The present invention relates to a process for the preparation of fine spherical particles of aluminium oxide. The particle size of the aluminium oxide is in the submicron range.
Fine spherical particles of aluminium oxide have a variety of uses, in particular within the field of ceramic materials.
As an example fine spherical particles of aluminium oxide may be used as pigments, abrasives and polishing agents, in refractory and fire-resistant products, in ceramics, as catalyst materials, or as fillers. Depending on the purity of the aluminium oxide the particles may also be used as high-performance structural ceramics, as high-performance polishing agents (for semiconductors), as starting materials for optical and functional ceramics, bioceramics and so forth.
In the prior art aluminium oxide has been prepared by a number of methods, a couple of which will be mentioned below.
U.S. Pat. No. 4,291,011 describes a method for production of aluminum oxide by continuously reacting high purity metallic aluminium, either solid or liquid, with high purity oxygen, present in stoichiometrically excessive amount, within a vertically oriented cylindrical vessel closed at the top and open at the bottom and having cooled side walls on which there forms a layer of solid aluminum oxide. Newly formed aluminum oxide deposits as a liquid film on the inside surface of this layer and flows downwardly thereover by gravity to the open bottom of the container and then falls to a collecting vessel below, solidifying either during this fall or after impingement on a moving metallic surface. An annular array of burners, e.g. oxy-hydrogen burners, limits downward growth of the layer below the vessel, and fosters detachment of the downwardly flowing film in the form of drops to fall to the collection vessel. This process does not give spherical submicron particles of aluminium oxide.
Canadian patent number 2110961 describes a process for preparing aluminum oxide particles, an aluminum oxide powder prepared according to the process and its use. The process comprises the following steps:
introduction of an aluminum carrier, such as Al or Al2O3 into a furnace unit, heating the aluminum carrier, reduction of the aluminum carrier, unless it is introduced as metallic aluminum, into metallic aluminum and/or aluminum carbides (including aluminum oxycarbides), increasing the furnace temperature to a value at which the metallic aluminum or the aluminum carbides evaporate, subsequent oxidation of the metallic aluminum or aluminum carbides into aluminum oxide in a gas flow, and introduction of the gas flow into a filter, wherein the temperature, the atmosphere, and the hold time of the aluminum oxide particles in the gas flow are adjusted according to the desired particle size. A disadvantage of this process is the use of carbon, which may lead to formation of impurities in the form of carbide and oxycarbides.
The object of the present invention is thus to provide an alternative and improved process, avoiding the disadvantages of the former processes, for the preparation of very fine and pure aluminium oxide particles, in the submicron range (<1.0 μm). An object is also to provide a process which may be carried out in a relatively inexpensive manner.
The principle of the invention is to produce aluminium sub-oxide vapours that are allowed to react with oxygen and thereby form aluminium oxide particles which are of a spherical nature.
The principle is to let aluminium oxide react with aluminium thereby producing gaseous aluminium sub-oxides (e.g AlO, Al2O) and aluminium vapour that serve as the combusting medium. The production of gaseous aluminium and aluminium sub-oxides by the partial reduction of the oxide is normally a heat consuming reaction. The existence of such a heat reservoir therefore facilitates and stabilizes the process.
The temperature of the aluminium oxide bath is above the meting point of the oxide. Preferred temperature ranges are: 2000-2100° C., 2100-2500° C., 2500-2700° C.
Described is thus a process for the production of spherical submicron particles of a metal oxide, in which a metal oxide and a reducing agent are injected into a reaction vessel comprising a pool of the metal oxide in molten state, serving as a heat reservoir for the process, whereby the metal oxide reacts with the reducing agent producing a metal vapour and metal sub-oxide vapours, whereafter said metal and metal sub-oxide vapours are oxidized to said metal oxide particles.
The present invention thus relates to a process for the production of spherical submicron particles of aluminium oxide (Al2O3), wherein aluminium oxide and aluminium metal are added into a reaction vessel comprising a pool of aluminium oxide in molten state, serving as a heat reservoir for the process, whereby aluminium oxide reacts with aluminium metal producing aluminium sub-oxides (AlO, Al2O) and aluminium vapour whereafter the sub-oxides and the Al vapour are oxidized above the molten pool of aluminium oxide to give aluminium oxide in the form of spherical submicron particles.
In a preferred embodiment the pool of aluminium oxide comprises 20-50 weight % aluminium oxide and 50-80 weight % zirconium dioxide.
In a further preferred embodiment the pool of aluminium oxide comprises 30-55 weight % aluminium oxide and 45-70 weight % zirconium dioxide
In another preferred embodiment the aluminium oxides and aluminium metal are injected into the reaction vessel.
In a further preferred embodiment the oxidation of the aluminium sub-oxides are carried out in air or oxygen.
In a further preferred embodiment a gas is introduced in the melted pool for increasing the partial pressure resulting in an increased amount of aluminium sub-oxide being released from the pool.
This gas is preferably air or nitrogen or other inert gases.
The size of the particles produced lies in the range from submicron to nano-size particles, which means in the range below 1 micrometer.
In a preferred embodiment of the invention the particles prepared have particle size in the range from 10−6 to 10−7 m.
In another preferred embodiment of the invention the particles prepared have particle size in the range from 10−7 to 10−8 m.
In still a preferred embodiment of the invention the particles prepared have a particle size less than 10−8 m.
The method of the present invention is used for the production of spherical submicron particles of aluminium oxide, Al2O3, whereby aluminium oxide is reduced with aluminium metal to give gaseous aluminium and aluminium sub-oxides (AlO, Al2O) at temperatures where the partial pressure of combustible gases exceeds 0.1 atmosphere, whereby the pool of reactant is molten aluminium oxide kept at temperatures above the melting point thereof, whereafter gaseous aluminium and the sub-oxides are oxidized above the molten aluminium oxide bath to aluminium oxide which is captured in a filter.
The main reaction for forming the sub-oxide will be:
Al2O3+4Al=3Al2O(g)
Al2O3+Al=3AlO(g)
This method is thus an aluminothermic process.
As indicated above, aluminium oxide and aluminium metal are added to the molten bath of aluminium oxide. Preferably the aluminium oxide and aluminium are injected into the molten pool of aluminium oxide, and the resulting aluminium vapours and aluminium sub-oxide gases are combusted immediately after production in the bath.
In one embodiment the pool of aluminium oxide comprises 20-50 weight % aluminium oxide and 50-80 weight % zirconium dioxide. In another embodiment the pool of aluminium oxide comprises 30-55 weight % aluminium oxide and 45-70 weight % zirconium dioxide.
In a molten pool having the above-indicated compositions, the molten pool will have a higher temperature than a molten pool consisting of aluminium oxide only; see e.g., G. Cervales, Ber. Deut. Keram. Ges., 45 [5] 217 (1968) for a phase diagram for the system Al2O3—ZrO2 showing that the melting point of the compositions described above is higher than for pure aluminium oxide. This will provide a faster reaction when aluminium oxide and metallic aluminium are added to the pool. Thus, a higher productivity of aluminium oxide particles is achieved. Zirconium dioxide in the molten pool will be inert and will not contaminate the aluminium oxide particles.
In the method for producing spherical submicron particles of aluminium oxide, the reaction of aluminium oxide and aluminium will, as indicated above, give primarily aluminium sub-oxides at temperatures above the melting point of aluminium oxide and at temperature where the partial pressure exceed a certain level. As illustrated in
The process for the preparation of aluminium oxide may be carried out in conventional or modified electrical furnaces for the preparation of fused alumina (brown fused alumina or white fused alumina). Such furnaces exist in different embodiments, known as for instance Higgins furnaces or tilt furnaces, as well as other designs. The typical furnaces will consist of a cylindrical shell of steel equipped with an inner lining of refractive material and an outer water cooling. The energy is provided using graphite or carbon electrodes arranged in a triangular arrangement. The furnace effect may typically be about 1-10 MW. Around the electrodes an open bath may be provided to which metallic aluminium and aluminium oxide may be added. Aluminium may be added in the form of chunks; however, the addition of liquid aluminium may also be envisaged. Aluminium has a lower density than molten alumina, and will therefore exist as a layer on the top of the pool.
The method for the production of alumina can thus be carried out in existing process equipment. In addition a filter will be needed for containing the produced alumina. If desired the off gases from the filter may comprise a simple cleaning facility for NOx, according to the state of the art.
The problem connected with the combustion of liquid aluminium is that a high temperature is necessary to provide ignition (according to our experiments about 1600-1700° C.). Further, it is difficult to maintain the combustion due to oxide (scull) formation. It is also assumed that the reaction proceeds via the gas phase where the first step is endothermic. Thus energy must be supplied continuously to avoid cooling of the aluminium oxide melt and thereby extinguishing of the process. This is possible in a melting furnace with electrodes. Even if the gross reaction Al+O2→Al2O3 is strongly exothermic, the heat of combustion is formed a distance above the pool, and may not be available down in the melt.
The pool or bath of molten aluminium oxide (about 2050 degrees C. or more) will serve as a heat buffer for stabilizing and facilitate the process.
The process according to the invention may be carried out using relatively inexpensive raw materials (calcined alumina and metallic aluminium). Compared to other processes this makes it possible to prepare affordable products. This is a decisive factor for high volume uses, such as for refractory materials.
The process for the preparation of spherical, submicron particles of aluminium oxide is aluminothermic and thus the disadvantages of carbothermic processes are avoided, such as the formation of carbides and oxycarbides.
The use of pure raw materials, such as high grade alumina, high purity aluminium and electrodes made of high-purity graphite makes it possible to produce high purity qualities of submicron/nanoalumina. This opens up a range of uses such as high-performance structural ceramics, advanced polishing agents such as for semiconductors, raw material for the preparation of optical and functional ceramics, bioceramics and so forth.
Having described preferred embodiments of the invention it will be apparent to those skilled in the art that other embodiments incorporating the concepts may be used. These and other examples of the invention illustrated above are intended by way of example only and the actual scope of the invention is to be determined from the following claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 20140162 | Feb 2014 | NO | national |