Claims
- 1. A propylene polymer composition comprising:
- (A) a propylene polymer in an amount of 10 to 90% by weight, said polymer having the following properties:
- (1) the melt flow rate, as measured at 230.degree. C. under a load of 2.16 kg, is in the range of 0.001 to 8 g/10 min,
- (2) the temperature at the maximum peak position of an endothermic curve of said polymer measured by a differential scanning calorimeter is in the range of 95 to 145.degree. C.,
- (3) the density is in the range of 885 to 905 kg/m.sup.3, and
- (4) the content of constituent units derived from an .alpha.-olefin of 4 to 20 carbon atoms is in the range of 1.5 to 11% by mol; and
- (B) a propylene polymer in an amount of 90 to 10% by weight, said polymer having the following properties:
- (1) the melt flow rate, as measured at 230.degree. C. under a load of 2.16 kg, is in the range of 0.1 to 600 g/10 min,
- (2) the temperature at the maximum peak position of an endothermic curve of said polymer measured by a differential scanning calorimeter is in the range of 145 to 170.degree. C.,
- (3) the density is in the range of 905 to 916 kg/m.sup.3, and
- (4) the content of constituent units derived from an .alpha.-olefin of 4 to 20 carbon atoms is in the range of 0 to 2% by mol;
- wherein (1) the melt flow rate (MFR.sub.A (g/10 min)) of the propylene polymer (A) and the melt flow rate (MFR.sub.B (g/10 min)) of the propylene polymer (B) satisfy the following relation
- 0.1.ltoreq.log (MFR.sub.B /MFR.sub.A).ltoreq.6.1,
- and
- (2) the density (d.sub.A (kg/m.sup.3)) of the propylene polymer (A) and the density (d.sub.B (kg/m.sup.3)) of the propylene polymer (B) satisfy the following relation
- 2.ltoreq.d.sub.B -d.sub.A .ltoreq.31.
- 2. The propylene polymer composition as claimed in claim 1, which has the following properties:
- (1) the melt flow rate, as measured at 230.degree. C. under a load of 2.16 kg, is in the range of 0.005 to 2.0 g/10 min,
- (2) the temperature at the maximum peak position of an endothermic curve of said composition measured by a differential scanning calorimeter is in the range of 128 to 157.degree. C.,
- (3) the density is in the range of 899 to 911 kg/m.sup.3, and
- (4) the flexural modulus of a pressed sheet specimen prepared from said composition at 200.degree. C. is in the range of 800 to 1,900 MPa.
- 3. The propylene polymer composition as claimed in claim 1, which has the following properties:
- (1) the melt flow rate, as measured at 230.degree. C. under a load of 2.16 kg, is in the range of 4 to 25 g/10 min,
- (2) the temperature at the maximum peak position of an endothermic curve of said composition measured by a differential scanning calorimeter is in the range of 128 to 157.degree. C.,
- (3) the density is in the range of 899 to 911 kg/m.sup.3, and
- (4) the flexural modulus of a pressed sheet specimen prepared from said composition at 200.degree. C. is in the range of 800 to 1,900 MPa.
- 4. The propylene polymer composition as claimed in any one of claims 1 to 3, wherein the propylene polymer (A) and the propylene polymer (B) are prepared by the use of a metallocene catalyst.
- 5. A heat molded product obtained by heat molding the propylene polymer composition as claimed in claim 1.
- 6. A pipe obtained by heat molding the propylene polymer composition as claimed in claim 2.
- 7. A film obtained by heat molding the propylene polymer composition as claimed in claim 3.
Priority Claims (1)
Number |
Date |
Country |
Kind |
9-2347 |
Jan 1997 |
JPX |
|
Parent Case Info
This application is the national phase under 35 U.S.C. .sctn.371 of prior PCT International Application No. PCT/JP98/00054 which has an International filing date of Jan. 09, 1998 which designated the United States of America, the entire contents of which are hereby incorporated by reference.
PCT Information
Filing Document |
Filing Date |
Country |
Kind |
102e Date |
371c Date |
PCT/JP98/00054 |
1/9/1998 |
|
|
9/1/1998 |
9/1/1998 |
Publishing Document |
Publishing Date |
Country |
Kind |
WO98/30629 |
7/16/1998 |
|
|
US Referenced Citations (2)
Number |
Name |
Date |
Kind |
4487871 |
Ishibashi |
Dec 1984 |
|
5358792 |
Mehta |
Oct 1994 |
|
Foreign Referenced Citations (6)
Number |
Date |
Country |
0316692 |
May 1989 |
EPX |
0646624 |
Apr 1995 |
EPX |
7-173317 |
Jul 1995 |
JPX |
9-302163 |
Nov 1997 |
JPX |
9416009 |
Jul 1994 |
WOX |
9907788 |
Feb 1999 |
WOX |