Claims
- 1. A process for the preparation of a coating which comprises
- a) applying to a water-resistant substrate an aqueous coating composition containing water and only one binder which consists essentially of a hydrophilically-modified polyisocyanate component containing one or more hydrophilically-modified polyisocyanates which are dispersible in water, said hydrophilically-modified polyisocyanate component having a viscosity at 23.degree. C. of 100 to 5000 mPa.s, an average NCO functionality of 2 to 4, a content of (cyclo)aliphatically bound isocyanate groups of 12 to 21.5% by weight, based on the weight of said hydrophilically modified polyisocyanate component, and a content of ethylene oxide units (calculated as C.sub.2 H.sub.4 O, molecular weight=44) present within polyether chains of 2 to 20% by weight, based on the weight of said hydrophilically modified polyisocyanate component, and
- b) curing said aqueous coating composition in the presence of moisture to form a polyurea coating.
- 2. The process of claim 1 wherein the aqueous coating composition is present in the form of an oil-in-water or a water-in-oil emulsion.
- 3. The process of claim 1 wherein 2 to 400 parts by weight of water are present per 100 parts by weight of said polyisocyanate component.
- 4. The process of claim 1 wherein the aqueous coating composition comprises one or more fillers selected from the group consisting of (i) sand, colored sand or decorative sand of various grain sizes, (ii) grit or decorative grit with a grain size of up to 10 mm, (iii) expanded clay granules with a grain size of up to 10 mm, and (iv) plastic granules of a grain size of up to 10 mm, wherein said fillers are present in an amount such that 2 to 20 parts by weight of binder a) are present per 100 parts by weight of said fillers.
- 5. The process of claim 1 wherein the aqueous coating composition contains a pigment.
- 6. The process of claim 5 wherein the aqueous coating composition additionally contains a water-dilutable pigment grinding agent.
- 7. A process for the preparation of a coating which comprises
- a) applying to a water-resistant substrate an aqueous coating composition containing water and only one binder which consists essentially of a polyisocyanate component containing one or more hydrophilically-modified polyisocyanates which are dispersible in water, said hydrophilically-modified polyisocyanate component having a viscosity at 23.degree. C. of 100 to 5000 mPa.s, an average NCO functionality of 2 to 4, a content of (cyclo)aliphatically bound isocyanate groups of 12 to 21.5% by weight, based on the weight of said hydrophilically modified polyisocyanate component, and a content of ethylene oxide units (calculated as C.sub.2 H.sub.4 O, molecular weight=44) present within polyether chains of 2 to 20% by weight, based on the weight of said hydrophilically modified polyisocyanate component, said polyether chains containing 6 to 9 alkylene oxide units and
- b) curing said aqueous coating composition in the presence of moisture to form a polyurea coating.
- 8. The process of claim 7 wherein the aqueous coating composition is present in the form of an oil-in-water or a water-in-oil emulsion.
- 9. The process of claim 7 wherein 2 to 400 parts by weight of water are present per 100 parts by weight of said polyisocyanate component.
- 10. The process of claim 7 wherein the aqueous coating composition comprises one or more fillers selected from the group consisting of (i) sand, colored sand or decorative sand of various grain sizes, (ii) grit or decorative grit with a grain size of up to 10 mm, (iii) expanded clay granules with a grain size of up to 10 mm, and (iv) plastic granules of a grain size of up to 10 mm, wherein said fillers are present in an amount such that 2 to 20 parts by weight of binder a) are present per 100 parts by weight of said fillers.
- 11. The process of claim 7 wherein the aqueous coating composition contains a pigment.
- 12. The process of claim 11 wherein the aqueous coating composition additionally contains a water-dilutable pigment grinding agent.
- 13. A process for the preparation of a coating which comprises
- a) applying to a water-resistant substrate an aqueous coating composition containing water and only one binder which consists of a hydrophilically-modified polyisocyanate component containing one or more hydrophilically-modified polyisocyanates which are dispersible in water, said hydrophilically-modified polyisocyanate component having a viscosity at 23.degree. C. of 100 to 5000 mPa.s, an average NCO functionality of 2 to 4, a content of (cyclo)aliphatically bound isocyanate groups of 12 to 21.5% by weight, based on the weight of said hydrophilically modified polyisocyanate component, and a content of ethylene oxide units (calculated as C.sub.2 H.sub.4 O, molecular weight=44) present within polyether chains of 2 to 20% by weight, based on the weight of said hydrophilically modified polyisocyanate component, and
- b) curing said aqueous coating composition in the presence of moisture to form a polyurea coating.
- 14. The process of claim 13 wherein the aqueous coating composition is present in the form of an oil-in-water or a water-in-oil emulsion.
- 15. The process of claim 13 wherein 2 to 400 parts by weight of water are present per 100 parts by weight of said polyisocyanate component.
- 16. The process of claim 13 wherein the aqueous coating composition comprises one or more fillers selected from the group consisting of (i) sand, colored sand or decorative sand of various grain sizes, (ii) grit or decorative grit with a grain size of up to 10 mm, (iii) expanded clay granules with a grain size of up to 10 mm, and (iv) plastic granules of a grain size of up to 10 mm, wherein said fillers are present in an amount such that 2 to 20 parts by weight of binder a) are present per 100 parts by weight of said fillers.
- 17. The process of claim 13 wherein the aqueous coating composition contains a pigment.
- 18. The process of claim 17 wherein the aqueous coating composition additionally contains a water-dilutable pigment grinding agent.
Priority Claims (1)
Number |
Date |
Country |
Kind |
42 03 217 |
May 1992 |
DEX |
|
Parent Case Info
This application is a continuation of application Ser. No. 08/009,522 filed Jan. 27, 1993 now abandoned.
US Referenced Citations (3)
Number |
Name |
Date |
Kind |
3428592 |
Youker |
Feb 1969 |
|
4663377 |
Hombach et al. |
May 1987 |
|
5075370 |
Kubitza et al. |
Dec 1991 |
|
Foreign Referenced Citations (5)
Number |
Date |
Country |
2055419 |
May 1992 |
CAX |
013112 |
Jul 1980 |
EPX |
516277 |
Dec 1992 |
EPX |
1444933 |
Aug 1976 |
GBX |
2018796 |
Oct 1979 |
GBX |
Non-Patent Literature Citations (2)
Entry |
Kunststoff Handbuch (Plastics Handbook), vol. 7, "Polyurethane" ("Polyurethanes"), Carl Hanser Verlag Munich/Vienna (1983), pp. 545 et seq. |
Cyanamid, "Aqueous Polyurethane Dispersions from TMXDI (Meta) Aliphatic Isocyanate" Feb. 1989. |
Continuations (1)
|
Number |
Date |
Country |
Parent |
009522 |
Jan 1993 |
|