The present invention relates to a process for the production of stable aqueous suspensions of sulphur, starting from hydrogen sulphide.
More specifically, the present invention relates to a process for the production of stable aqueous suspensions of sulphur, starting from hydrogen sulphide contained in fossil fuels, such as natural gas or associated gas, and from natural brackish or sea water, and their disposal by means of injection into geological structures. The term “natural brackish water” as used in the present description and claims, means water of a natural origin wherein the concentration of inorganic salts dissolved therein is higher than the drinkableness limit and can reach saturation limits, for example up to 3.5-4% by weight.
Sulphur, in the form of H2S, can be present even in a significant amount in both crude oil extracted and also in associated gas, in addition to natural gas. As hydrogen sulphide is a polluting substance which must be disposed of before the combustion of methane itself, its presence represents a problem to an extent that the higher the amount of hydrogen sulphide present, the more relevant this problem becomes from an economical point of view.
If its presence, in fact, is in the order of a few parts per million, the additional cost for its treatment is negligible, when the content reaches higher levels, however, for example when the amount of hydrogen sulphide is in excess of 15-20% of the gaseous blend, this cost increases up to prohibitive limits.
Natural gas containing considerable quantities of hydrogen sulphide (acid gas) is treated with solutions capable of selectively absorbing H2S, such as, for example, solutions of alkanolamines, thus obtaining a gaseous blend of hydrocarbons which can be used as fuel with no problems from an environmental point of view.
H2S is obtained, in its pure state, by the desorption of solutions of alkanolamines, and it can be subsequently transformed into sulphur through the Claus process. The application of this process, however, proves to be economically convenient only when high volumes of hydrogen sulphide are to be treated and the concentration of hydrogen sulphide in natural or associated gas is at least equal to 5% by volume.
The Claus process also has considerable construction and management costs, for producing a material whose supply widely exceeds the demand. At present, in fact, the supply of the product on the sulphur market exceeds the demand and the market projections for the next five-year period reveal a further increase in the difference between demand and supply. The ever-increasing supply of sulphur is due to a large extent to the exploitation of new oil and natural gas reservoirs, characterized by a high content of compounds containing sulphur.
There is therefore the problem of transforming hydrogen sulphide into elemental sulphur, also when the Claus process is not economically interesting, and also of finding a system for the disposal of sulphur when the market has a low demand for sulphur.
The sulphur currently produced, which does not find an immediate market, is stocked in the form of high dimensioned blocks in huge open-air deposits. This causes considerable problems from an environmental point of view as sulphur is subjected to erosion on the part of atmospheric agents and can therefore be diffused over a large area surrounding the storehouse. Furthermore, due to the presence of micro-organisms present on the surface of the sulphur, the sulphur is transformed into sulphuric acid thus acidifying the surrounding soil.
The ideal solution would be to keep the sulphur protected from atmospheric agents, as can happen in the case of underground disposal in suitable geological structures. In this case, however, the problem arises of how the sulphur can be injected into the formation, as it has a high melting point (119° C.)
In international patent application WO 2005/095271 a process is described for the disposal of sulphur coming from H2S contained in natural or associated gas, which consists in reacting hydrogen sulphide with an aqueous solution of sulphur dioxide, obtaining a sulphur dispersion in water having an exceptional stability. This dispersion of sulphur in water is stable for weeks and extremely high weight concentrations of sulphur can be reached (up to 30% or even more), whereas a common sulphur dispersion in water proves to be unstable when the sulphur concentration exceeds 1 g/l.
This process envisages the use of pure water to trigger the synthesis reaction of the sulphur dispersion in water. This characteristic can be a limitation when the production of the sulphur dispersion in water is programmed near the gas production wells, which are often in secluded areas, where sufficient amounts of fresh water are not always available. Furthermore, fresh water always represents a cost, which in some areas can be quite significant. Finally, increasing attention is being paid, from an environmental point of view, towards the consumption of fresh water.
The Applicants have now found a new process for the production of stable sulphur suspensions, present as H2S in natural or associated gas, by means of an alternative process to both the Claus process and also to that of the known art, which still envisages the synthesis of sulphur in the form of an aqueous suspension, which can be used for obtaining sulphur with a high degree of purity or for the disposal of the same in dedicated sites, in which, however, natural brackish or sea water is used as the liquid medium for the suspension. This is a very surprising result, as it is known—see, for example “Gmelin Handbuch der Anorganischen Chemie”, Schwefel, Teil, Lieferung, 1, 254-502,—that the presence of inorganic ions cause the coagulation of colloids in aqueous solutions, and this effect is particularly marked in common sulphur dispersions in water, which are also very sensitive to concentrations of ions, such as sodium or potassium, even in the order of a few mg/l (34 and 32, respectively) and even more so to the presence of earth alkaline metals (4 mg/l Be2+, 8.4 mg/l Mg2+, 7.6 mg/l Ca+2).
The object of the present invention therefore relates to a process for the production of stable sulphur suspensions starting from hydrogen sulphide contained in natural or associated gas, comprising:
2H2S+SO2→→3S+2H2O (I)
According to the present invention, hydrogen sulphide can be recovered from natural or associated gas or extracted from crude oil, according to conventional methods, for example by means of absorption with amines. These technologies allow streams of H2S to be obtained at a degree of purity higher than 90%. An aliquot of the H2S stream thus obtained, ranging from 5 to 35% by volume with respect to the total, is oxidised to SO2, which is dissolved in natural brackish water or sea water and reacted with the remaining H2S also at a temperature equal to or lower than room temperature (T=20° C.), thanks to the high solubility of the gaseous SO2 also in brackish water.
As an alternative to the previous process scheme, when the concentration of hydrogen sulphide is relatively high, higher than 1%, only a third of the gaseous stream of natural or associated gas can be treated with amine absorbing solutions.
According to this alternative process scheme, a third of the gaseous stream is treated with alkanolamines, obtaining a stream of concentrated hydrogen sulphide, which is burned to sulphur dioxide, which is absorbed in natural brackish water or sea water. The remaining gaseous stream, consisting of ⅔ of the initial stream, is put in contact with this aqueous solution of SO2. In this way the hydrogen sulphide reacts with the sulphur dioxide generating the aqueous suspension of sulphur, whereas the natural or associated gas leaves the reactor purified.
According to a further alternative to the initial process scheme, the treatment with solutions of alkanolamines can be avoided when the concentration of hydrogen sulphide is relatively high, higher than 2%.
According to this alternative process scheme, a third of the gaseous flow is treated with an amount of water in defect with respect to the total combustion, by oxidising hydrogen sulphide to SO2, but substantially not burning the methane. The gaseous stream thus obtained, containing mainly methane, SO2 and small amounts of CO2, is put in contact with natural brackish water or sea water which easily absorb SO2 creating a stream of gas essentially consisting of methane (with traces of CO2) and an aqueous solution of SO2. The remaining gas stream, consisting of ⅔ of the initial stream, is then put in contact with said aqueous solution of SO2. In this way, H2S reacts with SO2 producing the aqueous suspension of sulphur, whereas the natural or associated gas leaves the reactor purified.
The process object of the present invention, and its possible alternatives, is characterized by various very significant advantages:
If the stability of the aqueous suspension is to be increased, additives can be added, in a small quantity and absolutely non-toxic, consequently with null environmental impact, capable of guaranteeing the stability of the above-mentioned suspension for a very long periods of time.
A typical example of the above additives are emulsions stabilized by 0.1% by weight of Agar-agar, a natural product normally used in the food industry, which stabilises sulphur suspensions in water for extremely long periods of time.
Some examples are provided hereunder, for illustrative and non-limiting purposes, of the synthesis of the aqueous sulphur suspension according to the present invention and of the evaluation of the particle-size by means of a laser diffraction granulometer.
The graphs of
46.08 g of SO2 (0.72 moles) are dissolved in 1 liter of brackish water comprising 35 g of NaCl. Pure H2S is bubbled into said limpid and colourless solution, at a flow-rate of 2 Nl/h, collecting samples which are titrated in order to evaluate the residual concentration of SO2 and H2S. The SO2 is iodometrically titrated, whereas the H2S is titrated by complexometry, using hydroxymercurobenzoic acid as titration agent and ditizone as indicator. The H2S at the inlet is completely absorbed. Table 1 shows the trend of this titration.
A stable suspension of sulphur in water having a yellow colour is formed, from which both the SO2 and H2S disappeared, according to the reaction:
SO2+2H2S→→3S+2H2O
The pH of said aqueous suspension is equal to 2.64 and the weight content of sulphur 68.5 g/l (6.85%).
The suspension was maintained under rest conditions at room temperature for two weeks, at the end of which no formation of deposits was observed.
The particle-size distribution (PSD) of the sulphur particles of this suspension is evaluated by means of a laser diffraction granulometer (Coulter type LS730). The instrument, which uses a laser in the solid state with a wave-length of 750 nm, allows a measurement-range of between 0.04 and 2,000 μm to be obtained. The processing of the scattering signal was effected by applying the optical model of Mie (
46.08 g of SO2 (0.72 moles) are dissolved in 1 liter of sea water comprising 34.31 g of NaCl, 13.466 g of MgCl2.H2O and 3.06 g of CaCl2.H2O. Pure H2S is bubbled into said limpid and colourless solution, at a flow-rate of 2 Nl/h, collecting samples which are titrated in order to evaluate the residual concentration of SO2 and H2S. The SO2 is iodometrically titrated, whereas the H2S is titrated by complexometry, using hydroxymercurobenzoic acid as titration agent and ditizone as indicator. The H2S at the inlet is completely absorbed.
Table 2 shows the trend of this titration. A stable suspension of sulphur in water having a yellow colour is formed, from which both the SO2 and H2S disappeared, according to the reaction:
SO2+2H2S→→3S+2H2O
The pH of said aqueous suspension is equal to 4.3 and the weight content of sulphur 68.5 g/l (6.85%).
The suspension was maintained under rest conditions at room temperature for two weeks, at the end of which no formation of deposits was observed.
The particle-size distribution (PSD) of the sulphur particles of this suspension is evaluated by means of a laser diffraction granulometer (Coulter type LS730). The instrument, which uses a laser in the solid state with a wave-length of 750 nm, allows measurement-range of between 0.04 and 2,000 μm to be obtained. The processing of the scattering signal was effected by applying the optical model of Mie (
| Number | Date | Country | Kind |
|---|---|---|---|
| MI2006A 000689 | Apr 2006 | IT | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2007/002542 | 3/21/2007 | WO | 00 | 7/15/2008 |