Process for the production of plastic and rubber compositions filled with carbon black

Abstract

A process for the production of plastic and rubber compositions filled with carbon black in which an organosilicon compound is used and is reacted in situ with the carbon black. The organosilicon compound is selected from the following formulae:(R.sup.1.sub.n --(RO).sub.3-n Si-(Alk).sub.m --(Ar).sub.p).sub.q (B)(I)R.sup.1.sub.n --(RO).sub.3-n Si-(Alkyl) (II)orR.sup.1.sub.n --(RO).sub.3-n Si-(Alkenyl) (III)in whichB=--SCN, --SH, --Cl--NH.sub.2 (where q=1) or --S.sub.x -- (where q=2),R=a C.sub.1-4 alkyl or C.sub.1-4 alkoxy group or a phenyl group,R.sup.1 =a C.sub.1-4 alkyl group or a phenyl group,n=0, 1 or 2,Alk=a difunctional, linear or branched C.sub.1-6 hydrocarbon radical,m=0 or 1,Ar=a C.sub.6-12 preferably C.sub.6 arylene radical,p=0 or 1, with the proviso that p and n cannot both be 0,x=a number from 2 to 8,Alkyl=a monofunctional, linear or branched unsaturated C.sub.1-20 and preferably C.sub.2-8 hydrocarbon radical,Alkenyl=a monofunctional, linear or branched unsaturated C.sub.2-20 and preferably C.sub.2-6 hydrocarbon radical.

Description

BACKGROUND AND INTRODUCTION

The present invention relates to a process for the production of vulcanizable plastic and rubber compositions filled with carbon black in which one or more organosilicon compounds are incorporated.

It has long been known that oxidic surfaces can be treated with organosilicon compounds containing alkoxy groups (U.S. Pat. No. 3,227,675; EP 0,177,674; EP-PS 0,126,871). The object of all these efforts was and is to establish a bond between the inorganic component, the oxidic filler, whether for example glass or even silicate fillers of the type used for example in the rubber industry (e.g., precipitated and pyrogenic silicas, clays, aluminum silicates etc.), and an organic polymer differing widely in its chemical composition. This generally leads to an improvement in the properties of the vulcanizates. Carbon blacks, for example furnace blacks, lampblacks and gas blacks are not included among the oxidic fillers. The reaction between the alkoxysilyl groups and the OH groups on the surface which takes place in oxidic filler substances cannot take place on the carbon black so that the establishment of a chemical bond between the carbon black and the organosilicon compound would not appear to be possible.

Although granular mixtures of carbon black and organosilicon compounds are known from DE-PS 2,747,277 (U.S. Pat. No. 4,128,438), these mixtures are used for more effectively incorporating the organosilicon compound in silica-containing rubber compounds. In this case, the carbon black merely acts as a carrier for liquid organic silanes which are to be converted into the solid state. The silane can be removed from such mixtures by extraction with organic solvents.

Since, hitherto, attempts have always been made to establish the properties of carbon-black-filled rubber vulcanizates through the use of carbon blacks differing in their structure and specific surface, the problem now arises of improving the properties of vulcanizates through the use of silane-modified carbon blacks.

According to German patent application P 40 23 537, it is possible by adopting a suitable procedure to bind considerable quantities of organosilicon compounds to carbon black, depending on the surface and structure of the carbon and also upon the type of compounds used.

SUMMARY OF THE INVENTION

The present invention describes a process for the production of vulcanizable plastic and rubber compositions filled with carbon black, characterized in that one or more organosilicon compounds corresponding to the following general formulae:

(R.sup.1.sub.n --(RO).sub.3-n Si-(Alk).sub.m --(Ar).sub.p).sub.q (B)(I) R.sup.1.sub.n --(RO).sub.3-n Si-(Alkyl) (II) or R.sup.1.sub.n --(RO).sub.3-n Si-(Alkenyl) (III) in which B=--SCN, --SH, --Cl--NH.sub.2 (where q=1) or --S.sub.x -- (where q=2), R=a C.sub.1-4 alkyl or C.sub.1-4 alkoxy group or a phenyl group, R.sup.1 =a C.sub.1-4 alkyl group or a phenyl group, n=0, 1 or 2, Alk=a difunctional, linear or branched C.sub.1-6 hydrocarbon radical, m=0 or 1, Ar=a C.sub.6-12 preferably C.sub.6 arylene radical, p=0 or 1, with the proviso that p and n cannot both be 0, x=a number from 2 to 8, Alkyl=a monofunctional, linear or branched unsaturated C.sub.1-20 and preferably C.sub.2-8 hydrocarbon radical, Alkenyl=a monofunctional, linear or branched unsaturated C.sub.2-20 and preferably C.sub.2-6 hydrocarbon radical, are incorporated in the vulcanizable composition in quantities corresponding to the quantity which is determined as no longer extractable with an organic solvent in the reaction of carbon black and the particular organosilicon compound. The corresponding method for determining this quantity is described in German patent application P 40 23 537 (corresponding to U.S. patent application Ser. No. 07/716,108 which is incorporated by reference in its entirety).

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1-3 show loss angle tan .delta. at 60.degree. C., heat build-up and ball rebound, respectively, of the automobile tread of Example IV.

DETAILED DESCRIPTION OF THE INVENTION

In general, the quantity in question of the organosilicon compounds is a quantity of 0.1 to 30 parts by weight of one or more organosilicon compounds, preferably a quantity of 0.5 to 15 parts by weight and, more preferably, a quantity of 0.5 to 4 parts by weight, based on 100 parts by weight carbon black.

It has been found that the quantity of organosilicon compounds which can be maximally bound to the particular carbon black and, hence, can no longer be extracted by organic solvents, particularly diethyl ether, also results in the optimal rubber performance obtainable depending upon the carbon black and the organosilicon compounds.

Larger extractable quantities of the compound(s) not only do not lead to any further improvement in the properties of vulcanizates, they actually result in a deterioration in the rubber property spectrum.

Suitable carbon blacks are carbon blacks for purposes of the present invention with alkaline pH value which belong to any of the various classes known in rubber technology, for example furnace blacks (classification according to ASTM D 1765), lampblacks and gas blacks, and also non-rubber carbon blacks. These carbon blacks are added to the plastic and rubber compositions in quantities of 5 to 250 parts and preferably in quantities of 50 to 100 parts, based on 100 parts rubber or plastic.

The optimal quantities of organosilanes may also be determined by testing the rubber behavior of the vulcanizates in a range of concentrations and thus ascertaining the most suitable ratio of carbon black to organosilicon compound.

The exactly defined concentration required to obtain optimal properties for the product can be subsequently transferred from one organosilane to another through the equimolar bases, for example on the basis of the trialkoxysilyl groups, where bis-(triethoxysilylpropyl)-tetrasulfane (TESPT or Si69) is used to modify the carbon black, as is the case in the Examples.

Whereas, in the case of silicate fillers, the modification with an organosilane is carried out during incorporation in almost every case, this procedure could not be regarded as entirely suitable for carbon blacks because the speed of the reaction between carbon black and organosilane was not predictable.

It has been found that, in general, the number of hydrolyzable groups --(OR) is equivalent to the concentration of oxygen-containing groups (in mval) present on the surface of the carbon black. This is surprising in view of the diversity of the oxygen-containing groups on the surface of the carbon black (H. P. Boehm, Voll, Carbon 9 (1971), 481 et seq.; J. P. Bonnet et al., Rubber Conf. Proc. Sydney, 1988, Vol. 1, pages 113 et seq.). This is another possible method of determining the optimum quantity of organosilane to be used.

Accordingly, there are three different methods by which the quantity of organosilicon compounds can be bound and hence the optimal quantity of organosilicon compounds can be determined, naturally within the margins of error of these methods.

Suitable rubbers are rubbers, plastics and mixtures thereof which can be crosslinked with sulfur and vulcanization accelerator(s) and also with peroxide to form elastomers. These include the so-called diene elastomers, i.e. for example oil-extended natural and synthetic rubbers, such as natural rubbers, terpolymers of ethylene, propylene and unconjugated dienes; copolymers of ethylene and propylene and also carboxyl rubbers, epoxy rubbers, transpolypentenamer, halogenated butyl rubbers, rubbers of 2-chlorobutadiene, ethyl/vinyl acetate copolymers and, optionally, chemical derivatives of natural rubber and modified natural rubbers. Any suitable natural or synthetic vulcanizable rubber can be used for purposes of the invention.

The natural or synthetic vulcanizable rubber compositions produced in accordance with the present invention contain other components typically used in the rubber industry such as, for example:

vulcanization accelerators typically used in the rubber industry (for example sulfenamides, 2-mercaptobenzthiazole (MBT), di-2-benzothiazyl disulfide (MBTS, triazine accelerators, thiurams), either individually or in admixture, in quantities of 0.1 to 10 parts by weight, based on 100 parts by weight rubber; vulcanization retarders such as, for example, Vulkalent E, di-(phenylthio)acetamide (PVI), again in quantities of 0.1 to 10 parts by weight, based on 100 parts by weight rubber; zinc oxide and stearic acid as vulcanization promoters in quantities of 0.5 to 10 parts by weight, based on 100 parts by weight rubber; antioxidants, antiozonants and antifatigue agents used in the rubber industry, including for example N-isopropyl-N'-phenyl-p-phenylenediamine (IPPD), poly-2,2,4-trimethyl-1,1,2-dehydroquinoline (TMQ) and also waxes as light stabilizers and mixtures thereof; Plasticizers such as, for example, aromatic, naphthenic, paraffinic, synthetic plasticizers and blends thereof; optionally sulfur in a quantity of 0.1 to 10 parts by weight per 100 parts by weight rubber; optionally dyes and processing aids in the usual quantities known in the art.

The compositions are produced by methods known in the rubber industry, for example in an internal mixer or on mixing rolls. Mixing temperatures of up to 250.degree. C. may be applied. Mixing equipment and conditions are well known in the art.

By comparison with known compounds, the process according to the present invention (in which carbon black and organosilane are preferably introduced simultaneously) lead to a distinct improvement in the moduli, elasticity, dynamic properties and loss angle tan .delta. of the vulcanizates produced from the rubber and plastic compounds.

The range of application of the silane-modified carbon blacks according to the present invention extends to compounds of the type typically used in tire manufacture, for example in the belt, carcass and bead regions, in side wall compounds and binding compounds, and to industrial articles such as, for example, conveyor belts, V-belts, hoses, seals, engine mountings, spring and damping elements and rubber-coated fabrics.

Test standards for practical application:

______________________________________ Test method______________________________________Rheometer DIN 53 529Mooney test DIN 53 524Tensile strength DIN 53 504Elongation at break DIN 53 507Modulus at 100%, 200%, 300% DIN 53 507Firestone ball rebound AD 20 245Shore A hardness DIN 53 505Goodrich Flexometer ASTM D 623-62Heat build-up DIN 53 513MTS DIN 53 513______________________________________

EXAMPLE I

Example I shows the quantity of bindable silane, as determined for Degussa carbon blacks. The effect of the BET surface on the quantity of bindable Si 69 (bis-(triethoxysilylpropyl)-tetrasulfane (TESPT)) can clearly be seen.

______________________________________Silane-modified carbon blacks Opt. quantity of Si 69 in pbw per 100 pbw carbon BET DBP black______________________________________Printex 90/Si 69 300 800 4.7N 115/Si69 145 114 3.3N 234/Si69 125 125 2.2N 220/Si69 115 114 2.1N 375/Si69 96 114 1.9N 330/Si69 82 102 1.8N 326/Si69 83 72 1.8N 550/Si69 42 121 1.5N 660/Si69 35 90 1.2N 683/Si69 37 133 1.0N 765/Si69 35 122 0.8Durex O/Si69 20 104 0.4______________________________________

The carbon black compounds in the left hand column above are well known in the rubber industry.

EXAMPLE II

Comparison between N 234 (1) and N 234 with in situ addition of Si 69 (2) in an automobile tread compound:

______________________________________ 1 2______________________________________SBR 1500 50 50(styrene-butadiene rubber)SBR 1712 68.75 68.75CORAX N 234 60 60(carbon black made by Degussa AG)Si 69 -- 1.5ZnO RS 3 3Stearic acid 2 2Vulkanox 4010 NA 1.5 1.5(N-isopropyl-N'-phenyl-p-phenylene diamine)Protector G 35 1 1(ozone protective wax)Vulkacit CZ 1.6 1.6(benzothiazyl-2-cyclohexylsulfenamide)Sulfur 1.8 1.8Rheometer: 165.degree. C.D.sub.max -D.sub.min (Nm) 7.81 8.69Reversion (%) 9.8 5.8Vulcanizate data: 165.degree. C., t.sub.95%Tensile strength (MPa) 20.7 22.2Modulus 300% (MPa) 10.3 11.8Firestone ball rebound (%) 34.0 34.8Shore A hardness 68 71Goodrich Flexometer: (RT, 108N, 0.175 inch, 18 h)Delta T center (.degree.C.) 149.5 144.9Dyn. Compression (%) 25.5 22.8MTS testDyn. elasticity modulus (Mpa) 0.degree. C. 38.8 42.6 60.degree. C. 11.7 13.0Loss angle tan .delta. 0.degree. C. 0.317 0.300 60.degree. C. 0.224 0.209______________________________________

The addition of Si 69 to the carbon black mixture leads to an increase in the crosslinking yield, modulus, tensile strength, elasticity and Shore hardness.

Among the Flexometer data, delta T center shows a reduced heat build-up and lower dynamic compression.

The relatively low loss angle tan .delta. at 60.degree. C. is indicative of relatively low rolling resistance of the silane-treated compound.

EXAMPLE III

Comparison between N 110(1) and N110 with in situ addition of Si 69 (2) in a lorry tread compound:

______________________________________ 1 2______________________________________RSS 1 (ML (1 + 4) = 70-80) 100 100CORAX N 110 45 45Si 69 -- 1.5ZnO RS 4 4Stearic acid 3 3Protector G 35 1.5 1.5Vulkanox 4010 NA 2 2Vulkacit HS 1 1(2,2,4-trimethyl-1,2-dihydroquinoline)Naftolen ZD 5 5(aromatic plasticizer)Vulkacit MOZ 1.18 1.18(benzothiazyl-2-sulfene-morpholine)Sulfur 1.07 1.07Rheometer: 145.degree. C.D.sub.max -D.sub.min (Nm) 6.97 7.71D.sub.min (Nm) 1.08 0.91Mooney ViscosityML (1 + 4) (100.degree. C.) (ME) 75 69Vulcanizate data: 145.degree. C., t.sub.95%Tensile strength (MPa) 25.7 25.9Modulus 300% (MPa) 7.5 8.8Firestone ball rebound (%) 42.2 47.4Shore A hardness 62 64Goodrich Flexometer: (RT, 108 N, 0.175 inch, 18 h)delta T center (.degree.C.) 95.1 87.4Dyn. compression (%) 25.0 21.2MTS testDyn. elasticity (MPa) 0.degree. C. 11.9 12.8 60.degree. C. 7.5 8.0Loss angle tan .delta. 0.degree. C. 0.254 0.242 60.degree. C. 0.138 0.125______________________________________

EXAMPLE IV

Dependence of optimal rubber performance on the quantity of silane applied to the carbon black.

High-performance automobile tread with N 234 as carbon black and bis-(triethoxysilylpropyl)-tetrasulfane as silane, formulation: ______________________________________Buna 1712 55Buna 1721 55Buna CB 30 30N 234 90Si 69 0 -3.5ZnO RS 3Stearic acid 1.5Naftolen ZD 12Protector G 35 1.5Vulacit NZ 2.6Sulfur 1.6______________________________________ Buna 1712 and 1721 are a styrene-butadiene rubber.

This Example shows that the loss angle tan .delta. at 60.degree. C., a parameter for rolling resistance, decreases with increasing Si 69 concentration and then deteriorates again beyond a quantity of 2 parts Si 69 to 90 parts N 234; the same applies to heat build-up and to ball rebound (FIGS. 1-3).

Further variations and modifications of the invention will become apparent to those skilled in the art from the foregoing and are intended to be encompassed by the claims appended hereto.

German Priority Application P 41 19 959.6, filed on Jun. 18, 1991, is relied on and incorporated by reference.

Claims

1. A process for the production of a vulcanizable plastic or rubber composition, comprising incorporating one or more organosilicon compounds of the following formulae:

(R.sup.1.sub.n --(RO).sub.3-n Si-(Alk).sub.m --(Ar).sub.p).sub.q (B)(I)

R.sup.1.sub.n --(RO).sub.3-n Si-(Alkyl) (II)

or

R.sup.1.sub.n --(RO).sub.3-n Si-(Alkenyl) (III)

in which

B=--SCN, --SH, --Cl (where q=1) or --S.sub.x -- (where q=2),

R=a C.sub.1-4 alkyl or C.sub.1-4 alkoxy group or a phenyl group,

R.sup.1 =a C.sub.1-4 alkyl group or a phenyl group,

n=0, 1 or 2,

Alk=a difunctional, linear or branched C.sub.1-6 hydrocarbon radical,

m=0 or 1,

Ar=a C.sub.6-12 arylene radical,

p=0 or 1, with the proviso that p and n cannot both be 0,

x=a number from 2 to 8,

Alkyl=a monofunctional, linear or branched unsaturated C.sub.1-20 hydrocarbon radical,

Alkenyl=a monofunctional, linear or branched unsaturated C.sub.2-20 hydrocarbon radical,

and carbon black with an alkaline pH value into said vulcanizable composition in a quantity corresponding to the quantity which is determined as no longer extractable with an organic solvent in the reaction of carbon black with an alkaline pH value and said organosilicon compound; wherein said vulcanizable composition does not contain silica and wherein said carbon black has a specific surface area of less than or equal to 300 m.sup.2 /g.

2. The process according to claim 1, wherein said Ar is C.sub.6 arylene radical.

3. The process according to claim 1, wherein said Alkyl is C.sub.2-8 hydrocarbon radical.

4. The process according to claim 1, wherein said Alkenyl is C.sub.2-6 hydrocarbon radical.

5. The process according to claim 1 wherein said quantity is 0.1 to 30 parts by weight per 100 parts by weight carbon black.

6. The process according to claim 5, wherein said quantity is 0.5 to 15 parts by weight.

7. The process according to claim 6, wherein said quantity is 0.5 to 4 parts by weight.

8. The process according to claim 1, wherein said vulcanizable composition contains 5 to 250 parts by weight of said carbon black per 100 parts by weight rubber or plastic.

9. The process according to claim 8, wherein said vulcanizable composition contains 50 to 100 parts by weight of said carbon black.

10. The process according to claim 1, wherein said rubber is selected from the group consisting of diene elastomers, copolymers of ethylene and propylene, carboxyl rubbers, epoxy rubbers, transpolypentenamer, halogenated butyl rubbers, rubbers of 2-chlorobutadiene, ethyl/vinyl acetate copolymers, and chemical derivatives of natural rubber and modified natural rubbers.

11. The process according to claim 10, wherein said diene elastomers are oil-extended natural and synthetic rubbers.

12. The process according to claim 11, wherein said rubbers are natural rubbers, terpolymers of ethylene, propylene and unconjugated dienes.

13. The process according to claim 1 in which said carbon black and organosilicon compounds are introduced simultaneously.

14. A vulcanizable plastic or rubber composition produced by the process according to claim 1.

15. A vulcanized plastic or rubber composition produced by the process according to claim 1.

16. A tire comprising the vulcanized plastic or rubber composition according to claim 15.

17. An industrial article comprising the vulcanized plastic or rubber composition according to claim 15.

18. The process according to claim 1, wherein said carbon black has a specific surface area of 20 to .gtoreq.300 m.sup.2 /g.

19. The process according to claim 1, consisting essentially of incorporating one or more organosilicon compounds of the following formulae:

(R.sup.1.sub.n --(RO).sub.3-n Si-(Alk).sub.m --(Ar).sub.p).sub.q (B)(I)

R.sup.1.sub.n --(RO).sub.3-n Si-(Alkyl) (II)

or

R.sup.1.sub.n --(RO).sub.3-n Si-(Alkenyl) (III)

in which

B=--SCN, --SH, --Cl (where q=1) or --S.sub.x -- (where q=2),

R=a C.sub.1-4 alkyl or C.sub.1-4 alkoxy group or a phenyl group,

R.sup.1 =a C.sub.1-4 alkyl group or a phenyl group,

n=0, 1 or 2,

Alk=a difunctional, linear or branched C.sub.1-6 hydrocarbon radical,

m=0 or 1,

Ar=a C.sub.6-12 arylene radical,

p=0 or 1, with the proviso that p and n cannot both be 0,

x=a number from 2 to 8,

Alkyl=a monofunctional, linear or branched unsaturated C.sub.1-20 hydrocarbon radical,

Alkenyl=a monofunctional, linear or branched unsaturated C.sub.2-20 hydrocarbon radical,

and carbon black with an alkaline pH value into said vulcanizable composition in a quantity corresponding to the quantity which is determined as no longer extractable with an organic solvent in the reaction of carbon black with an alkaline pH value and said organosilicon compound; wherein said vulcanizable composition does not contain silica.

20. The process according to claim 19, wherein said carbon black has a specific surface area of less than or equal to 300 m.sup.2 /g.

21. The process according to claim 19, wherein said carbon black has a specific surface area of 20 to less than or equal to 300 m.sup.2 /g.