Claims
- 1. An article thermoformed from a poly(ethylene terephthalate) sheet reinforced with glass fibers, which fibers are present in an amount within the range of about 5-50% by weight of the sheet composition, said thermoformed article having been thermoformed at a draw ratio of less than about 1.8, defined as the ratio of the initial thickness of the poly(ethylene terephthalate) sheet to the minimum wall thickness of the article, said article having without any further treatment at least one surface having an average roughness, R.sub.A, of about 0.1-0.8 .mu.m, and a concave optical imperfection index of less than about 6% of the surface area as determined by image analysis using a microscope having a magnification of 70 times.
- 2. The article of claim 1 wherein the fibers have an average length to diameter ratio of at least 10.
- 3. The article of claim 1 wherein the amount of glass fibers in the reinforced polymer composition is about 10-35 weight percent.
- 4. An article of claim 1 wherein the reinforced polymer composition also contains another polymer material selected from the group consisting of dipolymers of ethylene with an unsaturated carboxylic acid, terpolymers of ethylene with an unsaturated carboxylic acid and an ester of an unsaturated carboxylic acid, and terpolymers of ethylene with an unsaturated carboxylic acid, and a vinyl ester, the proportion of the carboxylic acid in the dipolymers being about 2-20 weight percent, and the respective proportions of the carboxylic acid and of the ester in the dipolymers being about 1-30 weight percent of each; and the amount of the dipolymer or terpolymer being about 1-20% based on the weight of the reinforced polymer composition,
- with the proviso that the carboxylic groups may be completely or partially neutralized with divalent metal ions.
- 5. The article of claim 4, wherein the carboxylic groups are partially or completely neutralized with zinc, magnesium, or calcium ions.
- 6. The article of claim 3 wherein the proportion of the dipolymer or terpolymer in the reinforced polymer composition is about 3-10%.
- 7. An article having a face member and a backing member adhesively bonded to the face member, each member being thermoformed from a sheet of a poly(ethylene terephthalate) composition reinforced with a mineral filler, the face member having been thermoformed at a draw ratio of less than about 1.8, defined as the ratio of the initial thickness of the poly(ethylene terephthalate) sheet to the minimum wall thickness of the face member, said face member having without any further treatment at least one surface having an average roughness, R.sub.A, of about 0.1-0.8 .mu.m, and a concave optical imperfection index of less than about 6% of the surface area, as determined by image analysis using a microscope having a magnification of 70 times; with the proviso the mineral filler in the face member is glass fibers, and the amount of the glass fibers is about 5-50% by weight of the sheet composition.
- 8. The article of claim 7 wherein the face member is thermoformed at a draw ratio of at most 1.3.
- 9. The article of claim 7 wherein the backing member has the same composition as the face member.
- 10. The article of claim 9 wherein the average length to diameter ratio of the glass fibers is at least 10.
- 11. The article of claim 9 wherein the amount of glass fibers in the poly(ethylene terephthalate) composition is 10-35% by weight.
- 12. The article of claim 7 wherein the poly(ethylene terephthalate) sheet material also contains another polymeric material selected from the group consisting of dipolymers of ethylene with an unsaturated carboxylic acid, terpolymers of ethylene with an unaturated carboxylic acid and an ester of an unsaturated carboxylic acid, and terpolymers of ethylene with an unsaturated carboxylic acid and a vinyl ester, the proportion of the carboxylic acid in the dipolymers being about 2-20 weight percent, and the respective proportions of the carboxylic acid and of the ester in the terpolymers being about 1-30 weight percent of each; and the amount of the dipolymer or terpolymer being about 1-20% based on the weight of the reinforced polymer composition.
- 13. The article of claim 12, wherein the carboxylic groups are partially or completely neutralized with zinc, magnesium, or calcium ions.
- 14. The article of claim 13 wherein the amount of the dipolymer or terpolymer is 3-10% based on the weight of the reinforced polymer composition.
- 15. An article of claim 1 selected from the class consisting of automotive parts, aircraft parts, construction elements, marine parts, appliance parts, food service trays, sanitary articles, solar collectors, equipment housings, and furniture.
- 16. An article of claim 2 made of a composition containing a filler having an aspect ratio of about 10-35.
- 17. An article of claim 16 wherein the filler is glass fibers.
- 18. An article of claim 17 which is an automotive part.
- 19. An article of claim 17 which is an aircraft part.
- 20. An article of claim 17 which is a marine part.
- 21. An article of claim 17 which is a construction element.
- 22. An article of claim 17 which is a food service tray.
- 23. An article of claim 17 which is a sanitary article.
- 24. An article of claim 17 which is a solar collector.
- 25. An article of claim 17 which is an equipment housing.
- 26. An article of claim 17 which is an article of furniture.
- 27. An article of claim 7 selected from the class consisting of automotive parts, aircraft parts, construction elements, marine parts, appliance parts, food service trays, sanitary articles, solar collectors, equipment housings, and furniture.
- 28. An article of claim 27 made of a composition containing a filler having an aspect ratio of about 10-35.
- 29. An article of claim 28 wherein the filler is glass fibers.
- 30. An article of claim 29 which is an automotive part.
- 31. An article of claim 29 which is an aircraft part.
- 32. An article of claim 29 which is a marine part.
- 33. An article of claim 29 which is a construction element.
- 34. An article of claim 29 which is a food service tray.
- 35. An article of claim 29 which is a sanitary article.
- 36. An article of claim 29 which is a solar collector.
- 37. An article of claim 29 which is an equipment housing.
- 38. An article of claim 29 which is an article of furniture.
CROSS-REFERENCE TO RELATED APPLICATION
This is a division of application Ser. No. 390,683, filed June 21, 1982, now U.S. Pat. No. 4,457,797, which is a continuation-in-part of our Application Ser. No 355,711 filed Mar. 8, 1982 now abandoned.
US Referenced Citations (4)
Number |
Name |
Date |
Kind |
3496143 |
Siggel et al. |
Feb 1970 |
|
3935358 |
Wyeth et al. |
Jan 1976 |
|
4127631 |
Dempsey et al. |
Nov 1978 |
|
4414266 |
Archer et al. |
Nov 1983 |
|
Non-Patent Literature Citations (1)
Entry |
Thermoforming Crystallizing PET, J. L. Throne, Boston, SPE-Antec Meeting, 5/5/81, pp. 598-600. |