Process for the dyeing of thermoplastics in the melt

Abstract

Process for the dyeing of thermoplastics in the melt, which process comprises the use of dyestuffs of the formula ##STR1## wherein X.sub.1 - X.sub.4 represents H-atoms or halogen atoms, or one or two of the radicals X.sub.1 - X.sub.4 represent alkyl, alkoxy, phenyl or phenoxy groups, and those remaining represent H-atoms, R.sup.1 and R.sup.2 represent radicals of methylene-active compounds, or radicals of the formula .dbd.N--A wherein A stands for the radical of an aliphatic, cycloaliphatic, araliphatic, aromatic or heterocyclic amine or hydrazine, whereby, provided that R.sup.1 and R.sup.2 represent radicals of the formula .dbd.N--A, one A represents a heterocyclic radical containing N-atoms, optionally together with O- or S-atoms.

Description

The present invention relates to the dyeing of thermoplastics in the melt with dyestuffs of the formula ##STR2## wherein X.sub.1 - X.sub.4 represent H-atoms or halogen atoms, or one or two of the radicals X.sub.1 - X.sub.4 represent alkyl, alkoxy, phenyl or phenoxy groups, and those remaining represent H-atoms, R.sup.1 and R.sup.2 represent radicals of methylene-active compounds, or radicals of the formula .dbd.N--A wherein A stands for the radical of an aliphatic, cycloaliphatic, araliphatic, aromatic or heterocyclic amine or hydrazine, whereby, provided that R.sup.1 and R.sup.2 represent radicals of the formula .dbd.N--A, one A represents a heterocyclic radical containing N-atoms, optionally together with O- or S-atoms.

Preferred dyestuffs are those of the formula ##STR3## wherein R.sup.3 and R.sup.4 represent cyano, acyl, alkoxycarbonyl, carbamoyl or sulphamoyl groups, or radicals of the formula ##STR4## wherein V represents an O- or S-atom or an imino group, or an alkylimino group containing 1 - 4 C-atoms, Y.sub.1 and Y.sub.2 represent H-atoms or halogen atoms, or alkyl or alkoxy groups containing 1 - 4 C-atoms; and especially dyestuffs of the formula ##STR5## wherein Y.sub.1 and Y.sub.2 have the above-given meaning, Y.sub.3 represents a H-atom or halogen atom, an alkyl or alkoxy group optionally substituted by alkoxy groups having 1 - 4 C-atoms, or phenoxy or phenyl groups, an alkanoylamino or alkylsulphonyl group having 1 - 4 C-atoms, an alkoxycarbonyl group having 2 - 6 C-atoms, a nitro, trifluoromethyl or cyano group, or a phenoxy group optionally substituted by halogen atoms, or by alkyl or alkoxy groups having 1 - 4 C-atoms, Y.sub.4 and Y.sub.5 represent H-atoms or halogen atoms, or alkyl or alkoxy groups having 1 - 4 C-atoms.

Dyestuffs likewise preferred are those of the formula ##STR6## wherein R.sup.3 has the aforesaid meaning, and R.sup.5 represents an aromatic or heterocyclic radical; and especially those of the formula ##STR7## wherein Y.sub.1 and Y.sub.2 have the aforesaid meaning, and R.sup.6 represents a radical of the formulae ##STR8## wherein Y.sub.1 - Y.sub.5 have the aforesaid meaning.

Also preferred are dyestuffs of the formulae ##STR9## wherein R.sup.3, V, Y.sub.1 - Y.sub.5 have the above meaning, and Z represents an O-atom or S-atpm or an NH-group. R.sub.3 stands preferably for a radical of the formulae ##STR10##

The mentioned dyestuffs constitute for the most part known compounds that can be obtained by the processes described in the GB-patent specification No. 1,187,667, for example starting with 1,3-diiminoisoindoline according to the following reaction sequence: ##STR11## The 1,3-diiminoisoindoline to be used as starting material can be present or react also in its tautomeric form as amino-imino-isoindolenine.

The following diiminoisoindolines may be mentioned as examples:

1,3-diimino-isoindoline, 1,3 -diimino-5-methyl-isoindoline, 1,3-diimino-5-methoxy-isoindoline, 1,3-diimino-6-methoxy-isoindoline, 1,3-diimino-5-phenoxy-isoindoline, 1,3-diimino-5-phenyl-isoindoline, 1,3-diimino-6-phenyl-isoindoline, 1,3-diimino-4-chloro-isoindoline, 1,3-diimino-5-chloro-isoindoline, 1,3-diimino-6-chloro-isoindoline, 1,3-diimino-7-chloro-isoindoline, 1,3-diimino-5,6-diphenyl-isoindoline, 1,3-diimino-4,5-dichloro-isoindoline.

Suitable starting materials are also the 1,3,3-trichloro-isoindole derivatives of the formula ##STR12## wherein X.sub.1 - X.sub.4 have the aforementioned meaning, for example 1,3,3-trichloro-isoindolenine, or 1,3,3,4,5,6,7-hept chloro-isoindolenine.

From the trichloro-isoindolenines there are obtained, by reaction with ammonia or with amines or with alkali alcoholates, amino- or alkoxy-isoindolines which likewise are suitable as starting materials.

As compounds R.sup.1 H.sub.2 and R.sup.2 H.sub.2, which react successively with the 1,3-diiminoisoindolines or trichloroisoindolenines there are mentioned:

a. malonic acid-dialkyl esters such as malonic acid-dimethyl ester or malonic acid-diethyl ester, or malonic acid dinitrile;

b. cyanoacetic acid alkyl esters, the alkyl radicals of which can be derived from the widest variety of alcohols, such as from methanol, ethanol, normal-, iso- and tert.-butanol and amyl alcohols; from mixtures of C.sub.6 - C.sub.8 alcohols such as are generally obtainable by known syntheses; from alcohols of the aliphatic series such as lauryl alcohol or octadecanol; from cycloaliphatic alcohols such as cyclohexanol or menthol; from aliphatic alcohols containing further substituents, such as glycol-monoalkyl ether, ethylenechlorohydrin, .beta.-cyanethanol, .beta.-phenoxy- or .beta.-phenylmercaptoethanol, .beta.-phenylethyl alcohol, .gamma.-phenyl-propanol, .gamma.-phenylallyl alcohol; from benzyl alcohol and substitution products thereof, such as 4-methyl-, 2- and 4-chloro-, 3,4-dichloro- 2,4,6-trichlorobenzyl alcohols; or from alcohols derived from heterocycles, such as tetrahydrofurfural alcohol;

c. cyanacetamides, the amide radicals of which can be derived from ammonia and from the widest range of primary or secondary amines, such as methyl-, ethyl- or butylamine, 3-methoxypropylamine, anilines, for example 2-, 3- or 4-chloroaniline, 2,4-, 3,4- or 2,5-dichloroaniline, 2-, 3- or 4-methylaniline, 2,4-, 3,4- or 2,5-dimethylaniline, 2-, 3-or 4-methoxy- or -ethoxyaniline, 3-trifluoromethylaniline, 4-nitroaniline, 2,3- or 4-methoxycarbonylaniline or 4-phenoxyaniline;

d. .beta.-cyano ketones, such as cyanoacetone and cyanoacetophenone;

e. benzyl cyanide, as well as derivatives thereof substituted in the 2-, 3- and/or 4-position by fluorine, chlorine or bromine, and 3- and 4-nitrobenzyl cyanide;

f. acetonitriles carrying heterocyclic substituents, such as

pyrazolyl-(3)-acetonitrile, imidazolyl-(4)-acetonitrile, 2-cyanomethyl-benzimidazole, 2-cyanomethyl-6-methoxy-benzimidazole, 2-cyanomethyl-5,6-dimethyl-benzimimdazole, 2-cyanomethyl-5,7-dimethyl-benzimidazole, 2-cyanomethyl-6-chlorobenzimidazole, 2-cyanomethyl-5,6-dichlorobenzimidazole, 2-cyanomethyl-6-phenoxy-benzimidazole, 2-cyanomethyl-6-methyl-benzimidazole, 1-methyl-2-cyanomethyl-benzimidazole, 1-.beta.-hydroxyethyl-2-cyanomethyl-benzimidazole, 1.beta.-cyanoethyl-2-cyanomethyl-benzimidazole, 2-cyanomethyl-1H-naphth [2,3-d]-imidazole, 1-methyl-1,2,3-triazolyl-(4)-acetonitrile, 2-phenyl-1,2,3-triazolyl-(4)-acetonitrile, 5-phenyl-1,2,3-triazolyl-(4)-acetonitrile, tetrahydrobenzo-1,2,3-triazolyl-(1)-acetonitrile, 4-phenyl-1,2,4-triazolyl-(3)-acetonitrile, isoxazolyl-(3)-acetonitrile, 2-cyanomethyl-benzoxazole, thiazolyl-(4)-acetonitrile, 2-methyl-thiazolyl-(4)-acetonitrile, 2-cyanomethyl-benzothiazole, pyridyl-(2)-acetonitrile, pyridyl-(3)-acetonitrile, pyridyl-(4)-acetonitrile, quinolyl-(2)-acetonitrile, quinazolyl-(2)-acetonitrile, quinoxalyl-(2)-acetonitrile;

g. iso- or heterocyclic ketomethylene compounds having a 5- or 6-membered ring, or hydroxy compounds that are able to react like ketomethylene compounds, such as:

3-methyl-pyrazolone-(5), 1-phenyl-3-methyl:pyrozolone-(5), 1,2-diphenyl-3,5-dioxo-pyrazolidine, indoxyl, N-methyl-indoxyl, oxindole, N-methyl- and N-ethyl-oxindole, barbituric acid, 3-hydroxy-thionaphthene, 2,4-dioxo-1,2,3,4-tetrahydroquinoline, N-methyl-2,4-dioxo-1,2,3,4-tetrahydroquinoline, resorcin, dihydro-resorcin, phloroglucin, 1,3-diketohydrindene, coumarins;

h. Primary amines of the heterocyclic series, such as:

1-phenyl-3-methyl-5-amino-pyrazole, 2-amino-benzimidazole, 1-methyl-2-amino-benzimidazole, 2-amino-benzoxazole, 2-amino-5-nitro-benzoxazole, 2-amino-4-phenyl-thiazole, 2-amino-4-methyl-5-carbethoxy-thiazole, 2-amino-benzothiazole, 2-amino-6-methoxy-, 6-ethoxy- and -6-dimethylamino-benzothiazole, 3-amino-1,2,4-triazole, 3-amino-5-carbethoxy-1,2,4-triazole, 2-amino-1,3,4-oxidazole, 2-amino-5-cyclohexyl-, -5-benzyl- and 5-.gamma.-pyridyl-1,3,4-oxidiazole, 2-amino-5-phenyl-1,3,4-oxdiazole, 5-amino-3-phenyl-1,2,4-thiadazole, 2-amino-5-phenyl-1,3,4-thiadiazole, 3-amino-sulpholane, 2-amino-pyridine.

Suitable as compounds R.sup.2 H.sub.2, which can be reacted with the intermediate products (e.g. of the formula II), are also, for example:

i. primary amines of the aliphatic or aromatic series, such as methyl- and ethylamine,, 2l -hydroxy-ethyl-amine, ethylenediamine and .gamma.-dimethylamino-propylamine, benzylamine, aniline, o-, m- and p-toluidine, xylidines, mesidine, 2-, 3- and 4-chloro- or alkoxy-anilines, 3-nitroaniline, 3- and 4-amino-acetanilide or -benzanilide, N-monophthalyl-p-phenylenediamine, 3- and 4-aminobenzoic acid ester, 3-and 4-cyananiline, 3-amino-benzamide or -benzanilide, 3-amino-benzenesulphoneamide and 2-phenyl-5-amino-benzotriazole-(1,2,3);

k. hydrazines having a free NH.sub.2 -group, such as hydrazine, 1.1-dimethyl-hydrazine, phenylhydrazine, halogeno- and nitro-phenylhydrazines, N-amino-piperidine, N-aminomorpholine, N-amino-2-methyl-2,3-dihydro-indole and N-amino-1,2,3,4-tetrahydroquinoline.

The dyestuffs according to the invention can be used as individual products or as mixtures in the dyeing process.

Thermoplastics which can be dyed with the dyestuffs mentioned are: polystyrene, ABS-rubber, polyamides and, in particular, linear polyesters. The corresponding spinning fibres are preferred.

As linear polyesters there may be mentioned, in particular, those which are obtained by polycondensation of terephthalic acid or esters thereof with glycols of the formula (HO--(CH.sub.2).sub.n --OH, wherein n represents the number 2 - 10, or with 1,4-di(hydroxymethyl)-cyclohexane; or by polycondensation of glycol ethers of hydroxybenzoic acids, for example p-(.beta.-hydroxyethoxy)-benzoic acid. The term `linear polyesters` embraces also copolyesters that are obtained by partial replacement of the terephthalic acid with another dicarboxylic acid, and/or by partial replacement of the glycol with another diol.

Of particular interest however are the polyethylene terephthalates.

The linear polyesters to be dyed are intimately mixed advantageously in the form of powder, chips or granules with the dyestuff. This is carried out, for example, by sprinkling the polyester particles with the finely divided dry dyestuff powder, or by treating the polyester particles with a solution or dispersion of the dyestuff in an organic solvent and subsequently removing the solvent.

Finally, the substance to be dyed can also be added directly to the melted polyester, or it can be added before or during the polycondensation of the polyethylene terephthalate.

Depending on the depth of colour desired, the ratio of dyestuff to polyester can vary within wide limits. In general, the use of 0.01 - 3 parts of dyestuff to 100 parts of polyester is recommended.

The polyester particles treated in this manner are melted by known processes in the extruder, and moulded to form articles, particularly films or fibres, or they are cast into the form of sheets.

There are obtained evenly and thoroughly dyes articles having good fastness to light. The dyed fibres obtainable by the said processes are characterised also by good general textile fastness properties, especially fastness to wet-processing, dry-cleaning and heat. The dyestuffs have only a slight tendency to sublime away on application in the melt, an effect which results in particularly good fastness to bleeding and in only slight susceptibility to migration, as well as in good fastness to rubbing after thermofixing.

A special advantage of the dyestuffs to be used according to the invention is that they dissolve in the polyester melt and withstand surprisingly high temperatures of up to 300.degree. C without decomposing, so that there are obtained dyeings that are considerably more clear than those obtained using insoluble pigments.

Except where otherwise stated in the following Examples, the term `parts` denotes parts by weight; percentage denote per cent by weight, and temperature values are given in degrees Centigrade.

EXAMPLE 1

A non-delustered polyethylene terephthalate granulate suitable for producing fibres is shaken together with 1% of the dyestuff of the formula I ##STR13## in a closable vessel on a shaking machine for 15 minutes. The evenly dyed granules are spun on a melt spinning machine (285.degree. .+-. 3.degree., retention time in the spinning machine about 5 minutes) into filaments which are drawn and spooled on a draw twister. By virtue of the solubility of the dyestuff in polyethylene terephthalate, there is obtained a brilliant yellow dyeing which is characterised by outstanding fastness to light and by excellent fastness to washing, dry-cleaning, cross-dyeing and sublimation, as well as by a high resistance to chlorite bleaching.

There are given in the following Table further dyestuffs of the formula ##STR14## which are obtained by condensing 1,3-diimino-isoindoline stepwise with the compounds of the formulae R.sup.1 H.sub.2 and R.sup.2 H.sub.2 shown in Columns II and III. In Column IV are listd the shades of the resulting melt dyeings in polyester.

______________________________________ Shade ofNo. R.sup.1 H.sub.2 R.sup.2 H.sub.2 dyeing______________________________________2 2-cyanomethyl-benzimi- 2-cyanomethyl-benz- red dazole imidazole3 " 4-aminobenzoic acid yellow ethyl ester4 " cyanoacetamide orange5 " cyanoacetanilide orange6 2-cyanomethyl-6-chloro- " orange benzimidazole7 2-cyanomethyl-benzimi- 2',5'-dichlorocyano- orange dazole acetanilide8 " 3',4'-dichlorocyano- orange acetanilide9 2',4'-dimethyl-cyano- 4-methoxyaniline yellow acetanilide10 2-cyanomethyl-benzimi- 3,4-dichloroaniline yellow dazole11 " 4-chloroaniline yellow12 " 4-methoxyaniline yellow13 " 4'-methyl-cyano- orange acetanilide14 " 4'-chloro-cyano- orange acetanilide15 4'-chloro-cyanoacet- " yellow anilide16 2-cyanomethyl-benzimi- 2'-ethoxycarbonyl- orange dazole cyanoacetanilide17 2-cyanomethyl-6-meth- 4-chloroaniline yellow oxy-benzimidazole18 2-cyanomethyl-5,6-di- 4'-methyl-cyano- orange methyl-benzimidazole acetanilide19 2-cyanomethyl-5,7-di- " orange methyl-benzimidazole20 2-cyanomethyl-6-meth- 4'-chloro-cyano- orange oxy-benzimidazole acetanilide21 2-cyanomethyl-6-ethoxy- 4-chloroaniline yellow benzimidazole22 2-cyanomethyl-6-meth- 4-chloroaniline yellow oxycarbonyl-benzimi- dazole23 2-cyanomethyl-5,6-di- cyanoacetanilide red chloro-benzimidazole24 2-cyanomethyl-6-phen- 4-chloroaniline yellow oxy-benzmimidazole25 2-cyanomethyl-6-meth- " yellow yl-benzimidazole26 4'-.beta.-phenoxyethoxy- 4' -.beta.-phenoxyeth- cyanoacetanilide oxy-cyanoacetanilide red27 2',3'-dichloroacet- 2',3'-dichloroacet- yellow anilide anilide28 2-cyanomethyl-benzimi- cyanoacetic acid orange dazole methyl ester29 " cyanoacetic acid orange ethyl ester30 " cyanoacetic acid-.beta.- orange methoxyethyl ester31 " cyanoacetic acid- orange osibutyl ester32 2-cyanomethyl-6-meth- 4-.beta.-phenoxyethoxy- yellow oxy-benzimidazole aniline33 2-cyanomethyl-benz- 4'-phenoxy-cyano- red imidazole acetanilide34 " 4'-.beta.-phenoxyeth- oxy-cyanoacetanilide red35 " 4-phenoxyaniline yellow36 " benzylamine yellow37 " 4-.beta.-butoxyethoxy- yellow aniline38 " 4'-amino-dimethyl- yellow diphenyl-methane39 " malonitrile red40 2-aminobenzimidazole 4-aminobenzoic yellow ethyl ester41 2-aminobenzimidazole 4-aminodiphenyl- yellow ether42 2-amino-6-methoxy- " yellow benzimidazole43 cyanoacetic acid cyanoacetic acid yellow ether ester ethyl ester44 1-methyl-2-cyanometh- aniline yellow yl-benzimidazole45 " cyanoacetanilide orange46 1-.beta.-hydroxyethyl-2- 4-chloroaniline yellow cyanomethyl-benzimi- dazole47 1-.beta.-cyanoethyl-2-cyano- " yellow methyl-benzimidazole48 2-cyanomethyl-benzimi- cyanoacetic acid orange dazole cyclohexyl ester49 " cyanoacetic acid orange benzyl ester50 cyanoacetanilide 4-hydroxy-coumarin orange51 4'-chloro-cyanoacet- 4-hydroxy-6-methyl- orange anilide coumarin52 2-cyanomethyl-benzimi- 4-hydroxy-coumarin orange dazole53 " ethanolamine yellow54 " aminoresorcin-di- yellow o-cresyl ester55 " aminoresorcin- orange dimethyl ether56 " 4-.beta.-phenoxyethoxy- yellow aniline______________________________________

EXAMPLE 57

A solution of 4 g of 2-cyanomethyl-benzimidazole and 25 ml of methanol is added dropwise to a suspension of 12.75 g of 1,3,3-trimorpholino-4,5,6,7-tetrachloroisoindolenine in 50 ml of methanol. Stirring is maintained for 1 hour at room temperature, and the temperature is subsequently raised to the reflux temperature, with the reaction mixture, from which the condensation product precipitates as a red-brown substance, being diluted with a further 50 ml of methanol. Filtration is performed hot and the residue is washed with methanol and water to obtain, after drying, 9.0 g of the dyestuff of the formula ##STR15##

EXAMPLES 58 - 61

1000 parts of polyethylene terephthalate granulate and 10 parts of titanium dioxide and 1 part of the dyestuffs described in the following Table are mixed together in a closed vessel for 2 hours on a rolling device. The dyes granulate is extruded at about 260.degree. into the form of strands of 2 mm diameter, and the material is again granulated. The granulate obtained is injection moulded at 270 .degree. - 280.degree., in an anchor injection-extrusion automatic machine, into moulded articles. There are obtained delustered, intensively dyed moulded shapes having good fastness to light.

In the following Table there are listed dyestuffs of the formula ##STR16## which are obtained if the dyestuffs produced according to Example 57 of the formula ##STR17## wherein R.sup.1 is derived from the methylene-active compound given in Column II, are reacted with the compound R.sup.2 H.sub.2, given in Column III, in glacial acetic acid. Column IV shows the shade of the 1% dyed moulded articles made from polyesters. The dyeings are characterised by good fastness to light.

______________________________________ Shade ofNo. R.sup.1 H.sub.2 R.sup.2 H.sub.2 dyeing______________________________________58 2-cyanomethyl-benzimi- aniline orange dazole59 " 4-amino-diphenyl- orange ether60 " cyanoacetanilide orange61 cyanoacetanilide aniline yellow______________________________________

Claims

1. Process for the dyeing of thermoplastics in the melt, which process comprises the use of dyestuffs of the formula ##STR18## wherein X.sub.1 - X.sub.4 represents H-atoms or halogen atoms, or one or two of the radicals X.sub.1 - X.sub.4 represent alkyl, alkoxy, phenyl or phenoxy groups, and those remaining represent H-atoms, R.sup.1 and R.sup.2 represent radicals of methylene-active compounds, or radicals of the formula .dbd.N--A wherein A stands for the radical of an aliphatic, cycloaliphatic, araliphatic, aromatic or heterocyclic amine or hydrazine, whereby, provided that R.sup.1 and R.sup.2 represent radicals of the formula .dbd.N--A, one A represents a heterocyclic radical containing N-atoms, optionally together with O- or S-atoms.

2. Process according to claim 1, which process comprises the use of dyestuffs of the formula ##STR19## wherein R.sup.3 and R.sup.4 represent cyano, acyl, alkoxycarbonyl, carbamoyl or sulphamoyl groups, or radicals of the formula ##STR20## wherein V represents an O- or S-atom or an imino group, or an alkylimino group containing 1 - 4C-atoms, Y.sub.1 and Y.sub.2 represent H-atoms or halogen atoms, or alkyl or alkoxy groups containing 1 - 4 C-atoms.

3. Process according to claim 2, which process comprises the use of dyestuffs of the formula ##STR21## wherein Y.sub.1 and Y.sub.2 have the meaning given in claim 2, Y.sub.3 represents a H-atom or halogen atom, an alkyl or alkoxy group optionally substituted by alkoxy groups having 1 - 4 C-atoms, or by phenoxy or phenyl groups, an alkanoylamino or alkylsulphonyl group having 1- 4 C-atoms, an alkoxycarbonyl group having 2 - 6 C-atoms, a nitro, trifluoromethyl or cyano group, or a phenoxy group optionally substituted by halogen atoms or by alkyl or alkoxy groups having 1 - 4 C-atoms, Y.sub.4 and Y.sub.5 represent H-atoms or halogen atoms, or alkyl or alkoxy groups having 1 - 4 C-atoms.

4. Process according to claim 1, which process comprises the use of dyestuffs of the formula ##STR22## wherein R.sup.3 has the meaning given in claim 2, and R.sub.5 represents an aromatic or heterocyclic radical.

5. Process according to claim 4, which process comprises the use of dyestuffs of the formula ##STR23## wherein Y.sub.1 and Y.sub.2 have the meaning given in claim 2, R.sub.6 represents a radical of the formula ##STR24## and Y.sub.1 - Y.sub.5 have the meaning given in claims 2 and 3.

6. Process according to claim 5, which process comprises the use of a dyestuff of the formula ##STR25##

7. Process according to claim 5, which process comprises the use of a dyestuff of the formula ##STR26##

8. Process according to claim 1, wherein the thermoplastics dyed are spinning fibres.

9. Process according to claim 1, wherein the thermoplastics dyed are linear polyesters.