Process for the preparation of aluminum polymeric compounds of polyimine nature

Abstract

The present specification describes novel aluminum-polyimine compounds that are useful as catalysts for the polymerization of unsaturated compounds. The aluminum-polyimine compounds are of the formula:Al.sub.h (NR).sub.k H.sub.i Y.sub.jin which R is an aliphatic, aromatic or cycloaliphatic hydrocarbon radical, H is hydride hydrogen, Y is halogen, K ranges from 2 to 50, h/k>1, (i+j)/h>1, i.noteq.0 and j.gtoreq.0.

Description

The present invention relates to new aluminium compounds of polyimine nature, to the process for the preparation thereof and also to processes making use of these compounds as components of catalytic systems to be employed in the polymerization of unsaturated compounds.

It is known, from U.S. Pat. No. 3,895,133 that there are aluminium derivatives of polyimine nature containing halogen atoms bound to aluminium.

Moreover the same Applicant owns two copending patent applications. Ser. No. 524,312, filed Nov. 15, now U.S. Pat. No. 4,022,809 and Ser. No. 592,247, filed July 1, 1975 now U.S. Pat. No. 4,032,553 relating to oligomer N-alkyl-iminoalanes having chemical compositions, respectively

(a) - [AlX - NR].sub.n and (b) (X-Al NR).sub.x (XYAl).sub.y (NHR).sub.y In which X and Y, the same or different, mean hydride hydrogen and/or halogen atoms directly bound to aluminium, n is an integer lower than or equal to 10, the (x + y) sum is an integer lower than or equal to 10, y is an integer different from zero, R is an aliphatic, aromatic or cycloalyphatic hydrocarbon, characterized by a tridimensional structure and atomic ratios X/Al = 1 and N/Al = 1 as to (a) and (X + Y)/Al>1 and N/Al = 1 as to (b).

Some of these compounds, if employed as components of catalytic systems together with transition metal derivatives in the polymerization of conjugated dienes, allow the polymerization reaction to be carried out at a polymerization rate higher than those obtainable by other catalyst systems and, at the same time, side reactions or cyclizations of the polymeric chains can be avoided. Inter alia, this allows to obtain polymer at lower consumptions of transition metal derivatives.

We have now found, that the abovesaid aluminium compounds may be modified through a reaction with alkaline or alkaline-earth metal alanate, or with aluminium hydride complexes to give new aluminium derivatives having a substantial polyimine nature, that form a further object of the present invention and, besides preserving or improving the abovesaid characteristics in the polymerization of conjugated dienes, may be employed as components of catalytic systems in the polymerization of other unsaturated compounds, particularly of ethylene and mono-olefins.

The aluminium compounds, according to the present invention, have the following general formula

Al.sub.h (NR).sub.k H.sub.i Y.sub.j in which R is an aliphatic, aromatic or cycloaliphatic hydrocarbon radical, H is hydride hydrogen, Y is halogen, k ranges from 2 to 50, h/k>1, (i + j)/h>1, i .noteq. 0 and j .gtoreq. 0.

As abovesaid, the inventive aluminium compounds are obtained by reacting the cited polyimine compounds with alkaline or alkaline-earth metal alanates or with aluminium hydride complexes.

According to the employed starting compounds, hydrogen development can take place and/or the alkaline metal halide may separate.

The reaction easily occurs at temperatures ranging from 0.degree. to 70.degree. C and, preferably, at pressures equal to the vapor pressure of the solvent, in which the operations are carried out, at the working temperature.

Use may be made of solvents belonging to the class of ethers such as, for instance, dimethyl ether, diethyl ether, methyl ethyl ether, cyclic ethers or mixtures thereof with hydrocarbons or hydrocarbons only. As aforesaid the inventive compounds are useful components of catalytic systems for the polymerization of compounds having at least an olefine unsaturation together with a transition metal compound.

Therefore they can be used to give catalysts having a wide scale employment and the property, with respect to aluminium alkyls, to be not self-inflammable in the presence of air.

EXAMPLES

(1) 26 mmoles of LiAlH.sub.4 in an ether solution (1 M) were added, over 5 minutes to 176 mg atoms of polyiminoalane (as Al), dissolved in 300 ml of an ether-heptane mixture (30% as ethyl ether), having Cl/Al = 0.26, N/Al = 0.97, the addition being performed at 45.degree. C and under stirring. These conditions were kept for 4 hours, then the whole was filtered on a sintered glass septum. All operations were carried out under an inert and anhydrous atmosphere.

The filtrate was distilled under vacuum in order to eliminate ethyl ether and heptane was added.

The solution, after analysis, had the following composition

Al.sub.1 H.sub.1.25 N.sub.0.9 Cl.sub.0.1

(2) 28 mmoles of NaAlH.sub.4 suspended in ethyl ether were added to 187 mmoles of polyiminoalane (as Al) dissolved in 300 ml of an ether-hexane mixture (30% as ethyl ether) having Cl/Al = 0.26 N/Al = 0.97, the addition being performed under stirring and at a temperature of 45.degree. C. The whole was kept under these conditions for 4 hours and then was filtered from sodium chloride.

The filtrate was distilled under vacuum in order to eliminate ethyl ether and heptane was added. The solution, after analysis, had the following composition

Al = 0.724 mole/litre H = 0.864 mole/litre N = 0.602 mole Cl = 0.095 mole/liter

corresponding to the raw formula

Al.sub.1 N.sub.0.83 H.sub.1.19 Cl.sub.0.13

(3) 25 mmoles of NaH were added, under stirring at 45.degree. C, to 180 mg atoms of polyiminoalane (as Al) dissolved in 300 ml of an ether-heptane mixture and having Cl/Al = 0.25, N/Al = 0.86. The whole was kept under these conditions for 4 hours, then was cooled and filtered on sintered septum. The filtrate was distilled under vacuum in order to eliminate ethyl ether and heptane was added. The solution, analyzed, had the following composition

Al = 0.95 mole/litre N = 0.82 mole/litre Cl = 0.10 mole/litre H = 1.10 mole/litre corresponding to the raw formula Al.sub.1 N.sub.0.86 H.sub.1.16 Cl.sub.0.11

(4) An ether solution of polyiminoalane, having a N/Al molar ratio equal to 1, no chlorine and containing 30.78 mg atoms of aluminum, was added with an ether solution of anhydrous HCl in such an amount to have a molar ratio Al/Al = 0.165, then were added 6.05 ml of an ether solution of LiAlH.sub.4 having a concentration 0.824 M (4.98 mmoles). The whole was stirred for 1 hour and then kept resting over 20 hours.

LiCl was filtered and the solution was made free from the solvent through a distillation under vacuum. The solid residual was long dried under vacuum at room temperature and analyzed

Al 33.25% N 14.09% H 14.88 meq/g corresponding to the raw formula Al.sub.1 N.sub.0.86 H.sub.1.22

the obtained product was soluble in aromatic an cycloaliphatic hydrocarbon solvents.

(5) An ether solution of AlH.sub.3. Et.sub.2 O (6.2 mmoles) was added to an ether-hexane solution (30% as ethyl ether) of polyiminoalane having molar ratios N/Al = 0.99, Cl/Al = 0.10 containing 42.7 mg atoms of aluminium.

It was kept boiling, under stirring, for 4 hours, then the solvent was removed under vacuum and hexane was replaced by ethyl ether. Since the solution was lightly cloudy, it was filtered.

At analysis there was

Al.sub.1 N.sub.0.88 Cl.sub.0.09 H.sub.1.15

polymerization examples: ethylene

(1) A 5 1 autoclave equipped with an anchor stirrer was charged with 2 l of anhydrous and air-free n-heptane, then it was thermostated at 90.degree. C. Then the catalyst, prepared aside, was added, it being constituted by 1.00 g ot TiCl.sub.3.AA corresponding to 2.5 mg at/litre and 1.27 g of polyiminoalane (PIAPE) synthetized according to one of the abovesaid recipes corresponding to 7.5 mg at/l of H.

3 atmospheres of H.sub.2 were sent, as molecular weight regulator, then ethylene was sent up to a total pressure of 5 atmospheres, the pressure being kept at such a value by the running itself of the polymerization reaction.

After two hours reaction, the autoclave was open, the suspension was centrifugated and the polymer was dried under vacuum at 60.degree. C.

750 g of polymer were obtained having d = 0.958 and MFI = 0.720.

A polymerization test, carried out in the same conditions by using a polyiminoalane with N/Al = 1 according to Italian Pat. 885.567, gave g 250 of polymer having MFI =0 0.70

(2) The formalaties of the foregoing example were followed by using 5 atmospheres of hydrogen. 550 g were obtained of a polymer having MFI=3.60.

POLYMERIZATION EXAMPLE: ISOPRENE

(1) 90 ml of anhydrous and air-free hexane, 1.82 10.sup.-3 mole of TiCl.sub.4 and PIAPE in such amounts to have the Al/Ti ratio: 0.95 1 1.05 1.1 1.2, were introduced into a series of bottles. These were sealed and the catalyst was aged; then were added 30 ml of anhydrous freshly distilled isoprene. The bottles were sealed by crown plugs and put in a thermostat at 30.degree. C. All operations were carried out under inert armosphere.

After 2 hours polymerization, the reaction was stopped by an addition of ethyl alcohol and an ethyl alcohol coaglation was performed.

After drying, the following conversious were obtained:

______________________________________Al/Ti Conversion % g as dry polymer______________________________________1.00 351.05 901.10 601.20 45______________________________________

A comparative serie of polymerization, carried out again by using PIA according to Italian Pat. No. 885.567, gave the following results:

______________________________________Al/Ti Conversion % g as dry polymer______________________________________1.00 251.05 861.10 751.20 52______________________________________

Obtained polyisoprenes had a 1.4 cis content hygher than 95%.

COPOLYMERIZATIOH EXAMPLES: MONOOLEFINS

(1) A 5 l autoclave, provided with an anchor stirrer, was charged with 2 l of anhydrous and air-free n-heptane containing 15 g of anhydrous and air-free hexene-1; it was thermostated at 85.degree. C, then charged with the preformed catalyst constituted by 1.00 g of TiCl.sub.3 AA corresponding to 2.5 mg atoms/liter and 0.9 g of polyiminoalane (PIA-PE) corresponding to 5 mg atoms/liter as H.

H.sub.2 was sent, as molecular weight regulator, at 2 atm pressure, then ethylene was sent up to a total pressure of 5 atmospheres and such value was kept by an ethylene flow regulated by the running itself of the polymerization reaction. After two hours polymerization, during which were fed 20 g of hexene-1, the reaction was stopped by 250 ml of ethyl alcohol which too solubilized the catalyst.

The suspenson was centrifugated and the polymer was dried under vacuum.

620 g of a copolymer were obtained, it having an ash content equal to 300 ppm, d = 0.947 g/cm.sup.3, MFI = 0.20 g/10', ESCR>430 hours (enviromental stress-cracking resistance).

Claims

1. Process for the preparation of aluminum compounds of the formula Al.sub.h (NR).sub.k H.sub.i Y.sub.j wherein R is a aliphatic, aromatic or cycloaliphatic hydrocarbon radical, H is hydride hydrogen, Y is halogen, k ranges from 2 to 50 h/k>1, (i+j)/h>1, i.noteq.0 and j.gtoreq.0, said process consisting in reacting aluminum compounds of polyimine nature have the chemical compositions

(a) (Al X - NR).sub.n and

(b) (X-Al NR).sub.x (XYAl).sub.y (NHR).sub.y

in which X and Y are the same or different, and mean hydride hydrogen and/or halogen atoms directly bound to aluminum, n is an integer lower than or equal to 10, y is an integer higher than zero and R is an aliphatic, aromatic or cycloaliphatic hydrocarbon radical, with alkali or alkaline-earth metal alanates or with aluminum hydride complexes.

2. Process according to claim 1 characterized in that the reaction is carried out at temperatures of from 0.degree. to 70.degree. C.

3. Process according to claim 1 characterized in that the reaction is carried out in presence of a solvent selected from the group consisting of ethers, hydrocarbons or mixtures thereof.

4. Process according to claim 1 characterized in that the reaction is carried out at a pressure equal to the vapor pressure of the solvent at the working temperature.