The present invention relates to a process for the preparation of acetal polymers, in particular of polyoxymethylene (POM) by cationic polymerization where organophosphonic and/or organophosphinic acids and/or their derivatives and/or their precursors are used as the initiator.
Thermoplastic molding materials of POM homopolymers and copolymers have long been known as versatile construction materials. In many cases they can be used as a substitute for metals because of their outstanding mechanical properties, such as high rigidity, hardness and strength. At the same time they can be molded to strict tolerance limits. The good resistance of POM to many chemicals opens further applications, especially where stability to gasoline or organic solvents is required.
POM copolymers can be manufactured by the cationic polymerization of cyclic formals or cyclic acetals such as 1,3,5-trioxane (trioxane) or tetroxane in the presence of comonomers such as ethylene oxide or other cyclic ethers or cyclic acetals such as or 1,3-dioxolane. The comomoner content is typically in the range of from 0.5 to 25% by weight; preferred is the range of from 3 to 6% by weight. The copolymers exhibit enhanced stability over the homopolymers and are much more stable towards basic compounds.
Polymerization is conducted by the addition of an initiator to a reaction mixture comprising cyclic formals, comonomers, and optionally linear formals such as methylal as molecular weight regulators. The initiator does not only start the polymerization reaction but also has a pronounced influence on chain transfer and chain termination reactions. Therefore, the initiator is of paramount importance for the productivity of polymer formation as well as for polymer properties.
As cationic initiator all such compounds can be used that react with the cyclic acetals or cyclic ethers to form oxocarbenium and/or oxonium compounds. Typical initiators are strong Bronstedt and Lewis acids, such as perchloric acid, trifluoromethanesulfonic acid or boron trifluoride (U.S. Pat. No. 5,994,455). Acid anhydrides can also be used. In some cases, esters can initiate the polymerization of cyclic ethers. One such ester is methyl-(trifluoromethane)-sulfonate (EP 0 678 535 A1).
The initiator should be active in very small concentrations, so that after the desactivation of the initiator at the end of the polymerization reaction it is not necessary to separate the deactivated initiator from the polymer.
While currently used initiators have a good polymerization activity, they also cause side reactions like hydride shift of the growing polymer chain which limits the molecular weight of the polymers and increases the amount of unstable formate end groups. Unstable end groups are responsible for the thermal instability of the polymers.
The object of this invention is therefore to provide an initiator which
It has been found that high molecular weight POM polymers with high thermal stability can be produced conveniently and in high yield if the initiator contains an organophosphinic acid or its derivatives of the general structure (I) or an organophosphonic acid or its derivatives of the general structure (II).
where R1 and R2 are CF3—(CF2)n—, with n=0-10,
The term initiator extends to a single compound or to a mixture of compounds. This mixture may also contain organophosphorous compounds that are precursors of compounds with general structures I and II. Precursors are all such compounds that under the reaction conditions are converted by a chemical reaction to compounds with general structures I and II. The precursors may either react with components that have deliberately been added to the reaction mixture or are inevitably present in the reaction mixture such as traces of water or methanol. Typical examples for precursors are acid anhydrides, acid halogenides, acid phenolates or acid imidazolides.
The concentration of the initiator is typically from 0.01 to 50 ppm by weight based on the monomer. Preferred initiator concentrations range from 0.1 to 5 ppm. In order to distribute these small quantities of initiator quickly and homogeneously in the reaction mixture it has proven useful to premix the initiator with an inert solvent and then add it to the monomers. Examples for inert solvent are 1,4-dioxane, dimethoxyethane or dimethyleneglycol dimethyl ether. The use of additional solvents can be avoided if the initiator is premixed with methylal, which is commonly used as a molecular weight regulator (U.S. Pat. No. 5,994,455).
The polymerization can be performed in bulk, in solution or in the melt. In the first two instances, polymer precipitates out of the polymerization mixture during polymerization. The polymerization temperatures range from −20 to 100° C. for solution polymerization, from 20° C. to 150° C. for bulk polymerization and from 100° C. to 200° C. for melt polymerization. At the end of each of these polymerization reactions, the reaction mixture is deactivated by the addition of compounds that terminate the active polymer chain. Typical deactivators are organic bases. Examples are triethylamine or melamine.
Weight average molecular weights of the POM polymers can be quite high. It is possible to obtain molecular weights of up to 200,000. The molecular weight of the polymers can be adjusted by the addition of regulators to the reaction mixture. Convenient regulators are linear formals such as methylal. Depending on the amount of regulator used the molecular weight ranges from 10,000 to 200,000.
The following examples illustrate the invention but are not intended to limit the invention in any way.
Bis(trifluoromethyl)phosphinic acid, bis(pentafluoroethyl)phosphinic acid, trifluoromethyl phosphonic acid and pentafluoroethyl phosphonic acid were purchased from Hansa Fine Chemicals (Bremen, Germany, www.hfc-chemicals.com) and used as received.
Melt Volume Ratios (MVR) were measured according to ISO 1133 at 190° C. and 2.16 kg. The amount of unstable end groups was determined by measuring the amount of formaldehyde formed during 1 hour at 190° C. under alkaline (pH=9.5) conditions by titrating the formaldehyde formed using the sulfite method. Weight average molecular weights were determined by viscosimetry at 140° C. in γ-butyrolactone as disclosed by D. Braun, U. Brückner, P. Eckardt, M. Hoffmockel, Angew. Makromol. Chem. 265 (1999), 55.
A mixture of 95 g of 1,3,5-trioxane and 5 g of 1,3-dioxolane was mixed with 1 ppm by weight, based upon the total weight of 1,3,5-trioxane and 1,3-dioxolane, of bis(trifluoromethyl) phosphinic acid, which was employed as a 0.1% by weight solution in 1,4-dioxane. The polymerization was run at 80° C. for 4 minutes. The solidified reaction mixture was quenched with 400 g of water (containing 1,000 ppm of triethylamine) in a blender and subsequently hydrolyzed at 170° C. in a mixture of water and methanol (10/90 by volume). Upon cooling to room temperature the polymer precipitated. It was filtered and dried under nitrogen at 50° C.
The polymer was analyzed for MVR and unstable end groups. The MVR was 5 ml/10 min, and the amount of unstable formate end groups was <0.1% by weight.
The experiment of example 1 was conducted in the same way, except that 1 ppm of bis(pentafluoroethyl)phosphinic acid was used as the initiator. Analysis of the polymer gave an MVR of 7 ml/10 min and the amount of unstable endgroups was <0.1%.