Claims
- 1. A process for preparing a magnetic recording medium which comprises a substrate and a recording layer coated on the substrate comprising:
- immersing a substrate into an aqueous solution comprising a ferromagnetic metal ion, a reducing agent for the metal ion, a complexing agent for the metal ion, a pH buffer, an adjuster and 0.005 to 100 g per liter of an aromatic organic polymer (B') and
- co-depositing and continuously forming onto the substrate, a thin film of a ferromagnetic metal, and being contained in the film, 0.001 to 30 percent by weight, based on the film, of an aromatic organic polymer (B') having a weight-average molecular weight of 1,000 to 1,000,000 and comprising at least one aromatic ring and 1 to 10 hydroxyl groups (--OH) on the average based on 500 units of the molecular weight and further, as an indispensable component, 0.1 to 4 sulfone groups (--SO.sub.3) or 0.1 to 6 groups on the average, based on 500 units of the molecular weight, of at least one polar group selected from the group consisting of a phosphate group represented by the formula ##STR83## a phosphite group represented by the formula ##STR84## a phosphonate group represented by the formula ##STR85## a phosphonite group represented by the formula ##STR86## a phosphinate group represented by the formula ##STR87## a phosphinite group represented by the formula ##STR88## a tertiary amino group represented by the formula ##STR89## and a quaternary ammonium group represented by the formula ##STR90## wherein R is a hydrogen atom or a hydrocarbon group, R.sub.1, R.sub.2, and R.sub.3 which may be the same or different are each a straight-chain group, a branched alkyl group, a hydroxyalkyl group or an aromatic group, and X is a counter anion, a carboxyl group )--COOH), or a nitro group, wherein said aromatic rings are linked to each other through a main chain comprising at least one member selected from a C--C, C.dbd.C, or ether (C--O--C) bond.
- 2. The process as claimed in claim 1, in which R.sub.1, R.sub.2 and R.sub.3 are each a phenyl group or a benzyl group.
- 3. The process as claimed in claim 1, in which the film contains 0.001 to 10 percent by weight of polymer (B').
- 4. The process as claimed in claim 1, in which the film contains 0.001 to 10 percent by weight of polymer (B').
- 5. The process as claimed in claim 1, in which polymer (B') is contained in the crystal grain of the metal.
- 6. The process as claimed in claim 1, in which polymer (B') is soluble or dispersible in water.
- 7. The process as claimed in claim 1, in which a metal is contained in the molecule of polymer (B').
- 8. The process as claimed in claim 7, in which the metal is selected from the group consisting of Co, Ni, Ti, Pd, Pt, Zr, Hf, Rh, Fe, V, Cr, Mo and Si.
- 9. The process as claimed in claim 1, in which at least one of said hydroxy group is attached to at least one of said aromatic ring.
- 10. The process as claimed in claim 1, which is conducted while controlling proportions of polymer (B') to the entire codeposited thin film in a range of 0.01 to 30 percent by weight, to affect an electroless plating.
- 11. A process for preparing a magnetic recording medium which comprises a substrate and a recording layer coated on the substrate comprising:
- co-depositing and continuously forming by evaporation onto the substrate, a thin film of a ferromagnetic metal and being contained in the film, 0.001 to 10 percent by weight, based on the film of an aromatic organic polymer (B') having a weight-average molecular weight of 1,000 to 1,000,000 and comprising at least one aromatic ring and 1 to 10 hydroxyl groups (--OH) on the average based on 500 units of the molecular weight and further, as an indispensable component, 0.1 to 4 sulfone groups (--SO.sub.3) or 0.1 to 6 groups on the average, based on 500 units of the molecular weight, of at least one polar group selected from the group consisting of a phosphate group represented by the formula ##STR91## a phosphite group represented by the formula ##STR92## a phosphonate group represented by the formula ##STR93## a phosphonite group represented by the formula ##STR94## a phosphinate group represented by the formula ##STR95## a phosphinite group represented by the formula ##STR96## a tertiary amino group represented by the formula ##STR97## and a quaternary ammonium group represented by the formula ##STR98## wherein R is a hydrogen atom or a hydrocarbon group, R.sub.1, R.sub.2, and R.sub.3 which may be the same or different are each a straight-chain group, a branched alkyl group, a hydroxyalkyl group or an aromatic group, and X is a counter anion, a carboxyl group (--COOH), or a nitro group, wherein said aromatic rings are linked to each other through a main chain comprising at least one member selected from a C--C, C.dbd.C, or ether (C--O--C) bond.
- 12. The process as claimed in claim 11, which is conducted while controlling proportions of polymer (B') to the entire co-deposited thin film in a range of 0.01 to 30 percent by weight.
- 13. A process for preparing a magnetic recording medium which comprises a substrate and a recording layer coated on the substrate comprising:
- co-depositing and continuously forming by evaporation onto the substrate, a thin film of a ferromagnetic metal and being contained in the film 0.001 to 10 percent by weight, based on the film, of an aromatic organic polymer (A) defined by formula (A): ##STR99## wherein m.gtoreq.0 and n.gtoreq.3 and each is an arbitrary number necessary for said organic aromatic polymer defined by formula (A) to have a weight-average molecular weight up to 1,000,000;
- .gtoreq. k.gtoreq.2;
- 0.gtoreq.p.gtoreq.2;
- provided that k+p+m.gtoreq.0;
- R.sup.1, R.sup.2, and R.sup.3 are each H or an alkyl group having 1 to 5 carbon atoms;
- X is a polymerizable vinyl monomer; and
- Y and Z which may be the same or different are each selected from the group consisting of ##STR100## CR.sup.4 R.sup.5 OR.sup.6, --CH.sub.2 OH, an alkyl group having 1 to 18 carbon atoms and an aryl group, wherein M is H, an alkali metal, an alkaline earth metal, or an organic cation of an amine;
- Y.sup.1 and Y.sup.4 are each a halogen;
- Y.sup.2 and Y.sup.3 are each a counter ion selected from a halogen ion, an organic acid anion, or an inorganic acid anion;
- W is S or O;
- R.sup.4 to R.sup.8 which may be the same or different are each a straight-chain group, a branched alkyl group, a hydroxyalkyl group, an aromatic group, or H, provided that R.sup.6 R.sup.7 may be combined to form a ring together with the N group;
- R.sup.9 to R.sup.15 which may be the same or different are each a straight-chain group, a branched alkyl group, a hydroxyalkyl group, an aromatic group, or H;
- q, s, and t are each 0 or 1; and
- r is 0, 1, or 2.
- 14. The process as claimed in claim 13, which is conducted while controlling proportions of polymer (A) to the entire co-deposited thin film in a range of 0.01 to 30 percent by weight.
- 15. A process for preparing a magnetic recording medium which comprises a substrate and a recording layer coated on the substrate comprising:
- immersing a substrate into an aquesous solution comprising a ferromagnetic metal ion, a reducing agent for the metal ion, a complexing agent for the metal ion, a pH buffer, an adjuster and 0.005 to 100 g per liter of an aromatic organic polymer (A) and
- co-depositing and continuously forming onto the substrate, a thin film of a ferromagnetic metal, and being contained in the film, 0.001 to 30 percent by weight, based on the film, of an aromatic organic polymer (A) defined by formula (A): ##STR101## wherein m.gtoreq.0 and n.gtoreq.3 and each is an arbitrary number necessary for said organic aromatic polymer defined by formula (A) to have a weight-average molecular weight up to 1,000,000;
- .ltoreq. k.ltoreq.2;
- 0.ltoreq.p.ltoreq.2;
- provided that k+p+x.gtoreq.0;
- R.sup.1, R.sup.2, and R.sup.3 are each H or an alkyl group having 1 to 5 carbon atoms;
- x is a polymerizable vinyl monomer; and
- Y and Z which may be the same or different are each selected from the group consisting of ##STR102## CR.sup.4 R.sup.5 OR.sup.6, --CH.sub.2 OH, an alkyl group having 1 to 18 carbon atoms and an aryl group, wherein M is H, an alkali metal, an alkaline earth metal, or an organic cation of an amine;
- Y.sup.1 and Y.sup.4 are each a halogen;
- Y.sup.2 and Y.sup.3 are each a counter ion selected from a halogen ion, an organic acid anion, or an inorganic acid anion;
- W is S or O;
- R.sup.4 to R.sup.8 which may be the same or different are each a straight-chain group, a branched alkyl group, a hydroxyalkyl group, an aromatic group, or H, provided that R.sup.6 and R.sup.7 may be combined to form a ring together with the N group;
- R.sup.9 and R.sup.15 which may be the same or different are each a straight-chain group, a branched alkyl group, a hydroxyalkyl group, an aromatic group, or H;
- q, s, and t are each 0 or 1; and
- r is 0, 1, or 2.
- 16. The process as claimed in claim 15, which is conducted while controlling proportions of polymer (A) to the entire codeposited thin film in a range of 0.01 to 30 percent by weight, to affect an electroless plating.
Priority Claims (1)
Number |
Date |
Country |
Kind |
63-199 |
Jan 1988 |
JPX |
|
Parent Case Info
This application is a divisional of copending application Ser. No. 07/292,533, filed on Dec. 30, 1988, U.S. Pat. No. 5,080,982, now allowed, the entire contents of which are hereby incorporated by reference.
Divisions (1)
|
Number |
Date |
Country |
Parent |
292533 |
Dec 1988 |
|