Patent Application
20160297097
The present invention is generally directed to additive manufacturing processes and specifically to use of low temperature solidification in additive manufacturing.
Additive manufacturing (AM) refers to a process by which digital 3D design data is used to build up a component in layers by depositing material. Additive manufacturing includes 3D printing and other processes described in more detail below. AM is a manufacturing technique which may be distinguished from conventional methods of manufacturing which require material removal. Instead of milling a workpiece from solid block, for example, additive manufacturing builds up components layer by layer using materials which may be provided in fine powder form. A range of different metals, plastics and composite materials may be used in the various additive manufacturing processed discussed herein.
An embodiment is drawn to a method of producing a monolithic body from a porous matrix including using low temperature solidification in an additive manufacturing process.
Another embodiment is drawn to a method of producing a monolithic body from a porous matrix including providing a layer of a porous matrix having interstitial spaces and comprising at least a first reactant, contacting the layer of the porous matrix with an infiltrating medium that carries at least a second reactant, allowing the infiltrating medium to infiltrate at least a portion of the interstitial spaces of the layer of the porous matrix under conditions that promote a reaction between the at least first reactant and the at least second reactant to provide at least a first product allowing the at least first product to form and fill at least a portion of the interstitial spaces of the layer of the porous matrix and repeating the above steps to produce a monolithic body.
Another embodiment is drawn to a method of producing a monolithic body from a porous matrix including providing a plurality of successive layers of a porous matrix having interstitial spaces and comprising at least a first reactant, contacting the plurality of successive layers of the porous matrix with an infiltrating medium that carries at least a second reactant, allowing the infiltrating medium to infiltrate at least a portion of the interstitial spaces of the layer of the porous matrix under conditions that promote a reaction between the at least first reactant and the at least second reactant to provide at least a first product, and allowing the at least first product to form and fill at least a portion of the interstitial spaces of the layer of the porous matrix to form the monolithic body.
Another embodiment is drawn to a method of producing a monolithic body from a porous matrix including providing a first layer of a porous matrix having interstitial spaces and comprising at least a first reactant, contacting the first layer of the porous matrix with an infiltrating medium that carries at least a second reactant, allowing the infiltrating medium to infiltrate at least a portion of the interstitial spaces of the first layer of the porous matrix under conditions that promote a reaction between the at least first reactant and the at least second reactant to provide at least a first product, allowing the at least first product to form and fill at least a portion of the interstitial spaces of the first layer of the porous matrix, providing a plurality of successive layers of the porous matrix over the first layer of the porous matrix, contacting the plurality of successive layers of the porous matrix with the infiltrating medium, allowing the infiltrating medium to infiltrate at least a portion of the interstitial spaces of the successive layers of the porous matrix under conditions that promote a reaction between the at least first reactant and the at least second reactant to provide at least a first product and allowing the at least first product to form and fill at least a portion of the interstitial spaces of the first layer of the porous matrix, thereby producing a monolithic body.
Additive manufacturing methods such as 3D printing, stereolithography, fused-deposition modeling, electron-beam freeform fabrication, direct metal laser sintering, electron-beam melting, selective laser melting, selective heat sintering, selective laser sintering, plaster-based 3D printing, laminated-object manufacturing, digital-light processing, polyjet, and powder bed inkjet printing may be used to make monolithic bodies. These methods are described in more detail in Tables 1 and 2 below, which are reproduced from Tim Hayes, “The future of 3D printing”, Optics & Photonics News, July/August 2013, page 22, and from Wikipedia 3D Printing webpage visited Nov. 6, 2013, respectively. However, several of these methods are only suitable for manufacturing with metals while others are only suitable for manufacturing with polymers. The inventors have discovered that the use of the low temperature solidification processes in additive manufacturing results in methods that are capable of manufacturing monolithic bodies of any type of material including metals, ceramics, cermets, polymers, or composites thereof.
In the low temperature solidification or hydrothermal liquid phase densification process, porous matrix which includes a first reactant (i.e. a material capable of undergoing a chemical reaction) is contacted with an infiltrating medium which includes a second reactant. The first and second reactants react to form a product that fills the pores in the porous matrix. In an embodiment, the porous matrix containing the first reactant is in the form of a powder. In an embodiment, the porous matrix also includes a binder, such as a polymer binder, to agglomerate the powder. Alternatively, the binder may be omitted. In another embodiment, the porous matrix includes a fluid such as water, alcohol or a combination thereof. Alternatively, other non-aqueous fluids may be used. Any suitable matrix and infiltrating materials, such as those disclosed in U.S. Pat. No. 8,313,802 attached herewith as an attachment and hereby incorporated by reference in its entirety. The term low temperature solidification is used as a synonym for the Hydrothermal Liquid Phase Sintering method described in the U.S. Pat. No. 8,313,802.
An embodiment of the method includes producing a monolithic body from a porous matrix using low temperature solidification in an additive manufacturing process. A low temperature may be any temperature less than that usually associated with the sintering of metals and ceramics. Typically, the temperatures may be less than about 500° C., such as less than about 250° C., such as room temperature to 200° C., including 80 to 180° C. The reaction pressure may be less than 100,000 psi, such as 1 to 3 atmospheres.
Another embodiment includes a method of producing a monolithic body from a porous matrix including providing a layer of a porous matrix having interstitial spaces and comprising at least a first reactant, contacting the layer of the porous matrix with an infiltrating medium that carries at least a second reactant, allowing the infiltrating medium to infiltrate at least a portion of the interstitial spaces of the layer of the porous matrix under conditions that promote a reaction between the at least first reactant and the at least second reactant to provide at least a first product, allowing the at least first product to form and fill at least a portion of the interstitial spaces of the layer of the porous matrix and repeating the above steps to produce a monolithic body.
Still another embodiment is drawn to a method of producing a monolithic body from a porous matrix including providing a plurality of successive layers of a porous matrix having interstitial spaces and comprising at least a first reactant, contacting the plurality of successive layers of the porous matrix with an infiltrating medium that carries at least a second reactant, allowing the infiltrating medium to infiltrate at least a portion of the interstitial spaces of the layer of the porous matrix under conditions that promote a reaction between the at least first reactant and the at least second reactant to provide at least a first product and allowing the at least first product to form and fill at least a portion of the interstitial spaces of the layer of the porous matrix to form the monolithic body.
Another embodiment is drawn to a method of producing a monolithic body from a porous matrix, providing a first layer of a porous matrix having interstitial spaces and comprising at least a first reactant, contacting the first layer of the porous matrix with an infiltrating medium that carries at least a second reactant, allowing the infiltrating medium to infiltrate at least a portion of the interstitial spaces of the first layer of the porous matrix under conditions that promote a reaction between the at least first reactant and the at least second reactant to provide at least a first product, allowing the at least first product to form and fill at least a portion of the interstitial spaces of the first layer of the porous matrix, providing a plurality of successive layers of the porous matrix over the first layer of the porous matrix, contacting the plurality of successive layers of the porous matrix with the infiltrating medium, allowing the infiltrating medium to infiltrate at least a portion of the interstitial spaces of the successive layers of the porous matrix under conditions that promote a reaction between the at least first reactant and the at least second reactant to provide at least a first product and allowing the at least first product to form and fill at least a portion of the interstitial spaces of the first layer of the porous matrix, thereby producing a monolithic body.
In any of the above embodiments, each layer of the of the successive layers may be contacted with the infiltrating medium prior to providing the next successive layer. Alternatively, all of the layers of the monolithic body may be first provided and then contacted with the infiltrating medium. Further, in any of the above embodiments, the entire porous matrix is completely or partially infiltrated with the infiltrating medium. In an embodiment, the porous matrix may include a binder material. In an embodiment, the infiltrating medium may react with the binder, resulting in removal of the binder from the porous matrix.
In an embodiment, allowing the at least first product to form and fill at least a portion of the interstitial spaces of the layer of the porous matrix includes heating the layer(s) of the porous matrix. The heat may be applied via conduction, induction, convection or radiation. In an embodiment, the porous matrix includes a precursor for a metal, a ceramic, a cermet, a polymer, or a composite thereof.
In an embodiment, the porous matrix is a green body. That is, the as-deposited porous matrix has not yet been reacted with the infiltrating medium to form the final product phase (e.g., the monolithic body, such as a ceramic, metal, cermet, polymer or composite thereof body).
In an embodiment, the infiltrating medium may include a gas, such as CO2. In an embodiment, the porous matrix is a slurry. The slurry may include water or alcohol or a combination thereof, such as 0-20% alcohol. In an embodiment, the layer(s) of the porous matrix are provided (e.g., formed on a support) with a print head as discussed in more detail below. In an embodiment, the infiltrating medium is provided with a print head as discussed in more detail below.
In an embodiment, low temperature solidification is used to solidify a green body or to remove a binder from the green body in the additive manufacturing process. In an embodiment, the green body comprises a powder based ceramic, metal or cermet material or precursors thereof, deposited from a print head. In an embodiment, low temperature solidification includes providing a basic liquid (e.g., pH>7) to the green body and heating the green body to a temperature below 250 C to remove the binder from the green body. In another embodiment, the low temperature solidification includes providing a fluid to the green body and heating to a temperature below 250 C to solidify the green body into a monolithic solid body. In an embodiment, low temperature solidification is used to both solidify and remove the binder from the green body. In this step, the method includes providing a basic liquid to the green body and heating the green body to a temperature below 250 C to remove the binder from the green body and then solidifying the green body into a monolithic solid body during the same step as the binder removal step, or during a subsequent step with the same or with a different (e.g., neutral or acidic) fluid.
In an embodiment, the monolithic solid body has a size which is within 2% of a size of the green body size. Thus, the low temperature solidification of the green body porous matrix results in essentially no shrinkage in the layer(s) of a porous matrix. That is, the final monolithic body is essentially the same size as the original green body. For example, the shrinkage may be less than 2%, such as less than 1%. This is believed to be due to the lack of movement of the powder particles toward each other in the low temperature solidification process. In contrast, during conventional high temperature sintering, powder particles in the green body move toward each other generating shrinkage. Furthermore, materials which cannot withstand the high temperature sintering or high temperature additive manufacturing may be formed using the combination of low temperature solidification during additive manufacturing.
In another embodiment, the infiltrating fluid includes a gas and a liquid in a partially infiltrated low temperature solidification or the fluid includes a liquid in a fully infiltrated low temperature solidification. Embodiment also include products made by any if the methods discussed above.
Preparation of 3D Printer Ink Slurry
In the first example, 220 g of wollastonite (CaSiO3) powder was dispersed in 210 mL of deionized water and milled using yttria-stabilized zirconia ball media in a rolling jar for 6 hours. The ball media was separated from the resulting suspension. Powder that stuck to the ball media was washed back into the suspension using an additional 100 mL of water. Next, 1.1 g of Darvan 811™ dispersant was added to the suspension and ammonium hydroxide (NH4OH) was added dropwise to the suspension to adjust the suspension's pH to 9. The suspension was then filter-pressed into slurry with 45% solids volume fraction. Then, 1 mL of 1-octanol and 1.2 g of hydroxypropyl methylcellulose was added to the slurry, after which the slurry was shaken using a paint shaker for 30 minutes. Next, 0.5 g of a polyethylenimine (PEI) water-based solution (˜50% PEI by weight) was added to the slurry, after which the slurry was shaken by paint shaker for at least 1 hour. This process yielded approximately 175 mL of ink slurry.
Printing and Carbonation of CaSiO3 Bodies
The CaSiO3-based slurry was then loaded into a modified fused filament fabrication (FFF) delta-form 3D printer.
A CaSiO3 ink slurry was prepared and loaded into a 3D printer similar to the one described in Example 1 above. However, along with a heated deposition bed and filament extruder, the printer had a second nozzle for washing with deionized water and a third head containing an infrared beam emitter for direct localized heating of the spots. In one case, a cone was printed layer-by-layer. The filament extruder (print head) first deposited a 2-mm thick layer of slurry in the pattern of the bottom layer of the cone. This layer was dried at 90° C. in the print chamber for 15 minutes and then carbonated by g-rHLPD using the aforementioned conditions for another 30 minutes. The reaction yield achieved was 80 mol %, equating to a weight gain of 30% and a relative density increase from 64% to 88%. After carbonation, the next 2-mm layer was deposited and the drying/carbonation cycle was repeated. The entire process was repeated 9 times to obtain the cone through layer-by-layer printing.
In another example, a cuboid with 20 mm length, 10 mm width, and 10 mm height was printed voxel-by-voxel. First, a slurry was extruded in the pattern of a corner voxel that was 5 mm long, 5 mm wide and 2 mm thick. The drying/g-rHLPD carbonation cycle described above was performed. The reaction yield achieved was 95 mol %, equating to a weight gain of 36% and a relative density increase from 64% to 92%. The next voxel was subsequently deposited by printing the slurry. The cycle was repeated 39 times to obtain the cuboid.
An anatase-based (TiO2) slurry was prepared and printed into objects using a procedure similar to the one in Example 1. A cylindrical TiO2 monolithic body with a 30 mm diameter, 2 mm thickness and a dry weight of 3.30 g was infiltrated with a solution of 14.20 g of strontium hydroxide octahydrate (Sr(OH)2—8H2O) in 88 mL of water inside a small pressure vessel that is a part of the build-base where the part was printed. The pressure vessel was heated to 95° C. for 144 hours to convert the TiO2 in the object to SrTiO3, thereby solidifying the object by a reactive hydrothermal liquid phase densification (rHLPD) process. The solidified monolithic body was then removed from the vessel for washing and drying. The sample maintained virtually the same dimensions as it had before the rHLPD treatment, but weighed 6.09 g. The weight gain equated to a reaction completion of 65.5 mol % and a relative density increase from 60% to 88%.
An anatase-based (TiO2) slurry was prepared and loaded into a 3D printer similar to the one described in Example 2. However, this printer included an additional print head with a nozzle and a housing for holding a heated reactive solution. All four print heads could move independently of each other.
The filament extruder first deposited a 2-mm thick layer of slurry in the pattern of the first layer of the printed object. The printer bed was heated to quickly dry the printed material at 90° C. for 15 minutes. The second nozzle then deposited 15 mL of a 1 molar solution of Sr(OH)2—8H2O in water onto the printed layer at a rate of 500 μL/min. The solution infiltrated the porous matrix of the deposited material. Both the solution in the housing and the printer bed (print tray) were heated to 95° C. to allow labile reaction of the solution with the deposited layer so as to solidify it. This solidification step was performed for 30 minutes. The reaction completion was 70 mol % and the relative density increased from 60% to 91%. Next, the densified layer was washed free of unreacted strontium and base ions by the DI water nozzle and then dried at 90° C. for 15 minutes. Following this, a 2-mm layer of the object was then deposited following the above process. In another example, an additional cycle of 1 molar solution of Sr(OH)2—8H2O in water was used to further densify the layers prior to the next layer deposition. The entire process was repeated 59 times to produce a cone-shaped monolithic body.
In yet another example, a cuboid with 20 mm length, 10 mm width, and 10 mm height was printed voxel-by-voxel in a process similar to the one described in Example 2. The slurry was extruded in the pattern of a 5 mm length×5 mm wide×2 mm thick corner voxel. The printer bed was heated to dry the printed material for 15 minutes, after which the second nozzle deposited 3 mL of the aforementioned Sr(OH)2—8H2O at a rate of 200 μL/min. The deposited material was allowed to react for 15 minutes with the solution under the conditions described above in this example, after which it was washed and dried for another 15 minutes. The reaction completion was 83 mol % and the relative density increased from 60% to 96%. The next voxel was extruded and the cycle repeated 39 times to produce the full solidified cuboid.
Although the foregoing refers to particular preferred embodiments, it will be understood that the invention is not so limited. It will occur to those of ordinary skill in the art that various modifications may be made to the disclosed embodiments and that such modifications are intended to be within the scope of the invention. All of the publications, patent applications and patents cited herein are incorporated herein by reference in their entirety.
This application claims priority to U.S. Provisional Patent Application No. 61/900,774, filed on Nov. 6, 2013, the entire content of which is incorporated herein by reference.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US14/64269 | 11/6/2014 | WO | 00 |