Patent Grant
9731980
The present invention relates to a treatment method and a treatment device for a barren solution containing hydrogen sulfide, such as a process liquid after a sulfurization treatment of a nickel oxide ore plant. The present application claims a priority based on Japanese Patent Application No. 2012-270721 filled on Dec. 11, 2012 in Japan, and the Application is incorporated into the present application by reference.
Conventionally, as a hydrometallurgy method for recovering a valuable metal such as nickel and cobalt from a nickel oxide ore having a low nickel content represented by a limonite ore and the like, a high temperature pressure acid leaching (HPAL: High Pressure Acid Leaching) method using sulfuric acid has been known.
For example, in a high pressure acid leach method to obtain a nickel-cobalt mixed sulfide, as shown in
In a pretreatment step (1), a nickel oxide ore is ground and classified to obtain a slurry.
In a leaching step (2), sulfuric acid is added into the slurry obtained in the pretreatment step (1), the resultant mixture is stirred at a temperature of 220 to 280° C., and high temperature pressure acid leaching is performed to obtain a leach slurry.
In a solid-liquid separation step (3), a leach slurry obtained in the leaching step (2) is subjected to solid-liquid separation to obtain a leachate containing nickel and cobalt (hereinafter, referred to as “crude nickel sulfate aqueous solution”), and leach residues.
In a neutralization step (4), a crude nickel sulfate aqueous solution obtained in the solid-liquid separation step (3) is neutralized.
In a dezincification step (5), hydrogen sulfide gas is added into the crude nickel sulfate aqueous solution neutralized in the neutralization step (4), and zinc is precipitated and removed as a zinc sulfide.
In a sulfurization step (6), hydrogen sulfide gas is added into the dezincification final solution obtained in the dezincification step (5), and a nickel-cobalt complex sulfide and a nickel barren solution are obtained. In a detoxification step (7), a heavy metal is solidified and removed as a hydroxide by a final neutralization treatment, and a leach residue generated in the solid-liquid separation step (3) and a nickel barren solution generated in the sulfurization step (6) are detoxified.
In general, many kinds of heavy metals are contained in a nickel oxide ore, the nickel oxide ore is dissolved by using sulfuric acid under high temperature high pressure conditions, and then a chemical treatment is performed to remove impurities, subsequently, a required metal such as nickel is recovered in a sulfurization step. In a sulfurization reaction, hydrogen sulfide gas, and a salt such as sodium hydrogen sulfide, and sodium sulfide are used, however, an unreacted sulfide remains after the sulfurization step.
In a case where hydrogen sulfide gas is used in a sulfurization reaction, unreacted hydrogen sulfide gas is dissolved in a solution after the reaction, and also in a case where a salt such as sodium hydrogen sulfide, and sodium sulfide are used, hydrogen sulfide gas may be generated depending on the state of the solution. The solution after sulfurization is reused or subjected to a wastewater treatment in a step (for example, see Patent Document 2).
When hydrogen sulfide gas is generated in these steps, it is not desired from the viewpoint of the working hygiene and the environment.
Conventionally, as a removal method of dissolved hydrogen sulfide in a solution (barren solution) after sulfurization reaction, a method in which a nickel oxide ore slurry after leaching is added into a barren solution after sulfurization, a reduction action with trivalent iron existed in a large amount in the nickel oxide ore slurry after leaching is utilized, and hydrogen sulfide is oxidized to sulfur to decrease the concentration of the dissolved hydrogen sulfide has been known.
However, in a case where a method described above is used, the addition of acid and the slurry after leaching are repeatedly required, and further, dissolved hydrogen sulfide still exists in a solution after reaction, therefore, further decrease of the dissolved hydrogen sulfide is required.
The present invention has been made in consideration of these circumstances, and an object of the present invention is to provide a treatment method and a treatment device for a barren solution, with which the dissolved hydrogen sulfide gas can effectively be decreased for example, in a solution containing hydrogen sulfide gas such as a process liquid after a sulfurization treatment in a hydrometallurgy treatment for a nickel oxide ore.
Another object of the present invention, and a specific advantage obtained by the present invention become more apparent from the explanation of an embodiment described below.
In the present invention, an annular aeration tube having a large number of air outlets is arranged to a bottom part of a vertical-type cylindrical reaction vessel, aeration is performed by using a simple aeration device for blowing gas for aeration from a large number of air outlets of the annular aeration tube, while stirring a barren solution containing hydrogen sulfide in the reaction vessel, and the hydrogen sulfide is removed from the barren solution.
That is, the present invention characterized by a treatment method for a barren solution containing hydrogen sulfide, in which in an aeration tank provided with a vertical-type cylindrical reaction vessel, stirring blades is arranged in the reaction vessel, and an annular aeration tube has a large number of air outlets and is arranged to the bottom part of the reaction vessel, aeration is performed by introducing gas for aeration into the reaction vessel from a large number of air outlets of the aeration tube, while stirring a barren solution containing hydrogen sulfide by rotation of the stirring blades, and the hydrogen sulfide is removed from the barren solution.
Further, the present invention characterized by a treatment device for a barren solution containing hydrogen sulfide, in which the treatment device includes an aeration tank provided with a vertical-type cylindrical reaction vessel, stirring blades arranged in the reaction vessel, and an annular aeration tube having a large number of air outlets and being arranged to the bottom part of reaction vessel, and in the aeration tank, aeration is performed by introducing gas for aeration into the reaction vessel from a large number of air outlets of the aeration tube, while stirring a barren solution containing hydrogen sulfide by rotation of the stirring blades, and the hydrogen sulfide is removed from the barren solution.
In the present invention, the above-described barren solution can be a process liquid after a sulfurization treatment in a hydrometallurgy plant for a nickel oxide ore.
Further, in the present invention, aeration can be performed by the aeration tube formed in an annular shape having a diameter size of 70 to 90% of that of the reaction vessel.
In addition, in the present invention, aeration can be performed from the air outlets formed in a circular shape having a diameter of 10 to 20 mm.
Further, in the present invention, aeration with 10 to 20 short tube pipes that are arranged at equal intervals in the aeration tube as the air outlets can be performed.
In addition, in the present invention, the gas for aeration can be air.
Further, in the present invention, by performing aeration in the aeration tank, the hydrogen sulfide gas generated in a step of reusing a solution after sulfurization, or in a wastewater treatment step can be decreased.
According to the present invention, an annular aeration tube having a large number of air outlets is arranged to the bottom part in a vertical-type cylindrical reaction vessel, aeration is effectively performed by using a simple aeration device for blowing gas for aeration from a large number of air outlets of the annular aeration tube, while stirring a barren solution containing hydrogen sulfide in the reaction vessel, and hydrogen sulfide can be efficiently aerated and removed from a barren solution.
Further, in the present invention, in particular, a reaction tank with stirring blades, in which a slurry after leaching is added into a barren solution obtained from a sulfurization step in a wet treatment plant for a nickel oxide ore, can be suitably used as an aeration tank, and the hydrogen sulfide gas generated in a step of reusing a solution after sulfurization, or in the subsequent wastewater treatment step can be effectively decreased.
Hereinafter, a specific embodiment to which the present invention is applied will be described in detail with reference to the drawings.
A treatment method for a barren solution according to the present embodiment is, for example, performed by a barren solution treatment device 100 with the constitution as illustrated in
The barren solution treatment device 100 is an aeration tank provided with a vertical-type cylindrical reaction vessel 110, stirring blades 120 arranged in the reaction vessel 110, and an annular aeration tube 130 having a large number of air outlets 131 and being arranged to bottom part of the reaction vessel 110. Further, in the vertical-type cylindrical reaction vessel 110, three plates of baffle plates 151 are arranged.
In a treatment method for a barren solution according to the present embodiment, in a vertical-type cylindrical reaction vessel 110, aeration is performed by introducing gas for aeration into the reaction vessel 110 from a large number of air outlets 131 of the aeration tube 130, while stirring a barren solution containing hydrogen sulfide by rotation of stirring blades 120, and the hydrogen sulfide is removed from the barren solution.
For example, in a hydrometallurgy plant for a nickel oxide ore, in a detoxification step as described above, a heavy metal is solidified and removed as a hydroxide by a final neutralization treatment, and a leach residue generated in a solid-liquid separation step and a nickel barren solution generated in a sulfurization step are detoxified and discarded. In this case, in the present embodiment, for example, as shown in a process chart of
That is, in a reaction tank for removing hydrogen sulfide from a barren solution containing hydrogen sulfide, which is obtained as a process liquid after a sulfurization treatment in a preceding step of a detoxification step, an annular aeration tube 130 having a large number of air outlets 131 is arranged, and the reaction tank is used as the above-described barren solution treatment device 100.
Specifically, in the barren solution treatment device 100 that is the reaction tank, a barren solution containing hydrogen sulfide, which is obtained as a process liquid after a sulfurization treatment, is charged into the vertical-type cylindrical reaction vessel 110, and in the reaction vessel 110, the barren solution containing hydrogen sulfide is stirred by rotation of stirring blades 120. Further, in the reaction vessel 100, for the barren solution, aeration is performed by introducing air as gas for aeration from a large number of air outlets 131 of the annular aeration tube 130, and the sulfur content of the remaining hydrogen sulfide in the barren solution is reduced to sulfur, as a result, the hydrogen sulfide is removed from the barren solution.
In addition, in a hydrometallurgy plant for a nickel oxide ore, into a barren solution containing hydrogen sulfide, which is obtained as a process liquid after a sulfurization treatment, a slurry after leaching, which is obtained in a leaching step, is partly added. Therefore, in the hydrogen sulfide removal step, by the reducing power of Fe3+contained in the added slurry, the sulfur content of part of the remaining hydrogen sulfide in the barren solution is reduced to sulfur, therefore, hydrogen sulfide can more efficiently be removed from the barren solution.
That is, The barren solution treatment device 100 used for performing a treatment method for a barren solution according to the present embodiment includes an aeration tank provided with a vertical-type cylindrical reaction vessel 110, stirring blades 120 arranged in the reaction vessel 110, and an annular aeration tube 130 having a large number of air outlets 131 and being arranged to the bottom part of the reaction vessel 110, and in the aeration tank, aeration is performed by introducing gas for aeration into the reaction vessel 110 from a large number of air outlets 131 of the aeration tube 130, while stirring a barren solution containing hydrogen sulfide by rotation of stirring blades 120, and the hydrogen sulfide is removed from the barren solution.
As described above, in the barren solution treatment device 100, not only a barren solution containing hydrogen sulfide is stirred by rotation of stirring blades 120 in the reaction vessel, that is, in the aeration tank, but also gas for aeration is blown into the reaction vessel. As a result, the remaining hydrogen sulfide is discharged from the stirred barren solution by aeration, and the residual concentration of the hydrogen sulfide is decreased.
Moreover, in the barren solution treatment device 100, aeration is performed via an annular aeration tube 130 having a large number of air outlets 131 and being arranged to bottom part of the reaction vessel 110, so that bubbles to flow into the reaction vessel 110 are allowed to be split into small bubbles, and the total area of bubbles is tried to be increased. As a result, an abundance of bubbles can be brought into contact with the barren solution containing hydrogen sulfide, which is uniformly stirred in the reaction vessel 110, and a high aeration effect can be obtained. That is, the gas for aeration fed into the reaction vessel 110 becomes in the state of being dispersed on the bottom of the aeration tank from immediately after the feeding, therefore, the aeration can be efficiently performed over the entire barren solution.
In general, the set time of the reaction in a stirring reaction device is usually shorter than the sufficient aeration time by an ordinary aerator. However, according to the barren solution treatment device 100, the retention time in the reaction vessel 100 becomes a prerequisite by the providing of an aeration function in the reaction vessel 110, therefore, even if the sufficient aeration time is not necessarily ensured, the aeration can efficiently be performed as described above, and the hydrogen sulfide can effectively be decreased.
As shown in the process chart of
As described above, a hydrogen sulfide removal step is arranged as a preceding step of a detoxification step, and in the hydrogen sulfide removal step, the remaining hydrogen sulfide can effectively be removed by the aeration using the above-described barren solution treatment device 100, therefore, the generation of the hydrogen sulfide gas in a step in which a solution after sulfurization is reused, or in a wastewater treatment step can be suppressed.
The gas for aeration is not particularly limited as long as the gas for aeration is maintained the bubbles in a liquid, that is, not being easily dissolved into a liquid, however, air is preferably used in view of cost.
Further, the shape of the aeration tube is not particularly limited, however, is preferably formed in an annular shape having a diameter size of 70 to 90% of that of the reaction solution 120.
Herein, as to the shape of aeration tube 130, results of the observation of the relationship between the diameter of the aeration tube 130 and the aeration effect, when the diameter of the aeration tube 130 is changed based on the diameter of the reaction vessel 110, are shown in Table 1.
As is apparent from the observation results shown in Table 1, it has been found that a high aeration effect can be obtained by the forming of the aeration tube 130 in the barren solution treatment device 100 in an annular shape having a diameter size of 70 to 90% of that of the reaction vessel 110.
In order to stabilize the flow in the reaction vessel 110 of the barren solution treatment device 100, the air is required to be gone up along the vessel wall. In this respect, the air can efficiently be gone up along the vessel wall by the forming of the aeration tube 130 in the barren solution treatment device 100 in an annular shape having a diameter size of 70 to 90% of that of the reaction vessel 110.
Further, the air outlet 131 formed to the aeration tube is not particularly limited, however, is preferably formed in a circular shape having a diameter of 10 to 20 mm.
Herein, as to the air outlets 131 formed to an aeration tube, results of the observation of the relationship between the bore diameter of the air outlets 131 and the aeration effect, when the bore diameter of the air outlets 131 is changed by the setting of the bore shape as circular, are shown in Table 2.
As is apparent from the observation results shown in Table 2, it has been found that a high aeration effect can be obtained by the forming of the air outlets 131 of the aeration tube 130 in the barren solution treatment device 100 in a circular shape having a diameter of 10 to 20 mm.
It is presumed that there is an optimal bubble size for the density and flow characteristics of the barren solution, and it is considered that if the bubble size is smaller than 10 mm, the rising speed of bubbles in a barren solution is extremely slow, on the other hand, if the bubble size is larger than 20 mm, the rising speed is extremely fast.
Further, the number of the air outlets 131 is not particularly limited, and is preferably appropriately determined depending on the length of the circumference of the aeration tube, however, for example, the number of the air outlets 131 is preferably around 10 outlets, and more preferably 20 outlets.
Herein, as to the number of air outlets 131, results of the observation of the relationship between the number of the air outlets 131 and the aeration effect, when the number of the air outlets 131 is changed, are shown in Table 3.
As is apparent from the observation results shown in Table 3, it has been found that a high aeration effect can be obtained by the setting of the number of the air outlets 131 of the aeration tube 130 in the barren solution treatment device 100 as 10 outlets, and a much higher aeration effect can be obtained by the forming of 20 outlets.
In the aeration tube 130, when the number of air outlets is increased, the upflow of air becomes weak, and the retention time of the air in an aeration tank is increased, therefore, the aeration efficiency is increased. When the number of air outlets 131 is less than 10, the aeration effect is insufficient, and when the number of air outlets 131 is increased in series, the effect is increased, however, when the number is more than 20, the aeration effect is hardly improved any more.
In addition, the air outlets 131 are not mere pores, when a short pipe (outlet) is attached in the arranged pore, the gas flow is rectified, and the bubble size is stabilized, therefore, this is preferred. Further, the number of the outlets is preferably around 10 to 20.
That is, as to the aeration tube 130, for example, as shown in
Hereinafter, Examples of the present invention will be described, however, the present invention is not limited to the following Examples.
In the present Examples, in a hydrogen sulfide removal step provided as a preceding step of a detoxification step in a hydrometallurgy plant for a nickel oxide ore, a barren solution treatment was performed by using the above-described barren solution treatment device 100.
Table 4 shows results obtained by the measurement of the concentration of the dissolved hydrogen sulfide in a barren solution with or without aeration.
As is apparent from the measurement results shown in Table 4, when aeration was not performed, the concentration of the dissolved hydrogen sulfide was 20 ppm at an inlet of an aeration tank, and 15 ppm at an outlet of an aeration tank, on the other hand when aeration was performed, the concentration of hydrogen sulfide at an outlet of an aeration tank was largely decreased to 5 ppm, and the dissolved hydrogen sulfide in a barren solution could effectively be decreased by aeration. As described above, it has been found that when a barren solution is treated by using a barren solution treatment device 100, the concentration of the dissolved hydrogen sulfide in the barren solution could effectively be decreased by the aeration.
100, 200 heavy-metal removal device; 110 reaction vessel; 120 stirring blade; 130 aeration tube; 131 air outlet; 131A short tube pipe; 151 baffle plate
| Number | Date | Country | Kind |
|---|---|---|---|
| 2012-270721 | Dec 2012 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2013/081471 | 11/22/2013 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2014/091903 | 6/19/2014 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4519959 | Takeuchi et al. | May 1985 | A |
| 4779990 | Hjort et al. | Oct 1988 | A |
| 5939313 | Cheng | Aug 1999 | A |
| 6368381 | King | Apr 2002 | B1 |
| 20050265910 | Kobayashi et al. | Dec 2005 | A1 |
| 20100018350 | Shibayama et al. | Jan 2010 | A1 |
| 20110163042 | Kobayashi et al. | Jul 2011 | A1 |
| 20130001173 | Kobayashi et al. | Jan 2013 | A1 |
| Number | Date | Country |
|---|---|---|
| 2311517 | Oct 1997 | GB |
| S58-186425 | Oct 1983 | JP |
| S62-125834 | Jun 1987 | JP |
| H03-249930 | Nov 1991 | JP |
| H04-89541 | Aug 1992 | JP |
| H08-71585 | Mar 1996 | JP |
| H09-248576 | Sep 1997 | JP |
| H09-314169 | Dec 1997 | JP |
| H09-314170 | Dec 1997 | JP |
| H10-258222 | Sep 1998 | JP |
| 2001-239139 | Sep 2001 | JP |
| 3225836 | Nov 2001 | JP |
| 2002-282664 | Oct 2002 | JP |
| 2005-350766 | Dec 2005 | JP |
| 2010-031302 | Feb 2010 | JP |
| 2010-095788 | Apr 2010 | JP |
| 2010-207674 | Sep 2010 | JP |
| 2011-206757 | Oct 2011 | JP |
| 2011-225908 | Nov 2011 | JP |
| 2012-240012 | Dec 2012 | JP |
| 0118263 | Mar 2001 | WO |
| 2011132693 | Oct 2011 | WO |
| Entry |
|---|
| Jul. 14, 2016 Search Report issued in European Patent Application No. 13861760.0. |
| Feb. 10, 2014 International Search Report issued in International Patent Application No. PCT/JP2013/081471. |
| Oct. 16, 2014 International Preliminary Report on Patentability issued in International Patent Application No. PCT/JP2013/081471. |
| Number | Date | Country | |
|---|---|---|---|
| 20150329379 A1 | Nov 2015 | US |