This application claims priority to South African provisional patent application number 2013/08726, which is incorporated by reference herein.
This invention relates to the processing of carbonaceous materials and more particularly the thermochemical processing of carbonaceous materials by a process that includes the treatment of such materials with microalgae. In this specification the term thermochemical processing is intended to include, but is not limited to, such processes as pyrolysis, distillation, gasification, coking, liquefaction and combustion.
The carbonaceous materials may be of any origin but are most typically fossil fuels such as coal, charcoal and crude oil.
The conversion of carbonaceous materials into energy and other products often involves a thermochemical conversion step. In the production of energy, carbonaceous materials may for example be combusted to generate heat.
Alternatively, carbonaceous materials may be converted into other products through thermochemical processing. Examples include the conversion of coal into fuels by means of gasification followed by further chemical reaction of the resultant gas mixture comprising carbon monoxide and hydrogen.
Alternatively coal may be liquefied by heating at high temperature and pressure in the presence of catalysts and a hydrogen-transfer solvent to produce liquid products directly.
Coking coal is produced via the pyrolysis of coal under inert conditions or vacuum to produce essentially three products: a gaseous product, a liquid product (pyrolysis oil), and a solid product (coking coal). The latter process is normally carried out at very high temperatures (>1000° C.). In a variant of the latter process, pyrolysis may be carried out at moderate temperatures (˜600° C.) to produce pyrolysis oil and a partially de-volatilized coal.
Crude oil, on the other hand, is normally subjected to an initial high temperature distillation process in order to separate the oil into different boiling point fractions. Such distillation processes generally generate four crude products, namely a top fraction containing all the lowest boiling components; a middle fraction which contains components with medium boiling points; a heavy fraction (high boiling points); and a bottom fraction that cannot be distilled.
To date there is little that can be done to change the properties of materials such as coal, charcoal and crude oil with the view to improve the thermochemical processing of such materials to provide improved yields or improved product properties. As an example, during the distillation of crude oil, the nature of the crude oil typically determines the relative proportions of the basic products.
Our earlier international patent application publication number WO 2012/025806 discloses that fine coal and other carbonaceous material may conveniently be rendered usable by agglomeration using microalgae biomass as binder for fine carbon particles. This work with microalgae and carbonaceous material has led to further processes being developed as will be further described below.
In this specification the term coal or carbonaceous fines should generally be interpreted to mean sub 250 micron particle sizes. It is however preferred that the particle size actually to be sub 150 micron for the more efficient operation of the invention as will become more apparent from what follows.
In accordance with this invention there is provided a method of processing a carbonaceous material in the form of carbonaceous fines comprising treating the carbonaceous material with micro-algae so that the micro-algae adsorbs onto the carbonaceous material, and heating the carbonaceous material with the adsorbed microalgae in a heat activating step to a temperature within the range from a temperature at which water starts evaporating to a temperature at which volatile components of the carbonaceous material start to volatilize with the heating being continued for a duration selected to allow chemical interaction between the micro-algae and the carbonaceous material so as to alter the chemical structure of the carbonaceous material.
A further feature of the invention provides for the microalgae to be in the form of substantially intact cells that are preferably still in a photosynthetically active state. It is thus preferred that freshly harvested microalgae that have been harvested or concentrated by means of a mechanism that does not result in cell rupture be used. In order to facilitate adsorption of microalgae onto the carbonaceous material contacting between the micro-algae and the carbonaceous material may be done either by mixing dry carbonaceous materials such as coal or charcoal with micro-algae slurry in water, or by adding micro-algae as a wet filter or centrifuge cake to the carbonaceous material that is already present in water such as coal fines leaving a coal processing plant. The micro-algae in the form of a wet filter or centrifuge cake may, of course, be added to a liquid carbonaceous material such as a crude oil or tar. Contacting is preferably carried out in a manner aimed at loading the carbonaceous material evenly with micro-algae adsorbed thereon in a preferred amount of from 5 to 15% by weight of the carbonaceous material.
Clearly, the temperature range within which the heat activating step takes place will depend on the nature and composition of the carbonaceous material and may vary from one carbonaceous material to another.
In one instance the carbonaceous material was in the form of coal fines and at the ambient conditions the lower temperature was effectively about 80° C. whilst volatiles started coming off from a temperature of about 150° C. In that instance a preferred narrower temperature range would be from about 100 to about 130° C. with an indicated optimum being about 110° C.
The duration for which the heat activating step is carried out depends on the temperature and other physical characteristics of the carbonaceous material with micro-algae adsorbed thereon with a higher temperature typically requiring a shorter time and a lower temperature requiring a longer time. In this particular instance the duration of the heat activating step was from 0.5-3 hours and conveniently 1-2 hours. In any event, the heat activating step is preferably carried out until the carbonaceous material has a moisture content of not more than about 10 mass %.
When using a slurry of micro-algae in water, the micro-algae may be present in any concentration that would enable subsequent mixing with the carbonaceous materials. Typically, microalgae concentrations may vary from about 1 gram/litre to 10 grams/litre if taken directly from commercial growth systems. Alternatively, a wet cake of micro-algae, typically containing between 30 to 200 g/Kg of micro-algae, may be used to mix with a liquid carbonaceous material, or carbonaceous material slurry.
Microalgae will most typically be derived from commercial cultivation systems such as a photo-bioreactor, pond, or raceway system, in which instance the contact constitutes harvesting of microalgae in a manner that will preserve the integrity of the harvested microalgae cells. For the invention to function optimally, it is preferred that microalgae cells are not broken during any processing step such as harvesting and that the microalgae cells are contacted with the coal fines as whole, or intact cells.
In order that the invention may be more fully understood, different embodiments thereof will now be described with reference to the accompanying drawings.
In the drawings:
Solid state NMR studies were carried out on a particular coal sample in the form it was received and the same coal was modified by the adsorption of 10 mass % (dry-weight basis) micro-algae, followed by heating at 105° C. for two hours. The solid state NMR spectra of the two different materials are shown in
In Table 1, column 1 lists the various structural parameters of coals that may be derived from the information obtained by 13C solid state NMR (symbols in column 2). Column 3 lists the values of these parameters for the coal sample. Column 4 lists the values for the coal-micro-algae agglomerate. Column 5 gives an estimate of the magnitude of the experimental error present in the estimations and may be used to determine whether a particular difference between the parameter values for coal and coal-micro-algae is real or just error; for a particular difference to be real, the difference between the two parameter values must exceed the estimated experimental error. Columns 6 and 7 list parameter values for two typical types of coal as a way to illustrate the main differences between the coal-micro-algae agglomerate and coals in general.
From the comparisons listed in Table 1, it may be observed that micro-algae results in the largest changes to those parameters that appears in rows # 8, 9, 10, 13, 14, 15, and 16. A person skilled in the art may find it obvious that the results suggest that the effect of micro-algae bonding to fine coal particles causes the structure of the coal to become simplified in the sense that the large clusters of aromatic rings found within the coal structure are in some way split so that there are more, and smaller, clusters with fewer linkages between clusters of aromatic rings. In addition, the degree of protonation of the aromatic rings is increased.
The observations and conclusions described above led to the proposal that the adsorption of micro-algae onto fine coal particles followed by heating at relatively low temperatures typically in the range 105-150° C. so as not to drive off combustible volatile materials results in the formation of a coal-micro-algae agglomerate in which the chemical structure is different from both the constituent coal and the micro-algae constituents. In addition, it is postulated that this agglomerate will behave as a single substance under thermochemical processing conditions such as combustion, unlike what is typically observed for coal and biomass mixtures (as for example described by M. V. Gil, D. Cascal, C. Previda, J. J. Pis, and F. Rubiera, “Thermal behaviour and kinetics of coal/biomass blends during co-combustion”, Bioresource Technology, 101 (2010), 5601-5608; and C. Wang, F. Wang, Q. Yang, and R. Liang, “Thermogravimetric studies of the behaviour of wheat straw with added coal during combustion”, Biomass and Bioenergy, 33 (2009), 50-56) where the coal and biomass constituents give rise to thermal events traceable to either the biomass or coal constituent.
To test the hypothesis regarding the behaviour of the coal-micro-algae agglomerates or composites under thermochemical processing conditions, coal and coal-micro-algae composites were subjected to both combustion conditions with heating under oxygen atmosphere and pyrolysis conditions with heating under an inert atmosphere. The results of these tests are depicted in
The pyrolysis profiles for coal and micro-algae composite that were prepared from the same coal and using a 10 mass % micro-algae loading (dry weight basis) in
The difference between coal and the same coal treated with 10% microalgae (w/w%) was further tested under mild pyrolysis conditions but subjecting coal or coal-microalgae composites to pyrolysis under a nitrogen atmosphere at a temperature of 450° C. The results of these tests are summarized in Table 2 below. These results clearly show that under real life pyrolysis conditions, the amount of volatile products (gas and liquid) is increased significantly when coal is modified with microalgae prior to the pyrolysis step.
These results from the combustion and pyrolysis tests strongly suggest that the hypotheses that the micro-algae change the chemical structure of the coal, and that this change would change the behaviour under thermochemical processing conditions are correct.
The hypotheses were further tested by first comparing the combustion of coal with the combustion of a coal-micro-algae agglomerate/composite produced from the same coal.
It is envisaged that there will be numerous carbonaceous materials to which the invention can be applied with good effect.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2013/08726 | Nov 2013 | ZA | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/IB2014/066151 | 11/19/2014 | WO | 00 |