Claims
- 1. A process for producing a fiber reinforced composite consisting essentially of:
- preparing an aqueous slurry which consists essentially of reinforcing fibers selected from the group consisting of glass fibers and carbon fibers uniformly dispersed therein, a latex which is electrically neutral and has no charge, water-soluble organic polymers A as dispersing agents charged in water and particulate organic thermosetting polymers,
- adding thereto water-soluble organic polymers B as flocculating agents charged opposite to said organic polymers A in water to flocculate the aqueous slurry, dewatering and drying the slurry and molding the dried product, said polymers A being present in composite in an amount of 0.1 to 10% by weight, polymers B being added in an amount of 0.1 to 10% by weight, the amount of electrically neutral latex being present in an amount of 0.1 to 10% by weight, the particulate organic thermosetting polymers being present in an amount of 10% to 90% by weight, and the reinforcing fibers are present in an amount of 10 to 90% by weight, all based upon the weight of the composite, wherein said polymers A and B are selected from polymers charged minus in water, and polymers charged plus in water, wherein said polymers charred minus in water are selected from the group consisting of partially hydrolyzed polyacrylamide, poly(sodium acrylate) and partially hydrolyzed polyacrylonitrile, and said polymers charged plus in water are selected from the group consisting of a modified cationic polyacrylamide, a dialkylaminoethyl methacrylate polymer, a vinylimidazoline polymer and a diarylamine polymer.
- 2. The process according to claim 1 wherein said reinforcing fibers have an average length of 0.1 to 50 mm.
- 3. The process according to claim 1 wherein said reinforcing fibers have an aspect ratio of fiber length/fiber diameter of at least 40.
- 4. The process according to claim 1 wherein said polymers A and B have film-forming ability at room temperature or less.
- 5. The process according to claim 1 wherein said particulate organic thermosetting polymers nave a particle size of 10 to 300 micrometer.
- 6. The process according to claim 1 wherein said aqueous slurry further contains an inorganic filler, a pigment, a dye, an ultraviolet stabilizer, an antioxidant, a foaming agent, a defoamer, a bactericide or an electromagnetic wave absorbent.
- 7. The process according to claim 1 wherein the reinforcing fibers are glass fibers.
Priority Claims (2)
Number |
Date |
Country |
Kind |
2-406299 |
Dec 1990 |
JPX |
|
3-058326 |
Feb 1991 |
JPX |
|
Parent Case Info
This application is a continuation-in-part of application Ser. No. 07/954,494, filed Sep. 23, 1992, which in turn is a continuation-in-part of application Ser. No. 07/802,566, filed Dec. 5, 1991, both applications being now abandoned.
US Referenced Citations (2)
Number |
Name |
Date |
Kind |
2786759 |
Feigley |
Mar 1957 |
|
3119731 |
Strole et al. |
Jan 1964 |
|
Foreign Referenced Citations (1)
Number |
Date |
Country |
300909 |
Jan 1989 |
EPX |
Continuation in Parts (2)
|
Number |
Date |
Country |
Parent |
954494 |
Sep 1992 |
|
Parent |
802566 |
Dec 1991 |
|