Claims
- 1. A process for the production of a cupola-shaped plastic piece having a flat rim from flat plastic sheet the thickness of which is in the range of 1 to 12 mm, said process comprising the steps of:
- (a) while the flat plastic sheet is at a temperature T.sub.1 10.degree. C. or more beneath its softening temperature, holding the rim of the flat plastic sheet in a fashion which permits the flat plastic sheet to move in the plane of the sheet in response to thermal expansion but which does not permit the rim of the flat plastic sheet to warp out of the plane of the sheet; then
- (b) heating the exposed central area of the flat plastic sheet but not the rim surrounding the exposed central area of the flat plastic sheet until the softening temperature of the plastic in the exposed central area of the flat plastic sheet is exceeded;
- (c) applying a tight clamping pressure to the rim of the flat plastic sheet when the exposed central area of the flat sheet has reached a temperature T.sub.2 above 10.degree. C. below the softening temperature of the flat plastic sheet and below the softening temperature of the flat plastic sheet; then, after both step (b) and step (c) have been completed,
- (d) forming the exposed central area of the flat plastic sheet into the shape of a cupola while the exposed central area of the flat plastic sheet is above the softening temperature of the flat plastic sheet and while maintaining the tight clamping pressure on the rim of the flat plastic sheet; then
- (e) permitting the formed shape to cool a temperature that is beneath the softening temperature of the flat plastic sheet and above 10.degree. C. below the softening temperature of the flat plastic sheet; then
- (f) releasing the tight clamping pressure from the rim of the formed shape; and then
- (g) permitting the formed shape to cool to ambient temperature.
- 2. A process as recited in claim 1 wherein step (c) is effected when the exposed central area of the flat plastic sheet has reached a temperature just below the softening temperature of the flat plastic sheet.
- 3. A process as recited in claim 1 wherein step (c) is effected when the exposed central area of the flat plastic sheet has reached a temperature above the softening temperature of the flat plastic sheet.
- 4. A process as recited in claim 1 and comprising the further step of pre-heating the flat plastic sheet to a temperature that is more than 10.degree. C. below the softening temperature of the flat plastic sheet before step (a).
- 5. A process as recited in claim 1 wherein the flat plastic sheet is held in clamping tools which are heated to a temperature of between 20.degree. C. and 50.degree. C. below the softening temperature of the flat plastic sheet.
- 6. A process as recited in claim 1 wherein the heating step is accomplished by heat radiation.
- 7. A process as recited in claim 1 wherein step (c) occurs between two-thirds and three-quarters of the time between the beginning of step (a) and the beginning of step (d).
- 8. A process as recited in claim 1 wherein step (d) causes formation of a formed shape the greatest height of which is no more than one-fourth of the smallest planar dimension of the exposed central area of the flat plastic sheet.
Priority Claims (1)
Number |
Date |
Country |
Kind |
3410550 |
Mar 1984 |
DEX |
|
Parent Case Info
This application is a continuation of application Ser. No. 713,700, filed Mar. 19, 1985, now abandoned.
US Referenced Citations (2)
Number |
Name |
Date |
Kind |
3608016 |
Holmstrom et al. |
Sep 1971 |
|
4139586 |
Gasson |
Feb 1979 |
|
Continuations (1)
|
Number |
Date |
Country |
Parent |
713700 |
Mar 1985 |
|