Process for the cross-linking of halogenated polymers

Information

  • Patent Grant
  • 5250625
  • Patent Number
    5,250,625
  • Date Filed
    Tuesday, April 16, 1991
    33 years ago
  • Date Issued
    Tuesday, October 5, 1993
    31 years ago
Abstract
The cross-linking of halogenated polymers such as chlorinated polyethylene with bis-(2,5-dimercapto-1,3,4-thiadiazole) in the presence of a basic substance may easily be carried out and leads to improved properties of the vulcanisate, in particular when amidamines such as, for example, tetraethylene pentamine distearate are used as basic substances.
Description

This invention relates to a process for the cross-linking of halogenated polymers such as chlorinated polyethylene by means of bis-(2,5-dimercapto-1,3,4-thiadiazole), hereinafter referred to as BDTD, or bis-(2,5-dimercapto-1,3,4-thiadiazole) derivatives such as the monobenzoyl derivative and basic substances, in particular certain amidamines.
It is known from German Offenlegungsschriften Nos. 2 754 060 and 2 845 125 to cross-link saturated, halogenated polymers by heating them in the presence of 2,5-dimercapto-1,3,4-thiadiazole and a basic material. The basic material used is in particular a combination of an organic base and an inorganic base, the organic base used being an amine having a boiling point above circa 110.degree. C. and a pK-value below circa 4.5. Dicyclohexylamine and a reaction product of aniline and butyraldehyde are mentioned as preferred amines for this purpose.
These amines are difficult to handle as they are powerfully corrosive organic liquids and are difficult to incorporate in rubber mixtures.
Further, when these amines are used for the cross-linking of chlorinated polyethylene, the vulcanizate properties are found to be unsatisfactory and the moulds used for the production of the articles are found to be badly soiled and the articles are difficult to remove from the mould.
The present invention relates to a process for the cross-linking of halogenated polymers such as chlorinated polyethylene with bis-(2,5-dimercapto-1,3,4-thiadiazole) or derivatives thereof in the presence of a basic material. The basic material is preferably an amidamine corresponding to the following formula
R--CO--NH--[CH.sub.2 --CH.sub.2 --NH].sub.n --CO--R.sub.1 (I)
wherein
R stands for saturated or unsaturated hydrocarbon group having 6 to 22 carbon atoms,
R.sub.1 stands for alkyl, aryl, cycloalkyl, aralkyl or R--COCH.sub.2 -CH.sub.2 and
n stands for an integer from 1 to 10.
The alkyl group may be straight chained or branched and may in particular have 1 to 18 carbon atoms. The aryl group preferably has 6 to 12 carbon atoms and may carry substituents such as halogen, C.sub.1 -C.sub.4 -alkyl, nitro, cyano or C.sub.1 -C.sub.4 -alkoxy; the cycloalkyl group preferably has 5 to 8 carbon atoms; the aralkyl in particular has 7 to 12 carbon atoms and its aryl moiety may carry the same substituents as the above-mentioned aryl group.
Preferred compounds of formula I correspond to formula II
R.sub.2 --CO--NH--[CH.sub.2 --CH.sub.2 --NH].sub.m --CO--R.sub.3(II)
wherein
R.sub.2 and R.sub.3 may be identical or different and stand for straight chained, saturated alkyl with 8 to 18 carbon atoms and
m stands for an integer from 2 to 5.
The compounds of formulae I and II are generally solid, non-corrosive substances which can easily be incorporated in rubber mixtures.
The amidamine is preferably used in a quantity of from 1 to 5% by weight, in particular from 2 to 4.5% by weight, based on the rubber. BDTD is preferably used in a quantity of from 1 to 4% by weight, in particular from 2 to 3% by weight, based on the rubber.
The invention further relates to the use of bis-(2,5-dithio-1,3,4-thiadiazole) as cross-linking agent for halogenated polymers.
For information on the properties and fields of application of chlorinated polyethylene, known as CM according to ASTM-D 1418, see E.Rohde, Kautschuk + Gummi, Kunststoffe 35, 1982, pages 478 et seq).
The halogenated polymer used may be CM, i.e. a chlorinated polyethylene with a chlorine content of about 25 to 45% by weight prepared by suspension chlorination of low pressure polyethylene.
Other halogenated elastomers, such as CSM, CO/ECO, CR and CIIR, may be halogenated with BDTD in the same manner.





EXAMPLE 1
Demonstrates the influence of increasing quantities of amidamine on the activation of cross-linking of a CM mixture with BDTD. No true cross-linking takes place without the addition of amidamine. An optimum cross-linking characterstic is in most cases obtained with 3 to 4.5 phr of amidamine. Sufficiently long initial vulcanization times (T 10) and a short final vulcanization time (T 90) are obtained.
______________________________________ A D E F______________________________________CM 100MgO 10Carbon black 50Kaolin 60Alkyl sulphonic acid ester 20Aromatic mineral oil 20BDTD 2.5Amidamine -- 1.5 3.0 4.5Elastograph at 180.degree. C.F min (Nm) 0.051 0.046 0.032 0.031F max (Nm) 0.246 0.334 0.491 0.568T 10 (min) 0.70 1.00 1.40 1.40T 50 (min) 2.70 6.30 4.90 3.30T 90 (min) 16.70 18.20 13.60 9.20______________________________________
EXAMPLE 2
Demonstrates a comparison between the above-mentioned activation by powerfully corrosive liquids such as an aniline-condensation product and the cyclohexylamine, the optimum dose of which is about 1.5 phr. By comparison, the amidamine which has a substantially higher molecular weight must also be added in higher doses (see Example 1).
A more reliable initial vulcanization (T 10) with more rapid final vulcanization (T 90) is obtained with amidamine in spite of the considerably higher dosage. In addition, the viscosity of the mixture is lowered by the amidamine, whereby extrusion is facilitated and more advantageous properties are obtained for IM processing. The vulcanizate values of the mixture with amidamine are distinguished by their exceptionally good elongations at break. This advantage is also found after testing of the ageing in hot air.
______________________________________ B C F______________________________________CM 100MgO 10Carbon black N-550 50Kaolin 60Alkyl sulphonic acid ester 20Aromatic mineral oil 20BDTD 2.5Aniline condensation product 1.5 -- --Cyclohexylamine -- 1.5 --Amidamine -- -- 4.5Elastograph at 180.degree. C.F min (Nm) 0.047 0.049 0.031F max (Nm) 0.483 0.581 0.568T 10 (min) 0.80 0.90 1.40T 50 (min) 3.30 2.70 3.30T 90 (min) 15.70 12.60 9.20Viscosity of mixture:ML 1 + 4/100.degree. C. 36 36 30Vulcanization 30 min/170.degree. C.:Hardness (ShA) 82 82 83Elasticity (%) 13 13 13.sigma.100 (MPa) 6.7 8.0 5.3.sigma.300 (MPa) -- -- 8.0Tensile strength (MPa) 7.2 8.1 8.1Elongation at break (%) 190 190 305Hot air ageing 7d/125.degree. C.: B C FHardness (ShA) 86 86 88Elasticity (%) 13 13 13Tensile strength (MPa) 10.2 11.4 9.8Elongation at break (%) 95 85 160______________________________________
EXAMPLE 3
Demonstrates the cross-linking of chlorinated polyethylene (CM) with increasing quantities of BDTD. In the present mixture, the optimum dose is about 2.0 parts by weight. For other formulations, doses of 0.5 to 4.5 parts by weight may be used and are customary.
______________________________________(Example 1) A B C D______________________________________CM 100 100 100 100MgO 10 10 10 10Carbon black N-550 70 70 70 70HA mineral oil 30 30 30 30Ester plasticizer 10 10 10 10Amidamine activator 3.5 3.5 3.5 3.5BDTD 1.0 1.5 2.0 2.5Vulcanization 20 min/170.degree. C.Hardness (ShA) 77 80 82 82Elasticity (%) 16 16 15 15.sigma.100 (MPa) 5.1 6.2 6.7 7.1.sigma.300 (MPa) 12.1 13,2 13,6 13.7Tensile strength (MPa) 14.9 14.7 14.3 13.9Elongation at break (%) 430 390 340 320______________________________________
EXAMPLE 4
Demonstrates the cross-linking of epichlorohydrin rubber with BDTD by comparison with lead oxide and ethylene thiourea. With the doses used here, a somewhat more favourable initial vulcanization time combined with a substantially higher degree of cross-linking (see Hardness, o, Elongation at break) is achieved with BDTD.
______________________________________(Example 2) E F______________________________________Epichlorohydrin elastomer 60 60Epichlorohydrin/ethylene oxide copolymer 40 402-Mercapto-benzimidazole 1 1Nickel dibutyl dithiocarbamate (80%) 1.5 1.5Carbon black N-330 15 15Carbon black N-550 25 25Barium carbonate (80%) 4 --Urea activator 2 --Ethylene thiourea (70%) -- 1.5Red lead (70%) -- 6BDTD 2.5 --Initial vulcanization at 120.degree. C.t.sub.5 (min) 5.4 4.4T.sub.35 (min) 7.5 6.3Vulcanization 20 min/180.degree. C.Hardness (ShA) 71 67Elasticity (%) 25 23.sigma.100 (MPa) 6.1 3.5Tensile strength (MPa) 10.2 13.9Elongation at break (%) 155 335Compression set 24 22______________________________________
EXAMPLE 5
Demonstrates a comparison of the cross-linking of CM with peroxide and with BDTD. The higher tear propagation resistance and improved elongation at break obtained when cross-linking is carried out with BDTD are particularly noteworthy.
______________________________________(Example 3) G H______________________________________CM (chlorinate polyethylene) 100 100Magnesium oxide 10 10Carbon black N-330 60 60Ester plasticizer 30 30Age resistor 0.3 0.3Amide-amine activator 5.5 --BDTD 2.5 --Bis-(t-butyl-peroxy-isopropyl)benzene -- 7Triallyl cyanurate -- 2.5Vulcanization 15 min/170.degree. C.Hardness (ShA) 74 71Elasticity (%) 23 24Tear propagationresistance (N/mm).sigma.100 (MPa) 5.1 4.8.sigma.300 (MPa) 15.2 17.3Tensile strength (MPa) 16.8 17.9Elongation at break (%) 365 320Compression set (%)24 h/125.degree. C. 12 1124 h/150.degree. C. 29 32______________________________________
EXAMPLE 4
Demonstrates that BDTD is very suitable for cross-linking chlorine-containing elastomers. The use of DMTD and BMTD for such vulcanization is already known, as mentioned above. An intermediate position between these two cross-linking agents is obtained with BDTD. Thus the initial vulcanization time is longer with BDTD than with BMTD but shorter than with DMTD.
______________________________________ ##STR1## ##STR2## ##STR3##(Example 4) I K L______________________________________CM 100MgO 10Carbon black N-550 70Aromatic mineral oil 30Alkyl sulphonic acid ester 10Amidamine 3.5DMTD 2.0 -- --BMTD -- 2.0 --BDTD -- -- 2.0Vulcanization at 180.degree. C.ti (min) 5.3 2.6 3.8F 10 (dNm) 30.0 31.5 28.3F 24 (dNm) 49.0 37.0 43.5Vulcanization 20 min/170.degree. C.Hardness (ShA) 77 79 82Elasticity (%) 16 14 15.sigma.100 (MPa) 8.1 5.4 6.7.sigma.300 (MPa) 14.0 12.7 13.6Tensile strength (MPa) 14.9 14.5 14.3Elongation at break (%) 305 400 340Compression set24 h/100.degree. C. (%) 10 9 1124 h/125.degree. C. (%) 16 15 13______________________________________
Claims
  • 1. Process for the cross-linking of a halogenated polymer selected from the group consisting of chlorinated polyethylene, epichlorohydrine rubber and epichlorohydrine ethylene oxide copolymer, wherein the polymer is subjected to the action of bis-(2,5-dithio-1,3,4-thiadiazole) or derivatives thereof in the presence of a basic material consisting of an amidamine corresponding to the following formula
  • R--CO--NH--[CH.sub.2 --CH.sub.2 --NH].sub.n --CO--CO--R.sub.1(I)
  • wherein
  • R denotes a saturated or unsaturated hydrocarbon group having 6 to 22 C-atoms,
  • R.sub.1 denotes alkyl, aryl, cycloalkyl, aralkyl or R--COCH.sub.2 CH.sub.2 and
  • n denotes an integer from 1 to 10.
  • 2. The process of claim 1, wherein R.sub.1 is an alkyl group having 1 to 18 carbon atoms.
  • 3. The process of claim 2, wherein said alkyl group is straight chained.
  • 4. The process of claim 2, wherein said alkyl group is branched.
  • 5. The process of claim 1, wherein R.sub.1 is an aryl group having 6 to 12 carbon atoms.
  • 6. The process of claim 5, wherein said aryl group contains at least one substituent selected from the group consisting of halogen, C.sub.1 -C.sub.4 -alkyl, nitro, cyano and C.sub.1 -C.sub.4 -alkoxy.
  • 7. The process of claim 1, wherein R.sub.1 is a cycloalkyl group having 5 to 8 carbon atoms.
  • 8. The process of claim 1, wherein R.sub.1 is an aralkyl group having 7 to 12 carbon atoms.
  • 9. The process of claim 8, wherein said aralkyl group comprises an aryl moiety containing at least one substituent selected from the group consisting of halogen, C.sub.1 -C.sub.4 -alkyl, nitro cyano and C.sub.1 -C.sub.4 -alkoxy.
  • 10. The process of claim 1, wherein said amidamine corresponds to the following formula
  • R.sub.2 -CO--NH--[CH.sub.2 -13 CH.sub.2 --NH].sub.m --CO--R.sub.3(II)
  • wherein
  • R.sub.2 is a straight chained, saturated alkyl with 8 to 18 carbon atoms,
  • R.sub.3 is a straight chained, saturated alkyl with 8 to 18 carbon atoms,
  • and
  • m is an integer from 2 to 5.
  • 11. The process of claim 10, wherein R.sub.2 and R.sub.3 are identical.
  • 12. The process of claim 10, wherein R.sub.2 and R.sub.3 are different.
  • 13. The process of claim 1, wherein the amidamine is used in a quantity of from 1 to 5 percent by weight, based on the weight of the polymer.
  • 14. The process of claim 13, wherein the amidamine is used in a quantity of from 2 to 4.5 percent by weight.
  • 15. The process of claim 1, wherein the bis-(2,5-dithio-1,3,4-thiadiazole) or derivatives thereof is used in a quantity of from 1 to 4 percent by weight, based on the weight of the polymer.
  • 16. The process of claim 15, wherein the bis-(2,5-dithio-1,3,4-thiadiazole) or derivatives thereof is used in a quantity of from 2 to 3 percent by weight.
Priority Claims (1)
Number Date Country Kind
4013714 Apr 1990 DEX
Foreign Referenced Citations (2)
Number Date Country
0336735 Mar 1989 EPX
2356687 Nov 1978 FRX