Process for the manufacture of pentafluoroethane

Abstract

An improved process for the manufacture of CF.sub.3 CHF.sub.2 by contacting CF.sub.3 CHCl.sub.2 or CF.sub.3 CHClF with HF in the presence of a Cr.sub.2 O.sub.3 catalyst prepared by pyrolysis of ammonium dichromate, the reaction being conducted under controlled conditions whereby the production of CF.sub.3 CHF.sub.2 is maximized, and the formation of chloropentafluoroethane (CF.sub.3 CClF.sub.2) and other perhalo derivatives is minimized. The subject hydrogen-containing compound is useful as a blowing agent, propellant, refrigerant, fire extinguishing agent, or sterilant carrier gas.

Description

FIELD OF THE INVENTION

An improved process for the manufacture of pentafluoroethane (CF.sub.3 CHF.sub.2) comprising a gas-phase reaction of 2,2-dichloro-1,1,1-trifluoroethane (CF.sub.3 CHCl.sub.2) or 1,1,1,2-tetrafluorodichloroethane (CF.sub.3 CHClF) with HF in the presence of a Cr.sub.2 O.sub.3 catalyst prepared by pyrolysis of ammonium dichromate, the reaction being conducted under controlled conditions whereby the production of CF.sub.3 CHF.sub.2 is maximized, and the formation of chloropentafluoroethane (CF.sub.3 CClF.sub.2) and other perhalo derivatives is minimized. The subject hydrogen-containing compound is useful as a blowing agent, propellant, refrigerant, fire extinguishing agent, or sterilant carrier gas. It is desirable for its zero ozone depletion potential.

BACKGROUND OF THE INVENTION

U.S. Pat. No. 3,755,477 describes a process for producing fluorinated aliphatic hydrocarbons which comprises fluorinating a halogenated aliphatic hydrocarbon, including tetrachloroethylene and chlorotrifluoroethylene, by reaction in the gas phase with HF in the presence of a steam-treated and calcined chromium oxide catalyst prepared by a multi-step process. Example 23, column 5, shows tetrachloroethylene as a raw material with formation of CF.sub.3 CHCl.sub.2 (20%), CF.sub.3 CHClF (20%), CF.sub.3 CHF.sub.2 (30%), and CF.sub.3 CClF.sub.2 (20%) at 10/1 HF/C.sub.2 Cl.sub.4 mole ratio, 5.4 seconds contact time and 350.degree. C. reaction temperature. Example 25 shows that, with CF.sub.3 CHCl.sub.2 as starting material at 390.degree. C., CF.sub.3 CHClF (21%) and CF.sub.3 CHF.sub.2 (67%) are produced, but again these desirable hydrogen-containing products are accompanied by perhalogenated CF.sub.3 CClF.sub.2 (CFC-115, 2.5%). The formation of CF.sub.3 CClF.sub.2, 20% in 24 and 2.5% in 25, is objectionable; not only does it constitute a yield loss of the hydrogen-containing substances, but CF.sub.3 CClF.sub.2 is extremely close boiling to CF.sub.3 CHF.sub.2 with the resulting mix being costly to separate.

U.S. Pat. No. 3,258,500 describes a process for the catalytic vapor-phase reaction of HF with halohydrocarbons employing a catalyst that consists essentially of a heat-activated anhydrous chromium (III) oxide which may be supported on alumina. Example 17, column 14, shows that fluorination of tetrachloroethylene with this catalyst at 400.degree. C. produces 35.0% pentafluoroethane, 9.2% 1-chloro-1,2,2,2-tetrafluoroethane, and 3.5% 1,1-dichloro-2,2,2-trifluoroethane. At 300.degree. C. the product distribution is 38.3% 1-chloro-l,2,2,2-tetrafluoroethane, 25.4% pentafluoroethane, and 16.0% 1,1-dichloro-2,2,2-trifluoroethane. Example 20, column 19, shows that chlorotrifluoroethylene at 400.degree. C. yields 27% CF.sub.3 CHF.sub.2. It can be seen that, although the yield of the hydrogen-containing products is high, that of pentafluoroethane does not exceed about 35% even at temperatures as high as 400.degree. C.

U.S. Pat. No. 4,843,181 discloses a gas phase process for the manufacture of CF.sub.3 CHCl.sub.2 and/or CF.sub.3 CHClF by contacting a suitable tetrahaloethylene and/or pentahaloethane with HF in the presence of Cr.sub.2 O.sub.3 prepared by pyrolysis of (NH.sub.4).sub.2 Cr.sub.2 O.sub.7, the reaction being conducted under controlled conditions whereby the production of CF.sub.3 CHF.sub.2 is minimized.

Canadian Patent 849,024 also discloses the formation of CF.sub.3 CHF.sub.2 by reaction of HF with a perhaloethylene, e.g., C.sub.2 Cl.sub.4, CCl.sub.2 =CF.sub.2 and CClF=CF.sub.2, over a hydrous Cr.sub.2 O.sub.3 as catalyst, but the CF.sub.3 CHF.sub.2 yields are relatively poor.

Canadian Patent 1,196,345 discloses that addition of HF to perfluoroethylene over a chromium oxyfluoride as catalyst, which has been activated by treatment with a mixture of HF and F.sub.2, produces CF.sub.3 CHF.sub.2 in high yields. Much inferior yields are obtained using a comparable catalyst activated with HF alone. The disclosed process suffers in that the catalyst activation step not only involves the use of expensive and hazardous molecular fluorine, but requires a back-up scrubbing solution of hexafluoropropylene trimer to scavenge unreacted F.sub.2. All this represents a loss of F.sub.2 and catalyst activation potential, and further adds to the cost of the process.

The prior art, in general, has shown that CF.sub.3 CHCl.sub.2 is obtainable in good yields from tetrachloroethylene, a readily available and relatively inexpensive commodity. However, CF.sub.3 CHCl.sub.2 as starting material for the production of highly fluorinated hydrogen-containing products by reaction with HF also yields perhalo by-products, evidently via chlorination side reactions, especially when an attempt is made to increase conversion to the desired hydrogen-containing products by operating at high temperatures.

SUMMARY OF THE INVENTION

A process for the preparation of pentafluoroethane which comprises contacting HF with CF.sub.3 CHCl.sub.2 or CF.sub.3 CHClF in the gas phase in the presence of a Cr.sub.2 O.sub.3 catalyst at a reactant mole ratio, a feed rate of reactant per weight catalyst, temperature and pressure and for a time effective to form a gas product stream containing CF.sub.3 CHCl.sub.2 as the predominant component, the catalyst being prepared by pyrolysis of (NH.sub.4).sub.2 Cr.sub.2 O.sub.7.

Preferably, the Cr.sub.2 O.sub.3 catalyst has an alkali metal content of not more than 100 ppm.

Preferably, too, the starting material is CF.sub.3 CHCl.sub.2, and said conditions are controlled such that the CF.sub.3 CHF.sub.2 product is substantially free of CF.sub.3 CClF.sub.2.

This invention is based on the discovery that Cr.sub.2 O.sub.3 prepared by pyrolysis of (NH.sub.4).sub.2 Cr.sub.2 O.sub.7 is effective to catalyze conversion of CF.sub.3 CHCl.sub.2 and the next higher fluorinated intermediate, CF.sub.3 CHClF , to CF.sub.3 CHCl.sub.2 in high yields at high conversions of the starting materials without undue formation of CF.sub.3 CClF.sub.2 and other perhalogenated by-products.

Accordingly, it is an object of this invention to provide a process for the production of CF.sub.3 CHF.sub.2 using CF.sub.3 CHCl.sub.2 as starting material, which results in the formation of CF.sub.3 CHF.sub.2 in high yields at high conversions.

Another object of this invention is to provide such process which substantially avoids the formation of close boiling CF.sub.3 CClF.sub.2.

Still another object of this invention is to provide such process as above that utilizes a catalyst that is readily available and is effective in catalyzing the halogen exchange reaction of HF with CF.sub.3 CHCl.sub.2 and CF.sub.3 CHClF , such that the formation of CF.sub.3 CHF.sub.2 is maximized.

DETAILS OF THE INVENTION

The Cr.sub.2 O.sub.3 catalyst of this invention is prepared by pyrolysis of ammonium dichromate by any method known to the art, including methods such as that described in U.S. Pat. No. 4,471,985 incorporated herein by reference.

By pyrolysis is meant heating ammonium dichromate to a sufficient temperature and for a sufficient time to cause the following reaction to occur to substantial completion:

(NH.sub.4).sub.2 Cr.sub.2 O.sub.7 .fwdarw.Cr.sub.2 O.sub.3 +4H.sub.2 O+N.sub.2 For example, ammonium dichromate may be heated in a continuous kiln at 500.degree.-700.degree. C., preferably 540.degree.-640.degree. C., for 5-20 minutes so that it will undergo an internal oxidation-reduction reaction to produce mainly water, nitrogen and Cr.sub.2 O.sub.3. After the water and nitrogen are driven off, the remaining fine powder of Cr.sub.2 O.sub.3 may be cooled and compacted so as to increase its bulk density for ease of handling. For example, a bulk density of approximately 400-560 Kg/m.sup.3 may be desirable, preferably 448-512 kg/m.sup.3.

The Cr.sub.2 O.sub.3 obtained may contain low levels of contaminants which are present as a result of the manufacturing process for the original (NH.sub.4).sub.2 Cr.sub.2 O.sub.7. Although not totally destructive of catalyst efficacy, potassium, for example, as a contaminant has an adverse effect on the activity and life of the catalyst of this invention. It is desirable for the amount of potassium and other alkali metals to be 100 ppm by weight or less. The level may be reduced by a water-washing step. While the conditions are not critical, the water-washing step can include forming a slurry containing 5-15% Cr.sub.2 O.sub.3, preferably 10%, and deionized water. Stirring of this water slurry can be carried out at 35.degree.-65.degree. C. for at least one hour, preferably two or more hours. The solids are then recovered by filtration, suitably on a plate and frame filter press. The filter cake can be analyzed for alkali metal content. If its level is 100 ppm by weight or less (dry basis), the solids are, thereafter, dried. If not, the washing step can be repeated to obtain a desired level of alkali metal content.

The form of the catalyst is not critical and may be used as pellets, powders or granules.

For example, if the catalyst is desired to be in the pellet form, 5-15%, preferably 10%, of chromium acetate and 1-5%, preferably 2% of graphite can be added to the dried solids as pelletization aids. The chromium acetate can be added in aqueous solution of 30-70%, preferably 50% concentration. The resultant paste can be mulled to mix the ingredients and then pelletized to the desired size, preferably 0.32 cm.times.0.32 cm cylinders. The pellets can be dried at 80.degree.-120.degree. C., preferably 105.degree. C., for 8-48 hours, preferably 16-24 hours. The Cr.sub.2 O.sub.3 pellets then have a bulk density of 1120-1440 Kg/m.sup.3 for the preferred pellet size and a surface area of 40-57 m.sup.2 /g, preferably 45-55 m.sup.2 /g. Pore volume is 0.15-0.33 cc/g. The alkali metal content is 100 ppm or less.

Generally, the resulting Cr.sub.2 O.sub.3 will be pretreated with HF. It is thought that this converts some of the surface chrome oxide to chrome oxyfluoride. This pretreatment can be accomplished by placing the Cr.sub.2 O.sub.3 in a suitable container, which can be the reactor to be used to perform the reaction of the instant invention, and thereafter, passing HF over the pyrolyzed and dried Cr.sub.2 O.sub.3 so as to partially saturate the Cr.sub.2 O.sub.3 with HF. This is conveniently carried out by passing HF over the Cr.sub.2 O.sub.3 for a period of time, for example, about 15 to 300 minutes at a temperature of, for example, about 200.degree. C. to about 450.degree. C. The purpose of this pretreatment is to prevent damage to the catalyst due to possible high temperature excursions and resultant coking of the catalyst if the organic reactants were contacted with the catalyst without first having conditioned some of the surface chrome oxide with HF. Nevertheless, this pretreatment is not essential; initial process conditions and equipment could be selected so as to avoid the problem of high temperature and coking of the catalyst.

The contacting of the reactants with HF in the presence of the catalyst, preferably pretreated, of the instant invention is performed at effective temperature, mole ratio and contact time. By effective temperature, mole ratio and contact time is meant the temperatures, mole ratios and contact times which produce a product stream which contains CF.sub.3 CHF.sub.2 in a major proportion, preferably in an amount of at least about 50%, more preferably at least about 60%, as determined by gas chromatography.

With CF.sub.3 CHCl.sub.2 or CF.sub.3 CHClF as the reactant the temperature will normally range from about 300.degree. to about 370.degree. C., preferably about 330.degree. to 350.degree. C. The HF/CF.sub.3 CHCl.sub.2 mole ratio will normally range from 2/1 to about 10/1, preferably from about 3/1 to 8/1. The contact time can vary widely but preferably will be such as to provide an average residence time of from about 10 to 100 seconds, more preferably 20 to 50 seconds.

The pressure is not critical but should be sufficient to maintain HF, the organic reactant and the reaction product stream components in the vapor state at the operating temperature.

In general, the higher the temperature, the greater the HF/reactant mole ratio, and the longer the contact time, the greater is the conversion of the reactants to fluorinated products, and the greater is the degree of fluorination of the raw material. The above variables can be balanced, one against the other, so that formation of CF.sub.3 CHF.sub.2 is maximized and that of perhalogenated by-products is minimized, preferably to less than about 3%, with that of CF.sub.3 CClF.sub.2 to less than 2%, more preferably to less than 1%, said percents being mole percents as determined by gas chromatography.

Unreacted starting material and intermediate CF.sub.3 CHClF can be recycled to the reactor for the production of additional CF.sub.3 CHF.sub.2.

The reaction of the reactants with HF may be conducted in any suitable reactor, included fixed and fluidized bed reactors. The reaction vessel should be constructed from materials which are resistant to the corrosive effects of hydrogen fluoride and hydrogen chloride, such as "Hastelloy" and "Inconel".

EXAMPLES

The catalyst used in the following runs was Cr.sub.2 O.sub.3 prepared by pyrolyzing (NH.sub.4).sub.2 Cr.sub.2 O.sub.7 as described above and had an alkali metal content of 60 ppm. It was in cylindrical pellet form, 1/8 inch long and 1/8 inch in diameter; its bulk density was about 100 lbs/cubic foot. The catalyst was packed in a Schedule 40 "Inconel" 600 U-shaped pipe reactor, 1 inch in diameter and 4 feet long, which was immersed in a temperature-controlled molten salt bath which provided isothermal reaction conditions.

The catalyst was activated by gradually heating the packed reactor to 400.degree. C. while N.sub.2 gas at a flow rate of 50 ml/minute was passed through it to remove trace water. The temperature was lowered to 200.degree. C., and HF and N.sub.2 gases (1:4 molar ratio) were passed through the reactor. The HF employed for activation and all of the CF.sub.3 CHF.sub.2 production runs was commercial grade containing only trace amounts of water. The N.sub.2 flow was decreased with time until neat HF was passing through the reactor. At this point, the temperature was gradually raised to 420.degree. C. and maintained for 16 hours.

For hydrofluorination, the reactor temperature was decreased to that indicated in the runs described below. The organic and HF feeds were vaporized external to the salt bath, mixed and fed to a separate catalyst-free section of the pipe reactor, which served as a preheater, before entering the catalyst-packed reactor. The reactant flows were adjusted to give the indicated rates, mole ratios and average residence times, calculated by dividing the volume of the reactor by the volumetric flow rate of the combined HF and organic feeds at the temperature and pressure of operation. The reaction temperature was determined by the salt bath temperature; the pressure was set by a back-pressure regulator.

The reactor effluent was scrubbed with aqueous KOH, and its composition determined with an in-line gas chromatograph. The chromatograph was equipped with a flame ionization detector and used a 20 foot long, 1/8 inch diameter column, packed with "Krytox" perfluorinated polyether on an inert support, and a helium carrier at a flow rate of 20 cc/minute. The gas chromatograph was temperature programmed such that it was held at 40.degree. C. for 4 minutes, followed by a temperature ramp of 5.degree./minute until 180.degree. C. was reached and maintained for 5 minutes. The results recorded below are in mole percent.

EXAMPLE 1

A mixture of HF and CF.sub.3 CHCl.sub.2 was fed to the reactor at a mole ratio of HF/CF.sub.3 CH.sub.2 Cl.sub.2 =6:1 and a CF.sub.3 CHCl.sub.2 feed rate of 0.333 lb/hour per pound of catalyst. The reaction pressure was 100 psig; the temperature was varied in a series of runs as tabulated in Table 1.

TABLE 1__________________________________________________________________________ Composition, Mole %Run Temp. .degree.C. CF.sub.3 CHF.sub.2 CF.sub.3 CHClF CF.sub.3 CHCl.sub.2 CF.sub.3 CClF.sub.2 Other*__________________________________________________________________________1 305 6.6 52.1 40.9 0.0 0.42 315 14.9 57.0 27.6 0.0 0.53 325 36.4 44.0 18.8 0.04 0.84 340 67.5 19.3 11.2 0.22 1.8__________________________________________________________________________ *Included CF.sub.3 CH.sub.2 F, CClF.sub.2 CHF.sub.2, CF.sub.3 CH.sub.2 Cl CF.sub.3 Cl.sub.2 F, CClF.sub.2 CClF.sub.2 and CClF.sub.2 CHClF, each in an amount of less than 1%.

The results show that the invention catalyst is highly effective to catalyze the conversion of CF.sub.3 CHCl.sub.2 to hydrogen-containing products at relatively moderate temperatures, and that the CF.sub.3 CHF.sub.2 make increases sharply with increasing CF.sub.3 CHCl.sub.2 conversions at increasing temperatures without undue production of perhalo by-products.

Lowering the CF.sub.3 CHCl.sub.2 feed rate results in its increased conversion to CF.sub.3 CHClF and subsequently to CF.sub.3 CHF.sub.2. This is illustrated in the following Examples.

EXAMPLE 2

The procedure of Example 1 was repeated except that the temperature was held constant at about 326.degree. C. The HF/CF.sub.3 CHCl.sub.2 mole ratio (MR), the CF.sub.3 CHCl.sub.2 feed rate (FR) and the average residence time (ART) in seconds are tabulated in Table 2.

TABLE 2__________________________________________________________________________Run MR FR CF.sub.3 CHF.sub.2 CF.sub.3 CHClF CF.sub.3 CHCl.sub.2 Other* ART__________________________________________________________________________1 6/1 0.333 40.7 42.1 16.4 0.8 302 5.4/1 0.3 44.6 42.4 12.5 0.5 293 5.6/1 0.222 56.2 30.6 12.1 1.1 484 10/1 0.111 63.6 26.2 7.0 3.2 6019 7/1 0.111 70.8 19.8 6.9 2.5 73__________________________________________________________________________ *Included were CF.sub.3 CH.sub.2 F, CClF.sub.2 CHF.sub.2, CF.sub.3 CH.sub.2 Cl, CClF.sub.2 CHClF, CCl.sub.2 FCHClF, CF.sub.3 CCl.sub.3 and CF.sub.3 CClF.sub.2, each in an amount less than 1%.

It will be noted that conversion of CF.sub.3 CHCl.sub.2 to CF.sub.3 CHF.sub.2 is high, even at a temperature as low a 326.degree. C., and the conversion increases with decreasing CF.sub.3 CHCl.sub.2 feed rate per unit weight of catalyst.

EXAMPLE 3

Example 2 was repeated except the temperature was 350.degree.-351.degree. C., and the mole ratios were varied, as noted in Table 3.

TABLE 3__________________________________________________________________________Run MR FR CF.sub.3 CHF.sub.2 CF.sub.3 CHClF CF.sub.3 CHCl.sub.2 Other* ART__________________________________________________________________________1 5.2/1 0.333 79.1 11.5 6.9 2.5 322 5.1/1 0.333 75.6 13.8 8.2 2.4 293 6/1 0.222 81.9 10.3 5.2 2.6 43.54 5.8/1 0.222 80.2 11.0 6.0 2.8 42.55 8/1 0.111 85.9 7.9 3.2 3.0 66__________________________________________________________________________ *Included were CF.sub.3 CH.sub.2 F, CClF.sub.2 CHF.sub.2, CF.sub.3 CH.sub.2 Cl, CClF.sub.2 CHClF, CF.sub.3 CCl.sub.3, CClF.sub.2 CClF.sub.2, CF.sub.3 CCl.sub.2 F, CClF.sub.2 CCl.sub.2 F and CF.sub.3 CClF.sub.2, wit the CF.sub.3 CClF.sub.2 make reaching a maximum of about 1% in Run 5. No other byproduct amounted to more than 1%.

Again, the results demonstrate the outstanding activity of the subject catalyst to promote the production of CF.sub.3 CHF.sub.2 at the expense of chlorine-containing perhalo side-products, even at 350.degree. C. The overall results show that, the higher the temperature and the greater the residence time, the higher the conversion and the yields, with the yields of hydrogen-containing products amounting to 90% or better in Runs 3, 4 and 5. This is particularly significant since CF.sub.3 CHClF , the intermediately fluorinated product, can be recycled for further production of the desired pentafluorinated ethane.

Claims

1. A process for the preparation of CF.sub.3 CHF.sub.2 comprising:

(a) contacting HF with at least one reactant selected from the group consisting of CF.sub.3 CHCl.sub.2 and CF.sub.3 CHClF in the gas phase in the presence of a catalyst comprising Cr.sub.2 O.sub.3 at a mole ratio, feed rate of reactant per weight of catalyst, temperature and pressure and for a time effective to form a gas stream containing CF.sub.3 CHCl.sub.2 as the predominant component and thereafter,

(b) separating and recovering CF.sub.3 CHF.sub.2 from the product stream.

2. The process of claim 1 wherein the reaction temperature is in the range of from about 300.degree. to 370.degree. C.

3. The process of claim 2 wherein the temperature is 330.degree. to 350.degree. C.

4. The process of claim 3 wherein the CF.sub.3 CHF.sub.2 content is at least about 60 mole % of the gas product stream as determined gas-chromatographically.

5. The process of claim 4 wherein the CF.sub.3 CClF.sub.2 content of the gas product stream is less than about 2 mole %.

6. A process for producing pentafluoroethane comprising the steps of:

(a) pyrolyzing a material comprising ammonium dichromate to obtain Cr.sub.2 O.sub.3 ;

(b) contacting hydrogen fluoride with at least one member from the group consisting of CF.sub.3 CHCl.sub.2 and CF.sub.3 CHClF while in the presence of said Cr.sub.2 O.sub.3, wherein at least a portion of said at least one member is converted to pentafluoroethane without substantial formation of perhalogenated by-products, and;

(c) recovering the pentafluoroethane.

7. The process of claim 6 wherein the pentafluoroethane is CF.sub.3 CHF.sub.2.

8. The process of claim 6 wherein said chrome oxide has an alkali metal content of less than about 100 ppm.

9. The process of claim 6 wherein said perhalogenated by-products is CF.sub.3 CClF.sub.2.

10. The process of claim 6 further comprising pretreating said chrome oxide with hydrogen fluoride before said contacting.

11. The process of claim 6 wherein the pressure is sufficient to maintain at least one member of the group consisting of hydrogen fluoride, CF.sub.3 CHCl.sub.2, CF.sub.3 CHClF and pentafluoroethane, in a vapor state.

12. The process of claim 6 further comprising recycling at least a portion of said at least one member.

13. A process for preparing CF.sub.3 CHF.sub.2 comprising the steps of:

(a) contacting hydrogen fluoride with at least one member selected from the group consisting of CF.sub.3 CHCl.sub.2 and CF.sub.3 CHClF, while in the presence of Cr.sub.2 O.sub.3 to form a product comprising CF.sub.3 CHF.sub.2, wherein said product is substantially free of CF.sub.3 CClF.sub.2, and

(b) recovering said product.