Claims
- 1. A process for heat treating a copper film formed on a ceramic, comprising the steps of:
- placing at least one ceramic body having a surface and a copper film formed on at least a portion of said surface in a sealed chamber of a container, said container preventing gas located outside of said container from entering said chamber, said container permitting gas located in said chamber to discharge outside said container only when the pressure of said gas inside said chamber is increased above a predetermined level; and
- applying heat to said container while maintaining the outside of said container in an inert atmosphere so as to heat both said at least one ceramic body and said gas located in said chamber to a sufficient temperature that the pressure of said gas located in said chamber is raised above said predetermined level whereby said gas located inside said chamber is at least partially evacuated from said chamber and said copper film is heat treated.
- 2. A process for heat treating a copper film formed on a ceramic body in accordance with claim 1, wherein said heating step comprises a step of heating at the temperature between 300.degree. and 1000.degree. C.
- 3. A process for heat treating a copper film formed on a ceramic body in accordance with claim 1, wherein said heating step comprises a step of heating at the temperature between 500.degree. and 1000.degree. C.
- 4. A process for heat treating a copper film formed on a ceramic body in accordance with claim 1, wherein said step of placing said at least one ceramic body in said container comprises the step of placing a sufficient number of ceramic bodies in said container to ensure that said ceramic bodies take up 50-100% of the volume of said chamber.
- 5. A process for heat treating a copper film formed on a ceramic body in accordance with claim 1, wherein said container comprises a container body having an opening defined by a periphery thereof, and a lid being fitted to said periphery of said opening for closing said opening.
- 6. A process for heat treating a copper film formed on a ceramic body in accordance with claim 5, wherein a gap is formed between said fitting portion of said container body and said lid which allows evacuation of gas inside said container during said heating step.
- 7. A process for heat treating a copper film formed on a ceramic body in accordance with claim 5, wherein:
- said fitting portion of said container body and said lid cooperate to establish a gas tight state; and
- said container is provided with a valve permitting passage of gas only in a direction from the inside to the outside of said container.
- 8. A process for heat treating a copper film formed on a ceramic body in accordance with claim 4, wherein said ceramic bodies are placed in said container randomly.
- 9. A process for heat treating a copper film formed on a ceramic body in accordance with claim 8, wherein said heating step comprises the step of heating to a temperature between 500 degrees and 1000 degrees C.
- 10. A process for heat treating a copper film formed on a ceramic, comprising the steps of:
- providing a container having a chamber adapted to be sealed so as to prevent gas located outside of said container from entering said chamber and adapted to permit gas located in said chamber when said container is sealed to discharge outside said container only when the pressure of said gas inside said chamber is increased above a predetermined level;
- placing at least one ceramic body having a surface and a copper film formed on at least a portion of said surface in said chamber;
- sealing said chamber;
- establishing an inert atmosphere outside said container; and
- applying heat to said container while maintaining the outside of said container in said inert atmosphere so as to heat both said at least one ceramic body and said gas located in said chamber to a sufficient temperature that the pressure of the gas located in said chamber is raised above said predetermined level, whereby said gas located inside said chamber is at least partially evacuated from said chamber and said copper film is heat treated.
- 11. A process for heat treating a copper film formed on a ceramic body in accordance with claim 10, wherein said heating step comprises the step of heating to a temperature between 300 and 1000 degrees C.
- 12. A process for heat treating a copper film formed on a ceramic body in accordance with claim 11, wherein said heating step comprises the step of heating to a temperature between 500 and 1000 degrees C.
- 13. A process for heat treating a copper film formed on a ceramic body in accordance with claim 12, wherein said step of placing said at least one ceramic body in said container comprises the step of placing a sufficient number of ceramic bodies in said container to ensure that said ceramic bodies take up 50 to 100% of the volume of said chamber.
- 14. A process for heat treating a copper film formed on a ceramic body in accordance with claim 13 wherein said ceramic bodies are randomly placed in said container.
Parent Case Info
This application is a divisional of U.S. patent application Ser. No. 322,458, filed Nov. 18, 1981, now abandoned which in turn is a divisional of U.S. patent application Ser. No. 194,983, filed Oct. 8, 1980, now U.S. Pat. No. 4,402,494.
US Referenced Citations (13)
Non-Patent Literature Citations (2)
Entry |
The American Heritage Dictionary of the English Language, Houghton Mifflin Co., 1976, pp. 367, 681 and 1106. |
CRC Handbook of Chemistry and Physics, 54th edition, p. F-85. |
Divisions (2)
|
Number |
Date |
Country |
Parent |
322458 |
Nov 1981 |
|
Parent |
194983 |
Oct 1980 |
|