The present invention is directed toward a series of propane diol polyesters with tunable ascetics and performance in cosmetic formulation. These novel propane diol polyesters are designed to have tunable aesthetics. The physical and chemical properties of the current invention can be tuned rapidly by controlling the fatty group used, as well as the molecular weight of the polymer. Tuned here is meant the ability to adjust the physical properties to a desired value. The resulting propane diol polyesters have outstanding aesthetics and physical properties.
Propane diol is a common material of natural origin. The structure is:
CAS Registry Number: 504-63-2 Index Name: Propane-1,3-diol.
Propane diol is made from corn syrup effected by a genetically modified strain of E. Coli developed by DuPont Tate & Lyle Bioproducts. Propane diol is mainly used in the production of polymers such as polytrimethylene terephthalate, and formulated into a variety of industrial products including adhesives, laminates, coatings, aliphatic polyesters and moldings. Polymers synthesized with propane diol are made in a variety of ways.
The current invention is directed toward a series of propane diol polyesters that are synthesized by the reaction of a diacid and propane diol end-capped with a mono-functional fatty alcohol. This end capping allows for the product to have great film forming ability and great aesthetics.
The present invention is related to a series of novel propane diol polyesters that are prepared by the reaction of propane diol, diacid and a mono-functional fatty alcohol. The mono-functional fatty alcohol has a duel purpose in this polymerization: mono-functional monomers are commonly used to control the molecular weight of the polymer chain and are often referred to as a chain terminator. Once the chain terminator reacts onto the polymer backbone, the polymerization ceases. Chain terminators, being mono-functional, always end up on the end of the polymer chain. For this reason, the selection of the fatty groups and the diacid will drastically change the physical properties and cosmetic aesthetics of the resulting material.
The compounds of the present invention are made by the polymerization of a diacid and propane diol and a fatty alcohol. The resulting polymer has the film forming ability of the propane diol polymer but the end capping by the mono-functional fatty alcohol. This combination of groups results in a high efficient deposition of the skin, hair and fibers.
These propane diol polyesters have the ability to tune the overall aesthetics of a formulation based on the alcohol and diacid used. This ability to tune the aesthetics is easily demonstrated when considering an example. Two propane diol polyesters with different alcohols (Region 1) were used. Dimer acid was utilized as the diacid. When considering the structure of the finished polymer, it is easy to see two distinct regions: Region 1 and Region 2. Below is the structure of the finished polymer.
Polymer A was synthesized with a Guerbet alcohol containing 20 carbons, dimer acid and 1,3-propanediol. Region 1 in this example is a liquid that contains a dry feel on the skin. Region 2 is an amorphous polymer backbone that feels tacky on the skin and has limited solubility in polar esters. The finished polymer A is a transparent high viscosity liquid. In cosmetic formulation, this polymer gives a dry feel and provides a transfer restraint gloss. Polymer b was synthesized utilizing a linear fatty alcohol with 18 carbons, dimer acid and 1,3-propanediol. Region 1 in this polymer is a solid and feels waxy on the skin. Region 2 is an amorphous polymer backbone. The finished polymer is an opaque solid. It has very limited to no solubility in polar esters and in formulation gives a wax feel on the skin. While these two polymer (a & b) are very similar, they have very different physical properties and aesthetics.
The present invention is aimed at a series of novel polyester derived from propane diol that provide desired esthetics and structure in cosmetic formulations.
Propane Diol Polyester
A propane diol polyester having the following structure:
wherein,
R1 is an alkyl containing 8 to 26 carbons, or mixtures thereof;
R2 is independently selected from an alkyl containing 2 to 12 carbons, alkyl having the following structure:
or mixtures thereof;
n is an integer ranging from 3 to 10.
Another aspect of the present invention is a process for conditioning skin, which comprises contacting the skin with an effective conditioning amount of a propane diol polyester having the following structure:
wherein,
R1 is an alkyl containing 8 to 26 carbons, or mixtures thereof;
R2 is independently selected from an alkyl containing 2 to 12 carbons, or an alkyl having the following structure:
and mixtures thereof.
said effective conditioning concentration ranges from 0.1% to 25% by weight.
In a preferred embodiment R1 is a branched alkyl containing 20 carbons.
In a more preferred embodiment R2 is dimer acid.
In a more preferred embodiment R2 is an alkyl having 18 carbons.
In a more preferred embodiment R1 is a branched alkyl having 28 carbons.
In a more preferred embodiment R1 is a branched alkyl having 32 carbons.
In a more preferred embodiment n is 5.
In a more preferred embodiment n is 10.
Raw Materials
Fatty Alcohols
Fatty alcohols are useful in the practice of the present invention are items of commerce they are available as either single components or mixtures.
Fatty alcohols are useful as raw materials in the preparation of compounds of the present invention are commercially available from a variety of sources including Procter and Gamble of Cincinnati Ohio.
The structures are well known to those skilled in the art.
C8H18
Propane diol is useful as raw materials in the preparation of compounds of the present invention. Propane diol is commercially available from DuPont Tate Lyle of Bloomington, Del.
The structures are well known to those skilled in the art.
Dimer acid is an item of commerce available commercially from Cognis Corporation. It conforms to the following structure:
Hydrogenated dimer acid is an item of commerce available commercially from Henkel Corporation. It conforms to the following structure:
Dicarboxylic Acid
Dicarboxylic acid useful as raw materials in the synthesis of the compounds of the present invention are commercially available from a variety of sources including Cognis. They conform to the following structure;
wherein;
c is an integer ranging from 1 to 10.
Guerbet Alcohols
Guerbet alcohols useful as raw materials in the preparation of compounds of the present invention are commercially available from a variety of sources including Sasol North America Incorporated of Houston Tex., and Jarchem located in Newark N.J.
The structures are well known to those skilled in the art.
y is an integer ranging from 3-15 and x is an integer ranging from 5-17.
General Procedure
A specified number of grams propane diol (example 14) is added to a specified amount of Guerbet alcohol (examples 27-29) and a diacid (examples 15-26). The reaction mixture is heated to 160-180° C. Water is removed by vacuum during the reaction process. The reaction is monitored by the determination of acid value. The acid value will diminish as the reaction proceeds. The reaction is cooled once the acid value fails to change over an additional two hours at elevated temperature. The product is used without purification.
The compounds of the present invention are oily materials that provide conditioning to skin. They retard transepidermal water loss, and provide a water resistant barrier on the skin. In emulsions, they provide a water resistance holding actives on the skin. The actives include sunscreen actives, antioxidants, peptides and vitamins.
While the illustrative embodiments of the invention have been described with particularity, it will be understood that various other modifications will be apparent to and can be readily made by those skilled in the art without departing from the spirit and scope of the invention. Accordingly, it is not intended that the scope of the claims appended hereto be limited to the examples and descriptions set forth hereinabove but rather that the claims be construed as encompassing all the features of patentable novelty which reside in the present invention, including all features which would be treated as equivalents thereof by those skilled in the art to which the invention pertains.
This application is a divisional patent application of Ser. No. 13/986,020 filed Mar. 25, 2013, which in turn claims priority to and benefit of U.S. Provisional Application No. 61/689,981 filed Jun. 18, 2012, the disclosure of which is incorporated herein for all purposes.
| Number | Name | Date | Kind |
|---|---|---|---|
| 8148569 | O'Lenick | Apr 2012 | B1 |
| 8912233 | O'Lenick | Dec 2014 | B1 |
| Number | Date | Country | |
|---|---|---|---|
| 61689981 | Jun 2012 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13986020 | Mar 2013 | US |
| Child | 14121740 | US |