This invention is directed to conductive particle films and to methods for the manufacture of conductive particle films such as by electrostatic deposition.
Although a significant amount of research has been done on developing new battery materials - especially lithium ion intercalation materials - film deposition methodologies have remained relatively unchanged. Once anode or cathode powder materials are acquired, conventional deposition involves the production of a slurry that contains the appropriate mixture of intercalation, conduction, and binder particles. The slurry is then coated onto the suitable electrode metal sheeting, which is subsequently heated for solvent evaporation and transferred into a controlled atmosphere for assembly into battery. This multiple step process is time consuming, costly, and sufficiently labor intensive that outsourcing production is a necessity for long-term financial viability. Only a few other methods have been investigated as potential replacements for the slurry coating process for lithium ion batteries. Some of these are relatively expensive, such as pulsed laser deposition, vapor deposition, and sputtering. Other more economically feasible options include electrostatic spray deposition (ESD) (C. H. Chen et al., Solid State Ionics 86: 1301-1306, 1996.), and electrophoretic deposition (EPD) (H. Mazor et al., J. Power Sources 198: 264-272, 2012). These methods include a liquid phase, thereby ensuring a multistep method. ESD involves electrostatic deposition of charged precursor solution droplets that impinge and react on a hot, grounded substrate. EPD involves the migration of charged particles onto a grounded substrate in a liquid.
Less time consuming and labor intensive methods would be desired for the production of particle films for batteries and other products.
Thermal runaway is one of the biggest dangers of the lithium ion battery. At a certain temperature, a self-sustaining reaction will occur, leading to catastrophic failure. Although some battery chemistries require higher temperatures to initiate thermal runaway, it is possible for all lithium batteries.
Lithium batteries will generate heat due to the chemical reaction between anode and cathode, and internal electrical resistance. If the heat generation is equal to the heat flux out of the battery, then there will be no rise in temperature.
In a standard lithium ion cylindrical cell as shown in
The present invention overcomes the problems and disadvantages associated with current strategies and designs, and provides new tools and methods for forming particle films.
One embodiment of the invention is directed to a process for forming a particle film. The process preferably comprises co-aerosolizing conductive particles and a binder, applying charge to the aerosolized particle mixture by a corona; and applying the mixture to a heated substrate, preferably by aerodynamic or electrostatic forces, forming a film. Preferably the conductive particles comprise anodic or cathodic material and the anodic or cathodic material comprises carbon, a lithium metal phosphate, or a lithium metal oxide. Preferably applying the mixture comprises a reel-to-reel deposition system wherein particles are deposited in a single stream or multiple streams.
Another embodiment of the invention is a particle film deposited by the method of the invention and preferably which is a component of a lithium-ion battery.
Another embodiment of the invention is directed to a process for forming a conductive particle film. The process comprises mixing conductive particles with a binder to form a mixture, aerosolizing the mixture, applying a charge to the aerosol mixture, applying heat to a grounded substrate, and applying the mixture to the heated and grounded substrate by aerodynamic or electrostatic interaction, forming the conductive particle film.
Preferably, the substrate is a metal foil heated above the melting point of the binder by resistive, convective, or radiative heating. In a preferred embodiment, the conductive particles comprise anodic or cathodic material. Preferably, the anodic or cathodic material comprises at least one of carbon, lithium titanate, lithium cobalt oxide, lithium manganese oxide, lithium nickel manganese cobalt oxide, lithium nickel cobalt aluminum oxide, lithium iron phosphate, or lithium iron manganese phosphate.
In a preferred embodiment, the charge is applied to the conductive particles by a corona gun or by triboelectric charging. Preferably, the binder is selected from the group comprising PVDF, PTFE and SBR. Preferably, mixing the conductive particles with binder comprises a co-aerosolization.
In a preferred embodiment, applying the mixture to the film comprises a reel-to-reel deposition system wherein particles are deposited in multiple streams. The film is preferably applied to a roll of substrate in a continuous process. Preferably, the conductive particles are mixed with a binder by at least one of co-aerosolizing the binder as a dry powder using a turntable dust generator or fluidized bed disperser; dissolving the binder in a solvent, atomizing the dissolved binder into microdroplets, and mixed with the particles as an aerosol; or vaporizing the binder and allowing the vaporized binder to condense on the particles.
Another embodiment of the invention is directed to a system for forming a conductive particle film. The system comprises a mixer to combine conductive particles with a binder to form a mixture, an aerosolizer to aerosolize the mixture, an electrical charging device to charge the aerosol mixture, a heating device to heat a substrate, and a grounding device to ground the substrate. The film is applied to the substrate in a continuous process.
In a preferred embodiment, the substrate is a metal foil heated above the melting point of the binder and the heating device is a resistive, convective, or radiant heating device. Preferably, the conductive particles comprise anodic or cathodic material. Preferably, the anodic or cathodic material comprises at least one of carbon, lithium titanate, lithium cobalt oxide, lithium manganese oxide, lithium nickel manganese cobalt oxide, lithium nickel cobalt aluminum oxide, lithium iron phosphate, or lithium iron manganese phosphate.
In a preferred embodiment, the electrical charging device is at least one of a corona gun or by triboelectric charging. The binder is preferably selected from the group comprising PVDF, PTFE and SBR. Preferably, mixing the conductive particles with binder comprises a co-aerosolization. The system preferably further comprises a reel-to-reel deposition system wherein particles are deposited in multiple streams. In a preferred embodiment, the mixer at least one of co-aerosolizes the binder as a dry powder using a turntable dust generator or fluidized bed disperser; dissolves the binder in a solvent, atomizes the dissolved binder into microdroplets, and mixes with the particles as an aerosol; or vaporizes the binder and allows the vaporized binder to condense on the particles.
Other embodiments and advantages of the invention are set forth in part in the description, which follows, and in part, may be obvious from this description, or may be learned from the practice of the invention.
As embodied and broadly described herein, the disclosures herein provide detailed embodiments of the invention. However, the disclosed embodiments are merely exemplary of the invention that may be embodied in various and alternative forms. Therefore, there is no intent that specific structural and functional details should be limiting, but rather the intention is that they provide a basis for the claims and as a representative basis for teaching one skilled in the art to variously employ the present invention.
Conventional particle film deposition methodology has focused on automation to increase yields. Reduced yield and also batch-to-batch variations remain a bane to the lithium ion battery industry. It has been surprisingly discovered that yield can be increased and batch-to-batch variation minimized by the methodologies of the invention, and in particular, by co-aerosolization of a conductive particle and a binder. The conductive particles and binder are preferably aerosolized separately and mixed together in the aerosol phase prior to deposition. The process of the invention is not limited to battery chemistry, nor is the chemistry limited to the deposition process. Powder aerosolization can be combined with electrostatic powder deposition to produce nearly any particle film. Accordingly, the processes of the invention can be utilized in a wide variety products and methods that relate to particle deposition.
Particle deposition involves an application of particles to a surface. Particles are preferably nanoparticles, which are nanometers to tens of microns in grain size, or nanoparticle agglomerates. Reel-to-reel film deposition allows for the potential of in-situ battery assembly, so that coated electrodes may be prepared and assembled in the same controlled atmosphere. The resulting automated large-area deposition also facilitates the reliable production of large high-current, single-cells.
Electrostatic powder coating (EPC) was first developed in the 1950's as a means for creating uniform large-area particle films. The process has only been commercialized on a more widespread basis over the last two decades (A. G. Bailey, J. Electrostatics 45: 85-120, 1998). The basic principle is to charge aerosolized particles, either by a corona gun or by friction caused by flow of the particles through a TEFLON® tube, and to aerodynamically carry and deposit the charged particles on a surface. The surface preferably is electrically grounded or has an opposite charge to the charge of the particles, so that the particles follow electric field lines to the surface where they remain adhered due to the electrostatic attractive forces between the particle and surface. Preferably, the surface is a metal capable of conducting a charge, however the surface can be of another material, such as plastic, fiber, or other naturally occurring or manmade materials capable of conducting a charge. Current applications of the process are generally followed by a high temperature melting and curing step, forming the final continuous film. Constraints on the size and electrical properties of the particles have previously limited the industrial use of the process to environmentally friendly (e.g., no solvents) painting and epoxy coating.
The conventional constraints on the particle properties preclude the application of EPC to nano-sized particles and to particles that are either too conductive or too electrically resistive. There are resistivity limits because of the required electrostatic adhesive interaction between the particle and surface after deposition has occurred. While paint particles typically used in EPC stick to the substrate via electrostatic charges, conductive particles alone will not stick to the substrate due to the rapid loss of charge when the particles come into contact with the grounded substrate. Particles that are too conductive immediately lose their charge to the surface, and are therefore no longer electrostatically bound to the surface. They are then susceptible to aerodynamic re-entrainment in the carrier gas flow. Conversely, particles that are too resistive retain their charge to such an extent that the coated surface itself becomes highly charged. This results in: 1) a significant reduction in the magnitude of the electric field attracting the particles to the surface, and 2) a so-called back ionization effect, whereby electrical gas breakdown occurs within the particle film resulting in a local loss of charge, localized re-entrainment of particles, and thus a non-uniform or “orange peel” finish. One example of an EPC process used in battery making is U.S. Pat. No. 6,511,517 to Ullrich et al. However, the method taught by Ullrich uses EPC merely to create a wax coating on top of the positive electrode or the negative electrode.
The application of EPC to conductive nanoparticle films, such as a graphitic carbon anode or a conductive lithium iron phosphate (typically coated with carbon) cathode, involves film that is bound to a metal sheeting substrate immediately upon deposition. Conventional slurry coating of lithium ion battery electrodes typically employs a polyvinylidene fluoride (PVDF) binder for adequate film adhesion. The necessary presence of such a chemically inert binder may be exploited to enhance the immediate adhesion of the film to the substrate.
The anodic or cathodic material is preferably at least one of carbon, lithium titanate, lithium cobalt oxide, lithium manganese oxide, lithium nickel manganese cobalt oxide, lithium nickel cobalt aluminum oxide, lithium iron phosphate, or lithium iron manganese phosphate. Additional suitable polymer binders include styrene butadiene copolymer (SBR), polytetrafluoroethylene (PTFE) and others which are well-known in the art. Preferably, the binder is non-soluble. A secondary benefit to this mode of EPC deposition is that static charge build-up of insulating film particles is avoided, thus eliminating the self-limiting effects of back ionization. In other words, the film could be grown arbitrarily thick, as compared to conventional EPC applications.
Mixing the binder with the cathode or anode powder in the aerosol phase can be performed in variety of ways. For example, binder can be co-aerosolized as dry powder using a turntable dust generator (S. Seshadri et al., J. Aerosol Sci. 36: 541-547, 2006) or fluidized bed disperser. Alternatively, the binder can be dissolved in a solvent and atomized into microdroplets and mixed with the active powder as an aerosol. Finally, the binder can be vaporized and allowed to condense on the cathode/anode powder grains.
When coating a thin metal foil using either the system shown in
For thin foils, preferably, the foil is resistively heated during powder deposition by passing an electrical current (either AC or DC) directly through the metal foil substrate during reel-to-reel deposition. Using this method, heat is preferably generated continuously and uniformly throughout the foil, from below the coating. This preferably results in a small temperature gradient that allows for highly uniform coatings. A continuous reel-to-reel coating system is depicted in
The foils created by the system depicted in
Preferably, the battery design allows heat to flow out through the most thermally conductive part of the battery. In order increase heat dissipation even more, preferably, the shape of the cell is changed from a narrow cylinder to a wide, thin disk. Preferably, the diameter cylinder exceeds the length of the cylinder. Preferably, the ratio of the diameter to the length is greater than 5 to 1, greater that 6 to 1, or greater than 7 to 1. Preferably the cathode, anode, and polymer separator are arranged in a spiral configuration so that many layers of cathode/anode interaction can occur in the same battery. For example, the cross-section of the battery depicted in
The thin disk shape of the pancake-like cell, combined with continuous terminal welding, preferably allows heat to transfer a short distance to easily cooled, high surface area terminals. This cell design is preferably advantageous over standard battery designs in that individual cells can be safely made to much higher capacities than the standard designs. This may provide significant manufacturing cost reduction, especially when combined with a continuous single step production technique.
The following examples illustrate embodiments of the invention, but should not be viewed as limiting the scope of the invention.
As an example of the process, Carbon Black nanopowder was mixed with PVDF powder in a 10:1 carbon-to-binder mass ratio mixture and deposited on an aluminum foil substrate. The mixture was placed in a 5 lb fluidized bed hopper and fluidized using a vibrating element attached to the hopper. A venturi pump was used to deliver the fluidized powder from the hopper to a corona gun set at a voltage of 50 kV and positioned 1.5 inches away from foil substrate. The backside of the foil was heated convectively using a heat gun such that the front side of the foil was measured to exceed 200 C.—above the melting point of PVDF. Within 1 second, a thick powder film was formed on the foil substrate in a circular pattern indicative of the radial temperature distribution on the foil, as shown in
The deposition process shown schematically in
Prior to deposition, the cathode and anode powders are preferably aerosolized and delivered to the corona guns with a high mass throughput and at a steady rate. Aerosolization of dry powders is a common industrial process that may be accomplished efficiently using a variety of processes. For example, high mass loadings, resulting in the flow of several grams of powder per second per corona gun, is achieved through fluidized bed dispersion, wherein a carrier gas flows though a powder hopper inducing enough shear to break particle-particle adhesive bonds and resulting in their entrainment in the gas flow. This type of powder dispersion works well for grain sizes on the order of tens of microns. Nanometer-scale grains preferably involve a superimposed mechanical agitation for their effective entrainment as agglomerates. This agitation is preferably imposed by sound waves (C. Zhu et al., Powder Tech. 141: 119-123, 2004), vibrations, or centrifuging (S. Matsuda et al., AIChE J. 50: 2763-2771, 2004). Aerosolization of individual grains is not necessary and, in fact, may be detrimental to the deposition process. Optimum agglomerate size is preferably determined by varying the agitation frequency and the flow rate.
The proposed single-step deposition technique can be integrated into a fully automated battery manufacturing methodology. The system would limit the potential for film contamination, reduce batch-to-batch variations, and ultimately increase product yield. This in turn would significantly reduce retail costs to levels that would enable the widespread deployment of large batteries for residential usage.
Other embodiments and uses of the invention will be apparent to those skilled in the art from consideration of the specification and practice of the invention disclosed herein. All references cited herein, including all publications, U.S. and foreign patents and patent applications, are specifically and entirely incorporated by reference. The term comprising, where ever used, is intended to include the terms consisting and consisting essentially of. Furthermore, the terms comprising, including, and containing are not intended to be limiting. It is intended that the specification and examples be considered exemplary only with the true scope and spirit of the invention indicated by the following claims.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2015/057299 | 10/26/2015 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 62068830 | Oct 2014 | US |