Processes, compositions and compounds

[0001] This invention relates to compounds, to inks and to their use in ink jet printing (“IJP”). IJP is a non-impact printing technique in which droplets of ink are ejected through a fine nozzle onto a substrate without bringing the nozzle into contact with the substrate.

[0002] There are many demanding performance requirements for compounds and inks used in IJP. For example they desirably provide sharp, non-feathered images having good water-fastness, light-fastness and optical density. The inks are often required to dry quickly when applied to a substrate to prevent smudging, but they should not form a crust over the tip of an ink jet nozzle because this will stop the printer from working. The inks should also be stable to storage over time without decomposing or forming a precipitate which could block the fine nozzle.

[0003] WO 01/48090 relates to metal chelate azo compounds which comprise a naphthol component and heterocyclic groups. However, WO 01/48090 does not disclose such compounds further substituted by a triazole ring.

[0004] There is a need for compounds which meet the demanding performance requirements in IJP and, in particular, having a good combination of high chroma (i.e. brightness), hight light-fastness and fastness to oxidising gasses (e.g. ozone).

[0005] According to a first aspect of the present invention there is provided a metal chelate compound of the Formula (1) and salts thereof:

[0006] wherein:

[0007] one of A and B is OH and the other is an azotriazole group;

[0008] each W independently is a carboxy or carbonamido group;

[0009] each X independently is a substituent other than H, sulphonamido, carboxy, sulpho and carbonamido;

[0010] J is a sulphonamido group;

[0011] M is a metal or boron;

[0012] a, q, p and n are each independently 0, 1, 2, 3 or 4; and

[0013] (p+q+a+n) is 0, 1, 2, 3 or 4.

[0014] Preferably n is 1, 2 or 3, more preferably 1 or 2.

[0015] Preferred azotriazole groups are of the Formula (2a), (2b), (2c), (2d) or (2e):

[0016] wherein:

[0017] Z is H, —OH, —Br, —Cl, —F, —CN, —NO2, —PO3H2, —SO3H, —CO2H, optionally substituted phosphoramide, optionally substituted alkyl, optionally substituted alkenyl, optionally substituted alkynyl, optionally substituted aryl, optionally substituted aralkyl, —SR1, —SO2R1, —SO2NR2R3, —SOR1, —OR1, —C(O)R1, —C(O)OR1, —C(O)NR2R3, —NR2R3, —NHCOR1; and

[0018] Y is CF3 or any one of the groups defined for Z; and

[0019] wherein:

[0020] R1, R2 and R3 are each independently H, optionally substituted alkyl, optionally substituted alkenyl, optionally substituted alkynyl, optionally substituted aryl or optionally substituted aralkyl; or

[0021] R2 and R3 together with the nitrogen to which they are attached form an optionally substituted 5- or 6-membered ring.

[0022] When Y or Z is optionally substituted phosphoramide the phosphoramide is preferably substituted by optionally substituted alkyl, optionally substituted aryl or optionally substituted aralkyl. Preferred substituents include for example methyl, ethyl, n-propyl, iso-propyl, hydroxyethyl, optionally substituted phenyl or optionally substituted benzyl.

[0023] When Y or Z is optionally substituted alkyl, the alkyl group is preferably optionally substituted C1-4-alkyl, more preferably C1-4-alkyl optionally substituted by halo, hydroxy, carboxy, sulpho or cyano. Examples include methyl, ethyl, n-propyl, iso-propyl, trifluoromethyl, hydroxyethyl, cyanoethyl, sulphopropyl and carboxyethyl. However, when Y or Z is optionally substituted alkyl it is especially preferred that the alkyl group is methyl, ethyl or trifluoromethyl.

[0024] When Y or Z is optionally substituted alkenyl, Y or Z is preferably optionally substituted C2-C4 alkenyl.

[0025] When Y or Z is optionally substituted alkynyl, Y or Z is preferably optionally substituted C2-C6 alkynyl.

[0026] When Y or Z is optionally substituted aryl the aryl group is preferably optionally substituted phenyl, optionally substituted naphthyl or optionally substituted heteroaryl. It is especially preferred that when Y is optionally substituted aryl it is optionally substituted phenyl or optionally substituted heteroaryl.

[0027] Preferred optional substituents on Y when Y is optionally substituted aryl include sulpho, carboxy, nitro, cyano, halo (preferably chloro), alkoxy (preferably C1-6-alkoxy), alkyl ((preferably C1-6-alkyl) optionally substituted by halogen (preferably fluoro), hydroxy, carboxy, phosphoric acid and sulpho. Especially preferred optional substituents on Y when Y is optionally substituted aryl are selected from C1-4-alkyl, carboxy, phosphoric acid and sulpho. However, it is most preferred that when Y is optionally substituted aryl that the aryl group is substituted by carboxy.

[0028] Preferred optional substituents on Z when Z is optionally substituted aryl include sulpho, carboxy, nitro, cyano, halo (preferably chloro), alkoxy (preferably C1-6-alkoxy), alkyl (preferably C1-6-alkyl) optionally substituted by halogen (preferably fluoro), hydroxy, carboxy, phosphoric acid and sulpho. Especially preferred optional substituents on Z as optionally substituted aryl are selected from carboxy or halogen (preferably chloro).

[0029] When Y or Z is optionally substituted aralkyl the aralkyl group is preferably optionally substituted benzyl.

[0030] However, Y in Formulae (2a), (2b), (2c), (2d) or (2e) is preferably H, thiol, carboxy, halo (preferably chloro), alkyl ((preferably C1-6-alkyl) optionally substituted by hydroxy, carboxy, halo (preferably fluoro) or sulpho. It is especially preferred that Y in Formulae (2a) to (2e) is H, C1-4-alkyl or carboxy or sulpho. However, it is most especially preferred that Y is H or CO2H.

[0031] Z in Formulae (2a) to (2e) is preferably H, ethylester or alkyl (preferably C1-4-alkyl) optionally substituted by hydroxy, carboxy, halo (preferably fluoro) or sulpho. It is especially preferred that Z in Formulae (2a) to (2e) is H or C1-4-alkyl. However, it is most especially preferred that Z is H.

[0032] In one embodiment Z is H and Y is H or CO2H.

[0033] R1, R2 and R3 are each independently preferably H, optionally substituted C1-4-alkyl or optionally substituted aryl, more preferably H, C1-4-alkyl optionally substituted by hydroxy, carboxy, sulpho or cyano or phenyl optionally substituted by hydroxy, carboxy, sulpho, nitro, trifluoromethyl or cyano. Examples of groups represented by R1, R2 and R3 include methyl, ethyl, n-propyl, iso-propyl, hydroxyethyl, cyanoethyl, sulphopropyl, carboxyethyl or carboxyphenyl. It is especially preferred however that R1, R2 and R3 are H, optionally substituted C1-4-alkyl for example, trifluoromethyl, hydroxyethyl or cyanoethyl, or optionally substituted aryl for example phenyl optionally substituted by carboxy; or R2 and R3 together with the nitrogen to which they are attached form a 5- or 6-membered ring (preferably morpholine, piperidine or piperazine).

[0034] The optional substituent X is preferably —OH, —Br, —Cl, —F, —CF3, —CN, —NO2, —PO3H2, optionally substituted alkyl, optionally substituted alkenyl, optionally substituted alkynyl, optionally substituted aryl, optionally substituted aralkyl, —SR1, —SO2R1, —SOR1, —OR1, —C(O)R1, —C(O)OR5, or —NR3R4;

[0035] wherein:

[0036] R1, R3 and R4 are each independently H, optionally substituted alkyl, optionally substituted alkenyl, optionally substituted alkynyl, optionally substituted aryl or optionally substituted aralkyl; or

[0037] R3 and R4 together with the nitrogen to which they are attached form an optionally substituted 5- or 6-membered ring; and

[0038] R5 is any one of the groups defined for R1 other than H.

[0039] When X is optionally substituted alkyl it is preferably optionally substituted C1-4-alkyl, more preferably C1-4-alkyl optionally substituted by halogen, hydroxy, carboxy, sulpho or cyano. Examples include ethyl, n-propyl, iso-propyl, hydroxyethyl, cyanoethyl, sulpho, propyl and carboxyethyl. However, when X is optionally substituted C1-4-alkyl it is especially preferred that it is substituted by cyano or halogen (preferably fluoro).

[0040] When X is optionally substituted alkenyl, it is preferably optionally substituted C2-C4 alkenyl.

[0041] When X is optionally substituted alkynyl, it is preferably optionally substituted C2-C6 alkynyl.

[0042] When X is optionally substituted aryl it is preferably optionally substituted phenyl or optionally substituted naphthyl. It is especially preferred that when Y is optionally substituted aryl it is optionally substituted phenyl.

[0043] Preferred optional substituents on X when X is optionally substituted aryl include: sulpho, carboxy, halogen (preferably chloro) alkoxy (preferably C1-6-alkoxy) or alkyl (preferably C1-6-alkyl) optionally substituted by halogen, nitro, cyano, hydroxy, carboxy, phosphoric acid or sulpho.

[0044] When X is optionally substituted aralkyl it is preferably optionally substituted by benzyl.

[0045] It is especially preferred that X is an electron withdrawing group for example nitro, cyano or trifluoromethyl.

[0046] It is most especially preferred that X is CN.

[0047] The optionally substituted sulphonamido group J is preferably of the Formula SO2NR6R7, wherein R6 and R7 are each independently H, optionally substituted alkyl, optionally substituted alkenyl, optionally substituted alkynyl, optionally substituted aryl, optionally substituted aralkyl; or

[0048] R6 and R7 together with the nitrogen to which they are attached form an optionally substituted 5- or 6-membered ring.

[0049] When R6 or R7 is optionally substituted alkyl each is preferably optionally substituted C1-4-alkyl, more preferably C1-4-alkyl optionally substituted by halogen, hydroxy, carboxy, sulpho or cyano. Examples include ethyl, n-propyl, iso-propyl, hydroxyethyl, cyanoethyl, sulpho, propyl and carboxyethyl. However, when either of R10 and R11 is optionally substituted C1-4-alkyl it is especially preferred that each is substituted by cyano or halogen (preferably fluoro).

[0050] When R6 or R7 is optionally substituted alkenyl, each is preferably optionally substituted C2-C4 alkenyl.

[0051] When R6 or R7 is optionally substituted alkynyl, each is preferably optionally substituted C2-C6 alkynyl.

[0052] When R6 or R7 is optionally substituted aryl each is preferably optionally substituted phenyl or optionally substituted naphthyl. It is especially preferred that when R6 or R7 is optionally substituted aryl each is optionally substituted phenyl.

[0053] Preferred optional substituents on R6 or R7 when R6 or R7 is optionally substituted aryl include: sulpho, carboxy, nitro, cyano, halogen (preferably chloro), alkoxy (preferably C1-6-alkoxy) or alkyl (preferably C1-6-alkyl) optionally substituted by halogen, (preferably fluoro), hydroxy, carboxy, phosphoric acid or sulpho.

[0054] When R6 or R7 is optionally substituted aralkyl each is preferably optionally substituted by benzyl.

[0055] R6 and R7 are each most preferably independently H, or optionally substituted aryl, most preferably optionally substituted phenyl or optionally substituted naphthyl. Especially preferred optional substituents on R6 or R7 when R6 or R7 are optionally substituted aryl include C1-4-alkyl, carboxy, phosphoric acid or sulpho. However, it is most especially preferred that one of R6 and R7 is H and the other is optionally substituted aryl, preferably an aryl group carrying a carboxy group.

[0056] When W is a carbonamido group it is preferably of the formula —C(O)NR6R7 wherein R6 and R7 independently are as hereinbefore defined.

[0057] W is most preferably however a carboxylic acid group of the formula CO2H or salt thereof or a carbonamido group of the formula CONR6R7 wherein one of R6 and R7 is H and the other is optionally substituted aryl, preferably optionally substituted phenyl wherein the phenyl group carries one or more water-solubilising groups. Examples of such water-solubilising groups include phosphonic acid, carboxy and sulpho.

[0058] M preferably comprises boron or one or more of the following metals: nickel, chromium, cobalt, copper, zinc, iron or manganese. The metal is preferably able to co-ordinate to the portion of the compounds shown in square brackets in the ratio 1:1, 2:1, 2:2, 2:3 respectively. However, it is particularly preferred that M is nickel because this results in good chroma properties for the resultant compound. It is also preferred that M is able to co-ordinate to the portion in square brackets in the ratio 1:1 and 2:1.

[0059] First Preferred Embodiment

[0060] In a first preferred embodiment of the first aspect of present invention p is 1, 2, 3 or 4; a, q and n are each independently 0, 1, 2, 3 or 4; and (p+q+a+n) is 1, 2, 3 or 4.

[0061] Preferences specific to compounds of the first preferred embodiment of the first aspect of the present invention:

[0062] It is preferred that p is 1, 2 or 3, more preferably 1 or 2.

[0063] It is preferred that n is 0, 1 or 2, more preferably 1 or 2.

[0064] It is preferred that q is 0, 1 or 2, more preferably 0 or 1.

[0065] It is preferred that a is 0, 1 or 2, more preferably 0 or 1, especially 0.

[0066] Preferably the compounds of the first preferred embodiment of the first aspect of present invention comprise one or more water-solubilising groups, for example, sulpho, carboxy or phosphoric acid groups, more preferably at least one sulpho group.

[0067] Preferably (p+q+a+n) is 1, 2, 3 or 4, more preferably 2 or 3.

[0068] Second Preferred Embodiment

[0069] In a second preferred embodiment of the first aspect of the present invention the compound of Formula (1) is a metal chelate compound of Formula (1a) or a salt thereof:

[0070] wherein:

[0071] n and a are each independently 0, 1, 2, 3 or 4;

[0072] q is 1, 2, 3 or 4;

[0073] (a+q+n) is 1, 2, 3 or 4; and

[0074] A, B, X, J and M are as hereinbefore defined.

[0075] Preferences specific to compounds of the second preferred embodiment of the first aspect of the present invention:

[0076] It is preferable that n is 0, 1 or 2, more preferably 1 or 2 and especially 1.

[0077] It is preferred that a is 0, 1, 2 or 3, more preferably 0, 1 or 2, especially 0 or 1, more especially 0.

[0078] It is preferred that q is 1 of 2.

[0079] Preferably the value of (a+q+n) is 2 or 3.

[0080] Preferably the compound of Formula (1a) comprises one or more water-solubilising groups, for example such as sulpho, carboxy or phosphoric acid groups.

[0081] It is especially preferred that the compound of Formula (1a) is a metal chelate compound of the Formula (1a-1) or (1a-2):

[0082] wherein:

[0083] D is an azotriazole group, preferably of the Formula (2a), (2b), (2c), (2d) or (2e) as hereinbefore defined;

[0084] q is 1 or 2;

[0085] n is 1 or 2;

[0086] a is 0 or 1;

[0087] M is a metal, preferably nickel; and

[0088] J and X are as hereinbefore defined.

[0089] Preferably (a+q+n) is 2 or 3.

[0090] When the metal chelate compound is of Formula (1a-1), it is preferred that there is one sulphonamido group at the 4-position on the naphthylene ring and one sulphonamido group at the 8-position on the naphthylene ring, relative to D being at the 2-position on the naphthylene ring.

[0091] When the metal chelate compound is of Formula (1a-2), it is preferred that there is at least one sulphonamido group at the 3-position on the naphthylene ring or one sulphonamido group at the 6-position on the naphthylene ring, relative to D being at the 1-position on the naphthylene ring.

[0092] In view of the foregoing preferences the compound of Formula (1a) is preferably a metal chelate compound of the Formula (1a-3) or (1a-4) or a salt thereof:

[0093] wherein:

[0094] D, M and J are as hereinbefore defined.

[0095] In Formula (1a-3) and (1a-4) D is preferably of Formulae (2a), (2b), (2c), (2d) or (2e) as hereinbefore defined.

[0096] It is especially preferred that for the compound of Formula (1a-3) and (1a-4) J is SO2NR6R7 wherein one of R6 or R7 is H and the other is optionally substituted aryl, more especially an aryl group carrying a carboxy group. However, it is most preferred that one of R6 or R7 is H and the other is a carboxy phenyl group.

[0097] Third Preferred Embodiment

[0098] In a third preferred embodiment of the first aspect of present invention the compound of Formula (1) is a metal chelate compound of Formula (1b) or a salt thereof:

[0099] wherein:

[0100] a is 1, 2, 3 or 4;

[0101] n is 0, 1, 2, 3 or 4;

[0102] (a+n) is 1, 2, 3 or 4; and

[0103] A, B, X and M are as hereinbefore defined.

[0104] Preferences specific to compounds of Formula (1b) are as follows:

[0105] It is preferred that n is 0, 1 or 2, more preferably 1 or 2.

[0106] It is preferred that a is 1, 2 or 3 more preferably 1 or 2 and especially 1.

[0107] Preferably the value of (a+n) is 2, 3 or 4, more preferably 2 or 3, especially 3. Preferably the compounds of Formula (1b) comprise one or more water solubilising groups, for example a sulpho, carboxy or phosphoric acid group. More preferably the compound of Formula (1b) carries two sulpho groups.

[0108] It is especially preferred that the compound of Formula (1b) is a metal chelate compound of the Formula (1b-1) or (1b-2):

[0109] wherein:

[0110] D is an azotriazole group, preferably of Formula (2a), (2b), (2c), (2d) or (2e) as hereinbefore defined;

[0111] X is —OH, —Br, —Cl, —F, —CF3, —CN, —NO2, —PO3H2, optionally substituted alkyl, optionally substituted alkenyl, optionally substituted alkynyl, optionally substituted aryl, optionally substituted aralkyl, —SR1, —SO2R1, —SOR1, —OR1, —C(O)R1, —C(O)OR5, or —NR3R4;

[0112] wherein:

[0113] R1, R3 and R4 are each independently H, optionally substituted alkyl, optionally substituted alkenyl, optionally substituted alkynyl, optionally substituted aryl or optionally substituted aralkyl; or

[0114] R3 and R4 together with the nitrogen to which they are attached form an optionally substituted 5 or 6 membered ring; and

[0115] R5 is any one of the groups defined for R1 other than H.

[0116] M is a metal, preferably nickel;

[0117] a is 1 or 2; preferably 1; and

[0118] n is 1 or 2.

[0119] Fourth Preferred Embodiment

[0120] In a fourth preferred embodiment of the first aspect of the present invention the compound of Formula (1) is a metal chelate compound of Formula (1c) or a salt thereof:

[0121] wherein:

[0122] n is 0 to 4; and

[0123] A, B and M are as hereinbefore defined.

[0124] Preferences specific to compounds of Formula (1c) are as follows:

[0125] It is preferable that n is 0, 1, 2 or 3 more preferably 1, 2 or 3, especially 1 or 2.

[0126] It is especially preferred that the compound of Formula (1c) is a metal chelate compound of the Formula (1c-1) or (1c-2):

[0127] wherein D is an azotriazole group, preferably of Formula (2a), (2b), (2c), (2d) or (2e) as hereinbefore defined; n is 1 or 2; and M is nickel.

[0128] When the metal chelate compound is of Formula (1c-1), it is preferred that there is one sulphonic acid group at the 4-position on the naphthylene and one sulphonic acid group at the 8-position on the naphthylene ring, relative to D being at the 2-position on the naphthylene ring.

[0129] When the metal chelate compound is of Formula (1c-2), it is preferred that there is one sulphonic acid group at the 3-position on the naphthylene ring and one sulphonic acid group at the 7-position on the naphthylene ring, relative to D being at the 1-position.

[0130] In view of the foregoing preferences the compound of Formula (1c) is preferably a metal chelate compound of the Formula (1c-3) or (1c-4) or a salt thereof:

[0131] wherein:

[0132] D is a group of Formula (2a), (2b), (2c), (2d) or (2e) as hereinbefore defined and preferred, M is a metal, more preferably nickel.

[0133] When D is a group of Formula (2a), (2b), (2c), (2d) or (2e), Y is preferably H or CO2H and Z is preferably H.

[0134] The compounds of the second, third and fourth embodiments are preferred over the compounds of the first preferred embodiment due to their superior combination of good chroma, light-fastness and fastness to oxidising gasses. These compounds are particularly preferred when M is nickel.

[0135] It is especially preferred that the compounds of the present invention are magenta in colour. Preferably the compounds of the invention have a chroma of at least 50 when printed on plain paper.

[0136] The compounds of the first aspect of the present invention provide prints which exhibit a high light-fastness and good optical density when incorporated into inks for ink jet printing. The compounds of the first aspect of the present invention are also highly soluble which improves operability and reduces crusting and nozzle blockage when inks containing the compounds are used in an ink jet printer.

[0137] Compounds of the first aspect of the present invention are preferably free from fibre reactive groups. The term fibre reactive group is well known in the art and is described for example in EP 0356014 A1. Fibre reactive groups are capable, under suitable conditions, of reacting with the hydroxyl groups present in cellulosic fibres or with the amino groups present in natural fibres to form a covalent linkage between the fibre and the dye. As examples of fibre reactive groups preferably not present in the compounds of the first aspect of the present invention there may be mentioned aliphatic sulphonyl groups which contain a sulphate ester group in the beta-position to the sulphur atom, e.g. beta-sulphato-ethylsulphonyl groups, alpha, beta-unsaturated acyl radicals of aliphatic carboxylic acids, for example acrylic acid, alpha-chloro-acrylic acid, alpha-bromoacrylic acid, propiolic acid, maleic acid and mono- and dichloro maleic; also the acyl radicals of acids which contain a substituent which reacts with cellulose in the presence of an alkali, e.g. the radical of a halogenated aliphatic acid such as chloroacetic acid, beta-chloro and beta-bromopropionic acids and alpha, beta-dichloro- and dibromopropionic acids or radicals of vinylsulphonyl- or beta-chloroethylsulphonyl- or beta-sulphatoethyl-sulphonyl-endo-methylene cyclohexane carboxylic acids. Other examples of cellulose reactive groups are tetrafluorocyclobutyl carbonyl, trifluoro-cyclobutenyl carbonyl, tetrafluorocyclobutylethenyl carbonyl, trifluoro-cyclobutenylethenyl carbonyl; activated halogenated 1,3-dicyanobenzene radicals; and heterocyclic radicals which contain 1, 2 or 3 nitrogen atoms in the heterocyclic ring and at least one cellulose reactive substituent on a carbon atom of the ring.

[0138] The compounds of the first aspect of the present invention may be in the free acid or salt form. Preferred salts are water-soluble, for example alkali metal salts, especially lithium, sodium, potassium, ammonium, substituted ammonium and mixed salts thereof. Preferred alkali metal salts are those with sodium or lithium ammonium and substituted alkyl ammonium salts.

[0139] Preferred ammonium and substituted ammonium salts have cations of the formula +NV4 wherein each V independently is H or optionally substituted alkyl, or two groups represented by V are H or optionally substituted alkyl and the remaining two groups represented by V, together with the N atom to which they are attached, form a 5- or 6-membered ring (preferably a morpholinyl, pyridinyl or piperidinyl ring).

[0140] Preferably each V independently is H or C1-4-alkyl, more preferably H, CH3 or CH3CH2, especially H.

[0141] Examples of cations include +NH4, morpholinium, piperidinium, pyridinium, (CH3)3N+H, (CH3)2N+H2, H2N+(CH3)(CH2CH3), CH3N+H3, CH3CH2N+H3, H2N+(CH2CH3)2, CH3CH2CH2N+H3, (CH3)2CHN+H3, N+(CH3)4, N+(CH2CH3)4, N-methyl pyridinium, N,N-dimethyl piperidinium and N,N-dimethyl morpholinium.

[0142] It is especially preferred that the compound is in the form of a sodium, lithium, potassium, ammonium, or substituted ammonium salt because we have found that these salts provide prints which exhibit a high light-fastness when incorporated into an ink jet printing ink.

[0143] Preferably the metal chelate compound is not a copper or nickel chelate of any of Ligands a to e or any salt thereof:

[0144] Preferably the metal chelate compound is not a chrome chelate of Ligand f or any salt thereof:

[0145] Preferably the metal chelate compound is not a cobalt chelate of Ligands g or h or any salt thereof:

[0146] Preferably the metal chelate compound is not a chrome chelate of Ligand i or j or any salt thereof:

[0147] Preferably the metal chelate compound is not a metal chelate of Ligand k, l or m or any salt thereof:

[0148] Preferably the metal chelate compound is not a metal chelate of any of the above Ligands f to m inclusive, more preferably a to m inclusive, or any salt thereof.

[0149] The compounds of the first aspect of the present invention may be prepared using conventional techniques for the preparation of metal chelate compounds. For example a suitable method comprises adding together a solution of a metal salt to a solution of a compound of Formula (3):

[0150] wherein;

[0151] A, B, J, X, W, n, a, p and q are as hereinbefore defined in relation to Formula (1).

[0152] The product of the above process may be converted to a salt by conventional techniques as hereinbefore described. Alternatively the product may be isolated in its free acid form by acidifying the reaction mixture, preferably using a mineral acid, for example hydrochloric acid and when the product precipitates as a solid it may be separated from the mixture by filtration. Unwanted anions may be and preferably are removed from the product of the process by dialysis, osmosis, ultrafiltration or a combination thereof. Alternatively, the product solution is subjected to the above purification directly without isolation of the product.

[0153] The compounds of Formula (3) may be prepared, for example, by by diazotising a compound of the formula A1—NH2 to give a diazonium salt and coupling the resultant diazonium salt with a compound of the Formula (3a):

[0154] wherein A1 is a triazole group, one of L1 or B is OH and the other is H, and J, X, W, n, p and q are as hereinbefore defined.

[0155] The diazotisation is preferably performed at a temperature below 6° C., more preferably at a temperature in the range −10° C. to 5° C. Preferably the diazotisation is performed in water, preferably at a pH below 7. Dilute mineral acid, e.g. HCl or H2SO4, are often used to achieve the desired acidic conditions.

[0156] The present invention also covers mixtures comprising two or more compounds of the first aspect of the present invention or salts thereof. Furthermore, the compounds of the first aspect of the present invention may be mixed with commercially available dyes, especially those listed in the International Colour Index to adjust the shade or other properties as desired.

[0157] According to a second aspect of the present invention there is provided a composition comprising:

[0158] (a) one or more compound according to the first aspect of the present invention; and

[0159] (b) one or more water-soluble dye other than a compound according to the first aspect of the invention.

[0160] The water-soluble dye is preferably a water-soluble magenta dye, for example, a xanthene dye, an azo or bis azo dye, more preferably an anionic azo or bis azo dye and especially an azo or bis azo dye which contains one or more groups selected from sulphonate, carboxylate and thiocarboxylate groups.

[0161] Preferred water-soluble magenta dyes include C.I. Acid Red 50, 52, 87, 91, 92, 95, 249 and 289; C.I. Direct Violet 106 and 107; compounds 100 to 107, 200 and 201 described on pages 8 and 9 of WO96/24636; compounds 1 to 24 shown described on columns 4 to 10 in U.S. Pat. No. 5,542,970; compounds 1 to 55 described on pages 7 to 17 of EP-A-682 088; compounds 1 to 14 shown in Example 1 to 6 of EP-A-194,885; compounds 1 to 24 described on pages 8 to 13 of EP-A-717 089; the compounds described in examples 1 to 16 in columns 5 to 11 of U.S. Pat. No. 5,262,527; and the dyes described in Examples 1 to 21 in WO 94/16021.

[0162] Especially preferred water-soluble magenta dyes for use in the composition according to the second aspect of the invention include C.I. Acid Red 52, C.I. Acid Red 289 or a dye of the Formula (4), (5) and (6) and salts thereof:

[0163] The dye of Formula (4) may be prepared using the method described in Example 1 of EP 0 559 310. The dye of the Formula (5) may be prepared using the method described in Example 3 of PCT publication number WO 94/16021. The dye of Formula (6) may be prepared using the method described in Example 1 of WO 96/24636.

[0164] The composition according to the second aspect of the present invention preferably comprises:

[0165] (a) from 1 to 99, more preferably from 3 to 70 and especially from 5 to 50 parts in total of the compound(s) according to the first aspect of the invention; and

[0166] (b) from 99 to 1, more preferably from 30 to 97 parts and especially 95 to 50 parts in total of the water-soluble magenta dye(s);

[0167] wherein the parts are by weight and the sum of the parts (a)+(b)=100.

[0168] The composition may contain a single dye according to the first aspect of the present invention or a mixture thereof. Similarly, the composition may contain a single water-soluble magenta dye or a mixture of two or more water-soluble magenta dyes.

[0169] The compounds and compositions according to the first and second aspects of the present invention may be, and preferably are, purified to remove undesirable impurities before they are incorporated into inks for ink jet printing. Conventional techniques may be employed for purification, for example ultrafiltration, reverse osmosis and/or dialysis.

[0170] According to a third aspect of the present invention there is provided an ink comprising:

[0171] (a) a compound according to the first aspect of the present invention, or a composition according to the second aspect of the invention; and

[0172] (b) a liquid medium.

[0173] Preferably component (a) of the ink is or comprises one of the preferred compounds or compositions as hereinbefore described in relation to the first or second aspect of the invention.

[0174] The liquid medium preferably comprises:

[0175] (i) water;

[0176] (ii) a mixture of water and an organic solvent; or

[0177] (iii) an organic solvent free from water.

[0178] The number of parts by weight of component (a) of the ink is preferably from 0.01 to 30, more preferably 0.1 to 20, especially from 0.5 to 15, and more especially from 1 to 5 parts. The number of parts by weight of component (b) is preferably from 99.99 to 70, more preferably from 99.9 to 80, especially from 99.5 to 85, and more especially from 99 to 95 parts. The number of parts (a)+(b) is 100 and all parts mentioned herein are by weight.

[0179] Preferably component (a) is completely dissolved in component (b). Preferably component (a) has a solubility in component (b) at 20° C. of at least 10%. This allows the preparation of concentrates which may be used to prepare more dilute inks and reduces the chance of the compound(s) of component (a) of the ink precipitating if evaporation of the liquid medium occurs during storage.

[0180] When the liquid medium comprises a mixture of water and an organic solvent, the weight ratio of water to organic solvent is preferably from 99:1 to 1:99, more preferably from 99:1 to 50:50 and especially from 95:5 to 80:20.

[0181] It is preferred that the organic solvent present in the mixture of water and organic solvent is a water-miscible organic solvent or a mixture of such solvents. Preferred water-miscible organic solvents include C1-6-alkanols, preferably methanol, ethanol, n-propanol, isopropanol, n-butanol, sec-butanol, tert-butanol, n-pentanol, cyclopentanol and cyclohexanol; linear amides, preferably dimethylformamide or dimethylacetamide; ketones and ketone-alcohols, preferably acetone, methyl ether ketone, cyclohexanone and diacetone alcohol; water-miscible ethers, preferably tetrahydrofuran and dioxane; diols, preferably diols having from 2 to 12 carbon atoms, for example pentane-1,5-diol, ethylene glycol, propylene glycol, butylene glycol, pentylene glycol, hexylene glycol and thiodiglycol and oligo- and poly-alkyleneglycols, preferably diethylene glycol, triethylene glycol, polyethylene glycol and polypropylene glycol; triols, preferably glycerol and 1,2,6-hexanetriol; mono-C1-4-alkyl ethers of diols, preferably mono-C1-4-alkyl ethers of diols having 2 to 12 carbon atoms, especially 2-methoxyethanol, 2-(2-methoxyethoxy)ethanol, 2-(2-ethoxyethoxy)-ethanol, 2-[2-(2-methoxyethoxy)ethoxy]ethanol, 2-[2-(2-ethoxyethoxy) ethoxy]-ethanol and ethyleneglycol monoallylether; cyclic amides, preferably 2-pyrrolidone, N-methyl-2-pyrrolidone, N-ethyl-2-pyrrolidone, caprolactam and 1,3-dimethylimidazolidone; cyclic esters, preferably caprolactone; sulphoxides, preferably dimethyl sulphoxide and sulpholane. Preferably the liquid medium comprises water and 2 or more, especially from 2 to 8, water-miscible organic solvents.

[0182] Especially preferred water-soluble organic solvents are cyclic amides, especially 2-pyrrolidone, N-methyl-pyrrolidone and N-ethyl-pyrrolidone; diols, especially 1,5-pentane diol, ethyleneglycol, thiodiglycol, diethyleneglycol and triethyleneglycol; and mono-C1-4-alkyl and C1-4-alkyl ethers of diols, more preferably mono-C1-4-alkyl ethers of diols having 2 to 12 carbon atoms, especially 2-methoxy-2-ethoxy-2-ethoxyethanol.

[0183] A preferred liquid medium comprises:

[0184] (a) from 75 to 95 parts water; and

[0185] (b) from 25 to 5 parts in total of one or more solvents selected from diethylene glycol, 2-pyrrolidone, thiodiglycol, N-methylpyrrolidone, cyclohexanol, caprolactone, caprolactam and pentane-1,5-diol;

[0186] wherein the parts are by weight and the sum of the parts (a) and (b)=100.

[0187] Another preferred liquid medium comprises:

[0188] (a) from 60 to 80 parts water;

[0189] (b) from 2 to 20 parts diethylene glycol; and

[0190] (c) from 0.5 to 20 parts in total of one or more solvents selected from 2-pyrrolidone, N-methylpyrrolidone, cyclohexanol, caprolactone, caprolactam, pentane-1,5-diol and thiodiglycol;

[0191] wherein the parts are by weight and the sum of the parts (a), (b) and (c)=100.

[0192] Examples of further suitable ink media comprising a mixture of water and one or more organic solvents are described in U.S. Pat. No. 4,963,189, U.S. Pat. No. 4,703,113, U.S. Pat. No. 4,626,284 and EP 4,251,50A.

[0193] When the liquid medium comprises an organic solvent free from water, (i.e. less than 1% water by weight) the solvent preferably has a boiling point of from 30° to 200° C., more preferably of from 40° to 150° C., especially from 50 to 125° C. The organic solvent may be water-immiscible, water-miscible or a mixture of such solvents. Preferred water-miscible organic solvents are any of the hereinbefore described water-miscible organic solvents and mixtures thereof. Preferred water-immiscible solvents include, for example, aliphatic hydrocarbons; esters, preferably ethyl acetate; chlorinated hydrocarbons, preferably CH2Cl2; and ethers, preferably diethyl ether; and mixtures thereof.

[0194] When the liquid medium comprises a water-immiscible organic solvent, preferably a polar solvent is included because this enhances solubility of the dye in the liquid medium. Examples of polar solvents include C1-4-alcohols. In view of the foregoing preferences it is especially preferred that where the liquid medium is an organic solvent free from water it comprises a ketone (especially methyl ethyl ketone) and/or an alcohol (especially a C1-4-alkanol, such as ethanol or propanol).

[0195] The organic solvent free from water may be a single organic solvent or a mixture of two or more organic solvents. It is preferred that when the medium is an organic solvent free from water it is a mixture of 2 to 5 different organic solvents. This allows a medium to be selected which gives good control over the drying characteristics and storage stability of the ink.

[0196] Ink media comprising an organic solvent free from water are particularly useful where fast drying times are required and particularly when printing onto hydrophobic and non-absorbent substrates, for example plastics, metal and glass.

[0197] An especially preferred ink comprises:

[0198] (a) from 1 to 10 parts in total of a compound or composition according to the first or second aspect of the invention;

[0199] (b) from 2 to 60, more preferably 5 to 40 parts of water-soluble organic solvent; and

[0200] (c) from 30 to 97, more preferably 40 to 85 parts water;

[0201] wherein all parts are by weight and the sum of the parts (a)+(b)+(c)=100.

[0202] When the liquid medium in the ink comprises a mixture of water and an organic solvent; or an organic solvent free from water, component (a) of the ink may comprise a compound as hereinbefore defined in relation to the first aspect of the invention.

[0203] Preferred low melting solid media have a melting point in the range from 60° C. to 125° C. Suitable low melting point solids include long chain fatty acids or alcohols, preferably those with C18-24 chains, and sulphonamides. The compound of the first aspect of the present invention may be dissolved in the low melting point solid or may be finely dispersed in it.

[0204] The inks according to the present invention may also contain additional components conventionally used in ink jet printing inks, for example viscosity and surface tension modifiers, corrosion inhibitors, biocides, kogation reducing additives, anti-cockle agents to reduce paper curling and surfactants which may be ionic or non-ionic.

[0205] The pH of the ink is preferably from 4 to 11, more preferably from 7 to 10.

[0206] The viscosity of the ink at 25° C. is preferably less than 50 cP, more preferably less than 20 cP and especially less than 5 cP.

[0207] When the inks according to the invention are used as ink jet printing inks, the ink preferably has a concentration of less than 500 parts per million, more preferably less than 100 parts per million of halide ions. It is especially preferred that the ink has less than 100, more preferably less than 50 parts per million of divalent and trivalent metals, wherein parts refer to parts by weight relative to the total weight of the ink. We have found that purifying the inks to reduce the concentration of these undesirable ions reduces nozzle blockage in ink jet printing heads, particularly in thermal ink jet printers.

[0208] A fourth aspect of the present invention provides a process for printing an image on a substrate comprising applying thereto by means of an ink jet printer an ink containing a compound according to the first aspect of the invention or a composition according to the second aspect of the invention.

[0209] The ink used in this process is preferably as defined in the third aspect of the present invention.

[0210] The ink jet printer preferably applies the ink to the substrate in the form of droplets which are ejected through a small orifice onto the substrate. Preferred ink jet printers are piezoelectric ink jet printers and thermal ink jet printers. In thermal ink jet printers, programmed pulses of heat are applied to the ink in a reservoir by means of a resistor adjacent to the orifice, thereby causing the ink to be ejected in the form of small droplets directed towards the substrate during relative movement between the substrate and the orifice. In piezoelectric ink jet printers the oscillation of a small crystal causes ejection of the ink from the orifice.

[0211] The substrate is preferably paper, plastic, a textile, metal or glass, more preferably paper, an overhead projector slide or a textile material, especially paper.

[0212] Preferred papers are plain or treated papers which may have an acid, alkaline or neutral character. Examples of commercially available papers include, HP Premium Coated Paper, HP Photopaper (all available from Hewlett Packard Inc.), Stylus Pro 720 dpi Coated Paper, Epson Photo Quality Glossy Film, Epson Photo Quality Glossy Paper (available from Seiko Epson Corp.), Canon HR 101 High Resolution Paper, Canon GP 201 Glossy Paper, Canon HG 101 High Gloss Film (all available from Canon Inc.), Wiggins Conqueror paper (available from Wiggins Teape Ltd), Xerox Acid Paper and Xerox Alkaline paper, Xerox Acid Paper (available from Xerox).

[0213] A fifth aspect of the present invention provides a substrate, preferably a paper, an overhead projector slide or a textile material, printed with an ink according to the third aspect of the present invention or by means of the process according to the fourth aspect of the present invention.

[0214] According to a sixth aspect of the present invention there is provided an ink jet printer cartridge comprising a chamber and ink, wherein the ink is present in the chamber and the ink contains a compound or a composition according to the first or second aspect of the present invention. Preferably the ink is an ink according to the third aspect of the present invention.

[0215] According to a seventh aspect of the present invention there is provided an ink jet printer containing an ink jet printer cartridge, wherein the ink jet printer cartridge is as defined in the sixth aspect of the present invention.

[0216] The invention is further illustrated by the following Examples in which all parts and percentages are by weight unless otherwise stated.

EXAMPLE 1

Preparation of Compound (1) wherein M Is Nickel

[0217]

[0218] Stage (a):

[0219] 3-amino-1,2,4-triazole-5-carboxylic acid hydrate (1.28 g, 0.01 mol) was suspended in water (50 ml) and dissolved by the addition of 2M NaOH to pH 8. Sodium nitrite (0.76 g, 0.011 mol) was added and the solution stirred until the sodium nitrite had dissolved. The mixture was then added dropwise to a cooled mix of ice-water (30 g) and concentrated HCl (3.0 ml) at 0-5° C., the mixture was stirred for 30 minutes at 0-5° C. and then excess nitrous acid was removed by adding sulphamic acid. The diazo suspension was added slowly to a solution of 3-hydroxy-naphthalene-2-carboxylic acid (1.88 g, 0.01 mol) in water (100 ml) at pH 7-8 (2N NaOH) cooled below 5° C. The reaction mixture was then stirred at 0-5° C. for one hour, the product was precipitated by acidification to pH 4 with 2N HCl and collected by filtration. The product was washed with water and then dried in a vacuum desiccator to give 2.8 g of an orange solid.

[0220] Stage (b):

[0221] A solution of nickel acetate tetrahydrate (1.43 g, 0.0057 mol) in water (10 ml) was added dropwise to the product from stage (a) (2.5 g, 0.0076 mol) dissolved in water (100 ml) at pH 7 (2N NaOH). The reaction mixture was stirred for 2 hours at ambient temperature, dialysed using SpectraPor membrane tubing (molecular weight cut off 3500) to low conductivity (<100 μs). Compound (1) was obtained by evaporation under reduced pressure to afford a dark crystalline solid (3.5 g).

EXAMPLES 2 TO 11

[0222] Compounds (2) to (11) described in Table 1 were prepared using an analogous process to that described in Example 1 except that in stage (a) the Naphthol (N) shown in Table 1 was used in place of 3-hydroxy-naphthalene-2-carboxylic acid.

1TABLE 1ExampleNaphthol (N)Compound name2

Nickel chelate of [5-[2-hydroxy-3-(3-sulfo- phenylcarbamoyl)-naphthalen-1-ylazo]-2H- [1,2,4]triazole-3-carboxylic acid]. (“Compound (2)”). Analysis by mass spectrometry found m/z 537 (M − H)−.3

Nickel chelate of [5-(3-carboxy-2-hydroxy- 6,8-disulfonaphthalen-1-ylazo]-2H- [1,2,4]triazole-3-carboxylic acid]. (“Compound (3)”).4

Nickel chelate of [5-(3-carboxy-2-hydroxy- 6-sulfonaphthalen-1-ylazo]-2H- [1,2,4]triazole-3-carboxylic acid]. (“Compound (4)”).5

Nickel chelate of [5-(6-carboxy-2-hydroxy- 3-sulfonaphthalen-1-ylazo]-2H- [1,2,4]triazole-3-carboxylic acid]. (“Compound (5)”). Analysis by mass spectrometry found m/z 869 (M − H)−.6

Nickel chelate of [5-(8-acetylamino-1- hydroxy-3,5-disulfo-naphthalen-2-ylazo)- 2H-[1,2,4]triazole-3-carboxylic acid]. (“Compound (6)”) Analysis by mass spectrometry found m/z 555 (M − H)−.7

Nickel chelate of [5-(8-acetylamino-1- hydroxy-3,6-disulfo-naphthalen-2-ylazo)- 2H-[1,2,4]triazole-3-carboxylic acid]. (“Compound (7)”) Analysis by mass spectrometry found m/z 555 (M − H)−.8

Nickel chelate of [5-(4-acetylamino-1- hydroxy-8-sulfo-naphthalen-2-ylazo)-2H- [1,2,4]triazole-3-carboxylic acid]. (“Compound (8)”) Analysis by mass spectrometry found m/z 895 (M − H)−.9

Nickel chelate of [5-[6-(acetyl-methyl- amino)-1-hydroxy-3-sulfo-naphthalen-2- ylazo]-2H-[1,2,4]triazole-3-carboxylic acid]. (“Compound (9)”)10

Nickel chelate of [5-(6-acetylamino-1- hydroxy-3-sulfo-naphthalen-2-ylazo)-2H- [1,2,4]triazole-3-carboxylic acid]. (“Compound (10)”) Analysis by mass spectrometry found m/z 475 (M − H)−.11

Nickel chelate of [5-(7-acetylamino-1- hydroxy-3-sulfo-naphthalen-2-ylazo)-2H- [1,2,4]triazole-3-carboxylic acid]. (“Compound (11)”)

EXAMPLE 12

Preparation of Compound (12) wherein M Is Nickel

[0223]

[0224] Stage (a):

[0225] 3-amino-1,2,4-triazole-5-carboxylic acid hydrate (3.84 g, 0.03 mol) was suspended in water (180 ml) and dissolved by the addition of 2M NaOH to pH 8. Sodium nitrite (2.27 g, 0.033 mol) was added and the solution stirred until the sodium nitrite had dissolved.

[0226] The mixture was then added dropwise to a cooled mix of ice-water (150 g) and concentrated HCl (10 ml) at 0-5° C., the mixture was stirred for 30 minutes at 0-5° C. and then excess nitrous acid was removed by adding sulphamic acid. The diazo suspension was added slowly to a suspension of 2,7-dihydroxynaphthalene-3,6-disulfonic acid disodium salt (10.9 g, 0.03 mol) in water (450 ml) at pH 7-8 (2N NaOH) cooled below 5° C. The reaction mixture was then stirred at 0-5° C. for one further hour, the product was precipitated by acidification to pH 4 with 2N HCl and collected by filtration. The product was washed with 15% brine and then dried in a vacuum desiccator to give 11.4 g of an orange solid (85% yield).

[0227] Stage (b):

[0228] A solution of nickel acetate tetrahydrate (2.30 g, 0.0093 mol) in water (20 ml) was added dropwise to the product from stage (a) (5.0 g, 0.0093 mol) dissolved in water (100 ml) at pH 7-8 (2N NaOH). The reaction mixture was stirred for 2 hours at 50-60° C., dialysed using SpectraPor membrane tubing (molecular weight cut off 3500) to low conductivity (<100 μs). Compound (12) was obtained by evaporation as a dark crystalline solid (4.2 g).

EXAMPLE 13

Preparation of Compound (13) wherein M Is Nickel

[0229]

[0230] Compound (13) was prepared using an analogous process to that described in Example 12 except that in stage (a) 3-hydroxy-7-nitro-naphthalene-1-sulfonic acid was used in place of 2,7-dihydroxynaphthalene-3,6-disulfonic acid.

EXAMPLES 14 AND 15

[0231] Compounds (14) and (15) of the Formula (A) described in Table 2 were prepared using an analogous process to that described in Example 12 except that in stage (a) in place of 2,7-dihydroxynaphthalene-3,6-disulfonic acid was used the Naphthol (N) shown in Table 2 and the coupling reaction was performed at pH 10-10.5. M is nickel and X is ethoxy and hydroxy respectively.

2TABLE 2

Formula (A)CompoundNaphthol (N)Dye name(14)

Nickel chelate of [5-(8-ethoxy-1-hydroxy-3,6- disulfo-naphthalen-2-ylazo)-2H- [1,2,4]triazole-3-carboxylic acid]. Analysis by mass spectrometry found m/z 1085 (M − H)−.(15)

Nickel chelate of [5-(1,8-dihydroxy-3,6- disulfo-naphthalen-2-ylazo)-2H- [1,2,4]triazole-3-carboxylic acid].

EXAMPLE 16

reparation of Compound (16) wherein M Is Nickel

[0232]

[0233] Stage (a): Preparation of 2-acetoxynaphthalene-3,6-disulphonic acid

[0234] Acetic anhydride (350 ml, 3.8 mol) was added dropwise to a suspension of 2-hydroxynaphthalene-3,6-disulphonic acid di sodium salt (87 g, 0.25 mol) in N,N-dimethylacetamide (350 ml). The reaction mixture was stirred at 125° C. for 24 hours, cooled to room temperature and added to acetone (2500 ml). The product was filtered off, washed with acetone (3×100 ml) and dried to give 95.2 g of a cream coloured solid.

[0235] Stage (b): Preparation of 3,6-bis-(4-carboxy-phenylsulfamoyl)-2-hydroxy-naphthalene

[0236] POCl3 (50 ml, 0.538 mol) was added dropwise to a suspension of the product from stage (a) (50 g, 0.128 mol) in acetonitrile (250 ml) at reflux. The reaction mixture was stirred for 3 hours at 70° C., cooled, added to ice/water (4000 ml) and the naphthalene disulfonyl chloride extracted with dichloromethane (4×300 ml). The combined extracts were dried with MgSO4, evaporated under reduced pressure and the residue dissolved in N,N-dimethylacetamide (400 ml). 4-Aminobenzoic acid (34.3 g, 0.25 mol) was added to the above solution, the reaction mixture was stirred overnight at room temperature and then added to water (3000 ml). The pH was then lowered to 0.5 with concentrated H2SO4 and the precipitated product extracted from ethyl acetate (4×300 ml). The combined extracts were washed with 1N HCl (600 ml), dried with MgSO4 and evaporated under reduced pressure. The residue was dissolved in water (1000 ml) at pH 12 (2N NaOH) and then stirred for 1 hour at 50-60° C. The solution was allowed to cool, the pH lowered to pH 4 with concentrated HCl and the product filtered off and dried to give 41.5 g (53% yield) of a tan coloured solid.

[0237] Stage (c):

[0238] 3-amino-1,2,4-triazole-5-carboxylic acid hydrate (1.28 g, 0.01 mol) was suspended in water (50 ml) and dissolved by the addition of 2M NaOH to pH 8. Sodium nitrite (0.76 g, 0.011 mol) was added and the solution stirred until the sodium nitrite had dissolved. The mixture was then added dropwise to a cooled mix of ice-water (30 g) and concentrated HCl (3.0 ml) at 0-5° C., the mixture was stirred for 30 minutes at 0-5° C. and then excess nitrous acid was removed by adding sulphamic acid. The diazo suspension was added slowly to a solution of the product from stage (b) (5.42 g, 0.01 mol) in water (100 ml) at pH 7-8 (2N NaOH) cooled below 5° C. The reaction mixture was then stirred at 0-5° C. for one further hour, the product was precipitated by acidification to pH 4 with 2N HCl and collected by filtration. The product was then washed with water and dried in a vacuum desiccator to give 6.4 g of an orange solid.

[0239] Stage (d): Preparation of Compound (16)

[0240] A solution of nickel acetate tetrahydrate (1.38 g, 0.0055 mol) in water (10 ml) was added dropwise to the product from stage (c) (5.0 g, 0.0073 mol) dissolved in water (100 ml) at pH 7 (2N NaOH). The reaction mixture was stirred for 2 hours at ambient temperature, dialysed using SpectraPor membrane tubing (molecular weight cut off 3500) to low conductivity (<100 μs). The product was obtained by evaporation under reduced pressure to afford a dark crystalline solid (6 g). Analysis by mass spectrometry found m/z 1419. Requires M+=1420.

EXAMPLES 17 TO 20

[0241] Compounds (17) to (20) described in Table 3 of the Formula (B) wherein M is nickel were prepared using an analogous process to that described in Example 16 except that in stage (b) the amino compound shown in Table 3 was used in place of 4-aminobenzoic acid.

3TABLE 3

Formula (B)Mass SpectraCom-ExampleAmino compound (Ne—H)Analysispound17

m/z 824 (M − H)−(17)18

m/z 147 (M − H)−(18)19

Not measured(19)20

m/z 720 (M − H)−(20)

EXAMPLE 21

[0242] Compound (21) wherein M is nickel was prepared using an analogous process to that described in Example 16 except that in stage (b) 5-aminoisophthalic acid was used in place of 4-aminobenzoic acid in a 1:1 molar ratio (5-aminoisophthalic acid:disulfonyl chloride).

EXAMPLES 22 AND 23

[0243] Compounds (22) and (23) wherein M is nickel described in Table 4 of the Formula (C) were prepared using an analogous process to that described in Example 1 except that in stage (c) the amino triazole compound shown in Table 4 was used in place of 3-amino-1,2,4-triazole-5-carboxylic acid.

4TABLE 4

Formula (C)ExampleAmino TriazoleDye name22

Nickel chelate of 5-[3,6-bis-(4- carboxy-phenylsulfamoyl)-2- hydroxy-naphthalen-1-ylazo]-4H- [1,2,4]triazole-3-trifluoromethyl. (“Compound (22)”). Analysis by mass spectrometry found m/z 1465 (M − H)−.23

Nickel chelate of 5-[3,6-bis-(4- carboxy-phenylsulfamoyl)-2- hydroxy-naphthalen-1-ylazo]-4H- [1,2,4]triazole. (“Compound (23)”). Analysis by mass spectrometry found m/z 1329 (M − H)−.

EXAMPLE 24

Preparation of Compound (24) wherein M Is Nickel

[0244]

[0245] Stage (a): Preparation of 3-hydroxynaphthalene-2,6-disulfonic acid

[0246] 7-Hydroxynaphthalene-2-sulfonic acid (250 g, 1.16 mol) was added in portions to a mixture of concentrated H2SO4 (950 g) and water (50 g). The mixture was stirred at 110-120° C. for 3 hours, cooled to room temperature, added to a mixture of ice and water (5000 ml) and the product precipitated by the addition of sodium chloride. The slurry was warmed to 90° C. to dissolve the product, stirred for 1 hour at this temperature and then allowed to cool. The product was filtered off and the damp product dissolved in water (3000 ml) at pH 10 by the addition of concentrated sodium hydroxide solution. The solution was then filtered to remove a small amount of insoluble material. The pH of the filtrate was lowered to 7 with concentrated HCl and the product precipitated by the addition sodium chloride. The product was filtered off and dried in a vacuum oven to give 117 g of a cream coloured solid (68% yield).

[0247] Stage (b):

[0248] Compound (24) was prepared using an analogous process to that described in Example 16 except that in stage (a) 3-hydroxynaphthalene-2,6-disulfonic acid was used in place of 2-hydroxynaphthalene-3,6-disulphonic acid. Analysis by mass spectrometry found m/z 1417 (M-H)−.

EXAMPLE 25

Preparation of Compound (25) wherein M Is Nickel

[0249]

[0250] Compound (25) was prepared using an analogous process to that described in Example 16 except that in stage (a) 3-hydroxynaphthalene-2,6-disulfonic acid was used in place of 2-hydroxynaphthalene-3,6-disulphonic acid and in stage (c) 3-amino-1,2,4-triazole was used in place of 3-amino-1,2,4-triazole-5-carboxylic acid.

EXAMPLE 26

reparation of Compound (26) wherein M Is Nickel

[0251]

[0252] Stage (a):

[0253] 1,8-Naphthosultone (25 g, 0.119 mol) was added in portions to concentrated H2SO4 (75 ml). The mixture was then stirred at 80° C. for 1 hour allowed to cool and then added slowly to ice-water (150 ml) maintaining the temperature below 40° C. Sodium sulphate (46 g) was added to the reaction mixture, the resulting suspension was stirred for 10 minutes and then collected by filtration. The damp product was dissolved in water (150 ml) by warming to 45-50° C. and then precipitated by adding sodium chloride (35 g) and allowing to cool. The product was collected by filtration and dried in a vacuum oven at 40° C. to give 40 g of a cream solid (86% yield).

[0254] Stage (b):

[0255] The product from stage (a) (10 g, 0.035 mol) was added in portions to isobutylamine (25 ml). The reaction mixture was stirred for 30 minutes at 40-50° C., evaporated under reduced pressure and the residue slurried in acetone (200 ml). The product was collected by filtration and dried to give 6 g of a pale green powder.

[0256] Stage (c):

[0257] 3-amino-1,2,4-triazole-5-carboxylic acid hydrate (1.28 g, 0.01 mol) was suspended in water (50 ml) and dissolved by the addition of 2M NaOH to pH 8. Sodium nitrite (0.76 g, 0.11 mol) was added and the solution stirred until the sodium nitrite had dissolved.

[0258] The mixture was then added dropwise to a cooled mix of ice-water (30 g) and concentrated HCl (3.0 ml) at 0-5° C., the mixture was stirred for 30 minutes at 0-5° C. and then excess nitrous acid was removed by adding sulphamic acid. The diazo suspension was added slowly to a solution of the product from stage (b) (3.6 g, 0.01 mol) in water (100 ml) at pH 10-10.5 (2N NaOH) cooled below 5° C. The reaction mixture was then stirred at 0-5° C. for 1 hour, the product was precipitated by acidification to pH 4 with 2N HCl and collected by filtration. The product was washed with water and then dried in a vacuum desiccator to give 4.2 g of an orange solid.

[0259] Stage (d): Preparation of Compound (26)

[0260] Compound (26) was prepared using an analogous process to that described in Example 16, stage (d) except that in place of the product from Example 16, stage (c) there was used the product from Example 26, stage (c). Analysis by mass spectrometry found m/z 1051 (M-H)−.

EXAMPLE 27

Preparation of Compound (27) wherein M Is Nickel

[0261]

[0262] Stage (a):

[0263] 3-hydroxynaphthalene-2,6-disulfonic acid was prepared by the method described in Example 24, Stage (a).

[0264] Stage (b):

[0265] 3-amino-1,2,4-triazole-5-carboxylic acid hydrate (3.84 g, 0.03 mol) was suspended in water (180 ml) and dissolved by the addition of 2M NaOH to pH 8. Sodium nitrite (2.27 g, 0.033 mol) was added and the solution stirred until the sodium nitrite had dissolved.

[0266] The mixture was then added dropwise to a cooled mix of ice-water (150 g) and concentrated HCl (10 ml) at 0-5° C., the mixture was stirred for 30 minutes at 0-5° C. and then excess nitrous acid was removed by adding sulphamic acid. The diazo suspension was added slowly to. a solution of 3-hydroxynaphthalene-2,6-disulfonic acid (13.4 g, 0.03 mol) in water (300 ml) at pH 7-8 (2N NaOH) and cooled below 5° C. The reaction mixture was then stirred at 0-5° C. for one further hour, the product was precipitated by acidification to pH 4 with 2N HCl and collected by filtration. The product was washed with 15% brine solution and then dried in a vacuum desiccator to give 20 g of an orange solid (60% yield).

[0267] Stage (c): Preparation of Compound (27)

[0268] A solution of nickel acetate tetrahydrate (2.5 g, 0.01 mol) in water (20 ml) was added dropwise to the product from stage (b) (7.43 g, 0.01 mol) dissolved in water (100 ml) at pH 7-8 (2N NaOH). The reaction mixture was stirred for 2 hours at 20° C., dialysed using SpectraPor membrane tubing (molecular weight cut off 3500) to low conductivity (<100 μs). Compound (27) was obtained by evaporation under reduced pressure to afford a dark solid (5 g). Analysis by mass spectrometry found m/z 499 (M-H)−. Requires M+=500.

EXAMPLES 28 TO 31

[0269] Compounds (28) to (31) of the Formula (D) were prepared using an analogous process to that described in Example 27 except that in stage (c) a metal salt as shown in Table 5 was used in place of nickel acetate.

5TABLE 5

Formula (D)ExampleCompoundMetal saltMMass spectra analysis28(28)Copper acetateCum/z 504 (M − H)−29(29)Chromium acetateCrm/z 934 (M − H)−30(30)Zinc acetateZnm/z 947 (M − H)−31(31)Cobalt acetateCom/z 941 (M − H)−

EXAMPLE 32 TO 34

[0270] Compounds (32) to (34) of the Formula (E) described in Table 6 were prepared using analogous process to that described in Example 27 except that in stage (b) in place of 3-amino-1,2,4-triazole-5-carboxylic acid there was used the triazole compound shown in Table 2. The name of the resultant Compound is shown in the third column of Table 6. M is nickel.

6TABLE 6

Formula (E)ExampleTriazoleYCompound name32

CF3Nickel chelate of [3-hydroxy-4-(5-trifluomethyl- 1H-[1,2,4]triazole-3-ylazo)-naphthalene-2,7- disulfonic acid (“Compound (32)”). Analysis by mass spectrometry found m/z 989 (M − H)−.33

HNickel chelate of [3-hydroxy-4-(1H- [1,2,4]triazole-3-ylazo)-naphthalene-2,7- disulfonic acid. (“Compound (33)”). Analysis by mass spectrometry found m/z 853 (M − H)−.34

C6H5Nickel chelate of [3-hydroxy-4-(5-phenyl-1H- [1,2,4]triazole-3-ylazo)-naphthalene-2,7- disulfonic acid. (“Compound (34)”). Analysis by mass spectrometry found m/z 1007 (M − H)−.

EXAMPLE 35

[0271] Compound (35) of the Formula (F) described in Table 7 was prepared using an analogous process to that described in Example 27 except that in stage (b) in place of 3-hydroxynaphthalene-2,6-disulfonic acid there was used 2-hydroxynaphthalene-3,6-disulfonic acid.

[0272] Compounds (36) and (37) of the Formula (F) described in Table 7 were prepared using an analogous process to that described in Example 27 except that in stage (b) in place of 3-hydroxynaphthalene-2,6-disulfonic acid there was used 2-hydroxynaphthalene-3,6-disulfonic acid and in place of 3-amino-1,2,4-triazole-5-carboxylic acid there was used the amino triazole compound shown in Table 3.

7TABLE 7

Formula (F)ExampleTriazoleYDye name35

CO2HNickel chelate of [5-(2-hydroxy-3,6-disulfo- naphthalen-1-ylazo)-2H-[1,2,4]triazole-3- carboxylic acid]. (“Compound (35)”). Analysis by mass spectrometry found m/z 941 (M − H)−.36

SHNickel chelate of [3-hydroxy-4-(5-mercapto-1H- [1,2,4]triazole-3-ylazo)-naphthalene-2,7- disulfonic acid]. (“Compound (36)”).37

SCH3Nickel chelate of [3-hydroxy-4-(5-methylsulfanyl- 1H-[1,2,4]triazole-3-ylazo)-naphthalene-2,7- disulfonic acid]. (“Compound (37)”). Analysis by mass spectrometry found m/z 501 (M − H)−.

EXAMPLE 38

Compound (38) wherein M Is Copper

[0273]

[0274] Compound (38) was prepared using an analogous process to that described in Example 27 except that in stage (b) 2-hydroxynaphthalene-3,6-disulfonic acid was used in place of 3-hydroxynaphthalene-2,6-disulfonic acid and in stage (c) copper acetate was used in place of nickel acetate.

EXAMPLE 39

Preparation of Compound (39) wherein M Is Nickel

[0275]

[0276] Stage (a):

[0277] The product of Example 27 stage (a) (5 g), (0.016 mol) was added in portions during the course of 30 minutes to 27% oleum (10 ml) with stirring at room temperature. A second portion of 27% oleum (10 ml) was added and the reaction mixture stirred overnight at room temperature. The reaction mixture was then stirred for 3.5 hours at 120° C., cooled and the product collected by filtration using a sintered funnel and washed with concentrated H2SO4 (5 ml). The crude product was dissolved in water (20 ml) and precipitated by the addition of sodium chloride. The solid was collected by filtration and dried to give a pale pink solid.

[0278] Stage (b): Preparation of Compound (40) wherein M Is Nickel:

[0279] The Compound (40) was prepared using an analogous process to that described in Example 27 except that in stage (b) 2-hydroxy-naphthalene-1,3,5,7-tetrasulphonic acid was used in place of 3-hydroxynaphthalene-2,6-disulfonic acid. Analysis by mass spectrometry found m/z 579 (M-H)−.

EXAMPLE 41

Preparation of Compound (41) wherein M Is Nickel

[0280]

[0281] Compound (41) was prepared using an analogous process to that described in Example 27 except that in stage (b) 7-hydroxynaphthalene-1,3,6-trisulfonic acid was used in place of 3-hydroxynaphthalene-2,6-disulfonic acid. Analysis by mass spectrometry found m/z 1101 (M-H)−.

EXAMPLE 42

Preparation of Compound (42) wherein M Is Nickel

[0282]

[0283] Stage (a): Preparation of:

[0284] 3-amino-1,2,4-triazole-5-carboxylic acid hydrate (1.28 g, 0.01 mol) was suspended in water (50 ml) and dissolved by the addition of 2M NaOH to pH 8. Sodium nitrite (0.76 g, 0.11 mol) was added and the solution stirred until the sodium nitrite had dissolved.

[0285] The mixture was then added dropwise to a cooled mix of ice-water (30 g) and concentrated HCl (3.0 ml) at 0-5° C., the mixture was stirred for 30 minutes at 0-5° C. and then excess nitrous acid was removed by adding sulphamic acid. The diazo suspension was added slowly to a solution of 4-hydroxy-naphthalene-1-sulfonic acid sodium salt (2.46 g, 0.01 mol) in water (100 ml) at pH 10-10.5 (2N NaOH) and cooled below 5° C. The reaction mixture was then stirred at 0-5° C. for one further hour, the product was precipitated by acidification to pH 4 with 2N HCl and collected by filtration. The product was washed with water and then dried in a vacuum desiccator to give 2.9 g of an orange solid.

[0286] Stage (b): Preparation of Compound (42):

[0287] A solution of nickel acetate tetrahydrate (1.3 g, 0.005 mol) in water (10 ml) was added dropwise to the product from stage (a) (1.9 g, 0.005 mol) dissolved in water (100 ml) at pH 7-8 (2N NaOH). The reaction mixture was stirred for 2 hours at 20° C., dialysed using SpectraPor membrane tubing (molecular weight cut off 3500) to low conductivity (<100 μs). The product was obtained by evaporation under reduced pressure to afford a dark solid (1.7 g). Analysis by mass spectrometry found m/z 781 (M-H)−.

EXAMPLES 43 AND 44

[0288] Compounds (43) and (44) described in Table 8 of the Formula (G) were prepared using an analogous process to that described in Example 42 except that in stage (b) the metal salt (M) shown in Table 8 was used in place of nickel acetate.

8TABLE 8

Formula (G)Mass spectraExampleCompoundMetal saltManalysis.43(43)Cobalt acetateCom/z 781 (M − H)−44(44)Chromium acetateCrm/z 827 (M − H)−

EXAMPLE 45

Preparation of Compound (45) wherein M Is Nickel

[0289]

[0290] Compound (45) was prepared using an analogous process to that described in Example 42 except that in stage (a) 3-amino-5-methylthio-1,2,4-triazole was used in place of 3-amino-1,2,4-triazole-5-carboxylic acid. Analysis by mass spectrometry found mlz 785 (M-H)−.

EXAMPLE 46

Preparation of Compound (46) wherein M Is Nickel

[0291]

[0292] Stage (a):

[0293] 1,8-Naphthosultone (25.0 g, 0.119 mol) was added in portions to concentrated sulphuric acid (75 ml), the reaction mixture was then stirred for 2 hours at 80° C. and then added to a mixture of ice (70 g) and water (20 ml). Anhydrous sodium sulfate (46 g) was added in portions to the reaction mixture at 30° C., the product was collected by filtration and then dissolved in water (120 ml) at 50° C. The product was precipitated by the addition of sodium chloride (25%w/v), stirred at 40° C. for 1 hour and then collected by filtration. The solid was dried in a vacuum oven to give 30 g of a pink solid (76%).

[0294] Stage (b)—Preparation of 4-hydroxy-1,5-disulphonaphthalene:

[0295] The product from stage (a) (30 g) was dissolved in water (200 ml) at pH 11 by the addition of 2N sodium hydroxide. The solution was stirred at room temperature for 2 hrs to complete the hydrolysis and the solution of the product used in the next stage without isolation.

[0296] Stage (c):

[0297] Compound (46) was prepared using an analogous process to that described in Example 42 except that in the process of Example 42, stage (a) 4-hydroxy-1,5-disulphonaphthalene was used in place of 4-hydroxy-naphthalene-1-sulfonic acid. Analysis by mass spectrometry found m/z 941 (M-H)−.

EXAMPLES 47 AND 48

[0298] Compounds (47) and (48) described in Table 9 of the Formula (H) were prepared using an analogous process to that described in Example 42 except that in stage (a) 4-hydroxy-naphthalene-1,5-disulfonic acid was used in place of 4-hydroxy-naphthalene-1-sulfonic acid and in place of 3-amino-1,2,4-triazole-5-carboxylic acid the amino triazole compound shown in Table 9 was used.

9TABLE 9

Formula (H)ExampleYTriazoleDye name47—CF3

Nickel chelate of [4- hydroxy-3-(5-trifluoro- methyl-1H-[1,2,4]triazole- 3-ylazo)-naphthalene-1,5- disulfonic acid]. (“Compound (47)”). Analysis by mass spec- trometry found m/z 989 (M −H)−.48—H

Nickel chelate of [4- hydroxy-3-(1H-[1,2,4]triazol-3-ylazo)-naphthal- ene-1,5-disulfonic acid]. (“Compound (48)”). Analysis by mass spec- trometry found m/z 853 (M − H)−.

EXAMPLE 49

Preparation of Compound (49) wherein M Is Nickel

[0299]

[0300] Compound (49) was prepared using an analogous process to that described in Example 42 except that in stage (a) 8-hydroxynaphthalene-1,3,6-trisulfonic acid was used in place of 4-hydroxynaphthalene-1-sulfonic acid. Analysis by mass spectrometry found m/z1157(M-H)−.

EXAMPLE 50

Preparation of Compound (50) wherein M Is Nickel

[0301]

[0302] Compound (50) was prepared using an analogous process to that described in Example 42 except that in stage (a) 8-hydroxy-naphthalene-1,3,6-trisulfonic acid was used in place of 4-hydroxy-naphthalene-1-sulfonic acid and 3-amino-1,2,4-triazole was used in place of 3-amino-1,2,4-triazole-5-carboxylic acid. Analysis by mass spectrometry found m/z 534 (M-H)−.

EXAMPLE 51

Comparison of Compound (27) with Comparative Dye 1

[0303] The Compound described in EP 1,241,232 A1, page 19, Example 2-2 (hereinafter “Comparative Dye 1”) was prepared having the following structure wherein M is nickel:

[0304] In addition the Compound (27) from Example 27 above was prepared.

[0305] Inks were prepared containing each compound and the inks were printed onto HP Plain Paper. The resultant prints prepared from Compound (27) were bright and had good light fastness and ozone fastness. In contrast the prints prepared from Comparative Dye 1 were very dull, with ozone fastness poorer than Compound (27) and light-fastness similar to or slightly worse than Compound (27).

EXAMPLE 52

Comparison of Compound (23) with Comparative Dye 2

[0306] The dye described in EP 1,241,232 A1, page 25, Example 4-1 (hereinafter “Comparative Dye 2”) was prepared having the following structure:

[0307] In addition Compound (23) from Example 23 was prepared.

[0308] Inks were prepared containing each compound and the inks were printed onto HP Plain Paper. The resultant prints Compound (23) were bright and had good light fastness and ozone fastness. In contrast the resultant prints prepared from Comparative Dye 2 were very dull, with poorer ozone fastness and light-fastness than Compound (23).

[0309] Inks

[0310] The inks described in Tables I, II, III, IV, V, VI, VII and VIII may be prepared wherein the Compound described in the first column is the Compound made in the above example of the same number. Numbers quoted in the second column onwards refer to the number of parts of the relevant ingredient and all parts are by weight. The inks may be applied to paper by thermal or piezo ink jet printing.

[0311] The following abbreviations are used in Tables I, II, III, IV, V, VI, VII and VIII:

[0312] PG=propylene glycol

[0313] DEG=diethylene glycol

[0314] NMP=N-methyl pyrollidone

[0315] DMK=dimethylketone

[0316] IPA=isopropanol

[0317] MEOH=methanol

[0318] 2P=2-pyrollidone

[0319] MIBK=methylisobutyl ketone

[0320] P12=propane-1,2-diol

[0321] BDL=butane-2,3-diol

[0322] CET=cetyl ammonium bromide

[0323] PHO=Na2HPO4 and

[0324] TBT=tertiary butanol

[0325] TDG=thiodiglycol

10TABLE IDyeNaCompoundContentWaterPGDEGNMPDMKNaOHStearateIPAMEOH2PMIBK12.080564523.090550.2310.0853335142.1918153.18650.24561.18190.50.5972.56041533610548565201092.47554565104.180352100.3113.2655465465105.19641110.89055910.08026251481.88051562.68411573.38021026512.09070.3345.469220213336.09145

[0326]

11

TABLE II

Dye

Compound
Content
Water
PG
DEG
NMP
CET
TBT
TDG
BDL
PHO
2P
PI2

1
3.0
80
15

0.2

5

2
9.0
90

5

1.2

5

1
1.5
85
5
5

0.15
5.0
0.2

5
2.5
90

6
4

0.12

4
3.1
82
4
8

0.3

6

6
0.9
85

10

5
0.2

5
8.0
90

5
5

0.3

9
4.0
70

10
4

1

4
11

2
2.2
75
4
10
3

2

6

11
10.0
91

6

3

1
9.0
76

9
7

3.0

0.95
5

3
5.0
78
5
11

6

7
5.4
86

7

7

2
2.1
70
5
5
5
0.1
0.2
0.1
5
0.1
5

1
2.0
90

10

6
2
88

10

10
5
78

5

12

5

8
8
70
2

8

15

5

2
10
80

8

12

1
10
80

10

[0327]

12

TABLE III

Dye

Na

Compound
Content
Water
PG
DEG
NMP
DMK
NaOH
Stearate
IPA
MEOH
2P
MIBK

12
2.0
80
5

6
4

5

13
3.0
90

5
5

0.2

14
10.0
85
3

3
3

5
1

15
2.1
91

8

1

12
3.1
86
5

0.2
4

5

13
1.1
81

9

0.5
0.5

9

14
2.5
60
4
15
3
3

6
10
5
4

15
5
65

20

10

12
2.4
75
5
4

5

6

5

13
4.1
80
3
5
2
10

0.3

12
3.2
65

5
4
6

5
4
6
5

13
5.1
96

4

14
10.8
90
5

5

15
10.0
80
2
6
2
5

1

4

12
1.8
80

5

15

13
2.6
84

11

5

14
3.3
80
2

10

2

6

15
12.0
90

7
0.3

3

12
5.4
69
2
20
2
1

3
3

13
6.0
91

4

5

[0328]

13

TABLE IV

Dye

Compound
Content
Water
PG
DEG
NMP
CET
TBT
TDG
BDL
PHO
2P
PI2

12
3.0
80
15

0.2

5

13
9.0
90

5

1.2

5

14
1.5
85
5
5

0.15
5.0
0.2

15
2.5
90

6
4

0.12

12
3.1
82
4
8

0.3

6

13
0.9
85

10

5
0.2

14
8.0
90

5
5

0.3

15
4.0
70

10
4

1

4
11

12
2.2
75
4
10
3

2

6

13
10.0
91

6

3

12
9.0
76

9
7

3.0

0.95
5

13
5.0
78
5
11

6

14
5.4
86

7

7

15
2.1
70
5
5
5
0.1
0.2
0.1
5
0.1
5

14
2.0
90

10

12
2
88

10

13
5
78

5

12

5

12
8
70
2

8

15

5

12
10
80

8

12

12
10
80

10

[0329]

14

TABLE V

Dye

Na

Compound
Content
Water
PG
DEG
NMP
DMK
NaOH
Stearate
IPA
MEOH
2P
MIBK

16
2.0
80
5

6
4

5

17
3.0
90

5
5

0.2

18
10.0
85
3

3
3

5
1

19
2.1
91

8

1

20
3.1
86
5

0.2
4

5

21
1.1
81

9

0.5
0.5

9

22
2.5
60
4
15
3
3

6
10
5
4

23
5
65

20

10

24
2.4
75
5
4

5

6

5

25
4.1
80
3
5
2
10

0.3

26
3.2
65

5
4
6

5
4
6
5

16
5.1
96

4

16
10.8
90
5

5

17
10.0
80
2
6
2
5

1

4

18
1.8
80

5

15

19
2.6
84

11

5

21
3.3
80
2

10

2

6

20
12.0
90

7
0.3

3

22
5.4
69
2
20
2
1

3
3

23
6.0
91

4

5

[0330]

15

TABLE VI

Dye

Compound
Content
Water
PG
DEG
NMP
CET
TBT
TDG
BDL
PHO
2P
PI2

16
3.0
80
15

0.2

5

17
9.0
90

5

1.2

5

18
1.5
85
5
5

0.15
5.0
0.2

19
2.5
90

6
4

0.12

20
3.1
82
4
8

0.3

6

21
0.9
85

10

5
0.2

22
8.0
90

5
5

0.3

23
4.0
70

10
4

1

4
11

24
2.2
75
4
10
3

2

6

25
10.0
91

6

3

26
9.0
76

9
7

3.0

0.95
5

16
5.0
78
5
11

6

18
5.4
86

7

7

22
2.1
70
5
5
5
0.1
0.2
0.1
5
0.1
5

20
2.0
90

10

24
2
88

10

26
5
78

5

12

5

16
8
70
2

8

15

5

17
10
80

8

12

16
10
80

10

[0331]

16

TABLE VII

Dye

Na

Compound
Content
Water
PG
DEG
NMP
DMK
NaOH
Stearate
IPA
MEOH
2P
MIBK

27
2.0
80
5

6
4

5

28
3.0
90

5
5

0.2

29
10.0
85
3

3
3

5
1

30
2.1
91

8

1

31
3.1
86
5

0.2
4

5

32
1.1
81

9

0.5
0.5

9

33
2.5
60
4
15
3
3

6
10
5
4

34
5
65

20

10

35
2.4
75
5
4

5

6

5

36
4.1
80
3
5
2
10

0.3

37
3.2
65

5
4
6

5
4
6
5

38
5.1
96

4

39
10.8
90
5

5

40
10.0
80
2
6
2
5

1

4

41
1.8
80

5

15

42
2.6
84

11

5

43
3.3
80
2

10

2

6

44
12.0
90

7
0.3

3

45
5.4
69
2
20
2
1

3
3

46
6.0
91

4

5

[0332]

17

TABLE VIII

Dye

Compound
Content
Water
PG
DEG
NMP
CET
TBT
TDG
BDL
PHO
2P
PI2

47
3.0
80
15

0.2

5

48
9.0
90

5

1.2

5

49
1.5
85
5
5

0.15
5.0
0.2

30
2.5
90

6
4

0.12

31
3.1
82
4
8

0.3

6

27
0.9
85

10

5
0.2

33
8.0
90

5
5

0.3

34
4.0
70

10
4

1

4
11

35
2.2
75
4
10
3

2

6

36
10.0
91

6

3

27
9.0
76

9
7

3.0

0.95
5

38
5.0
78
5
11

6

39
5.4
86

7

7

46
2.1
70
5
5
5
0.1
0.2
0.1
5
0.1
5

41
2.0
90

10

27
2
88

10

28
5
78

5

12

5

27
8
70
2

8

15

5

27
10
80

8

12

27
10
80

10

Number	Date	Country
0217443.1	Jul 2002	GB
0217444.9	Jul 2002	GB
0217446.4	Jul 2002	GB
0217442.3	Jul 2002	GB

Number	Date	Country
60410814	Sep 2002	US
60410805	Sep 2002	US
60410810	Sep 2002	US
60410806	Sep 2002	US

Processes, compositions and compounds

Information

Publication Number

Date Filed

Date Published

Inventors

Original Assignees

CPC

US Classifications

International Classifications

Abstract

Description

Claims