Patent Grant
7393877
The present invention relates to a process for the conversion of synthesis gas to C2+ hydrocarbons by Fischer-Tropsch synthesis. It also relates to a Fischer-Tropsch synthesis process which produces an effluent exhibiting a specific distribution of the liquid fraction, and to this effluent.
Numerous documents are known which describe the Fischer-Tropsch (FT) synthesis using metal catalysts supported on various catalytic supports.
The documents WO-A-01/12323 and WO-A-01/54812 (Battelle) mention carbides generically as support or as interfacial layer for catalytic systems for the FT synthesis. There is no mention of the type of carbide which may be used.
U.S. Pat. Nos. 5,648,312, 5,677,257 and 5,710,093 (Intevep) disclose a specific catalytic support suitable for the FT synthesis (capable of being employed in a fixed bed, an ebullating bed or as a slurry). The catalytic entity in these documents is a metal from Group IVB or VIII, or a mixture, in particular zirconium and cobalt.
This support is obtained in particular by the formation of a suspension of silica and of silicon carbide in a basic solution, the formation of drops and then their separation as spheres, and then the transfer of the spheres into an acidic solution to result in a catalytic support comprising a substantially homogeneous mixture of silica and of SiC. Processes for the synthesis of hydrocarbons from synthesis gas use this catalytic support, which is a homogeneous mixture of particles of silica and of SiC, in an amount of 10 to 50% of the support, the support having a specific surface of at least approximately 30 m2/g (preferably of greater than 40 m2/g), mean pore diameters of at least approximately 150 Å and a particle size of at least 0.1 mm. From the synthesis, the SiC necessarily has the alpha form in these documents, the binder of this SiC being the silica. The specific surface is conferred by the silica binder rather than by the form of the SiC; the latter is used in fact more as a heat sink rather than as a support as such.
The presence of silica and/or of alumina as binder can have a negative effect on the thermal conductivity of the support. In addition, this binder, as support, additionally exhibits the disadvantage of reacting with the catalytic entity, thus resulting in a loss in the activity over time.
The invention provides a novel FT synthesis process using a novel catalytic support comprising β-SiC. A support is thus obtained which, in comparison with the supports of the prior art, is particularly suitable for the exothermic reaction of the FT synthesis.
Thus, the invention provides a process for the conversion of carbon monoxide to C2+ hydrocarbons in the presence of hydrogen and of a catalyst comprising a metal and a support comprising silicon carbide, characterized in that the support comprises more than 50% by weight of silicon carbide in the beta form.
A further subject-matter of the invention is a process for the conversion of carbon monoxide to C2+ hydrocarbons in the presence of hydrogen and of a catalyst, characterized in that the hydrocarbon effluent comprises more than 70 mol % of a mixture comprising from 50 to 90 mol % of C6 to C12 hydrocarbons and from 10 to 50 mol % of C13 to C24 hydrocarbons.
A further subject-matter of the invention is a C2+ hydrocarbon effluent comprising hydrocarbons, methane and CO2 which comprises more than 70 mol % of a mixture comprising from 50 to 90 mol % of C6 to C12 hydrocarbons and from 10 to 50 mol % of C13 to C24 hydrocarbons.
The invention is described in more detail with reference to the appended drawings, in which:
The beta-SiC is prepared by a gas/solid reaction between intimately mixed (without liquid) SiO vapour and solid carbon. For further details with regard to the β-SiC, reference may be made to the following patent applications and patents, incorporated by reference in the present application: EP-A-0 313 480, EP-A-0 440 569, U.S. Pat. No. 5,217,930, EP-A-0 511 919, EP-A-0 543 751 and EP-A-0 543 752. In comparison with the alpha form, the β-SiC is characterized in particular in that it exists in the pure state without binder. The crystals are of face-centred cubic type. In general, the specific surface of the β-SiC is between 5 and 40 m2/g and preferably between 10 and 25 m2/g.
The β-SiC can be prepared in the form of a powder, grains, extrudates (without binder), foam, monolith, and the like. The size of the SiC can vary according to the type of process employed (fixed bed, ebullating bed, slurry bed). It is thus possible, according to one alternative form, to use a size of between 0.1 and 20 mm, preferably between 1 and 15 mm. According to another alternative form, it is possible to use a size of between 1 and 200 μm, preferably between 5 and 150 μm.
This β-SiC has very good mechanical properties. Because of its very good thermal conductivity, generally much greater than that of metal oxides, hot spots are limited to the surface of the catalyst. The selectivity is thus improved.
According to one embodiment, the support of the catalyst comprises from 50 to 100% by weight of beta silicon carbide in the particulate state and preferably 100% of the said silicon carbide.
Use may conventionally be made, as main metal catalyst, of metals from Group VIII, for example in particular cobalt, iron or ruthenium, cobalt being particularly preferred. Use may also be made conventionally, at the same time, of a promoter. Mention may be made, among the promoters, of another metal from Group VIII or also of metals chosen from the group consisting of Zr, K, Na, Mn, Sr, Cu, Cr, W, Re, Pt, Ir, Rh, Pd, Ru, Ta, V, Mo and their mixtures. Mo is preferred.
The content of main metal, in particular cobalt, is conventionally greater than 5%, typically between 10 and 50%, of the final weight of the catalyst, in particular between 20 and 35% by weight. The content of promoter, in particular molybdenum, is conventionally between 0.1 and 15% of the final weight of the catalyst, in particular between 2 and 10% by weight. A primary metal/promoter ratio by weight is conventionally from 10:1 to 3:1.
The catalytic metal is deposited conventionally. For example, use may be made of the impregnation of the pore volume by a salt of the metal, for example cobalt nitrate. Use may also be made of the evaporated drop (also known as egg shell) method, by dropwise addition of a metal salt solution at ambient temperature to a support at high temperature, resulting in deposition essentially at the surface, for example a cobalt nitrate solution under air to a support at 200° C.
The catalytic bed can be fixed, ebullating or as a slurry. A fixed bed will be preferred.
The Fischer-Tropsch synthesis reaction is generally carried out under the following operating conditions:
The present invention also relates to an FT synthesis process which produces a hydrocarbon effluent which comprises at least 70 mol % of C5 to C25 hydrocarbons and in which the distribution is centred around relatively light hydrocarbons, approximately from C7 to C10. This type of distribution is not conventional, in particular for a process carried out in a fixed bed.
According to one embodiment, the hydrocarbon effluent comprises more than 70 mol % of a mixture comprising from 50 to 90 mol % of C6 to C12 hydrocarbons and from 10 to 50 mol % of C13 to C24 hydrocarbons.
According to one embodiment, the hydrocarbon effluent comprises at most 10 mol % of branched hydrocarbons and olefins and/or less than 2 mol % of C1 to C20 alcohol.
According to one embodiment, in the hydrocarbon effluent, the content of methane and of CO2 is less than 20 mol %.
Another subject-matter of the invention is this specific FT synthesis effluent.
In the patent application, the ratios are molar, unless otherwise mentioned.
The following examples illustrate the invention without limiting it.
Fischer-Tropsch Synthesis Over a Catalyst Based on Cobalt Supported on β-SiC.
In this example, the support based on β-SiC, in the form of grains with a diameter of between 0.4 and 1 mm, is impregnated by the pore volume method with an aqueous solution comprising the cobalt salt in the nitrate form. The weight of the precursor salt is calculated in order to have a final cobalt charge of 30% by weight with respect to the weight of catalyst after calcination and reduction. The impregnated product is subsequently dried under air at 100° C. for 2 h and then calcined under air at 350° C. for 2 h, in order to convert the precursor salt to its corresponding oxide. The product after calcination is reduced under a stream of hydrogen at 400° C. for 2 h in order to obtain the metallic form of the active phase.
The Fischer-Tropsch synthesis reaction is carried out under the following conditions:
The results obtained, expressed in terms of yields of the various fractions, are presented in
Influence of Molybdenum as Promoter on the Fischer-Tropsch Synthesis Activity of a Catalyst Based on Cobalt Supported on β-SiC.
In this example, the consequences on the performance of the Co/β-SiC catalyst in the presence of a promoter which is molybdenum are recorded. In this example, the support based on β-SiC, in the form of grains with a diameter of between 0.4 and 1 mm, is impregnated by the pore volume method with an aqueous solution comprising the cobalt salt in the nitrate form and an aqueous solution comprising an ammonium molybdate tetrahydrate. The weight of the precursor salt is calculated in order to have a final cobalt charge of 30% by weight with respect to the weight of the catalyst and a molybdenum charge of 5% by weight with respect to the weight of the catalyst, after calcination and reduction. The preparation of the catalyst is the same as in Example 1.
The Fischer-Tropsch synthesis reaction is carried out under the same conditions as in Example 1.
The results obtained at a reaction temperature of 200° C., expressed in terms of yield, are presented in
The concentration of the olefinic and branched hydrocarbons likewise remains low (less than 1% on average).
Influence of the Reaction Temperature on the Activity in the Fischer-Tropsch Synthesis Over Catalysts Based on Co and on Co with Mo Promoter.
In this example, the support based on β-SiC is identical to that of Example 2.
The Fischer-Tropsch synthesis reaction is carried out under the following conditions:
In the presence of molybdenum, the yield of the fraction comprising liquid hydrocarbons is always higher compared with that obtained in the absence of molybdenum on the catalyst, this being the case whatever the reaction temperature. The presence of molybdenum reduces the formation of the light products, such as CO2 and CH4, and promotes the formation of the liquid hydrocarbons, this being the case whatever the reaction temperature, i.e. 200° C. or 210° C. It should also be noted that, in the presence of molybdenum, the activity in the Fischer-Tropsch synthesis of the catalyst is more stable than in the absence of molybdenum.
The various results in terms of yields of the various fractions during the Fischer-Tropsch synthesis are given in
Fischer-Tropsch Synthesis Over a Catalyst Based on Cobalt Supported on a β-SiC Monolith.
In this example, the support based on β-SiC, in the form of a monolith with a mean cell opening size of approximately 500 μm, is impregnated by the pore volume method with an aqueous solution comprising the cobalt salt in the nitrate form. The impregnation process is the same as in Example 1.
The Fischer-Tropsch synthesis reaction is carried out under the following conditions:
The results obtained, expressed in terms of yields of the various fractions, are presented in
In the preceding examples, analysis at very high definition demonstrates unquantifiable C1 to C10 alcohols: the effluent is substantially devoid of alcohol.
| Number | Date | Country | Kind |
|---|---|---|---|
| 03 15622 | Dec 2003 | FR | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4260521 | Kostka | Apr 1981 | A |
| 4914070 | Ledoux | Apr 1990 | A |
| 5196389 | Dubots | Mar 1993 | A |
| 5217930 | Dubots | Jun 1993 | A |
| 5427761 | Grindatto | Jun 1995 | A |
| 5449654 | Prin | Sep 1995 | A |
| 5460759 | Dubots | Oct 1995 | A |
| 5585316 | Nay | Dec 1996 | A |
| 5648312 | Rivas | Jul 1997 | A |
| 5677257 | Rivas | Oct 1997 | A |
| 5710093 | Rivas | Jan 1998 | A |
| 6121190 | Zennaro et al. | Sep 2000 | A |
| 6217841 | Grindatto | Apr 2001 | B1 |
| 6251819 | Prin | Jun 2001 | B1 |
| 6296757 | Wittenbrink et al. | Oct 2001 | B1 |
| 6361861 | Gao | Mar 2002 | B2 |
| 6921778 | Minkkinen | Jul 2005 | B2 |
| 20050171218 | Savin-Poncet | Aug 2005 | A1 |
| Number | Date | Country |
|---|---|---|
| 1351954 | Jun 2002 | CN |
| 0 440 569 | Aug 1991 | EP |
| 0 511 919 | Nov 1992 | EP |
| 0 543 751 | May 1993 | EP |
| 0 543 752 | May 1993 | EP |
| 0 857 513 | Aug 1998 | EP |
| 1 284 281 | Feb 2003 | EP |
| 1 338 335 | Aug 2003 | EP |
| 2 062 615 | Jun 1971 | FR |
| 2 832 415 | May 2003 | FR |
| 2 864 532 | Jul 2005 | FR |
| WO 9714768 | Apr 1997 | WO |
| WO 9714769 | Apr 1997 | WO |
| WO 9805740 | Feb 1998 | WO |
| WO 9834998 | Aug 1998 | WO |
| WO 9834999 | Aug 1998 | WO |
| WO 9838147 | Sep 1998 | WO |
| WO 9901218 | Jan 1999 | WO |
| WO 9913028 | Mar 1999 | WO |
| WO 9913029 | Mar 1999 | WO |
| WO 9913030 | Mar 1999 | WO |
| WO 9913031 | Mar 1999 | WO |
| WO 9921943 | May 1999 | WO |
| WO 0011116 | Mar 2000 | WO |
| WO 0011117 | Mar 2000 | WO |
| WO 0020534 | Apr 2000 | WO |
| WO 0020535 | Apr 2000 | WO |
| WO 0060029 | Oct 2000 | WO |
| WO 0061707 | Oct 2000 | WO |
| WO 0112323 | Feb 2001 | WO |
| WO 0116259 | Mar 2001 | WO |
| WO 0149812 | Jul 2001 | WO |
| WO 0154812 | Aug 2001 | WO |
| WO 0159034 | Aug 2001 | WO |
| WO 0162875 | Aug 2001 | WO |
| WO 0183406 | Nov 2001 | WO |
| WO 0183641 | Nov 2001 | WO |
| WO 0183647 | Nov 2001 | WO |
| WO 0183648 | Nov 2001 | WO |
| WO 0202490 | Jan 2002 | WO |
| WO 02070628 | Sep 2002 | WO |
| WO 03000398 | Jan 2003 | WO |
| WO 03004588 | Jan 2003 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20060194888 A1 | Aug 2006 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11027706 | Jan 2005 | US |
| Child | 11411085 | US |