Claims
- 1. In the process of casting in a silica container an ingot of a material having a tendency to form a tenacious bond with the interior wall of the silica container, said process including the steps of first melting and thereafter solidifying said material to form said ingot, that improvement wherein said material is solidified in a silica container the wall of which comprises:
- an interior surface defined by a thin glass skin; and,
- without said skin, silica varying in cristobalite phase silica content, said content being greater in a region near said skin than in a region more distant from said skin, whereby contracting of said ingot of said material within and bonded to said skin of said Container will break said skin rather than cracking the ingot.
- 2. The process of claim 1 wherein the percentage of cristobalite phase silica in said wall decreases generally according to the distance outward from said skin.
- 3. The process of claim 1 wherein the density of silica in said wall is greatest adjacent said interior surface.
- 4. The process of claim 1 wherein a thin region of said wall adjacent and without said skin comprises glass and cristobalite silica, and regions of said wall without said thin region comprise cristobalite and vitreous silica.
- 5. The process of claim 4 wherein said thin region is microcracked prior to solidifying said material in said container.
- 6. The process of claim 1 wherein said glass skin has a thickness less than about 0.40 in.
- 7. The process of claim 1 wherein the thickness of said skin is in the range of about 0.010 in. to about 0.020 in.
- 8. The process of claim 1 wherein said container is cylindrical and said interior surface is defined by the cylindrical wall and base of said container.
- 9. The process of claim 1 including the step of forming said container by heating the interior surface of a vitreous silica container to melt the silica defining said interior surface but not silica behind said interior surface; and thereafter cooling said container to cause said melted silica to form said glass skin.
- 10. The process of claim 9 wherein said interior surface is heated to a temperature above the glass formation and cristobalite phase cut-off temperatures of silica, and during said heating the temperature of silica without said interior surface remains below said cristobalite phase cut-off temperature.
- 11. The process of claim 10 wherein during said heating the temperature of silica in a first region without said interior surface remains below said cristobalite phase cut-off temperature, and the temperature of silica in a second region without said first region remains below said glass formation temperature.
- 12. The process of claim 11 wherein during said heating the temperature of silica adjacent the exterior surface of said container remains below the cristobalite formation temperature of silica.
- 13. In the process of making a container for use in casting ingots, that improvement comprising:
- forming said container by heating the interior surface of the walls of a vitreous silica container to melt the silica defining said interior surface but not silica behind said interior surface; and thereafter cooling container to cause said melted silica to form a glass skin defining said interior surface and to form in regions without said skin silica varying in cristobalite phase silica content, said content being greater in a region nearer said skin than in a region more distant from said skin.
- 14. The process of claim 13 wherein said interior surface is heated to a temperature above the glass formation and cristobalite phase cut-off temperatures of silica, and during said heating the temperature of silica without said interior surface remains below said cristobalite phase cut-off temperature.
- 15. The process of claim 14 wherein during said heating the temperature of silica in a first region without said interior surface remains below said cristobalite phase cut-off temperature, and the temperature of silica in a second region without said first region remains below said glass formation temperature.
- 16. The process of claim 11 wherein during said heating the temperature of silica adjacent the exterior surface of said container remains below the cristobalite formation temperature of silica.
- 17. The process of claim 13 wherein said glass skin has a thickness in the range of about 0.010 in. to about 0.040 in.
- 18. The process of claim 13 wherein said container is cylindrical and interior surface is defined by the cylindrical wall and base of said container.
- 19. The process of claim 1 wherein said material is silicon.
- 20. The process of claim 1 wherein said material includes silicon.
- 21. The process of claim 20 wherein said material is glass.
CROSS-REFERENCE TO RELATED APPLICATION
This application is a continuation-in-part of copending application Ser. No. 918,056, filed June 22, 1978 and now abandoned.
US Referenced Citations (8)
Foreign Referenced Citations (1)
Number |
Date |
Country |
590458 |
Jul 1947 |
GBX |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
918056 |
Jun 1978 |
|