Claims
- 1. A process for vapor phase catalytic hydrogenation of a feed compound selected from maleic anhydride, succinic anhydride, maleic acid, succinic acid, and mixtures thereof, to gamma-butyrolactone, in a conversion of about 95%, or more, and a selectivity of about 80%, or more, which comprises:
- (a) providing an activated catalyst composition in a reactor, said catalyst being capable of production of gamma-butyrolactone for at least about 100 hours before reactivation of the catalyst, and for at least about 2000 hours without requiring fresh catalyst, comprising:
- (1) said composition consisting essentially of about 30-65% by weight of CuO, about 18-50% by weight of ZnO, about 8-22% by weight of Al.sub.2 O.sub.3, having a total pore volume of about 0.05 to 0.5 cc/g, and a surface area of about 20 to 120 m.sup.2 /g,
- (2) reducing said catalyst composition with hydrogen in a gradually increasing hydrogen concentration of from about 0.5% to about 10% initial concentration of hydrogen in an inert diluent to 100% hydrogen in the final concentration under conditions of an increasing reduction temperature of about 150.degree. to about 350.degree. C. for about 5 to 20 hours, and
- (3) activating the reduced catalyst in hydrogen at an activation temperature of at least 400.degree. C., for a period of at least about 8 hours, to provide an activated catalyst having a total pore volume of about 0.08 to 0.3 cc/g, and a surface area of about 15 to 100 m.sup.2 /g,
- (b) providing a vapor mixture of said feed compound in hydrogen at a molar ratio of hydrogen to feed compound of about 200:1 to 500:1, and
- (c) passing said vapor mixture over said activated catalyst at (i) a pressure of about 50 to 500 psig, and (ii) a feed rate space velocity of about 0.03 to 1.0 hours.sup.-1, for (iii) a contact time of less than about 10 seconds, at (iv) a reaction temperature of about 200.degree. to about 400.degree. C.,
- said process being capable of production of gamma-butyrolactone for at least about 100 hours before reactivation of the catalyst, and of at least about 2000 hours without requiring fresh catalyst.
- 2. A process according to claim 1 wherein, in (b), said molar ratio of hydrogen to feed compound in the vapor mixture is about 230:1 to 280:1.
- 3. A process according to claim 1 wherein, in (c) (i), the vapor phase catalytic hydrogenation reaction is carried out at a pressure of about 75 to 250 psig.
- 4. A process according to claim 1 wherein, in (c) (iii), the contact time is about 2.0 to about 3.5 seconds.
- 5. A process according to claim 4 wherein, in (c) (iii), the contact time is about 2.5-3.0 seconds.
- 6. A process according to claim 1 wherein, in (c) (iv), the vapor phase catalytic hydrogenation reaction is carried out at a reaction temperature of about 150.degree. to 300.degree. C.
- 7. A process according to claim 1 wherein the conversion is about 100% and selectivity is about 90-95%.
- 8. A process according to claim 1 wherein the feed compound is maleic anhydride.
- 9. A process according to claim 1 wherein the reactor is a fixed bed reactor.
- 10. A process according to claim 1 wherein, in (b), said vapor mixture is obtained by forming finely divided droplets of said feed compound and contacting said droplets with hot recycle hydrogen gas to vaporize said droplets.
- 11. A process according to claim 1 wherein, in (a) (3), said activation temperature is 400.degree. to 525.degree. C.
- 12. A process according to claim 1 wherein, in (a) (3), said activation temperature is 425.degree. to 450.degree. C.
- 13. A process according to claim 1 wherein, in (a) (1), said catalyst composition consists essentially of about 50-60% by weight of CuO, about 20-25% by weight of ZnO, and about 15-20% by weight of Al.sub.2 O.sub.3.
- 14. A process according to claim 1 wherein, in (a) (1), said catalyst composition has a total pore volume of about 0.1 to 0.4 cc/g, and a surface area of about 40 to 100 m.sup.2 /g, and, in (c), said activated catalyst has a total pore volume of about 0.10 to 0.25 cc/g, and a surface area of about 30 to 65 m.sup.2 /g.
- 15. A process according to claim 1 wherein, in (a) (1), said catalyst composition is prepared by calcining the metal carbonates or nitrates to the respective oxides.
CROSS-REFERENCE TO RELATED PATENT APPLICATIONS
This application is a continuation-in-part of U.S. patent application Ser. No. 521,065, filed Apr. 16, 1990, by the same inventors and assigned to the same assignee as herein now abandoned.
This application is related to U.S. patent application Ser. No. 509,431, filed Apr. 16, 1990, now U.S. Pat. No. 5,041,564, assigned to the same assignee as herein, which disclosure is incorporated by reference.
US Referenced Citations (3)
Number |
Name |
Date |
Kind |
3580930 |
Miya et al. |
May 1971 |
|
4420622 |
Van de Moesdijk et al. |
Dec 1983 |
|
4652685 |
Cawse et al. |
Mar 1987 |
|
Foreign Referenced Citations (1)
Number |
Date |
Country |
46-3775 |
Jan 1971 |
JPX |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
521065 |
Apr 1990 |
|