Patent Application
20110098941
1. Field of Invention
The present invention relates to the detection of cracks and incomplete fusions in pipeline welds and, more particularly, to a screening process which utilizes pattern recognition to identify the location of cracks and incomplete fusions along a welded pipeline using transverse magnetic flux technology.
2. Description of Related Art
Pipelines with welded longitudinal-seams have experienced in-service failures due to incomplete fusion and hook cracks. These issues are well known, well understood, and have been serious considerations of pipeline integrity management groups throughout the industry for a number of years. They have also been one of the focus elements of the regulatory agencies responsible for assuring that pipeline operators are assessing all threats to the integrity of their pipelines.
In normal analysis processes utilizing transverse flux technology, detection processes have been primarily focused on the identification and quantification of volumetric metal loss anomalies along a pipeline. These algorithms utilize the amount of flux leakage detected, the length of anomaly and width of anomaly (number of channels) to determine depth. When a “metal-loss” sizing algorithm is applied to narrow axial anomalies, the resulting predicted depth can be considerably shallower than the actual depth. Because there are a limited number of channels affected by the anomalies, the calculated depth is low and most often below a minimum reporting threshold. This results in a non-reported anomaly, which could lead to pipeline failures, As such, recognized by Applicants is the need for a new identification process that overcomes such limitations.
In view of the foregoing, embodiments of the present invention provide a new identification process developed through utilization of transverse flux inspection technology taken to a new level of sophistication with a disciplined methodical evaluation of anomaly signals. Particularly, embodiments of the present invention provide supplemental screening processes applied to pipeline survey data, which utilize a transverse magnetic flux leakage method and pattern recognition to identify potential longitudinal-seam anomalies in welded pipe, specifically focusing on the detection of incomplete fusion and hook cracks for example. The screening process of embodiments of the present invention does not affect or change how the survey data is recorded in the in-line inspection (“ILI”) survey tools; only how it is analyzed after the survey data is completed. The flux leakage method is primarily influenced by anomaly air gap, which is a function of anomaly length and depth, steel properties, and hoop stress. Embodiments of the present invention, for example, can be used to screen for very narrow axial crack-like anomalies in the pipeline longitudinal welds, and may also be used to estimate the length of such anomalies. Embodiments of the present invention also produce a characterization and anomaly evaluation list based on their relative signal characteristics.
Embodiments of the present invention, for example, specifically identify electric resistance weld (“ERW”) anomalies using a pattern recognition process. The application of this process can be sensitive to the pipeline steel properties, the capabilities of the specific ILI tool employed, and the pipeline operating conditions under which the survey was run. Thus, when applying embodiments of the present invention to other conditions, each variable can be considered for application specific adjustment if desired.
Embodiments of systems, program pr oduct, and methods of the present invention, as applied to this complex anomaly discrimination, preferably requires confirmation and validation of the process applicability in each case. The confirmation will minimally consist of several validation excavations utilizing “highest level” non-destructive evaluation (“NDE”) methods and, in some cases, will require removal of appropriate samples for destructive metallurgical evaluation in a laboratory.
Embodiments of the present invention also are designed to identify certain potentially injurious anomalies such as hook cracks and incomplete fusion in, and immediately adjacent to, the longitudinal weld in pipeline. An embodiment of a method of process, for example, should begin by determining the critical flaw dimensions to be used to determine the maximum length of an anomaly in the magnetic flux leakage data that will be considered during the review of a linear anomaly using conventional critical flaw analysis equations. Examples of such equations include, but are not limited to, engineering based calculations such as Corlas and Keifner. Prior to the review beginning, the data then should be reviewed to determine C-Scan (a 3-D color contour plot utilizing a few of the pipeline from a top plane view) and A-Scan (plot of trace signals from individual magnetic flux sensors) display settings for optimum identification of linear anomalies. The data then can be visually or electronically scanned, joint by joint, along the weld utilizing the C-Scan display to identify signal patterns generally consistent with longitudinal-seam anomalies. This, for example, can be defined as a level one (or Level 1) candidate screen.
Once the data pattern is deemed to be a level one (or Level 1) candidate anomaly, an embodiment of the method or process utilizes one or more saved C-Scan display settings as previously established and zooms (or enlarges a visual display) as necessary to analyze anomalies identified for pattern confirmation. This, for example, can be defined as a level two (or Level 2) candidate screen. If the pattern is deemed to be a level two candidate anomaly, an embodiment of a method or process then goes on to determine the approximate length of the anomaly and compare it to the maximum allowed for classification in this pipeline section, assuring that it does not exceed critical length. This, for example, can be defined as a level three (or Level 3) candidate screen. If the anomaly is determined to be below the critical flaw length, it qualifies as a level 3 candidate and can be documented in a table, chart, or summary spreadsheet, for example.
Note, the critical flaw length for each pipeline segment under review can be selected according to standard calculations considering actual pipeline operating conditions and pipeline material properties, to establish the maximum length of anomalies for consideration as potential axial crack-like defects located within the weld. That is, for a pipeline operating, for example, at pressures substantially less than standard, an equivalent critical length can be established using actual operating conditions. Beneficially, such selection aids in differentiating the crack-like defects from trim issues. Beneficially, such selection aids in differentiating the crack-like defects from trim issues.
If the pattern is deemed to be a level three candidate anomaly, an embodiment of a method goes on to analyze the anomaly using an A-Scan display, zoom as necessary and manipulate the gain to enhance the signal pattern. This, for example, can be defined as a level four (or Level 4) candidate screen. If the pattern is deemed to be a level four candidate anomaly, a table, chart, or summary spreadsheet, for example, of the results is generated for further analysis and final confirmation. This, for example, can be defined as a level five (or level 5) candidate screen. Thereafter, embodiment of the present invention generates a validation dig list for a representative sample of all confirmed level five Candidates for excavation, extensive NDE analysis, and possible removal for laboratory analysis. In view of the foregoing, embodiments of the present invention provide a screening processes developed which utilize transverse magnetic flux technology to a new level of sophistication and detail.
The patent or application file contains at least one drawing executed in color. Copies of this patent or patent application publication with color drawing(s) will be provided by the Office upon request and payment of the necessary fee. Some of the features and benefits of the present invention having been stated, others will become apparent as the description proceeds when taken in conjunction with the accompanying drawings, in which:
a is a flow chart illustrating a method for detecting longitudinal-seam anomalies according to an embodiment of the present invention;
b is a perspective view of a C-Scan computer display showing the magnetic flux leakage data according to an embodiment of the present invention—the x-axis corresponds to length and the y-axis corresponds to o'clock position;
c-2f are perspective views of a display of a computer showing the optimal display settings used to detect longitudinal-seam anomalies according to an embodiment of the present invention;
The present invention will now be described more fully hereinafter with reference to the accompanying drawings in which embodiments of the invention are shown. This invention may, however, be embodied in many different forms and should not be construed as limited to the illustrated embodiments set forth herein; rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art. Like numbers refer to like elements throughout.
An embodiment of the present invention, for example, can include a supplemental screening process applied to survey data utilizing display software such as, for example, the Rosen Rosoft Display Software manufactured by the ROSEN Swiss AG of Stans, Switzerland (such as, for example, versions 6.60), to identify potential longitudinal-seam anomalies in welded pipelines, specifically focusing on the issues of incomplete fusion and hook cracks. Although the present disclosure describes the present invention in conjunction with the Rosoft Display Software only, other forms of display software can be utilized as well as understood by those skilled in the art.
An embodiment of a method of the present invention, such as shown in
At step 105, the processor will begin analyzing the T-MFL data based upon its respective signal characteristics and critical flaw dimensions, both of which are used to determine whether the data represents a potential crack-like defect in the, pipeline weld. The critical flaw dimensions are a maximum length of an anomaly, which is represented by the T-MFL data being displayed on the display, to be considered as a potential crack-like defect in the weld.
The determination of the critical flaw dimensions will now be discussed. As stated above, embodiments of the present invention can focus on the characterization of signals that may prove to be injurious crack-like defects in a longitudinal weld. The transverse magnetic flux leakage (“T-MFL”) inspection produces anomaly signatures from crack-like defects and from trim issues that can sometimes have very similar signal patterns. Critical flaw sizes for anomalies are determine for each pipeline segment under review using industry standard calculations considering actual pipeline operating conditions and pipeline steel material properties. Anomaly signals that have lengths substantially longer than the critical size are generally considered the result of non-injurious metal edges associated with trimming of the long seam. The industry standard calculations, for example, can establish the maximum length of anomalies for consideration as potential narrow axial crack-like defects located within a weld and can be used to filter out long anomalies that would have failed due to hoop stress, for example.
More specifically, or example, a conservative minimum detection limit for the transverse T-MFL tool is approximately 2″ long and 60% wall thickness penetration. For example, as understood by those skilled in the art, anomalies with lengths greater than 150% of the calculated critical length (for a 60% through-wall flaw) may not be considered as potential defects since they would have failed previously under normal pipeline operating conditions at or near 72% of its specific minimum yield strength (“SMYS”). As understood by those skilled in the art, these percentages or lengths can be adjusted or varied by an operator/user or by a program controller to obtain any desired result. In the event that the pipeline is operating at pressures substantially less than 72% of SMYS, an equivalent critical length can be established as discussed above using actual operating conditions. The value supplied for length determination during the analysis screening process is 150% of the calculated critical length with no changes to the value being necessary. Other references to the “critical length” in this disclosure, by way of example, are the 150% value. Other values, however, may be used according to desired parameters.
Once the T-MFL data has been analyzed by the appropriate ILI vendor and a summary report/spreadsheet generated, a separate secondary analysis can be performed based on the signal characteristics and critical flaw dimensions to thereby develop a list of potential anomalies (step 107). Such an output can typically be a summary spreadsheet, associated screen captures and dig location sheets. Thereafter the process may end or be refined after having been excavated and evaluated as another step in the validation process (step 109).
Another embodiment of the present invention (see e.g.
When determining the optimal display parameters (step 205), the analyst selects various locations throughout the survey to determine one or more C-Scan and A-Scan display settings for optimum identification of linear ERW anomalies. One or more settings may be required for each wall thickness present in the pipeline. In doing so, the analyst can adjust the T-MFL display contrast and color intensity until there is a high contrast between the weld line within the T-MFL data 32 and the surrounding display background. For example, as illustrated in
Different pipelines, for example, may require unique software or program product display values due to differences in magnetic characteristics and due to diameter, wall thickness, grade, and tool speed during the actual inspection. The display software utilized as part of embodiments of the present invention, for example, can have an icon, button, know or other user interface on the display that, when clicked or operated, automatically sets the display values for optimum contrast. The processor then analyzes all the displayed data and responsively adjusts the values. This responsive setting, however, produces varying results depending on the amount of data displayed on the screen (i.e., how long a section of pipe and how much of the pipe circumference is displayed).
As illustrated at step 205 of
Embodiments of the present invention also allow the length of pipeline data displayed (as T-MFL data 32) to be set. As illustrated in
In step 205 of
In step 207 of
At step 207, for example, the C-Scan scrolling process is used to look for a, e.g., red anomaly pattern with a yellow transition ring centered and contained within the green weld of display 30. In a preferred configuration, the background of the display will be colored green to blue in order to further magnify the contrasting nature of the display. Please note, however, that any color pallet may be utilized according to embodiments of the present invention. These contrasting anomalies are considered to be level one candidates.
If the anomaly fails to meet the characteristics of this first anomaly level, the anomaly will be ignored and the process will continue collecting data at step 201 of
As illustrated in
If the anomaly fails to meet the characteristics of this second anomaly level, the anomaly will be ignored and the process will continue collecting data (step 201 of
When a level two candidate is found, the scrolling process can be stopped and the anomaly evaluated in greater detail. The zoom function can be used as necessary to evaluate the anomaly signal characteristics.
After review of the level two candidate is complete, the level two candidate is analyzed to determine if it qualifies as a level three candidate anomaly (step 211). If the anomaly length is less than the critical flaw length discussed previously, the anomaly qualifies as a level three candidate. As illustrated in
If, however, the anomaly does meet the characteristics of the third anomaly level, the anomaly will be further analyzed (step 213) to determine if the anomaly is consistent with a level four candidate anomaly. To determine if the pattern is a level four candidate, the anomaly is reviewed using the A-Scan display, zooming as necessary and manipulating the gain to increase the amplitude of the signal.
If the anomaly meets the above criteria, for example, it becomes a level four candidate. The appropriate information is entered into a summary spreadsheet for further review and final confirmation. The information is included in a table, chart, or spreadsheet, such as, for example, an Excel Spreadsheet that lists: (1) joint number containing the anomaly (U/S girth weld number); (2) absolute distance to U/S girth weld; (3) absolute surrey distance to the anomaly; (4) o'clock position of the weld; and (5) classification categories to be one of the following: (a) “A”—anomaly signal exhibits all of the subject characteristics, (b) “B”—anomaly signal exhibits some of the subject characteristics, but there is a question about its validity as an anomaly, (c) “C”—anomaly signal exhibits only a few of the subject characteristics but there are indications. that it potentially could be an anomaly for consideration for other stated reasons or (d) “D”—anomalies that were excluded from the process. The reasons for the exclusion can be noted in a documentation spreadsheet; for example longer than determined critical length. The summary spread sheet may also include the length of the potential anomaly, any descriptions or comments and reasons why anomalies were included/excluded from anomaly conclusion. Once the anomaly is included or excluded the display is returned to the C-Scan view and the scrolling continued.
It is important to remain informed of anomalies that fall into “B” or “C” categories so the process can be refined to only include “A” anomaly signals and a limited number of the other categories in the final report. Moreover, for each “A”, “B”, or “C” anomaly reported, the analyst may provide screen captures as follows, having all screen captures in PEG image format, for example, (hard copy in a book plus electronic copy on DVD):
1. Full Screen of C-Scan in optimum display mode with display set to 20 feet, 3 hours, and with centered. Include a girth weld if possible.
2. Full Screen of C-Scan in optimum display mode with display set to 5 feet, 1 hour, and with centered. Measurement Display is on and properly positioned to show measured length legibly.
3. Full Screen of A-Scan in optimum display mode with display set to 20 feet, 3 hours, and with centered. Gain should be increased until “noise” comes up equally with “signal” as gain is increased. Include a girth weld if possible.
4. Full Screen of A-Scan in optimum display mode with display set to 5 feet, as little circumference as possible, and with centered. Gain should be increased until “noise” comes up equally with “signal” as gain is increased.
Once the “A”, “B”, or “C” anomalies have been reviewed and confirmed, a complete dig sheet package can be generated utilizing embodiments of program product, e.g., software, if required to validate the callouts and develop an excavationlrepair program. This listing can include a listing of each anomaly based upon the presence of the signal characteristics corresponding to Level four anomalies (i.e., “A”, “B”, “C” or “D” level anomalies).
Upon confirmation (step 215), embodiments of program product can create a list of all level five candidates (step 217). In other words, after Levels one thru four have excluded the non-qualifying anomalies, those remaining are considered Level five anomalies. All level five candidates can be investigated further by exposing the pipe and performing a complete NDE examination. As such, from time to time it may become necessary to remove certain defects from the pipeline for additional and sometimes destructive metallurgical testing.
The present invention has numerous advantages. The T-MFL screening process of the present invention can locate anomalies, such as cracks, in pipelines that otherwise go undetected by existing methods. If left undetected, these cracks would typically fail in “rupture mode,” thereby leading to large volumes of contamination in the surrounding area and is hereby incorporated by reference in its entirety.
This application is a divisional and claims priority and benefit to U.S. Ser. No. 12/270,432, filed on Nov. 13, 2008 which claims priority and benefit to U.S. Provisional Application Ser. No. 61/008,822, filed Dec. 21, 2007 and is hereby incorporated by reference in its entirety.
It is to be understood by those skilled in the art that the invention is not limited to the exact details of construction, operation, exact materials, or embodiments shown and described, as modifications and equivalents will be apparent to one skilled in the art. For example, although discussed as steps in a computerized process, steps of the present invention may also be accomplished manually. In addition, although aspects of the present invention have been described with respect to a computer, a computer device, a computer system, or processor executing program product or software that directs the functions of embodiments of the present invention, it should be understood by those skilled in the art that the present invention can be implemented as a program product for use with various types of data processing systems as well. Programs defining the functions of embodiments of the present invention, for example, can be delivered to a data processing system via a variety of signal-bearing media, which include, without limitation, non-rewritable storage media (e.g., CD-ROM, DVD-ROM), rewritable storage media (e.g., floppy disks, hard drive disks, CD-R, or rewritable ROM media), and communication media, such as digital and analog networks. It should be understood, therefore, that such signal-bearing media, when carrying or embodying computer readable instructions that direct the functions of embodiments of the present invention, represent alternative embodiments of the present invention. In the drawings and specification, there have been disclosed illustrative embodiments of the invention and, although specific terms are employed, they are used in a generic and descriptive sense only and not for the purpose of limitation. Accordingly, the invention is therefore to be limited only by the scope of the appended claims.
This application is a divisional and claims priority and benefit to U.S. Ser. No. 12/270,432, filed on Nov. 13, 2008 which claims priority and benefit to U.S. Provisional Application Ser. No. 61/008,822, filed Dec. 21, 2007 and is hereby incorporated by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 61008822 | Dec 2007 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12270432 | Nov 2008 | US |
| Child | 12949896 | US |