This application is the U.S. national phase of International Application PCT/EP03/01296, filed Feb. 10, 2003.
The present invention relates to a process for the polymerization of ethylene and one or more alpha-olefins of formula CH2═CHR, wherein R is a C2-C20 alkyl radical, in the presence of a metallocene catalyst.
It is known that polyethylene can be modified by the addition, during the polymerization reaction, of small quantities of alpha-olefins, generally 1-butene, 1-hexene or 1-octene. This gives LLDPE (linear low density polyethylene) copolymers which have short branches along the main chain due to the units derived from the alpha-olefin comonomers. These branches have the effect that the degree of crystallinity and hence the density of copolymer turn out to be lower than in polyethylene homopolymer. Typically, the LLDPE copolymers have densities of the order of 0.915-0.940 g/cm3 Consequently, the LLDPE copolymers have optimum mechanical properties, in particular for the production of films. The lowering of the degree of crystallinity and of the density of the copolymers depends on the type and quantity of the incorporated alpha-olefin. In particular, the greater the quantity of incorporated alpha-olefin, the lower are the resulting degrees of crystallinity and density.
Besides the type and quantity of the incorporated alpha-olefin comonomer, the properties of the copolymer depend on the distribution of the branches along the polymer chain. In particular, a uniform distribution of the branches has a positive effect on the properties of the copolymers. In fact, with the same type and quantity of incorporated alpha-olefin, a higher uniformity of distribution allows lower degrees of crystallinity and density to be obtained.
Metallocene compounds having two bridged cyclopentadienyl groups are known as catalyst components for the homo- and copolymerization reaction of ethylene. For example in WO 01/47939 a particular class of metallocenes containing a dithiophene-cyclopentadienyl ligand is reported and several compounds are exemplified in ethylene/propylene copolymerization. Nevertheless, in these examples the molecular weight of the obtained copolymers (expressed as intrinsic viscosity) is very low and not suitable for industrial use. Moreover, it is well known in the art that propylene is not a good comonomer for preparing LLDPE.
WO 01/48040 relates to a process for the polymerization of ethylene in the presence of a class of metallocenes comprising a ligand formed by a dithiophene-cyclopentadienyl derivative linked through a silicon bridge to a tetrasubstituted cyclopentadienyl radical. In this document ethylene is copolymerized with 1-hexene to give LLDPE. The claimed compounds are completely different from that of the present invention.
WO01/48039 relates to a slightly different class of metallocene compounds in which two cyclopentadienyl moieties are bridged with a methylene group. In this case the ethylene/hexene copolymers obtained show molecular weight values that are not satisfactory for industrial use.
Thus it would be desirable to develop a new process that, by using a particular class of metallocene compounds, allow ethylene copolymers having a high molecular weight to be obtained.
According to a first aspect of the present invention, it is provided a process for producing a polymer of ethylene containing from 0.1 to 50% by weight of one or more derived units of alpha-olefins of formula CH2═CHR, wherein R is a C2-C20 alkyl radical, comprising contacting, under polymerization conditions, ethylene and one or more alpha-olefins in the presence of a catalyst system obtainable by contacting:
Preferably in the compound of formula (I):
R1, R2 and R3, equal to or different from each other, are C1-C10 alkyl radicals; more
preferably R1 and R2 are methyl group and R3 is a methyl or an isopropyl radical;
R4 is preferably hydrogen, a C6-C20-aryl radical or form with R5 a condensed aromatic 5 of 6 membered ring such as a condensed benzene ring a condensed thiophene ring or a condensed pyrrole ring;
R5 is preferably a hydrogen atom or form with R4 a condensed 5 or 6 membered aromatic ring;
R6 preferably hydrogen atom; and R7 is preferably hydrogen atom or a methyl radical;
R8 and R9 are preferably C1-C10 alkyl or C6-C20 aryl radicals; more preferably they are methyl radicals.
Compounds of formula (I) can be synthesized according to the procedures known in the art, for example as described in WO 01/47939.
Alumoxanes used as component b) can be obtained by reacting water with an organo-aluminum compound of formula HjAlU3-j or HjAl2U6-j, where U substituents, same or different, are hydrogen atoms, halogen atoms, C1-C20-alkyl, C3-C20-cyclalkyl, C6-C20-aryl, C7-C20-alkylaryl or C7-C20-arylalkyl radicals, optionally containing silicon or germanium atoms, with the proviso that at least one U is different from halogen, and j ranges from 0 to 1, being also a non-integer number. In this reaction the molar ratio of Al/water is preferably comprised between 1:1 and 100:1.
The molar ratio between aluminum and the metal of the metallocene is comprised between about 10:1 and about 10000:1, more preferably between about 50:1 and about 5000:1, even more preferably between 100:1 and 1000:1.
The alumoxanes used in the catalyst according to the invention are considered to be linear, branched or cyclic compounds containing at least one group of the type:
wherein the substituents U, same or different, are described above.
In particular, alumoxanes of the formula:
can be used in the case of linear compounds, wherein n1 is 0 or an integer from 1 to 40 and the substituents U are defined as above, or alumoxanes of the formula:
can be used in the case of cyclic compounds, wherein n2 is an integer from 2 to 40 and the U substituents are defined as above.
Examples of alumoxanes suitable for use according to the present invention are methylalumoxane (MAO), tetra-(isobutyl)alumoxane (TIBAO), tetra-(2,4,4-trimethyl-pentyl)alumoxane (TIOAO), tetra-(2,3-dimethylbutyl)alumoxane (TDMBAO) and tetra-(2,3,3-trimethylbutyl)alumoxane (TTMBAO).
Particularly interesting cocatalysts are those described in WO 99/21899 and in WO01/21674 obtained by contacting water with organometallic aluminum compounds in which the alkyl and aryl groups have specific branched patterns.
Non-limiting examples of aluminum compounds according to WO 99/21899 and WO01/21674 are:
Amongst the above aluminum compounds, trimethylaluminum (TMA), triisobutylaluminum (TIBAL), tris(2,4,4-trimethyl-pentyl)aluminum (TIOA), tris(2,3-dimethylbutyl)aluminum (TDMBA) and tris(2,3,3-trimethylbutyl)aluminum (TTMBA) are preferred.
Non-limiting examples of compounds able to form an alkylmetallocene cation are compounds of formula D+E−, wherein D+ is a Brønsted acid, able to donate a proton and to react irreversibly with a substituent X of the metallocene of formula (I) and E− is a compatible anion, which is able to stabilize the active catalytic species originating from the reaction of the two compounds, and which is sufficiently labile to displaced by an olefinic monomer. Preferably, the anion E− comprises one or more boron atoms. More preferably, the anion E− is an anion of the formula BAr4(−), wherein the substituents Ar, which can be identical or different, are aryl radicals such as phenyl, pentafluorophenyl or bis(trifluoromethyl)phenyl. Tetrakis-pentafluorophenyl borate is particularly preferred; examples of these compounds are described in WO 91/02012. Moreover, compounds of the formula BAr3 can be conveniently used. Compounds of this type are described, for example in WO 92/00333. Other examples of compounds able to form an alkylmetallocene cation are compounds of formula BAr3P wherein P is a substituted or unsubstituted pyrrol radicals. These compounds are described in EP 1173445. Compounds containing boron atoms can be conveniently supported according to the description of DE-A-19962814 and DE-A-19962910. All these compounds containing boron atoms can be used in a molar ratio between boron and the metal of the metallocene comprised between about 1:1 and about 10:1; preferably 1:1 and 2.1; more preferably about 1:1.
Non limiting examples of compounds of formula D+E− are: Triethylammoniumtetra(phenyl)borate, Tributylammoniumtetra(phenyl)borate, Trimethylammoniumtetra(tolyl)borate, Tributylammoniumtetra(tolyl)borate, Tributylammoniumtetra(pentafluorophenyl)borate, Tributylammoniumtetra(pentafluorophenyl)aluminate, Tripropylammoniumtetra(dimethylphenyl)borate, Tributylammoniumtetra(trifluoromethylphenyl)borate, Tributylammoniumtetra(4-fluorophenyl)borate, N,N-Dimethylbenzylammonium-tetrakispentafluorophenylborate, N,N-Dimethylhexylamonium-tetrakispentafluorophenylborate, N,N-Dimethylaniliniumtetra(phenyl)borate, N,N-Diethylaniliniumtetra(phenyl)borate, N,N-Dimethylaniliniumtetrakis(pentafluorophenyl)borate, N,N-Dimethylaniliniumtetrakis(pentafluorophenyl)aluminate, N,N-Dimethylbenzylammonium-tetrakispentafluorophenylborate, N,N-Dimethylhexylamonium-tetrakispentafluorophenylborate, Di(propyl)ammoniumtetrakis(pentafluorophenyl)borate, Di(cyclohexyl)ammoniumtetrakis(pentafluorophenyl)borate, Triphenylphosphoniumtetrakis(phenyl)borate, Triethylphosphoniumtetrakis(phenyl)borate, Diphenylphosphoniumtetrakis(phenyl)borate, Tri(methylphenyl)phosphoniumtetrakis(phenyl)borate, Tri(dimethylphenyl)phosphoniumtetrakis(phenyl)borate, Triphenylcarbeniumtetrakis(pentafluorophenyl)borate, Triphenylcarbeniumtetrakis(pentafluorophenyl)aluminate, Triphenylcarbeniumtetrakis(phenyl)aluminate, Ferroceniumtetrakis(pentafluorophenyl)borate, Ferroceniumtetrakis(pentafluorophenyl)aluminate. Triphenylcarbeniumtetrakis(pentafluorophenyl)borate, and N,N-Dimethylaniliniumtetrakis(pentafluorophenyl)borate.
Organic aluminum compounds used as compound c) are those of formula HjAlU3-j or HjAl2U6-j described above.
The catalyst system of the present invention can also be supported on an inert carrier. This is achieved by depositing the metallocene compound a) or the product of the reaction thereof with the component b), or the component b) and then the metallocene compound a) on an inert support such as, for example, silica, alumina, Al—Si, Al—Mg mixed oxides, magnesium halides, styrene/divinylbenzene copolymers, polyethylene or polypropylene. The supportation process is carried out in an inert solvent, such as hydrocarbon selected from toluene, hexane, pentane and propane and at a temperature ranging from 0° C. to 100° C., more from 30° C. to 60° C.
A particularly suitable process for supporting the catalyst system is described in WO01/44319, wherein the process comprises the steps of:
A suitable class of supports comprises porous organic supports functionalized with groups having active hydrogen atoms. Particularly suitable are those in which the organic support is a partially crosslinked styrene polymer. Supports of this type are described in EP 633 272.
Another class of inert supports particularly suitable for use according to the invention is that of polyolefin porous prepolymers, particularly polyethylene.
A further suitable class of inert supports for use according to the invention is that of porous magnesium halides, such as those described in WO 95/32995.
The process for the polymerization of olefins according to the invention can be carried out in the liquid phase, in the presence or absence of an inert hydrocarbon solvent, or in the gas phase. The hydrocarbon solvent can either be aromatic, such as toluene, or aliphatic, such as propane, hexane, heptane, isobutane or cyclohexane.
The polymerization temperature is generally comprised between 0° C. and +100° C. and, particularly, between 50° C. and +90° C. The polymerization pressure is generally comprised between 0.5 and 100 bar.
The components of the catalyst system can be brought into contact with each other before the polymerization. The pre-contact concentrations are generally between 0.1 and 10−8 mol/l for the metallocene component a), while they are generally between 2 and 10−8 mol/l for the component b). The pre-contact is generally effected in the presence of a hydrocarbon solvent and, if appropriate, of small quantities of monomer. In the pre-contact it is also possible to use a non-polymerizable olefin such as isobutene, 2-butene and the like.
The molecular weight distribution can be varied by using mixtures of different metallocene compounds or by carrying out the polymerization in several stages which differ as to the polymerization temperature and/or the concentrations of the molecular weight regulators and/or the monomers concentration. Moreover by carrying out the polymerization process by using a combination of two different metallocene compounds of formula (I) a polymer endowed with a broad melting is produced.
In the copolymers obtainable by the process of the invention, the content of ethylene derived units is between 99.9% by weight and 50% by weight; preferably is it between 99% by weight and 70% by weight; and more preferably it is between 95% by weight and 80% by weight.
The content of alpha-olefins derived units is between 0.1% by weight and 50% by weight; preferably is it between 1% by weight and 30% by weight; and more preferably it is between 5% by weight and 20% by weight.
Non-limiting examples of alpha-olefins of formula CH2═CHR which can be used as alpha-olefins in the process of the invention are 1-butene, 1-pentene, 4-methyl-1-pentene, 1-hexene, 1-octene, 4,6-dimethyl-1-heptene, 1-decene, 1-dodecene, 1-tetradecene, 1-hexadecene, 1-octadecene and 1-eicosene. Preferred comonomers are 1-hexene and 1-octene.
With the process of the present invention it is possible to obtain copolymers having a high molecular weight (I.V.) that makes the process object of the present invention fit for an industrial use.
The following examples are given for illustrative purpose and do not intend to limit the invention.
Analytical Methods
The intrinsic viscosity (I.V.) was measured in tetrahydronaphtalene (THN) at 135° C.
The melting points of the polymers (Tm) were measured by Differential Scanning Calorimetry (D.S.C.) on Perkin Elmer DSC-7 instrument, according to the standard method. A weighted sample (5-10 mg) obtained from the polymerization was sealed into aluminum pans and heated at 200° C. with a scanning speed corresponding to 20° C./minute. The sample was kept at 200° C. for 5 minutes to allow a complete melting of all the crystallites. Successively, after cooling to 0° C. with a scanning speed corresponding to 20° C./minute, the peak temperature was taken as crystallization temperature (Tc). After standing 5 minutes at 0° C., the sample was heated for the second time at 200° C. with a scanning speed corresponding to 20° C./min. In this second heating run, the peak temperature was taken as the melting temperature (Tm) and the area as global melting enthalpy (ΔHf).
The molecular weight distribution was determined on a WATERS 150 C using the following chromatographic conditions:
13C-NMR spectra were acquired on a DPX-400 spectrometer operating at 100.61 MHz in the Fourier transform mode at 120° C.
Preparation of Catalyst Components
Metallocene Compounds
The ethylene polymers used as supports were obtained from a Ziegler-Natta catalyst system, prepared according to the process described in WO 00/78820.
Support A
The polymerization was carried out in liquid propane at 30° C. at an ethylene partial pressure of 1.5 bar. Since once discharged the prepolymer resulted still active, a following treatment was necessary to deactivate the titanium catalytic system. A sample of 650 g of the obtained polymer was steamed in a fluidized bed reactor (0.1 kg steam/kg polymer, 110° C. for 30 minutes) and then dried in the same reactor, under hot nitrogen flow at 125° C. for several hours. The polymer has an intrinsic viscosity of 10.2 dL/g, average pore size of 386 μm, porosity of 1.27 mL/g (excluding macropores), average pore size of 1.1 μm and surface area of 7.7 m2/g.
Preparation of the Catalyst System
Catalysts 1-3
The catalytic solution was prepared by adding, under inert conditions, the metallocene compound and MAO as indicated in table 1. The solution was stirred at room temperature for 15 minutes. Separately, the amount described in table 1 of the porous polyethylene prepolymer obtained as described above, was loaded in the equipment described in WO 01/44319. The jacket temperature of column 1 was set to 40° C. and that of column 2 to 110° C. The agitator of column 1 was activated and recirculation of the solid in the loop was initiated opening the nitrogen flow trough column 2. The catalytic solution was dosed to the support in 1.5 hours. At the end of the addition, the supported catalyst was maintained in recirculation for 15 minutes to eliminate the last traces of solvent. The composition of the obtained catalyst is described in table 1.
Catalyst 4
0.475 mmol of the metallocene compound C-2 were dissolved in 12.4 ml MAO (30% in toluene) and stirred for 1 h at room temperature. The solution was then dropped onto 9.5 g silica (ES70X, calcinated at 600° C., 6 h) and stirred for 1 h. The mixture was dried under vacuum at room temperature. The yield was 13.1 g of a free flowing yellow powder. The obtained catalyst had the following characteristics: zirconium content 50 mol/g SiO2; Al/Zr 120/1
Catalyst 5
Catalyst 5 was obtained according to the same procedure used for catalyst 4, with the exception that metallocene compound C-3 was used.
A 4 L autoclave, equipped with a blade turbine magnetic stirrer, pressure indicator, temperature indicator, system for loading the catalyst, feed line for monomer equipped with a thermal-mass flowmeter for the measure of the ethylene uptake and a thermosetting jacket, was used. At room temperature 2.5 mmol of TIBA (100 g/L hexane solution) as scavenger and 50 g of 1-hexene were loaded, followed by 1.6 L of propane; then the reactor was pressurized with 5 bar of ethylene partial pressure. The polymerization was started by injecting the catalyst at 30° C. A prepolymerization step was carried out at 30° C. for 30 minutes, then the temperature was raised up to 75° C. and the ethylene partial pressure was increased to 10 bar. These conditions were maintained by continuously feeding ethylene for 1 hour. Polymerization was stopped by venting and cooling the autoclave. The characterization of the obtained polymers is reported in table 2.
In a 11 reactor 80 g polyethylene were introduced as a seed bed. 10 mg isoprenyl aluminum (IPRA) as a 2 molar solution in heptane, 5 mg of the antistatic agent Costelan AS 100 and 11 ml heptane were added and stirred for 10 min. The amount of catalyst indicated in table 3 were added to the reactor, the reactor was closed and pressurized with 10 bar nitrogen. The reactor was heated to 70° C. and pressurized with 10 bar of an ethylene/hexene mixture to reach an overall pressure of 20 bar. After 1 h the reactor was depressurized and cooled to room temperature. The characterization of the obtained polymers is reported in table 3.
Number | Date | Country | Kind |
---|---|---|---|
02075757 | Feb 2002 | EP | regional |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/EP03/01296 | 2/10/2003 | WO | 00 | 8/10/2004 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO03/070778 | 8/28/2003 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
5698487 | Sacchetti et al. | Dec 1997 | A |
6399533 | Sacchetti et al. | Jun 2002 | B2 |
6423660 | Albizzati et al. | Jul 2002 | B1 |
6444604 | Albizzati et al. | Sep 2002 | B1 |
6559252 | Horton et al. | May 2003 | B1 |
6608224 | Resconi et al. | Aug 2003 | B2 |
6627710 | Sacchetti et al. | Sep 2003 | B1 |
6774194 | Albizzati et al. | Aug 2004 | B2 |
6787619 | Dall'Occo et al. | Sep 2004 | B2 |
6822106 | Dall'Occo et al. | Nov 2004 | B2 |
6841501 | Resconi et al. | Jan 2005 | B2 |
6864333 | Dall'Occo et al. | Mar 2005 | B2 |
6878786 | Resconi et al. | Apr 2005 | B2 |
6953829 | Kratzer et al. | Oct 2005 | B2 |
7002031 | Resconi et al. | Feb 2006 | B2 |
7041750 | Covezzi et al. | May 2006 | B1 |
7101940 | Schottek et al. | Sep 2006 | B2 |
7112638 | Nifant'ev et al. | Sep 2006 | B2 |
7141527 | Van Baar et al. | Nov 2006 | B1 |
20030008984 | Kratzer et al. | Jan 2003 | A1 |
20030013913 | Schottek et al. | Jan 2003 | A1 |
20060235173 | Resconi | Oct 2006 | A1 |
Number | Date | Country |
---|---|---|
19962814 | Jun 2001 | DE |
19962910 | Jul 2001 | DE |
0633272 | Jan 1995 | EP |
1173445 | Jan 2002 | EP |
9102012 | Feb 1991 | WO |
9200333 | Jan 1992 | WO |
9532995 | Dec 1995 | WO |
9921899 | May 1999 | WO |
0078820 | Dec 2000 | WO |
0121674 | Mar 2001 | WO |
0144319 | Jun 2001 | WO |
0147939 | Jul 2001 | WO |
0148039 | Jul 2001 | WO |
0148040 | Jul 2001 | WO |
WO 0147939 | Jul 2001 | WO |
03057705 | Jul 2003 | WO |
2004099269 | Nov 2004 | WO |
2005095468 | Oct 2005 | WO |
2005095473 | Oct 2005 | WO |
2005095474 | Oct 2005 | WO |
2006005648 | Jan 2006 | WO |
Number | Date | Country | |
---|---|---|---|
20050222349 A1 | Oct 2005 | US |