveyor 28 as shown in
As seen in
In another aspect of the method of the present invention, a method for continuous production of aligned carbon nanotubes having a tightly controlled range of external diameters is disclosed. Surprisingly, it has been discovered that the external diameter of aligned carbon nanotubes produced in accordance with the method of the present invention may be controlled by regulating the inner diameter of the injector tubing through which the feed solution dispersed in the inert carrier gas is passed to improve yield and selectivity, followed by passing the feed solution through an inert, porous medium prior to delivery into the reactor. Referring to
The inert, porous medium may be fabricated from any suitable inert powdered metal or ceramic, including the transition element metals and alloys thereof, as well as alumina, zirconia, silicon carbide, or silica ceramics. Specific examples include, but are not limited to, ceramic, alumina, steel, stainless steel, nickel, titanium, nickel-chromium alloys, and any mixture thereof. In a preferred embodiment, the inert, porous medium contains pores of from about 0.1 μm to about 1 μm in diameter.
The method of controlling the external diameter of carbon nanotubes of this invention therefore comprises the steps of: (1) dissolving a metal catalyst in a liquid hydrocarbon source to form a feed solution; (2) dispersing the feed solution in an inert carrier gas in a dispersion chamber; (3) passing the feed solution/inert carrier gas dispersion through an inert, porous medium of the disclosed poresizes; (4) volatilizing the feed solution in a reactor; (5) continuously passing a substrate through the reactor to allow growth of aligned carbon nanotubes thereon; and (6) recovering the aligned carbon nanotubes from the substrate.
Suitable dimensions and materials for fabrication of components necessary for accomplishing the method for restricting external diameter of aligned carbon nanotubes grown in a continuous process are as disclosed supra. However, it should be appreciated that the method as described is also suitable for restricting external diameter of carbon nanotubes grown in traditional batch procedures. In accordance with the pore size of the porous medium selected, growth of aligned carbon nanotubes having homogenous external diameters of from about 4 nm to about 300 nm is made possible by the method herein disclosed.
The apparatus of this invention was prepared substantially as described in Example 1, with the exception that a batch procedure for production of aligned carbon nanotubes was conducted rather than the continuous procedure of Example 1. All other conditions were maintained as in Example 1. The feed solution as disclosed in Example 1 was passed through stainless steel sinters as described herein, placed terminally on the injector adjacent the dispersion chamber. Sinters having poresizes of 0.2 μm and 0.5 μm were compared to negative controls (no sinter). Feed solution composition and run conditions were as described for Example 1, with the exception of use of a batch procedure.
As seen in
A device 10 for continuous production of aligned carbon nanotubes was constructed in accordance with the method and apparatus previously described in Examples 1 and 2, and substantially as depicted in
a and 5b show examples of aligned carbon nanotubes produced according to the method of the present invention, providing for demonstration purposes aligned carbon nanotubes produced at a feed solution delivery rate (partial pressure of carbon) of 250 mbar (
As described herein and demonstrated in the foregoing examples, the present invention provides numerous advantages over currently employed batch processing methods. The method significantly reduces labor required, and allows rapid synthesis of aligned carbon nanotubes without need for use of specially patterned substrates. In contrast to batch processing techniques, batch to batch variation in quality is reduced. The ability to narrowly restrict the range of external diameters of the carbon nanotube population further improves the quality of the product. Accordingly, the method and apparatus of the present invention provide a viable, rapid, low cost route for large scale production of high quality, aligned carbon nanotubes for subsequent use in a variety of applications.
The foregoing description of preferred embodiments of the invention has been presented for purposes of illustration and description. It is not intended to be exhaustive or to limit the invention to the precise form disclosed. Obvious modifications or variations are possible in light of the above teachings. The embodiments were chosen and described to provide the best illustration of the principles of the invention and its practical application to thereby enable one of ordinary skill in the art to utilize the invention in various embodiments and with various modifications as are suited to the particular use contemplated. All such modifications and variations are within the scope of the invention as determined by the appended claims when interpreted in accordance with the breadth to which they are fairly, legally and equitably entitled.
This application is a continuation-in-part of U.S. application Ser. No. 10/141,423 filed May 8, 2002 entitled “Process for the Continuous Production of Aligned Carbon Nanotubes,” the disclosure of which is incorporated herein in its entirety by reference, which in turn claims the benefit of U.S. Provisional Patent Application Ser. Nos. 60/289,415 filed May 8, 2001, 60/289,745 filed May 9, 2001, and 60/356,272 filed Feb. 11, 2002, the disclosures of each of which are incorporated herein in their entirety by reference.
This invention was made with Government support under NSF-MRSEC grant DMR-9809606. The Government may have certain rights in this invention.
| Number | Date | Country | |
|---|---|---|---|
| 60289415 | May 2001 | US | |
| 60289745 | May 2001 | US | |
| 60356272 | Feb 2002 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10141423 | May 2002 | US |
| Child | 11620262 | US |