The present invention relates to the production of silicon hydrides or silanes by acid hydrolysis of silicon alloys or of silicides.
Some silanes and more particularly monosilane or silicon tetrahydride (SiH4) are used as silicon vector in techniques for the deposition of amorphous silicon, of polycrystalline silicon, of nanocrystalline or microcrystalline silicon, also known as nano- or micro-morphous silicon, of silica, of silicon nitride or of another silicon compound, for example in vapor phase deposition techniques.
Depositions as a thin layer of amorphous silicon and monocrystalline silicon obtained from silane make it possible to manufacture solar cells.
It is also possible to obtain coatings resistant to corrosion by acids, by cracking of silane and manufacture of compounds such as silicon carbide.
Finally, the silane is capable of adding to single or multiple bonds of unsaturated hydrocarbons to give organosilanes.
The monosilane market will experience very strong expansion simultaneously in the manufacture of integrated semiconductors and the manufacture of thin-layer or crystalline solar (photovoltaic) cells, semiconductor components and the manufacture of flat screens.
Several types of processes described below have been used to date.
First of all, the reduction of SiCl4 by LiH in a KCl/LiCl bath at temperatures between 450° C. and 550° C. is known. The reaction yield is advantageous but the process is based, on the one hand, on the availability of LiH, whereas lithium resources are very limited, and, on the other hand, on the possibility of recycling the lithium metal by electrolysis. The reaction medium is highly corrosive and employs specific materials. This process has been used to produce small amounts of silane.
The reduction of SiF4 by NAlH4 in organic solvents medium is another example. This process is only viable industrially when there exists SiF4, the byproduct of another chemical production, and sodium to manufacture the sodium aluminum hydride. This process cannot be easily used, in particular for these two reasons.
Another known reaction is the acid attack in a liquid NH3 medium on a stoichiometric SiMg2 alloy. The reaction balance is as follows:
This process is carried out at a temperature close to ambient temperature at atmospheric pressure. This process is not satisfactory because of the difficulty of controlling the process and the use of liquid ammonia, which is subject to strict regulatory control.
Another known reaction is the dismutation of SiHCl3 over boronate resins or other resins. The complete process is thus described:
a) 4SiMetal+12HCl→4SiHCl3+4H2 (temperature between approximately 800° C. and approximately 1100° C.)
b) 4SiHCl3←→SiH4+3SiCl4 (ambient temperature)
i.e. the following reaction balance:
4SiMetal+9HCl→SiH4+3SiHCl3+H2
An alternative form of the above reaction is thus described:
a) 4SiMetal+16HCl→4SiCl4+8H2 (temperature of between approximately 1000° C. and approximately 1100° C.)
b) 4SiCl4+4H2→4SiHCl3+4HCl (temperature of approximately 1000° C.)
4SiHCl3→SiH4+3SiCl4, i.e. the following reaction balance:
4SiMetal+12HCl→SiH4+3SiCl4+4H2.
This process requires high temperatures in an extremely corrosive medium and consumes a great deal of energy (approximately 50 kWh/kg for stage b)). In order to achieve the maximum yield, stage b) requires numerous loops for recirculations of mixtures of chlorosilanes. Apart from the use of extremely corrosive, toxic and inflammable products, processes of such a type are very expensive in energy.
The generation of monosilane and higher silanes has been described in the Gmelin Handbook of Inorganic Chemistry, Si-Silicon, by reacting, in the aqueous phase, silicides and silicon alloys in an acidic or basic medium.
In patent applications EP 1 46 456 and WO2006/041272, a description is given of the synthesis of monosilane in the aqueous phase by dropping an AlxSiyCaz powder, x, y and z representing the respective percentages of aluminum, silicon and calcium, into an HCl solution. The composition of the gases produced was approximately 80% monosilane, 10% disilane and 5% trisilane, along with traces of disiloxane. This type of process exhibits the disadvantage of the handling and storage of pure or highly concentrated HCl. Byproducts resulting from such a reaction are produced in a large amount and are harmful to the environment. Another disadvantage of such a process is the copious formation of a foam in the reaction medium, which reduces the reaction yield and requires the presence of an antifoaming agent. Such a reaction is highly exothermic and temperatures of greater than 100° C. are fairly quickly achieved if the rate of introduction of the alloy powder is not greatly reduced.
None of these studies described above guarantees the conditions necessary for the achievement of a profitable process for industrial development.
A simple process has been found which uses inexpensive starting materials and which produces silicon hydrides with an industrial yield and which does not exhibit all the disadvantages seen above.
One aim of the present invention is to overcome all or some of the disadvantages of the prior art noted above.
To this end, a subject matter of the invention is a process for the preparation of a compound of formula SinH2n+2 in which n is an integer greater than or equal to 1 and less than or equal to 4, comprising a stage b) of reaction of at least one silicide or silicon alloy in the powder form of formula M1xM2ySiz, in which M1 is a reducing metal, M2 is an alkali metal or alkaline earth metal and x, y and z vary from 0 to 1, z being other than 0 and the sum x+y being other than 0, with an aqueous solution comprising CO2, said solution being or not being saturated with CO2 at the temperature and pressure of the reaction.
Preferably, said aqueous solution is saturated with CO2 at the temperature and at the pressure of the reaction.
A solution is saturated when the CO2 introduced can no longer dissolve and forms a deposit.
By way of example, the weight of CO2 which it is appropriate to add to said solution as a function of the temperature, at atmospheric pressure, in order to obtain a solution saturated with CO2, is presented in table 1.
The aqueous solution can comprise an acidic solution comprising an inorganic acid (for example, HCl, H2SO4 or H3PO4) or an organic acid, such as CH3COOH, between 0.1N and 3N, saturated or not saturated with CO2 at the temperature of the reaction.
The reducing metals are, for example, Al, B, Ga or In. The alkali metals are, for example, Li, Na, K or Cs. The alkaline earth metals are, for example, Mg, Ca, Sr or Ba.
Furthermore, embodiments of the invention can comprise one or more of the following characteristics:
The term “higher silanes” is understood to mean disilane, trisilane or tetrasilane.
The alloys or silicides employed in the implementation of the process according to the invention are alloys or silicides which are also used to control the foaming and the deoxygenation of the slags in steel foundries. These are low cost industrial products. One of the advantages of the process which is the subject matter of the invention is that of being able to carry out the reactions under conditions close to ambient conditions (temperature and pressure) in equipment standard in the inorganic chemical industry, such as reactors made of wired glass, for example. The processes employing these alloys or silicides can make it possible to produce the silane in units having small sizes as close as possible to the markets. Whatever the alloys and silicides available and the working and environmental constraints, the same unit can be used by adjusting the operating parameters.
In all cases, the byproducts are reusable inorganic products.
It has also been discovered that the particle size of the alloy powder has an effect on the reaction kinetics and consequently on the reaction yield. The kinetics increase when the size of the particles decreases. The formation of foams during the reaction constitutes the factor limiting the size of the particles. All conditions otherwise being equal, when the size of the particles is divided by 10, the amount of silane produced in the same time is multiplied by approximately 15.
In addition, the process according to the invention exhibits the advantage that, during the hydrolysis reaction, the foaming is greatly reduced and the reaction rate greatly accelerated in comparison with the reactions of the processes of the state of the art described above, which improves the quality of the manufacturing output of the silanes desired.
The process according to the invention also exhibits the advantage that the proportion of monosilane formed with respect to the silanes produced during the reaction is at least equal to 70%, which is important in view of the fact that the silane desired for the applications targeted by the present invention is above all the monosilane.
Furthermore, the use of CO2 as acid for the hydrolysis carried out during the process according to the invention has the advantage, inter alia, that, for a pressure close to atmospheric pressure, the temperature of the reaction is of the same order of magnitude as ambient temperature, this being the case without, however, having to reduce the rate of introduction of the silicon alloy.
Another advantage of the process according to the invention is that the presence of hydrogen for producing precursors of silanes during the synthesis stage is not necessary.
Other distinctive features and advantages will become apparent on reading the following description, made with reference to
The production unit 1 comprises at least three parts comprising a reactor 3, a purification system and a tank 13 for separating by settling and filtering the liquid products.
The hydrolysis reaction for the production of silanes takes place in a reactor 3 equipped with a mixing means 4, such as a close-clearance impeller or a kneader, which makes it possible to mix the solid/liquid mass. The reactor is filled, on the one hand, by means of dip pipes 5 filled with water resulting from a water tank 6 and, on the other hand, with an acidic solution resulting from a system 7 for storage of the acidic solution. Said acidic solution can be CO2 alone or as a mixture with other acids, such as HCl, H2SO4 or H3PO4, for example, the proportions of the mixture being chosen prior to the reaction by the user with the aim of obtaining the best possible yield in view of the problems to be solved identified above. In order to fill the reactor 3 with the water/acid mixture via the pipe 5, the water and the acidic solution are mixed using a mixer 8. The CO2 alone can, for example, be run into the reactor in the liquid form from a liquid CO2 tank. The reactor 3 can, for example, be integral with a lid, removable via the top, attached via U-bolts. Several dip pipes 5 are then also integral with the lid and are positioned so as to touch the wall of the reactor 3. The lid has a leaktight opening which makes it possible to connect a leaktight hopper 9. Preferably, the reactor is surrounded with a heat insulating cladding.
A means 9 for discharge of the silicon alloy is present in the vicinity of the reactor 3. Such a discharge means is, for example, a hopper 9 initially filled with a silicon alloy in the powder form of formula M1xM2ySiz, in which M1 is a reducing metal, M2 is an alkali metal or alkaline earth metal and x, y and z vary from 0 to 1, z being other than 0. For example, the hopper 9 comprises an endless screw and a constricting hose 10, making it possible to isolate the hopper 9 from the reactor 3. The design of the hopper 9 is, for example, similar to the hoppers used to pour calcium carbide into the acetylene reactors. The alloy is conveyed in kegs similar to the kegs used to transport the calcium carbide in acetylene production units. The flow rate for injection of the acidic solution can be controlled by a pH probe 18.
According to a specific embodiment of the invention, two leaktight shutoff valves for gas and for isolation in series comprising, between the two, a side branch which makes it possible to purge the reactor 3 before disconnection are positioned above the lid of the reactor 3. An analogous device 11 equips the outlet at the bottom of the reactor 3 in order to discharge the liquids. The bottom of the reactor 3 is blocked off by means 12, for example a hatch, which prevents the liquid products from stagnating in the bottom channel. This hatch is raised by actuating the bottom valve 11.
The liquids are conveyed to a tank for separating by settling/filtering 13 via a pipe 15.
Air is kept excluded from the reaction region and, at the end of the reaction, the unreacted alloy is neutralized. The reaction region is purged with nitrogen or other inert gases, such as argon, and also all the ancillary parts of this region and the fractionation region (21, 22).
The tank 13 for separating by settling/filtering receives, by pressurizing the reactor 3 under an inert gas, the solution and the products in suspension at the end of the hydrolysis reaction which takes place in the reactor 3. This tank 13 has at least a working volume twice that of the reactor 3. The silanes emitted during the degassing in the tank are conveyed into the purification circuit described in detail below. Said tank 13 comprises, at the bottom of its height, a removable jacket 16 comprising a circular spider supporting a filtering agent 14.
In order to optimize the purification/filtration stage, a water/acid mixture resulting from the mixer 8 can be conveyed via a pipe 19 to the purification/filtration tank 13.
The clear waste solutions resulting from this purification/filtration stage are subsequently conveyed to a storage tank 17. These waste solutions exhibit the advantage of not being harmful to the environment and of being able to be recycled by virtue of the reaction of the process according to the invention.
In order to recover the desired silanes, the products resulting from the hydrolysis which are not conveyed to the tank 13 for separation by settling are directed to a purification system via a pipe 24. Said purification system comprises at least one reflux column 2 which stops the steam resulting from the hydrolysis reaction in the reactor 3. A demister is introduced at the outlet of said reflux column 2, which demister is intended to retain the water droplets which would be entrained in the atmosphere. Two receptacles for drying and neutralizing in parallel 20 are placed downstream of the demister. These two receptacles are filled with sodium aluminate. A fractionation column 21 is then present in order to separate the silanes and siloxanes present and, finally, a double distillation column 22 is used to recover the pure monosilane subsequently used for the desired applications.
Some nonlimiting examples of reaction schemes for reactions carried out according to the process of the invention are related below:
Example1:
AlSiCa+2CO2+5H2O→Al(OH)3+SiH4+Ca(HCO3)2+½H2 (1)
This reaction scheme is not described in the literature. By operating with a saturated CO2 solution, it is possible to dissolve Ca(OH)2 to give soluble calcium hydrogencarbonate, which can be easily converted to reusable calcium carbonate. Likewise, the presence of CO2 tends to destroy the colloidal structure of the aluminum hydroxides and silica. These two factors promote a high reaction rate and a high yield.
Material balance (based on the reaction (1)): by assuming a 60% yield at least of silanes with respect to the silicon present
1 kg silanes (eq. SiH4)
5 kg AlSiCa;
4.85 kg CO2;
4.7 kg H2O; this amount is very low in comparison with the weight necessary for the reactions of the state of the art (several m3);
4.95 kg Al(OH)3;
8.44 kg Ca(HCO3)2→14.74 kg of easily recyclable byproducts;
1.25 kg of colloidal silica;
0.58 m3H2.
This route introduces the advantage of only giving byproducts already existing in nature, of reusing the CO2 emitted furthermore and of resulting in a “cake” of byproducts which can be more easily filtered and is more easily treated by the tank for separation by settling/filtering 13.
In the reaction scheme (1), a rise in temperature promotes the formation of the higher silanes. Thus, the reaction temperature close to ambient temperature by virtue of the use of CO2 promotes the formation of monosilane.
The reaction can be carried out in water at neutral pH but the formation of calcium hydroxide, of colloidal aluminum and of colloidal silica interferes with the reaction as far as rendering the reaction rate very low.
Example2
SiCa2+4CO2+4H2O→SiH4+2Ca(HCO3)2 (2)
The alloy used here is SiCa2 but the result would be similar with the use of SiMg2.
The silicide reacts spontaneously with the water at neutral pH but results in the formation of sparingly soluble Ca(OH)2, reducing the reaction rate.
This reaction scheme is not described in the literature. By operating with a saturated CO2 solution, it is possible to dissolve Ca(OH)2 and thus to render the solution free to access the silicide and destroy the colloidal structure of the silicon hydroxide.
Material balance (based on the reaction (2)): by assuming a 60% yield at least of silanes with respect to the silicon present
1 kg silanes (eq. SiH4)
6.25 kg SiCa2;
10 kg CO2;
3.75 kg H2O; this amount is very low in comparison with the weight necessary for the reactions of the state of the art (several m3);
18.87 kg Ca(HCO3)2;
1.25 kg colloidal silica.
The advantage of this reaction scheme is of giving only colloidal silica as solid byproduct, of using CO2 already emitted moreover and producing dissolved calcium bicarbonate which can be recycled to give calcium carbonate.
An example of a procedure to be followed for the implementation of a process according to the invention can be as described as follows.
At the end of the preceding reaction cycle, the reactor 3 is purged under inert gas, maintained under a slight excess pressure.
The particle size of the alloy is between 0.2 mm and 0.5 mm, giving a density of between 1.5 kg per liter and 2 kg per liter. Preferably, the alloy is introduced into the reactor 3 after the initial acidic solution has been introduced into the reactor 3.
The flow rate is determined by practical experience as a function of the foaming effect.
The amount of alloy is introduced by sequences in order for the level of solution to remain low to promote degassing.
The reaction temperature is kept below 50° C. in order to promote the production of monosilane. The reactor 3 is filled with a volume of acidic solution resulting from the storage system 7 so that the low solution height promotes the degassing of the solution and minimizes the foaming effect. The alloy resulting from the hopper 9 is introduced steadily after having started the stirring of the reactor 3 by the stirrer 4. The injection of acid takes place simultaneously while keeping the pH at the chosen value.
When the CO2 is used as sole acidic reactant, the CO2 is injected directly into the solution and contributes a portion of the negative kilocalories necessary for the cooling of the reaction medium.
At the end of the sequence, the reactor 3 is kept stirred for a few minutes and then the liquid present in the reactor 3 is conveyed to the tank for separating by settling/filtering 13.
After each sequence, the solution and the products in suspension are transferred by gravity and slight excess pressure into the tank for separating by settling/filtering 13 stirred by virtue of the means 16. The solution is kept in the stirred tank 13 for a few minutes in order to complete the degassing and then the bottom valve 23 of the tank 13 is opened to start the filtration. The solution flows through the filtering agent 14. The solution comprises, according to the acid used, either Ca(HCO3)2, giving calcium carbonate by evaporation of the water, or CaCl2.6H2O, which can be recycled in the chemical or pharmaceutical field. The cake obtained on the filtering agent 14 is subsequently extracted from the tank 13. This cake comprises either alumina and silica, which gives a clay by calcination, or silica, which can be converted into silica gel.
In order to specify the orders of magnitudes, the conditions of a production unit 1 and the complete material balance are given below for the production of 100 T/year of monosilane using CO2 as acidic reactant.
In the table which follows, 1 T=1000 kg.
Whatever the silicide or alloy selected, the general conditions prevail:
Generally, the process according to the invention exhibits the following advantages in comparison with the processes of the state of the art described above:
Number | Date | Country | Kind |
---|---|---|---|
0853321 | May 2008 | FR | national |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/FR09/50734 | 4/21/2009 | WO | 00 | 11/22/2010 |