Magnesium ammonium phosphate has been produced in solid form and is used primarily as a fertilizer. It is formed as a by-product in the treatment of waste water and in the making of magnesium phosphate cements.
Processes of making the monohydrate form of magnesium ammonium phosphate (“dittmarite”) are provided. The processes can produce dittmarite in an environmentally friendly manner.
An exemplary process comprises introducing at least magnesium, phosphorous and nitrogen into a vessel by introducing at least two reactants into the vessel, and reacting the at least two reactants to produce a slurry. In preferred embodiments, the solid portion of the slurry contains a high percentage of dittmarite.
Embodiments of processes of making paper, such as cigarette paper, use dittmarite containing slurries produced by reacting environmentally friendly non-caustic reactants. An exemplary process comprises combining the slurry with paper making feedstock in a paper making process. The slurry is preferably maintained under conditions that substantially prevent the transformation to struvite before it is combined with the paper making feedstock.
Exemplary embodiments of processes of making magnesium ammonium phosphate (also referred to herein as “AMP”) are described. The monohydrate form of AMP (NH4MgPO4.H2O, or “dittmarite”) can be produced by the processes.
Exemplary embodiments of the processes produce dittmarite by reacting environmentally friendly reactants, without using reactants like phosphoric acid that are used in known processes. The processes can produce dittmarite directly from the reaction of the environmentally friendly reactants. The dittmarite can have high purity.
Processes of making cigarette paper by producing dittmarite, and then combining the dittmarite with paper making feedstock in a paper making process, are described. These processes can utilize dittmarite in slurry form produced by reacting environmentally friendly reactants, by embodiments of the above-described processes. The dittmarite can be fed directly from the reactor vessel to the paper making process.
Dittmarite can transform to struvite below certain temperatures. By combining the as-produced dittmarite, while in slurry form and at a sufficiently high temperature, with the paper making feedstock in a paper making process, potential phase changes from dittmarite to struvite can preferably be substantially eliminated. Embodiments of the processes can reduce, and preferably substantially prevent, the occurrence of such phase changes by maintaining dittmarite in a slurry form at a sufficiently high temperature until it is combined with paper making feedstock.
In some embodiments of the processes, the as-produced dittmarite in slurry form can first be converted to a dried form of dittmarite. The dried magnesium ammonium phosphate can be stored and then reslurried when needed for later use. The reslurried magnesium ammonium phosphate can be combined with paper making feedstock in a paper making process, or used for other purposes.
Production of Dittmarite Slurries Using Environmentally Friendly Reactants
Current commercial processes for producing magnesium ammonium phosphate react magnesia and/or magnesium hydroxide, ammonium hydroxide and/or anhydrous ammonia, and phosphoric acid. Ammonium hydroxide, anhydrous ammonia, and phosphoric acid each pose environmental and safety issues. In addition, a strongly exothermic reaction occurs when phosphoric acid is added to the basic magnesium hydroxide mixture. Consequently, current processes that utilize these reactants require added safety precautions, which introduce added costs, handling procedures, and require special permits for practicing the processes.
Embodiments of processes of producing magnesium ammonium phosphate by reacting environmentally friendly reactants can overcome these problems. Exemplary embodiments of the processes do not utilize phosphoric acid, but rather utilize phosphate. Consequently, problems associated with using phosphoric acid are avoided.
Exemplary embodiments of the processes comprise introducing at least magnesium, phosphate and nitrogen into a vessel in which magnesium ammonium phosphate is to be produced. These components are reacted to produce a slurry containing magnesium ammonium phosphate.
Magnesium, phosphate and nitrogen can be introduced into the vessel in any suitable form or manner. For example, magnesium, phosphate and nitrogen can be provided by introducing at least two reactants into the vessel. In a preferred embodiment, the at least two reactants include at least one magnesium containing reactant, and at least one phosphate and nitrogen containing reactant. The at least one magnesium containing reactant is preferably magnesium hydroxide (Mg(OH)2) and/or magnesium oxide (MgO). However, magnesium acetate and other suitable magnesium compounds can be used as the magnesium containing reactant. Magnesium acetate provides good particle size control, and by-product acetate can be readily recovered from the product.
The at least one magnesium containing reactant is preferably supplied to a reactor vessel in the form of an aqueous slurry. Magnesium hydroxide and magnesium oxide are completely insoluble in water. Dry powders of these magnesium compounds can be mixed with water to provide an aqueous slurry.
The phosphate containing compound is preferably ammonium dihydrogen phosphate (NH4H2PO4). Ammonium dihydrogen phosphate provides a phosphate group (PO4) and nitrogen for the reaction to produce magnesium ammonium phosphate. Ammonium dihydrogen phosphate is completely soluble in water (20 g/100 g at 25° C.). Thus, the phosphate can be added to the reactor vessel in aqueous form.
Preferably, dittmarite is produced by reacting magnesium hydroxide and/or magnesium oxide with ammonium dihydrogen phosphate. The reaction is conducted at boiling temperatures. For example, the reaction between magnesium hydroxide and ammonium dihydrogen phosphate is as follows:
Mg(OH)2+NH4H2PO4→NH4MgPO4.H2O+H2O
Referring to
Magnesium hydroxide and magnesium oxide are completely insoluble in water. At least one of these compounds is preferably added to the reactor vessel in slurry form. Ammonium dihydrogen phosphate is completely soluble in water. Accordingly, ammonium dihydrogen phosphate is preferably added to the reactor vessel as an aqueous solution. Preferably, the magnesium hydroxide and/or magnesium oxide containing slurry is added to the reactor vessel before adding the ammonium dihydrogen phosphate to the reactor vessel.
The solids content of the magnesium hydroxide and/or magnesium oxide containing slurry added to the reactor vessel 10 can be selected based on different considerations. First, the slurry is preferably stirred both before it is added to the reactor vessel, and after it has been added. If the solids concentration of the magnesium hydroxide and/or magnesium oxide solids in water exceeds about 30 wt. %, a paste may form, which is difficult to stir. Accordingly, the solids content of the magnesium hydroxide and/or magnesium oxide containing slurry is preferably below 30 wt. %.
A second consideration is the desired concentration of solids in the magnesium ammonium phosphate containing slurry produced by the reaction. For example, if the magnesium ammonium phosphate containing slurry is supplied to a cigarette paper making process 18, the magnesium ammonium phosphate containing slurry can be pumped from the reactor vessel directly to paper making equipment. The concentration of solids in the magnesium ammonium phosphate containing slurry can be selected to achieve desired pumping and/or mixing with other ingredients supplied to the paper making equipment. The concentration of solids in the magnesium ammonium phosphate containing slurry preferably is no greater than about 25 wt. %, more preferably no greater than 20 wt. %, to achieve desired pumping performance.
In preferred embodiments, dittmarite is formed directly from the reaction between magnesium hydroxide and/or magnesium oxide with ammonium dihydrogen phosphate. In order to preferably minimize conversion of dittmarite to struvite in the reactor vessel, the temperature inside the reactor vessel is preferably kept sufficiently high so that struvite is thermally unstable and does not form. Preferably, the temperature inside the reactor vessel is above about 55° C., more preferably above about 60° C., and most preferably above about 100° C.
The reaction of magnesium hydroxide and/or magnesium oxide with ammonium dihydrogen phosphate is mildly exothermic. Accordingly, this reaction generates heat, which raises the temperature of the reactants and product inside the reactor vessel. The temperature inside the reactor vessel is preferably monitored during the reaction. Heat can be supplied to the reactor vessel to maintain the temperature inside the reactor vessel sufficiently high to make struvite thermally unstable. For example, heat can be supplied to the reactor vessel to ensure that the temperature is above about 55° C., more preferably above about 60° C., and most preferably above about 100° C. during the reaction. Heat can be supplied to the reactor vessel by any suitable source.
To minimize the transformation of dittmarite formed by the reaction to struvite, the temperature of the magnesium ammonium phosphate containing slurry in the reactor vessel is preferably maintained sufficiently high after the reaction has occurred.
The reaction to form dittmarite is preferably performed in a sealed reactor vessel under pressure. Mild pressure is generated during the reaction at the preferred temperatures described above.
An experimental example was performed to demonstrate that dittmarite can be produced directly in slurry form, and at a high purity level, by reacting environmentally friendly reactants by the above-described processes. Particularly, magnesium hydroxide was reacted with ammonium dihydrogen phosphate to form dittmarite having high purity.
A solution was formed by adding 50 g of ammonium dihydrogen phosphate (MAP) to 250 ml of deionized water in a container. The solution was stirred. A slurry was formed by adding 25 g of magnesium hydroxide to 183 mL of deionized water in another container. The amounts of water in the solution and slurry were determined based on an estimated final solids concentration of about 16 wt. %.
The magnesium hydroxide slurry was placed in a sealed reactor vessel. The slurry was agitated in the reactor vessel and heated to boiling. The ammonium dihydrogen phosphate solution was added to the slurry in the reactor vessel. Samples were taken from the reactor vessel at intervals of time (to monitor reaction kinetics) and dried immediately for analysis.
The dried samples were analyzed to determine the degree of reaction completeness, i.e., the completeness of the reaction to form NH4MgPO4.H2O, or dittmarite. Using thermogravimetric analyses (TGA), TGA curves were generated. The weight loss contributed to the degradation of unreacted magnesium hydroxide (Mg(OH)2) to magnesium oxide (MgO) was determined. Because some weight loss in the curve in the temperature range for the decomposition of magnesium hydroxide is also contributed to the degradation of magnesium ammonium phosphate, the weight loss from the magnesium ammonium phosphate within the same temperature range was determined using a high purity magnesium ammonium phosphate. The two values were subtracted to obtain the true weight loss due to degradation of unreacted magnesium hydroxide. The amount of unreacted ammonium dihydrogen phosphate was also determined.
Table 1 sets forth numerical values determined from the samples taken from the reactor vessel at different times.
As shown in Table 1, the product formed after 30 minutes of reaction contained about 98wt. % dittmarite, and contained substantially no magnesium hydroxide, as described above. The example demonstrated that high yields of dittmarite containing slurries of a high purity of preferably at least 95 wt. %, and more preferably at least 97 wt. %, can be produced by embodiments of the processes by reacting environmentally friendly reactants.
Production of Paper Containing Dittmarite
The monohydrate form of magnesium ammonium phosphate is the desirable form of magnesium ammonium phosphate fillers in cigarette paper. Dittmarite containing slurry produced by reacting environmentally friendly reactants by the above-described processes can be mixed with feedstock of a paper making apparatus 26 (
Feeding the hot slurry directly to the paper making machine can eliminate the need to supply additional heat to the paper making equipment to maintain a temperature above the phase transition temperature of dittmarite to struvite. Accordingly, energy consumption can be reduced in the paper making process.
In a paper making operation, dittmarite can be supplied directly to a tank in which the dittmarite is mixed with one or more components of the paper making feedstock, preferably at a temperature and/or pressure sufficient to maintain stability of the reaction product, i.e., prevent transformation to struvite. In an exemplary cigarette paper making process, the overall process steps can include:
In order to provide a desired dittmarite particle size to the paper making equipment, as indicated in
Alternatively, the slurry of monohydrate magnesium ammonium phosphate can be dried to particle form (e.g., powder), and such powder can be incorporated in the paper making feedstock. The slurry is preferably maintained above about 55° C., more preferably above about 60° C., until the slurry is dried. As shown in
For paper making, the particle size of dittmarite is preferably in the range of approximately 2 μm to 8 μm, more preferably in the range of 2 μm to 4 μm. As shown in
The cigarette making process can produce traditional cigarettes, or other less traditional cigarettes, such as cigarettes usable with electronic smoking devices, which are described in U.S. Pat. No. 6,289,898.
Thus, embodiments of the processes can conserve energy by feeding the slurry directly from the reactor vessel to the paper making equipment, without first drying and then reslurrying dried dittmarite. Producing dittmarite at the site of the paper making process can eliminate storage and transportation costs, and minimize potential transformation of dittmarite to struvite during such storage.
Embodiments of the processes also eliminate problems associated with the use of corrosive, dangerous reactants including phosphoric acid, such as handling, special permit requirements, and controlling strongly exothermic reactions.
While the invention has been described in detail with reference to specific embodiments thereof, it will be apparent to those skilled in the art that various changes and modifications can be made, and equivalents employed, without departing from the scope of the appended claims.
This application claims priority under 35 U.S.C. § 119 to U.S. Provisional Application No. 60/540,067 entitled PROCESS OF MAKING MONOHYDRATE FORM OF MAGNESIUM AMMONIUM PHOSPHATE AND PROCESSES OF MAKING PAPER USING SAME and filed on Jan. 30, 2004, the entire content of which is hereby incorporated by reference.
Number | Date | Country | |
---|---|---|---|
60540067 | Jan 2004 | US |