Process for the oxychlorination of ethylene and catalyst compositions for the oxychlorination

Information

  • Patent Grant
  • 4910354
  • Patent Number
    4,910,354
  • Date Filed
    Friday, June 26, 1987
    37 years ago
  • Date Issued
    Tuesday, March 20, 1990
    34 years ago
Abstract
The invention relates to a process for the oxychlorination of ethylene by means of a catalyst composition comprising an alumina support impregnated with cupric chloride, magnesium chloride and a chloride of an alkali metal chosen from sodium and lithium. The oxychlorination performed in this manner makes it possible to obtain an excellent yield without the reactor being corroded by the catalyst composition employed.
Description

FIELD OF THE INVENTION
The present invention relates to a process for the oxychlorination of ethylene with the use of a catalyst composition permitting an improved yield to be obtained and simultaneously giving rise to a reduced corrosion effect in stainless steel reactors, particularly through a reduction in the adhesion and lumping of the catalyst particles.
TECHNOLOGY REVIEW
Chlorination of gaseous hydrocarbons with the use of hydrogen chloride and air or oxygen is an operation which has been known for a long time. This chlorination is usually carried out in the presence of catalysts consisting of metal salts deposited on inert supports. The metal salts which are generally employed are halides such as cupric chloride which, when employed by itself, has nevertheless the disadvantage of being relatively volatile, and this results in a drop in catalytic activity and in the yield of the oxychlorination reaction, which is industrially unacceptable, when this compound is employed in a fluidized bed in an industrial plant.
To overcome these disadvantages it has been proposed to incorporate into the catalyst compositions other metal salts such as the chlorides of alkali and alkaline-earth metals and of other metals derived from the rare earths or lanthanides (British Patent GB-969,937, Belgian Patent BE-741,055).
These various catalyst compositions have activities which depend in particular on the nature of the hydrocarbon which is to be used and the nature of the metal salt or salts added to reduce the effects of the volatility of cupric chloride. Furthermore, these various catalyst compositions also give rise to corrosive action on the steel of industrial reactors, due in particular to the adhesion and lumping of the catalyst particles on the walls. This corrosion is one of the effects which, in the present state of knowledge, cannot be deduced either qualitatively or quantitatively from the technical data relating to the nature of the salts used, and which must be investigated empirically in the case of each catalyst composition which is envisaged.
SUMMARY OF THE INVENTION
Copper- and magnesium-based catalyst compositions have now been found, which make it possible to manufacture 1,2-dichloroethane by the oxychlorination of ethylene, with an activity and a yield which have never been reached industrially with compositions containing these two metals. At the same time, these compositions give rise to minimum adhesion and lumping of the catalyst particles, as well as minimum corrosion of the industrial reactor.





BRIEF DESCRIPTION OF THE DRAWINGS
FIGS. 1 to 4 illustrate corrosion of stainless steel reactors in which four tests were carried out using catalyst compositions containing different quantities of sodium, as shown in Table 1 below. FIGS. 1, 2 and 3 illustrate a weak and acceptable steel corrosion. On the other hand, FIG. 4 illustrates a high and industrially unacceptable steel corrosion.
FIGS. 5 to 13 also illustrate corrosion of stainless steel reactors (AISI 316 L steel) in which six tests were carried out with catalyst compositions containing various quantities of lithium, as set forth in Table 2 below. FIG. 9 illustrates that when operating above a certain lithium limit, unacceptable adhesion and lumping of catalyst particles. occurs. FIGS. 10 and 12 illustrate that when the lithium limits of the catalysts of the invention are exceeded, high adhesion and high lumping are obtained, and this makes corrosion measurements in an erosimeter impossible (FIG. 11 and FIG. 13).





DETAILED DESCRIPTION OF THE INVENTION
Consequently, the present invention relates to a process for the oxychlorination of ethylene to 1,2-dichloroethane, in which the oxychlorination reaction is catalysed by a catalyst composition comprising an alumina support on which there are deposited cupric chloride, magnesium chloride and an alkali metal chloride chosen from sodium chloride and lithium chloride.
When the alkali metal employed is sodium, the operation is preferably carried out with atomic ratios of copper salts to sodium salts of 1:0.01-0.2. It has been found, in fact, that in the case of sodium salts, corrosion of stainless steel reactors is observed, and this becomes considerable or even unacceptable when Cu:Na atomic ratios of 1:0.2 are exceeded.
On the other hand, when the alkali metal is lithium, the atomic ratio Cu:Li is less critical and it is possible to operate with Cu:Li ratios ranging from 1:0.0001 to 1:2.
The invention also relates to catalyst compositions for the oxychlorination of hydrocarbons comprising either
(1) cupric chloride, magnesium chloride and NaCl in atomic ratios of between 1:0.1-1.5:0.01-0.2, deposited on alumina, or
(2) cupric chloride, magnesium chloride and LiCl, deposited on alumina. In this case, the ratios of the various salts are usually between 1:0.1-1.5:0.0001-1.5 and preferably between 1:0.3-1:0.001-1.
The alumina employed in the catalyst compositions of the invention may be of any provenance and may be produced by any known process; eta- or gamma-type aluminas are usually employed. Good results have been obtained with a gamma-type alumina.
The alumina generally employed in the catalyst compositions of the invention has a mean particle diameter of between 20 and 100 .mu.m and preferably a mean diameter of between 25 and 75 .mu.m.
The specific surface of the alumina, measured according to the B.E.T. method, is generally between 50 m.sup.2 /g and 250 m.sup.2 /g. Good results have been obtained with an alumina having a specific surface between 100 m.sup.2 /g and 210 m.sup.2 /g.
Lastly, the pore volume of the aluminas usually employed lies between 0.1 and 1 cm.sup.3 /g. The pore volume is preferably between 0.2 and 0.8 cm.sup.3 /g and good results have been obtained with an alumina having a pore volume between 0.3 and 0.6 cm.sup.3 /g.
It should be noted that alumina naturally contains a greater or lesser quantity of sodium atoms which may be integrated into the crystalline lattice or may be bonded in any chemical form. The presence of these sodium atoms, which may be described more conveniently as "unwashable sodium atoms", is of no importance for the present invention, which relates solely to catalyst compositions which contain an alkali metal, in salt form, which can be considered as being a "washable alkali metal". These alkali metal salts are not bonded chemically to the alumina support and are generally introduced into the catalyst compositions by impregnating the alumina with the salt in question. This impregnation with the alkali metal salt required may be carried out either at the same time as impregnation with the other salts, or before, or after this impregnation.
The way in which the catalyst compositions according to the invention are produced is not critical per se, provided that the catalyst compositions finally obtained correspond to the characteristics described above. A preparative method which has produced good results consists in impregnating a .gamma. alumina having the following characteristics:
mean particle diameter of approximately 50 .mu.m,
B.E.T. specific surface of between 170 and 190 m.sup.2 /g,
pore volume of between 0.4 cm.sup.3 /g, and
free-flow packing density of 0.75 kg/dm.sup.3.
This impregnation is carried out in a single step at a temperature of 75.degree. C. with an aqueous solution containing the required quantities of copper, magnesium and alkali metal chlorides. The appearance of a liquid phase which is not adsorbed by the solid is avoided by restricting the volume of the impregnating solution to 70 to 100% of the pore volume of the quantity of alumina employed. This impregnated alumina is then dried before being introduced into the oxychlorination reactor as such.
The catalyst compositions finally employed in the oxychlorination process generally have a copper content, calculated as metal, of between 30 g/kg and 90 g/kg. This quantity preferably lies between 50 and 75 g/kg and catalyst compositions which are most particularly preferred are those having a copper content between 60 and 70 g/kg.
The content of the other salts in the catalyst compositions can, in its turn, be readily deduced from the copper contents specified in this manner together with the atomic ratios already detailed above.
The final catalyst compositions generally have a B.E.T. specific surface of between 25 m.sup.2 /g and 200 m.sup.2 /g and preferably between 50 and 150 m.sup.2 /g. Good results have been obtained with catalyst compositions having a B.E.T. specific surface between 100 and 140 m.sup.2 /g.
The catalyst compositions may be employed in any oxychlorination process carried out with a catalyst arranged in a stationary bed or a fluidized bed. They are particularly advantageous in a process in which the catalyst is in the form of a fluidized bed, because of an improved yield and because of the absence of corrosion in stainless steel reactors.
When the operation is carried out with a catalyst arranged in a fluidized bed, the temperature at which the oxychlorination reaction takes place is usually between 200.degree. and 300.degree. C. Preferably, this temperature lies between 220.degree. and 280.degree. C. Lastly, good results have been obtained with a temperature situated in the region of 240.degree. C.-270.degree. C.
The pressure at which the oxychlorination reaction is performed is not critical in itself. Usually, the operation is carried out using pressures of between 1 and 10 atm and preferably using pressures of between 1 and 8 atm.
The fluidization velocity of the catalyst compositions is not critical in itself and depends essentially on the particle size distribution of the catalyst and on the size of the apparatus. In general, the operation is carried out using velocities of between 5 and 100 cm/s and preferably between 10 cm/s and 50 cm/s.
Lastly, the reactant ratio which is used is the same as that generally employed in earlier processes. The operation is customarily carried out with a slight excess of ethylene relative to the quantity of HCl employed. However, the catalyst compositions of the invention also make it possible to work in the vicinity of stoichiometry, or even excess of HCl.
The invention is more fully illustrated by the examples which follow.
EXAMPLE 1
225 cm.sup.3 of a catalyst composition consisting of a gamma-type alumina, having a mean specific surface of 190 m.sup.2 /g, impregnated with an aqueous solution of copper, magnesium and sodium chlorides, are arranged, after drying, in a reactor made of Inconel 600, for fluid bed oxychlorination of ethylene to 1,2-dichloroethane, and equipped with small plates made of AISI type 316L austenitic stainless alloy.
In this reactor, the reactant gases are introduced via the bottom through a sintered metal filter. The reaction products are then depressurized to atmospheric pressure by a reactor pressure control valve. The reaction products are then cooled in a trap maintained at -20.degree. C. and the uncondensed gases are washed in a water scrubber before sweeping over a sampling bulb. The balance of the products formed is established from chromatographic analyses of the liquid and gaseous products collected and from acidimetric titration of the aqueous solution collected at the foot of the scrubber.
4 tests are carried out using catalyst compositions containing different quantities of sodium, such as are shown in Table 1 below. This Table 1 also includes the reactor operating conditions and the results obtained.
The yields obtained in these laboratory trials are limited by the residence time, restricted to 5 s. The conversion of C.sub.2 H.sub.4 is consequently limited in all the trials (the operating conditions of an industrial reactor make it possible to reach residence times which are markedly longer: 10 to 80 s, and in most cases from 20 to 50 s, in order to ensure better ethylene conversion).
TABLE 1______________________________________TEST 1 2 3 4______________________________________I. Catalyst(a) supportalumina:type .gamma. .gamma. .gamma. .gamma.specific-surface 190 190 186 190(m.sup.2 /g)(b) catalyst compositionCu in g/kg 57 60 58 58.5Mg in g/kg 16.5 17 17.7 16.2Na in g/kg 0.1 1.0 1.7 6.2BET specific surface 120 122 124 113m.sup.2 /gII. Operating conditions for the oxychlorinationHCl: Nl/h 160 160 160 160air: Nl/h 260 260 260 260C.sub.2 H.sub.4 : Nl/h 84 84 84 84t.degree.: .degree.C.* 255 255 255 255pressure: bars absolute 6 6 6 6fluidization velocity 10 10 10 10(cm/s)contact time: s 5 5 5 5YIELD:1,2-DCE (mol %)C.sub.2 H.sub.4 employed 90.5 91.5 91.8 91.8C.sub.2 H.sub.4 conversion 95.5 96 96 95mol %Formation of:C.sub.2 H.sub.5 Cl mol % 1.6 0.6 0.5 0.6based on theC.sub.2 H.sub.4 employedCorrosion of weak weak weak strongAISI 316 L steel (FIG. 1) (FIG. 2) (FIG. 3) (FIG. 4)______________________________________ *Stable temperature profile in the reactor: the temperature of the fluid bed does not deviate by more than 2.degree. C. from average temperature.
From the comparison of the results of the various tests it may be concluded that:
when operating below the sodium limits of the present invention (test 1), the yield of 1,2-dichloroethane is lower than that obtained with the catalyst compositions of the invention (tests 2 and 3). On the other hand, the steel corrosion is weak and acceptable;
when operating above the sodium limits of the present invention (test 4) the yield of 1,2-dichloroethane is excellent and comparable to that obtained according to the invention (tests 2 and 3). On the other hand, the steel corrosion is high and thus unacceptable from an industrial standpoint;
when operating within the sodium limits of the present invention (tests 2 and 3), an excellent yield of 1,2-dichloroethane and a weak and acceptable steel corrosion are observed at the same time.
EXAMPLE 2
225 cm.sup.3 of a catalyst composition consisting of a gamma-type alumina, having a mean specific surface of 180 to 190 m.sup.2 /g, impregnated with an aqueous solution of copper, magnesium and lithium chlorides, are arranged, after drying, in a reactor made of Inconel 600, for fluid bed oxychlorination of ethylene to 1,2-dichloroethane, and equipped with small plates made of AISI type 316L austenitic stainless alloy.
In this reactor, the reactant gases are introduced via the bottom through a sintered metal filter. The reaction products are then depressurized to atmospheric pressure by a reactor pressure control valve. The reaction products are then cooled in a trap maintained at -20.degree. C. and the uncondensed gases are washed in a water scrubber before sweeping over a sampling bulb. The balance of the products formed is established from chromatographic analyses of the liquid and gaseous products collected and from acidimetric titration of the aqueous solution collected at the foot of the scrubber.
6 tests are carried out with catalyst compositions containing various quantities of lithium such as are given in Table 2 below. This Table 2 also includes the reactor operating conditions and the results obtained.
The yields obtained in these laboratory trials are limited by the residence time, restricted to 5 s. The conversion of C.sub.2 H.sub.4 is consequently limited in all the trials (the operating conditions of an industrial reactor make it possible to reach residence times which are markedly longer: 10 to 80 s, and in most cases from 20 to 50 s, in order to ensure better ethylene conversion).
TABLE 2__________________________________________________________________________TEST 5 6 7 8 9 10__________________________________________________________________________I. Catalyst(a) support:alumina:type .gamma. .gamma. .gamma. .gamma. .gamma. .gamma.specific surface (m.sub.2 /g) 190 190 180 180 180 180(b) catalyst compositionCu in g/kg 59 60 59.6 58.1 56.5 56.9Mg in g/kg 16.6 16.1 16.1 16.2 13.6 14.5Li in g/kg 0.3 1 2.1 4.2 11.2 21.4BET specific surface m.sup.2 /g 117 123 99 94 88 67II. Operating conditions for the oxychlorinationHCl: Nl/h 160 160 160 160 160 160air: Nl/h 260 260 260 260 260 260C.sub.2 H.sub.4 : Nl/h 84 84 84 84 84 84t.degree.: .degree.C.* 255 255 255 255 255 255pressure: bars absolute 6 6 6 6 6 6fluidization velocity (cm/s) 10 10 10 10 10 10contact time: s 5 5 5 5 5 5YIELD:1,2-DCE (mol %)C.sub.2 H.sub.4 employed 91.5 91.6 91.7 88 83 ndC.sub.2 H.sub.4 conversion/mol % 97 96.4 95.4 91.2 88 ndFormation of:C.sub.2 H.sub.5 Cl mol % based 0.7 0.6 1.15 2.25 3.25 --on the C.sub.2 H.sub.4 employedCorrosion of weak weak weak weak -- --AISI 316 L steel FIG. 5 FIG. 6 FIG. 7 FIG. 8 FIG. FIG. and 9 10 and 12 and 11 13__________________________________________________________________________ *Stable temperature profile in the reactor: the temperature of the fluid bed does not deviate by more than 2.degree. C. from average temperature. nd: not determined
From the comparison of the results of the various tests it may be concluded that when operating above a certain lithium limit, the yield of 1,2-dichloroethane falls rapidly (tests 8 and 9) although the steel corrosion is weak but becomes unacceptable because of the adhesion and lumping of the catalyst particles (FIG. 9). From the results of the various tests it may also be concluded that when the lithium limits of the catalysts according to the invention are exceeded, the catalysts become unusable in practice because, in this case, high adhesion and high lumping are obtained (FIG. 10 and FIG. 12), and this makes corrosion measurements in an erosimeter impossible (FIG. 11 and FIG. 13).
Claims
  • 1. A process for the oxychlorination of ethylene to 1,2-dichloroethylene, wherein the oxychlorination reaction is catalyzed by a catalyst composition consisting essentially of an alumina support on which there are deposited cupric chloride, magnesium chloride, and sodium chloride, in an atomic ratio of:
  • Na:Mg:Cu=0.05-0.08:0.74-0.80:1.
  • 2. The oxychlorination process of claim 1, wherein said cupric chloride, magnesium chloride, and sodium chloride are deposited in an atomic ratio of about 1:0.74:0.05.
  • 3. The oxychlorination process of claim 1, wherein said cupric chloride, magnesium chloride, and sodium chloride are deposited in an atomic ratio of about 1:0.74:0.08.
  • 4. The oxychlorination process of claim 1, wherein said cupric chloride, magnesium chloride, and sodium chloride are deposited in an atomic ratio of about 1:0.80:0.08.
Priority Claims (1)
Number Date Country Kind
86 09504 Jun 1986 FRX
US Referenced Citations (5)
Number Name Date Kind
3468968 Baker et al. Apr 1987
3624170 Wakiyama et al. Nov 1971
4069170 Blake et al. Jan 1978
4124534 Leitert et al. Nov 1978
4460699 Convers et al. Jul 1919
Foreign Referenced Citations (5)
Number Date Country
2095351 Feb 1972 FRX
43-003761 Feb 1968 JPX
46-040251 Nov 1971 JPX
958458 May 1964 GBX
969937 Sep 1964 GBX