Process for the photochemical and thermal stabilization of undyed and dyed or printed polyester fiber materials

The present invention relates to a process for the photochemical and thermal stabilization of undyed and dyed or printed polyester fiber materials.
Dyed or printed polyester fiber materials are damaged by the action of light and, in particular, by the simultaneous action of heat. For use in the automotive field, the provision of an effective protection of undyed and dyed or printed fiber materials from UV radiation is indispensable.
Accordingly, the invention provides a process for the photochemical and thermal stabilization of undyed and dyed or printed polyester fiber materials, which comprises treating said materials with a compound of formula ##STR2## wherein R.sub.1 is hydrogen or C.sub.1 -C.sub.5 alkyl,
R.sub.2 is C.sub.1 -C.sub.12 alkyl, and
n is 0 to 5.
C.sub.1 -C.sub.12 Alkyl groups are straight-chain or branched hydrocarbon radicals, typically methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, amyl, isoamyl or tert-amyl, heptyl, octyl, isooctyl, nonyl, undecyl or dodecyl.
It is preferred to use compounds of formula (1), wherein R.sub.1 and R.sub.2 are each independently of the other C.sub.1 -C.sub.4 alkyl.
Among this group of compounds, those compounds are of particular interest wherein R.sub.1 and R.sub.2 are each independently of the other methyl or ethyl and, most preferably, those compounds wherein n=1 to 3.
Typical examples of compounds of formula (1) are:
4,6-bis(2-hydroxy-4-methoxyphenyl)-2-(2-propoxyethoxy)-1,3,5-triazine
4,6-bis(2-hydroxy-4-propoxyphenyl)-2-(2-methoxyethoxy)-1,3,5-triazine
4,6-bis(2-hydroxy-4-ethoxyphenyl)-2-(2-methoxyethoxy)-1,3,5-triazine
4,6-bis(2-hydroxy-4-methoxyphenyl)-2-(2-methoxyethoxy)-1,3,5-triazine
4,6-bis(2-hydroxy-4-methoxyphenyl)-2-(2-ethoxyethoxy)-1,3,5-triazine
4,6-bis(2-hydroxy-4-methoxyphenyl)-2-[2-(2-ethoxyethoxy)ethoxy]-1,3,5-triazine
4,6-bis(2-hydroxy-4-ethoxyphenyl)-2-(2-ethoxyethoxy)-1,3,5-triazine
4,6-bis(2-hydroxy-4-ethoxyphenyl)-2-[2-(2-ethoxyethoxy)ethoxy]-1,3,5-triazine
4,6-bis(2-hydroxy-4-ethoxyphenyl)-2-(2-ethoxy-2-methylethoxy)-1,3,5-triazine
4,6-bis(2-hydroxy-4-methoxyphenyl)-2-{2-[2-(2-ethoxy)ethoxy]ethoxy}ethoxy-triazine
4,6-bis(2-hydroxy-4-ethoxyphenyl)-2-{2-[2-(2-ethoxy)ethoxy]ethoxy}ethoxy-1,3,5-triazine
4,6-bis(2-hydroxy-4-ethoxyphenyl)-2-butoxy-1,3,5-triazine.
The compounds of formula (1) are prepared in a manner known per se by reacting a 4,6-bis(2-hydroxy-4-alkoxyphenyl)-1,3,5-triazine of formula ##STR3## with a compound of formula
M--(OCH.sub.2 CH.sub.2).sub.n --OR.sub.1 ( 3)
according to the following scheme: ##STR4## wherein R is halogen or a radical of formula S-R',
R' is C.sub.1 -C.sub.4 alkyl, phenyl or benzyl,
R.sub.1 is hydrogen or C.sub.1 -C.sub.5 alkyl,
R.sub.2 is C.sub.1 -C.sub.12 alkyl,
M is alkali metal, and
n is 0 to 5.
It is preferred to use starting compounds of formula (2), wherein R is thio-C.sub.1 -C.sub.4 alkyl, preferably thiomethyl.
The starting compounds of formula (2) are known, inter alia from CH-436,285. These starting compounds may be prepared substantially in accordance with the process disclosed in EP-A-0,395,938 by reacting cyanuric chloride with C.sub.1 -C.sub.4 alkylmercaptan and the corresponding benzenoid compound.
The compounds of formula (3) will be understood as meaning the alkali metal salts of alcohols of general formula
H--(OCH.sub.2 CH.sub.2).sub.n --OR.sub.1. (3a)
Suitable compounds of formula (3) are polyethylene glycol monoalkyl ethers containing 1 to 5, preferably 1 to 3 ethylene oxide units. Exemplary of such compounds are ethylene glycol monoalkyl ethers such as methyl cellosolve, ethyl cellosolve or propyl cellosolve or diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol monopropyl ether or diethylene glycol monobutyl ether or the corresponding tri-, tetra- or pentaethylene glycol monoalkyl ethers.
It is also possible to use saturated, branched and unbranched aliphatic C.sub.1 -C.sub.5 monoalcohols, typically methanol, ethanol, propanol, isopropanol, butanol, isobutanol, tert-butyl alcohol or amyl alcohol.
It is preferred to use the alcohols in the form of their lithium, potassium or sodium salts, the corresponding sodium alcoholates being preferred.
Some of the compounds of formula (1) are known, inter alia from CH-436,285, and some are also novel compounds.
The novel compounds have the formula ##STR5## wherein R'.sub.1 is hydrogen or C.sub.1 -C.sub.5 alkyl,
R'.sub.2 is C.sub.1 -C.sub.12 alkyl, and
n' is 1 to 5.
Preferred compounds of formula (1') are those wherein R'.sub.1 and R'.sub.2 are each independently of the other C.sub.1 -C.sub.4 alkyl.
Particularly interesting compounds are those wherein R'.sub.1 and R'.sub.2 are each independently of the other methyl or ethyl and, most especially, those compounds wherein n'=1 to 3.
The UV absorbers of this invention are used in an amount of 0.5 to 7.5% by weight, preferably of 0.2 to 3% by weight and, most preferably, of 0.5 to 2% by weight, based on the weight of the fibre material.
The UV absorbers of this invention are sparingly soluble in water are therefore applied in dispersed form. To this end they are milled with an appropriate dispersant, conveniently using quartz balls and an impeller, to a particle size of 1-2 .mu.m.
Suitable dispersants for the UV absorbers of formula (1) are:
acid esters or their salts of alkylene oxide adducts, typically acid esters or their salts of a polyadduct of 4 to 40 mol of ethylene oxide with 1 mol of a phenol, or phosphated polyadducts of 6 to 30 mol of ethylene oxide with 1 mol of 4-nonylphenol, 1 mol of dinonylphenol or, preferably, with 1 mol of compounds which are prepared by addition of 1 to 3 mol of styrenes to 1 mol of phenol,
polystyrene sulfonates,
fatty acid taurides,
alkylated diphenyl oxide mono- or disulfonates,
sulfonates of polycarboxylates,
the polyadducts of 1 to 60 mol of ethylene oxide and/or propylene oxide with fatty amines, fatty acids or fatty alcohols, each containing 8 to 22 carbon atoms in the alkyl chain, with alkylphenols containing 4 to 16 carbon atoms in the alkyl chain, or with trihydric to hexahydric alkanols containing 3 to 6 carbon atoms, which polyadducts are converted into an acid ester with an organic dicarboxylic acid or with an inorganic polybasic acid,
ligninsulfonates, and, most preferably,
formaldehyde condensates such as condensates of ligninsulfonates and/or phenol and formaldehyde, condensates of formaldehyde with aromatic sulfonic acids, typically condensates of ditolyl ether sulfonates and formaldehyde, condensates of naphthalenesulfonic acid and/or naphthol- or naphthylaminesulfonic acids with formaldehyde, condensates of phenolsulfonic acids and/or sulfonated dihydroxydiphenylsulfone and phenols or cresols with formaldehyde and/or urea, as well as condensates of diphenyl oxide-disulfonic acid derivatives with formaldehyde.
Suitable dyes are disperse dyes which are only sparingly soluble in water. They are therefore substantially present in the dye liquor in the form of a fine dispersion. They may belong to different dye classes, including the acridone, azo, andiraquinone, coumarin, methine, perinone, naphthoquinone-imine, quinophthalone, styryl or nitro dyes. Mixtures of disperse dyes may also be used in the practice of this invention.
Polyester fiber material which can be dyed or printed and treated with the cited UV absorbers will be understood as including cellulose ester fibers such as cellulose secondary acetate and cellulose triacetate fibers and, preferably, linear polyester fibers which may also be acid-modified, and which are obtained by the condensation of terephthalic acid with ethylene glycol or of isophthalic acid or terephthalic acid with 1,4-bis(hydroxymethyl)cyclohexane, as well as copolymers of terephthalic and isophthalic acid and ethylene glycol. The linear polyester fiber material hitherto used almost exclusively in the textile industry consists of terephthalic acid and ethylene glycol.
The fiber materials may also be used as blends with each other or with other fibers, typically blends of polyacrylonitrile/polyester, polyamide/polyester, polyester/cotton, polyester/viscose and polyester/wool, and they can be dyed or also printed batchwise or continuously.
The textile material can be in different forms of presentation, preferably as piece goods such as knitgoods or wovens or also as yam on cheeses, warp beams and the like.
Dyeing is carried out from an aqueous liquor by a continuous or batch process. In batchwise dyeing, the liquor ratio may be chosen over a wide range, typically from 1:4 to 1:100, preferably from 1:6 to 1:50. The dyeing temperature is at least 50.degree. C. and is normally not higher than 140.degree. C. The preferred temperature range is from 80.degree. to 135.degree. C.
In continuous dyeing methods, the dye liquors, which my contain further auxiliaries in addition to the dyes, are applied to the piece goods by padding or slop-padding and developed by thermofixation or HT steaming processes.
Linear polyester fibers and cellulose fibers are preferably dyed by the high temperature process in closed and pressure-resistant apparatus in the temperature range >100.degree. C., preferably in the range from 110.degree. to 135.degree. C., and at normal or elevated pressure. Suitable closed apparatus includes typically circulation dyeing machines such as cheese or beam dyeing machines, winch becks, jet or drum dyeing machines, muff dyeing machines, paddles or jiggers.
For continuous dyeing, padders or lick rollers are used and development is carried out with hot air in stenter frames or in HT steamers.
Cellulose secondary acetate is preferably dyed in the temperature range from 80.degree.-85.degree. C.
When using the novel UV absorbers for dye application, the procedure is such that the fiber material is first treated with these compounds and then dyeing is carried out or, preferably, the fiber material is treated simultaneously in the dyebath with the UV absorber and the dye. The application of the UV absorber can, however, also be made subsequently to the ready prepared dyeing by thermofixation, conveniently at 190.degree.-230.degree. C. over a period of 30 seconds to 5 minutes.
The dye liquors may also contain further ingredients such as dyeing assistants, dispersants, carriers, wool protectives, and wetting agents as well as antifoams.
The dyebaths may also contain mineral acids, typically sulfuric acid or phosphoric acid, or conveniently organic acids, typically aliphatic carboxylic acids such as formic acid, acetic acid, oxalic acid or citric acid and/or salts such as ammonium acetate, ammonium sulfate or sodium acetate. The acids are used in particular to adjust the pH of the liquors used in the practice of this invention to 4-5.
Preferably the fiber material is first run in the bath which contains the dye, the UV absorber and any further auxiliaries and which has been adjusted to pH 4.5-5.5 at 40.degree.-80.degree. C., then the temperature is raised to 125.degree.-130.degree. C. over 10 to 20 minutes, and further treatment is carried out for 15 to 90 minutes, preferably for 30 minutes, at this temperature.
The dyeings are finished by cooling the dye liquor to 50.degree.-80.degree. C., washing off the dyeings with water and, if necessary, reduction clearing them in conventional manner in alkaline medium. The dyeings are then again washed off and dried. When using vat dyes for dyeing the cellulose moiety, the goods are first treated with hydrosulfite at pH 6-12.5, then treated with an oxidising agent and finally washed off.
For producing prints, the novel UV absorbers are mixed in the form of aqueous dispersions with the print pastes. The print paste then contains the UV absorber in an amount of 0.5 to 5%, preferably 1 to 2%, based on the weight of the print paste.
The amount of dye added to the print pastes will depend on the desired shade. Normally amounts of 0.01 to 15% by weight, preferably of 0.02 to 10% by weight, have been found useful.
In addition to containing the dyes and the aqueous dispersion of he UV absorber, the print pastes conveniently contain acid-stable thickeners, preferably of natural origin such as carob bean flour derivatives, especially sodium alginate by itself or in admixture with modified cellulose, preferably with 20 to 25% by weight of carboxymethyl cellulose. If desired, the print pastes may further contain acid donors such as butyrolactone or sodium hydrogen phosphate, preservatives, sequestering agents, emulsifiers, water-insoluble solvents, oxidizing agents or dearating agents.
Particularly suitable preservatives are formaldehyde donors such as paraforrnaldehyde and trioxane, preferably c. 30 to 40% by weight aqueous formaldehyde solutions. Suitable sequestering agents are sodium nitrilotriacetate, sodium ethylenediaminetetraacetate, preferably sodium polymethaphosphate, more particularly sodium hexamethaphosphate. Emulsifiers are preferably polyadducts of an alkylene oxide and a fatty alcohol, more particularly a polyadduct of oleyl alcohol and ethylene oxide. Water-insoluble solvents are preferably high-boiling saturated hydrocarbons, more particularly paraffins having a boiling range from about 160.degree. to 210.degree. C. (white spirits). Oxidizing agents are typically aromatic nitro compounds, preferably an aromatic mono- or dinitrocarboxylic acid or mono- or dinitrosulfonic acid which may be in the form of an alkylene oxide polyadduct, preferably a nitrobenzenesulfonic acid. Deaerating agents are suitably high-boiling solvents, preferably terpentine oils, higher alcohols, C.sub.8 -C.sub.10 alcohols, terpene alcohols or deaerating agents based on mineral and/or silicone oils, preferably commercial formulations comprising about 15-25% by weight of a mixture of mineral and silicone oils and about 75-85% by weight of a C.sub.8 alcohol such as 2-ethyl-n-hexanol.
For printing the fiber materials, the print paste is applied direct to the whole or to a part of the surface, conveniently using printing machines of conventional construction, typically rotogravure, rotary screen printing and surface screen printing machines.
The fiber material is dried after printing in the temperature range up to 150.degree. C., preferably in the range from 80.degree. to 120.degree. C.
The subsequent fixation of the fiber material is usually carried out by a heat treatment, preferably in the temperature range from 100.degree. to 220.degree.. The heat treatment is normally carried out with superheated steam under atmospheric pressure.
Depending on the temperature, fixation is carried out for 20 seconds to 10 minutes, preferably for 4 to 8 minutes.
The prints are also finished in conventional manner by washing off with water, followed by an optional reductive afterclear in alkaline medium, conveniently with sodium dithionite. In this last mentioned case, the prints are again washed off, hydroextracted and dried.
The process of this invention makes it possible to obtain dyeings and prints of superior lightfastness and sublimation fastness on polyester material. A systematic pre- or aftertreatment of the fibre material is not necessary in the inventive process.

In the following working and application Examples percentages are by weight. The amounts of dye and UV absorber are based on pure substance.
PREPARATION OF THE UV ABSORBERS
Example 1
3.5 g (0.15 mol) of sodium are dissolved in 180 ml of propyl cellosolve. With stirring, 18.6 g (0.05 mol) of 2-thiomethyl-4,6-bis(2-hydroxy-4-methoxyphenyl)-1,3,5-triazine are added and the reaction mixture is stirred for 4 hours at 83.degree.-85.degree. C. The reaction mixture is cooled to room temperature and then poured into 200 ml of ice-water and 170 ml of 1N HCl and filtered. The filter product is washed with methanol and dried at 80.degree. C. in a vacuum drier, giving 20.6 g of a pale product of formula ##STR6##
Yield: 96.4% of theory, mp: 119.degree.-120.degree. C, .lambda..sub.max : 296/351 nm.
Elemental analysis: found: 61.70% C; 5.9% H; 9.9% N; calcd. as C.sub.22 H.sub.25 N.sub.3 O.sub.6 : 61.82% C; 5.89% H; 9.83% N.
Examples 2-14
The following compounds (102) to (114) are prepared in accordance with the general procedure described in Example 1 (Table 1).
TABLE 1______________________________________ ##STR7##Com- Yield mp .lambda..sub.maxpound R.sub.1 R [.degree.C.] [nm]______________________________________(102) C.sub.3 H.sub.7 CH.sub.2 CH.sub.2 OCH.sub.3 n.f. 127-128 297/352(103) CH.sub.3 CH.sub.2 CH.sub.2 OCH.sub.3 97.1 190-191 296/351(104) CH.sub.3 CH.sub.2 CH.sub.2 OC.sub.2 H.sub.5 96.1 155-156 296/350(105) CH.sub.3 (CH.sub.2 CH.sub.2 O).sub.2 C.sub.2 H.sub.5 94.4 126-127 295/350(106) C.sub.2 H.sub.5 CH.sub.2 CH.sub.2 OC.sub.2 H.sub.5 93.8 161-162 297/352(107) C.sub.2 H.sub.5 (CH.sub.2 CH.sub.2 O).sub.2 C.sub.2 H.sub.5 75.4 133-134 297/352(108) C.sub.2 H.sub.5 CH.sub.2 CH.sub.2 OC.sub.3 H.sub.7 96.6 144-145 297/352(109) C.sub.2 H.sub.5 CH.sub.2 CH.sub.2 OCH.sub.3 90.3 150- 151 297/352 (110)* CH.sub.3 (CH.sub.2).sub.7 CH.sub.3 79.8 110-111 295/350(111) CH.sub.3 (CH.sub.2 CH.sub.2 O).sub.3 C.sub.2 H.sub.5 91.3 106-107 296/351(112) C.sub.2 H.sub.5 (CH.sub.2 CH.sub.2 O).sub.3 C.sub.2 H.sub.5 66.5 99-100 298/353 (113)* C.sub.2 H.sub.5 (CH.sub.2).sub.7 CH.sub.3 71.8 129-130 296/351 (114)* C.sub.2 H.sub.5 C.sub.4 H.sub.9 73.8 173-174 296/351______________________________________
APPLICATION EXAMPLES
Examples 15-29
Use in dyeing
Fifteen 10 g samples of PES tricot are dyed in a HT dyeing machine, e.g. .RTM.Turbomat (supplied by Mathis, Niederhasli) at a liquor ratio of 1:10. The liquors contain 2 g/l of ammonium sulfate, 0.5 g/l of a dyeing auxiliary .RTM.Univadin 3-flex and the dyes of formulae (I) to (IV) in the following amounts:
0.05% of the dye of formula ##STR8##
0.025% of the dye of formula ##STR9##
0.03% of the dye of formula ##STR10##
0.025% of the dye of formula ##STR11##
Whereas liquor 1 contains no further ingredients, 2% of each of the formulated compounds (101) to (114) are added to liquors 2 to 15.
The UV absorbers are formulated before addition to the dye liquor or as print paste. This is done by milling
the respective compounds,
the naphthalenesulfonic acid/formaldehyde condensate used as dispersant in the ratio 1:1,
the 2-4-fold amount of water, and
the 4-fold amount of quartz balls (.phi.1 mm)
with an impeller until the product has a particle size of 1-2 .mu.m. The dispersion is separated with a fine mesh sieve and stabilised with 0.5% of carboxymethyl cellulose and adjusted to 30%.
The tricot samples are dyed in the dispersed liquors in pressure bombs. The samples are put into the liquors at 70.degree. C. and after a treatment time of 5 minutes heated for 10 minutes to 100.degree. C. and finally for 20 minutes to 130.degree. C. Dyeing is carried out for 30 minutes at this temperature and then, after cooling to 50.degree. C., the dyed samples are rinsed with warm and cold water. A reductive afterclear is subsequently carried out at 70.degree. C. for 30 minutes with 2 ml/l of aqueous sodium hydroxide of 36 Be and 3 g/l of sodium dithionite. Afterwards the samples are again washed off with warm and cold water, centrifuged and dried.
The lightfastness properties are determined by irradiating the dyeings in accordance with DIN 75.202 (FAKRA) and SAE J 1885. The results are reported in Table 2.
TABLE 2______________________________________ Lightfastness according to FAKRA FAKRA SAEDyeing (liquor) 3 cycles 5 cycles 420 KJ______________________________________no addition 2-3 2 H 1-2 (1) + compound (101) 4 3-4 H 3 H (2) + compound (102) 4 3-4 H 3 H (3) + compound (103) 4 3-4 H 3 H (4) + compound (104) 4 3-4 H 3 H (5) + compound (105) 4 3-4 H 3 H (6) + compound (106) 4 3-4 H 3 H (7) + compound (107) 4 3-4 H 3 H (8) + compound (108) 4 3-4 H 3 H (9) + compound (109) 4 3-4 H 3 H(10) + compound (110) 3-4 3 H 2-3 H(11) + compound (111) 3-4 3 H 2-3(12) + compound (112) 3-4 3 H 2-3(13) + compound (113) 4 3 2-3(14) + compound (114) 4 2-3 2-3______________________________________
Table 2 demonstrates that the use of the UV absorbers (101)-(114) markedly enhances the lightfastness properties of the pale grey dyeings obtained.
Examples 30-35
Use for printing
Print pastes of the following composition are used for printing PES automobile upholstery:
750 parts of a stock thickening comprising
9 parts of starch ether as thickener
18 parts of sodium alginate as thickener
3.75 parts of sodium dihydrogen phosphate
2.48 parts of sodium chlorate and
716.77 parts of water.
This stock thickening is mixed with
6.4 parts of the dye mixture consisting of
2.0 parts of the dye of formula ##STR12## 1.4 parts of the dye of formula ##STR13## 2.0 parts of the dye of formula ##STR14## 1.0 part of the dye of formula ##STR15## 213.6 parts of water, and 30 parts of the dispersed 30% UV absorber formulation of Example 15 containing each of the compounds (101), (103), (109), (113) and (114).
The pre-cleaned PES tricot samples are printed with these print pastes on a Zimmer printing table (supplied by Zimmer, Klagenfurt/Austria). These samples are dried and steamed with superheated steam at 180.degree. C. for 8 minutes. The samples are then rinsed with cold water and given a reductive afterclear at 70.degree. C. for 30 minutes in baths containing 2 ml/l of aqueous sodium hydroxide of 360 Be and 3 g/l of sodium dithionite. The samples are rinsed with warm and cold water, centrifuged and dried at 80.degree. C. They are then tested for their lightfastness properties in accordance with SN-ISO 105 B02 (XENON), DIN 75.202 (FAKRA), and according to SAE J 1885 (SAE). The results are reported in Table 3.
TABLE 3______________________________________ Lightfastness properties according to XENON FAKRA SAE SAEPrints 800 h 4 cycles 489 KJ 600 KJ______________________________________no addition 7-8 1-2 RH 1 RH 1 RH(1) + compound (101) 7-8 4 3-4 H 3-4 H(2) + compound (103) 7-8 4 3-4 H 3 H(3) + compound (109) 8 4 3-4 H 3 H(4) + compound (113) 7-8 3 2-3 2-3(5) + compound (114) 8 3-4 H 3 H 2-3 H______________________________________
The results reported in Table 3 show that the UV absorbers effect a marked enhancement of the hot lightfastness properties.

Number	Name	Date
4831068	Reinert et al.	May 1989
4950304	Reinert et al.	Aug 1990
5197991	Rembold	Mar 1993

Number	Date	Country
03528	Jun 1986	WOX
10006	Jul 1991	WOX

Process for the photochemical and thermal stabilization of undyed and dyed or printed polyester fiber materials

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

US Referenced Citations (3)

Foreign Referenced Citations (2)