The disclosure herein relates to a production method and to a production system for producing a continuous-fiber-reinforced component.
Fiber-reinforced composite parts are usually produced with more or less adapted fiber orientation. In this case, composite components may contain not only plastics materials or polymer materials. Composite components composed of metal or light metal and fibers are also conceivable. The possibilities for adaptation are generally exhausted within the limits of the manufacturing process. However, this can lead to a more elaborate manufacturing operation, particularly if a high degree of fiber orientation is to be achieved; this is generally associated with more complex and slower manufacturing methods.
Examples of improved manufacturing methods which increase the degree of fiber orientation are 3D printing, overmolding of fiber reinforcements, winding fibers around metal eyes or lugs, compression molding of carbon-fiber-reinforced semifinished polymer products.
The European patent application 19 380 014.1, yet to be published at the priority date of the present application, discloses a method in which continuous fibers are introduced into oriented tubular openings of the component by injecting resin and continuous fibers together. The contents of patent application 19 380 014.1 are incorporated by way of reference into the present application for the purposes of disclosure.
The disclosure herein is based on the object of improving the range of application of such manufacturing methods, in particular of enabling the introduction of fibers into a larger number of geometries.
The object is achieved by the subject matter disclosed herein.
The disclosure herein provides a production method for producing a component composed of a composite material with a fiber reinforcement which is formed from fiber bundles and resin, the method comprising the steps of:
a) providing a component body with a plurality of tube-like cavities;
b) introducing resin and a pulling apparatus for the fiber bundles into at least one of the cavities, the pulling apparatus having at least one pulling member which is configured to pull the fiber bundles and to transmit compressive force;
c) pulling at least one fiber bundle into the cavity by way of the at least one pulling member.
It is preferred that step a) comprises:
It is preferred that step a) comprises:
It is preferred that step a) comprises:
It is preferred that step a) comprises:
It is preferred that step a) comprises:
It is preferred that step a) comprises:
It is preferred that step a) comprises:
It is preferred that step a) comprises:
It is preferred that step a) comprises:
It is preferred that step a) comprises:
Preferably, at least 60% by weight, more preferably 70% by weight to 95% by weight, of the component body is formed from the first polymer material.
It is preferred that step a) comprises:
It is preferred that step a) comprises:
It is preferred that step a) comprises:
It is preferred that step b) and/or c) comprises:
It is preferred that step b) and/or c) comprises:
It is preferred that step b) comprises:
It is preferred that step b) comprises:
It is preferred that step b) comprises:
It is preferred that step c) comprises:
It is preferred that step c) comprises:
It is preferred that step c) comprises:
It is preferred that step b) and/or c) comprise:
It is preferred that step c) comprises:
It is preferred that step c) comprises:
It is preferred that step c) comprises:
It is preferred that step c) comprises:
It is preferred that step c) comprises:
It is preferred that step c) comprises:
It is preferred that the component body has a first region composed of a first polymer material and a second region composed of a second polymer material, the first polymer material being selected such that it can be dissolved in a solvent, the second polymer material being selected such that it cannot be dissolved in the solvent.
The method preferably comprises the step:
d) at least partially removing the first polymer material by dissolving the first polymer material in the solvent.
It is preferred that step d) comprises:
It is preferred that step d) comprises:
It is preferred that step d) comprises:
The method preferably comprises the step:
e) curing the resin.
A composite material component is obtainable by one of the production methods disclosed herein.
The composite material component is preferably configured in the form of a reinforced framework structure.
A production system for carrying out a production method as disclosed herein comprises:
An unprocessed component with cavities along the load paths can initially be provided, for example by 3D printing. The material selection between thermoplastic and thermosetting polymers can be made such that an optimized interdiffusion bond to the fibers is possible. Substructures can also be bonded by interdiffusion. It is also conceivable for an unprocessed component with cavities along the load paths to be 3D-printed based on metal, for example titanium, aluminum, steel and the like.
The fiber material is selected and integrated depending on the desired function. By way of example, reinforcing fibers composed of carbon, glass, ceramic and the like are conceivable. The cross-sectional shape of the cavities can also be adapted to the expected load. The cavities can thus be of circular or non-round form. For example, a star-shaped cross section serves for improved protection against buckling. By the method described herein, these different cross sections can be handled in a simpler manner.
The pulling member can be configured in the form of a rod provided with a sliding coating. It is for example possible for impregnated fiber bundles to be attached to the pulling member. A gripper or the like is also conceivable. The pulling-in operation permits a variation of the diameters of the cavities, wherein fiber bundles which are adapted to the cavities are spliced and pulled in. Fiber bundles can thus also be supplied to branches and merging points of cavities.
It is furthermore possible for the movement of the pulling apparatus to be facilitated in that the pulling-in operation is aided in a water bath and/or with ultrasound. Entangled nodes can also be formed at intersection points by piercing the fiber bundles and pulling through a further fiber bundle.
The entire method can be accelerated if the pulling apparatus is guided through all of the cavities. It is thus possible for continuous fibers to be pulled through all of the cavities in a single step.
Finally, the resin can be cured. Superfluous regions can also be removed, for example by a solvent. The component can be created by additive manufacturing, which, in particular, uses different materials simultaneously. Even though the focus is on fiber composite materials, the method described herein can also be utilized for ceramic or metal composite components.
It should be noted that the enumerations serve merely for better reference and do not imply a sequence of the method steps.
Example embodiments are explained in more detail with reference to the attached schematic drawings, in which:
Reference is first made to
The component body 10 contains a second region 14. The second region 14 is produced from a polymer material which cannot be dissolved in the solvent. The second region 14 preferably forms the basic structure of the component body 10 which is intended to be reinforced by fibers.
The component body 10 contains a plurality of tube-like cavities 16. The tube-like cavities 16 each have an end opening 18, by which the cavities 16 are in fluidic connection with the surroundings. The properties of the cavities 16, for instance their profile in the component body 10, their extent or their cross-sectional shape, are ascertained for example on the basis of load simulations.
The cavities 16 can form branches 20, merging points 22 or intersections 24.
In order to produce a fiber-reinforced component 26, the component body 10 is initially provided. This can take place for example by way of additive manufacturing. The first region 12 and the second region 14 can be created for example by way of a fused layer process, for example filament layer manufacturing (FLM).
In a further step, fiber bundles 27 are introduced into the cavities 16. The fiber bundles 27 can be dry or pre-impregnated. For introduction of the fiber bundles 27, a pulling apparatus 28 having at least one pulling member 30 is initially provided. The pulling member 30 is introduced into one of the cavities 16.
The pulling member 30 is created such that it withstands compressive loading. The pulling member 30 is configured for example in the form of a flexible rod or wire. More complex pulling member(s) 30 with grippers or with a controllability similar to an endoscope are also possible.
The fiber bundle 27 is fastened to the pulling member 30 and pulled into the cavity 16. Curable resin 32 is also introduced into the cavity 16. The resin 32 can be introduced by a resin-injecting apparatus (not illustrated in any more detail) or by the pulling apparatus 28. Furthermore, the fiber bundles 27 can also be soaked in the resin 32 such that an additional injection operation can be dispensed with.
The pulling-in of the fiber bundles 27 is preferably effected with application of an ultrasonic field to the component body 10. This can be effected for example in a liquid, which preferably does not dissolve the first polymer material.
The resin 32 is cured in a manner known per se. The first region 12 is also removed by solvent.
The fiber-reinforced component 26 remains.
The pulling member 30 contains a first pulling member 40 and a second pulling member 42. The two pulling members 40, 42 are initially introduced into the common cavity 34 and subsequently divided into the first cavity 36 and the second cavity 38, respectively.
The fiber bundles 27 are designed such that the fiber bundles 27 together fill the common cavity 34 in a desired quantity. The fiber bundles 27 are pulled in by the first and second pulling members 40, 42. Resin 32 is also introduced. The curing is then effected in a customary manner.
The pulling member 30 contains a first pulling member 40 and a second pulling member 42. The two pulling members 40, 42 are introduced in each case into the first cavity 36 and the second cavity 38 and subsequently brought together in the common cavity 34.
The fiber bundles 27 are designed such that the fiber bundles 27 together fill the common cavity 34 in a desired quantity. It is also conceivable for merely one fiber bundle 27 to be used which has been divided into two ends. The fiber bundles 27 are pulled in by the first and second pulling members 40, 42. Resin 32 is also introduced. The curing is then effected in a customary manner.
The pulling member 30 can be introduced successively into the first cavity 36 and the second cavity 38 and can pull in a respective fiber bundle 27. During the introduction of the pulling member 30 into the second cavity 38, the fiber bundle 27 which is already located in the first cavity 36 can be pierced by the pulling member. The fiber bundles 27 then crisscross at this point. Resin 32 is also introduced. The curing is then effected in a customary manner.
The pulling member 30 makes it possible to pull the fiber bundle 27 through the first and second cavities 32, 34 in one step. This procedure is preferably selected for the reinforcement of eyes and the like. The fiber bundle 27 which is not located in the cavity 16 can be cut away before or after the curing operation. Resin 32 is also introduced. The curing is then effected in a customary manner.
Overall, the method described herein can be used to generate components 26 which are more complex than hitherto. In particular, it is possible to manufacture a fiber reinforcement in fewer work steps than hitherto. Configurations which hitherto cannot be produced, or can be produced only with difficulty, are also possible.
In order to improve the range of application of manufacturing methods for fiber-reinforced components 26, and preferably to enable the introduction of fiber bundles into a larger number of geometries, such as branches, merging points and intersections, a production method for producing a component 26 composed of a composite material with a fiber reinforcement which is formed from fiber bundles 27 and resin 32 is proposed. A component body 10 with a plurality of tube-like cavities 16 is initially provided. Curable resin 32 is introduced into the cavities. A pulling apparatus 28 for the fiber bundles 27 is also inserted into at least one of the cavities 16. The pulling apparatus 28 comprises at least one pulling member 30 which is suitable for pulling the fiber bundles 27 and transmitting compressive force. As a result of pulling of the pulling member 30, the fiber bundles 27 are pulled into the cavities 16.
While at least one example embodiment of the present invention(s) is disclosed herein, it should be understood that modifications, substitutions and alternatives may be apparent to one of ordinary skill in the art and can be made without departing from the scope of this disclosure. This disclosure is intended to cover any adaptations or variations of the example embodiment(s). In addition, in this disclosure, the terms “comprise” or “comprising” do not exclude other elements or steps, the terms “a”, “an” or “one” do not exclude a plural number, and the term “or” means either or both. Furthermore, characteristics or steps which have been described may also be used in combination with other characteristics or steps and in any order unless the disclosure or context suggests otherwise. This disclosure hereby incorporates by reference the complete disclosure of any patent or application from which it claims benefit or priority.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2020 109 741.7 | Apr 2020 | DE | national |