Claims
- 1. In a method of producing carbon fibers having high molecular orientation, anisotropy, strength and modulus of elasticity from pitch as the raw material through the process steps of forming the pitch into fibers, subjecting the same to infusibilization, carbonization, and optionally graphitization treatments, the improvement which comprises forming said raw material pitch through the steps of
- (a) heat-treating crude petroleum oil or its fractionated components at a temperature of from 700.degree. C to 2000.degree. C for a period of from 1/1000 to 1/10 second to form resinous pitch or tar,
- (b) subjecting the resinous pitch or tar thus-obtained to heat treating at a temperature of 250.degree. C to 550.degree. C for 1 to 300 minutes while distilling off rather volatile matters, and
- (c) subjecting the thus heat-treated resinous pitch or tar to a second heating at a temperature of 380.degree. to 450.degree. C for 60 to 300 minutes while removing fine solid particles by filtration,
- said raw material pitch thus-obtained having a carbon content in the range of from 95% to 96.5% by weight, a mean molecular weight of from 400 to 2,000, a melt viscosity of from 0.4 to 700 poises at a temperature range of from 320.degree. C to 480.degree. C, and optical anisotropy to such an extent that an isotropic portion thereof can hardly be recognized on examination by a polarization microscope.
- 2. The improvement according to claim 1, wherein in step (a), the crude petroleum oil or its fractionated components is heated at 1800.degree. C for 4/1000 second to obtain a resinous pitch or tar, the resinous tar or pitch is then heated at a temperature and time sufficient to remove volatile components which are distilled off at 380.degree. C/10 mmHg or below under reduced pressure according to step (b) and then heating the pitch to 410.degree. C to eliminate the non-melting components according to step (c).
Priority Claims (1)
Number |
Date |
Country |
Kind |
44-24161 |
Mar 1969 |
JPX |
|
CROSS-REFERENCE TO A RELATED APPLICATION
This application is a continuation-in-part application of Application Ser. No. 564,895, filed Apr. 3, 1975, now U.S. Pat. No. 4,016,247 which is in turn a continuation-in-part application of Application Ser. No. 20,050, filed Mar. 16, 1970 for "Production of Carbon Shaped Articles Having High Anisotropy", now abandoned.