Prosthesis with highly convoluted surface

Abstract
A technique for producing a highly convoluted surface on a prosthetic device is achieved by applying a layer of aspherical metallic powder on the surface of the device. The metallic powder, which may be the same as or different from the material of the device, is applied in a thickness of up to approximately 200 microns and has a size range of approximately -80 to +635 mesh so as to result in a surface roughness defined by a peak to valley variation of up to approximately 200 microns. A resulting device has an enhanced surface which provides, alternatively, an improved press fit into a receiving bone, or improved cement fixation, or improved reception of a ceramic coating.
Description

BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a technique for producing a highly convoluted surface on a prosthetic device. Throughout the specification, the terms "aspherical" and "non-spherical" are used interchangeably and are intended to mean other than the spherical form.
2. Description of the Prior Art
There are a number of design criteria which have long been sought for the ideal segmental bone replacement implant. Three of these criteria are foremost: (1) the implant should last the lifetime of the patient without loss of function or initiating any adverse process response; (2) the implant should be designed to restore the normal function of the bone in which it is implanted; and (3) the implant must be producible on a commercial scale. To satisfy the foregoing criteria, it is necessary not only that the implant support the imposed load, often of a fluctuating nature, but also that the interface between the implant and the bone withstand the load requirement. This must be achieved on a regular and continuing basis.
A plastic cement such as polymethyl methacrylate is often used to affix the implant to the bone as well as to improve the fit between the implant and the bone. In another instance, prosthetic devices have been provided with porous coatings which fittingly mate with the bone and invite bone ingrowth such that, after a period of time, the prosthesis becomes integrated into the bone structure. Typical of such coatings are the disclosures in Philliar U.S. Pat. Nos. 3,855,638 and 4,206,516, Collier U.S. Pat. No. 4,156,943, and Donlevy et al U.S. Pat. No. 4,612,160.
Ceramic coatings have also been used to good effect and are particularly desirable because of the affinity between the bone and ceramic materials such as alumina (Al.sub.2 O.sub.3).
Typical of the prior art in this regard are Suzuki et al U.S. Pat. Nos. 4,145,764 and Nishio et al U.S. Pat. No. 4,483,678 which are particularly concerned with dental implants and Heide et al U.S. Pat. No. 4,309,488 and Kurze et al U.S. Pat. No. 4,846,837 which more broadly disclose implantable bone replacement material for use throughout the body as appropriate.
It was in light of the prior art as just indicated that the present invention was conceived and has now been reduced to practice.
SUMMARY OF THE INVENTION
The present invention relates to a technique for producing a highly convoluted surface on a prosthetic device which is achieved by applying a coating of aspherical metallic powder on the surface of the device. The metallic powder, which may be the same as or different from the material of the device, is applied in a approximate thickness of up to approximately 200 microns and has a size range of approximately -80 to +635 mesh so as to result in a desirable surface roughness defined by a peak to valley variation up to approximately 200 microns R.sub.t as measured by laser profilometry. A resulting device has an enhanced surface which provides, alternatively, an improved press fit into a receiving bone, or improved cement fixation, or improved reception of a ceramic coating.
As originally conceived, the invention was intended to dramatically improve the interface bond strength of a ceramic coating to the prosthetic device itself. To this end, a highly convoluted surface is formed on the prosthetic device to which the ceramic coating can be applied, by whatever means. The highly convoluted surface can be produced, for example, by the sintering of a fine non-spherical powder on the surface of the implant. The fine powder yields a surface which is relatively non-porous but very highly convoluted. The convoluted surface provides greatly increased surface area for the chemical and mechanical interlock bonding of the ceramic to the implant substrate. The convoluted nature of the coating provides sites which protect the ceramic material from shear and tensile forces, thereby improving the bond strength.
Ceramic coatings are currently being applied to the surface of a prosthetic device in numerous ways which are cataloged, for example, in the patents noted above. Thus, application may be by way of sintering, hot-pressing, flame-spraying, plasma-spraying, sputtering, or other surface deposition techniques. The surface of the implant, in these instances, may or may not have any special treatments to enhance attachment of the coating. A typical surface treatment is to grit blast the surface of the device with an alumina abrasive to roughen the surface. The roughened surface provides an increase in surface area for improved bond strength as compared to a smooth surface and, to a certain extent, improves the shear strength of the interface bond between the ceramic and the implant. It is also known to apply the ceramic coatings to porous coatings intended for biological ingrowth for enhanced fixation.
The current method of grit blasting the surface, however, only slightly increases the roughness of the surface of the implant. Typically, the surface roughness after grit blasting is 50 microns R.sub.t which, offers only a minimal increase in surface area and mechanical interlocking of the ceramic to the implant. By way of contrast, the present invention provides a surface roughness up to approximately 200 microns R.sub.t. Thus, the present invention goes beyond the point of a simple roughened surface to the point of utilizing a convoluted surface created specifically for ceramic attachment. As will be shown below, the convoluted surface of the invention yields far greater shear strength of the coating to the substrate as compared to conventionally roughened surface coatings.
Although, as noted above, the invention was originally conceived to improve the interface bond strength of a ceramic coating to the prosthetic device itself, it has been found to render superior results when applied to prosthetic devices utilizing different implanting techniques. Specifically, the resulting convoluted surface provided by the invention results in significantly greater friction between implant and bone when the implant is press fitted into the bone. Stronger bonding between cement and implant results also when cement is used for implant fixation.
Accordingly, it is an object of the invention to provide an improved technique for producing a highly convoluted surface on a prosthetic device.
It is a further object of the invention to apply a layer of aspherical metallic powder to the surface of a prosthetic device so as to yield a treated surface which is relatively non-porous and highly convoluted.
It is another object of the invention to apply to the surface of a prosthetic device a layer of aspherical metallic powder having a size range of approximately -80 to +635 mesh and in such a manner as to result in a surface roughness defined by a peak to valley variation of up to approximately 200 microns R.sub.t.
Yet another object of the invention is to apply to the surface of a prosthetic device a layer of aspherical metallic powder composed of the same material as that of the surface.
Still another object of the invention is to apply to the surface of a prosthetic device a layer of aspherical metallic powder composed of a material different from that of the surface.
Yet a further object of the invention is to develop a surface of a prosthetic device which is formed from a powder coating of up to 200 microns in thickness and resulting in convolutions having a peak to valley variation of up to approximately 200 microns R.sub.t.
Still a further object of the invention is to provide a prosthetic device with such a convoluted surface as recited above which results in significantly increased shear strength with bone cement.
Other and further features, advantages, and benefits of the invention will become apparent in the following description taken in conjunction with the following drawings. It is to be understood that the foregoing general description and the following detailed description are exemplary and explanatory but are not to be restrictive of the invention. The accompanying drawings which are incorporated in and constitute a part of this invention, illustrate one of the embodiments of the invention, and, together with the description, serve to explain the principles of the invention in general terms. Like numerals refer to like parts throughout the disclosure.





BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 is a perspective view of a femoral component for a hip prosthesis which has been modified in accordance with the present invention;
FIG. 2A is a scanning electron microscope (SEM) photomicrograph, magnification 100X, illustrating a typical surface of an implant which has been roughened by the conventional grit blast method;
FIG. 2B is an SEM photomicrograph, magnification 100X, of the surface of an implant which has been modified in accordance with the invention;
FIGS. 3A and 3B are SEM photomicrographs, similar to FIGS. 2A and 2B, but with magnification 500X; and
FIGS. 4A and 4B are SEM photomicrographs, similar to FIGS. 2A and 2B, with magnification 1000X.





DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT
Turn now to the drawings and, initially, to FIG. 1 which illustrates a typical prosthetic implant 20 which has been modified in accordance with the invention. For purposes of explanation, the prosthetic implant 20 is a femoral component which includes a stem 22 intended for reception in the intramedullary cavity of a femur. Hence, the stem 22 is a mounting member for firmly attaching the implant to the bone. However, it will be appreciated that the invention is applicable to any prosthetic implant which is attachable to bone at any location within the body. The implant 20 may be composed of any of the biocompatible metals and alloys commonly used for prosthetic purposes, including titanium, cobalt chromium, and stainless steel.
The main thrust of the present invention is to produce a highly convoluted surface on the mounting member 22. This highly convoluted surface offers superior characteristics in resisting shear between the surface of the mounting member and any structure or coating which is intimate with that surface. In one such instance, the mounting member may be provided with a ceramic coating of the type commonly used in combination with a prosthetic implant. In another instance, the mounting member, in its roughened state, may be fittingly engaged with the bone as, for example, the stem 22 being fittingly received in the intramedullary canal of an associated femur. In still another instance, bone cement may be employed for fixing the mounting member to an underlying bone and, in that instance, improved bond strength between the mounting member and the cement, then with the bone, is achieved.
Ceramic coatings may be applied to the surface of a mounting member in a variety of ways including the plasma spray technique, sputtering, electro-phoresis and other surface deposition techniques. The surface of the implant may or may not have any special treatments to enhance attachment of the coating. A typical surface treatment is to grit blast the surface of the device with an alumina oxide abrasive to roughen the surface. The roughened surface provides an increase in surface area for improved bond strength as compared to a smooth surface, improving the shear strength of the interface bond between the ceramic and the implant. However, the current method of grit blasting the surface only slightly increases the surface roughness of the implant, typically, to about 50 microns R.sub.t. The roughened surface thereby provided by grit blasting offers only a minimal increase in surface area and mechanical interlocking of the ceramic to the implant. In contrast, the present invention goes beyond the point of a simple roughened surface to the point of utilizing a highly convoluted surface which is vastly more tortuous than that produced by the grit blast method. The convoluted surface of the invention yields significantly greater shear strength of the coating to the substrate as compared to roughened surface coatings.
In order to achieve this desirable end result, a layer of non-spherical or aspherical material powder is suitably deposited onto the outer surface of the mounting member. The thickness of the coating may be up to approximately 200 microns. The implant is then subjected to a suitable heat treatment which may be by sintering according to any known process. The powder utilized for this purpose is of a biocompatible metal or metal alloy of the types normally employed for prosthetic implants, including titanium, cobalt chromium and stainless steel. However, the powder used need not be the same as its underlying substrate. Powders acceptable for purposes of the invention may be of a range of sizes between -80 mesh and +635 mesh, the larger the mesh size of the asymmetrical powder, the greater the surface roughness achieved. Optimum surface roughness achieved by the invention is a peak to valley variation of up to approximately 200 microns. Powders suitable for purposes of the invention may be made using a variety of techniques including atomization, hydrogenization, and grinding, and are available from Cerac, Inc. of Milwaukee, Wisc. under Product No. T-1146. In comparison, aspherical powders of both the -200 and -325 mesh size produce a more textured surface than any of the spherical powders of the same size.
While the practice of the invention results in a more textured surface, it also results in a substantially non-porous surface in contrast to highly porous coatings used on implants intended for bone ingrowth fixation such as the coating provided by DePuy Inc. under its proprietary POROCOAT trademark. It will be appreciated that a range of sizes of the powder utilized for coating the mounting member is a carefully defined range. If the powder is too fine in its texture, minor, ineffective, convolutions are obtained, while if the powder is too coarse in its texture, increased porosity occurs which is also unnecessary for purposes of the invention. The preferred range of powder sizes has been found to be approximately -80 mesh to +635 mesh in order to achieve the goals of the invention.
The following example is indicative of the mechanical performance achieved by the convoluted surface structure of the invention:
EXAMPLE
Titanium rods 5/8" in diameter were either polished to a typical polished implant finish, grit blasted with a 20 grit alumina oxide media (typical roughening process utilized), or a -200 or -325 mesh powder convoluted coating was applied. No ceramic material was applied to these specimens. What was being evaluated was the difference in shear strength provided by the different surface preparation techniques. A one inch length of the coated end of each bar was potted in Armstrong A-12 epoxy. The specimens were pulled apart in an Instron test machine. The resulting shear strengths of the various coating techniques are indicated in Table 1.
TABLE 1______________________________________SHEAR TEST RESULTS (PSI)SATIN 20 -200 -325SMOOTH GRIT BLAST CON SUF CON SUF______________________________________870 2290 2903 29551483 2004 2804 29201044 1915 2978 3419770 2232 2746 32871656 1771 2222 2275AVG1165 2042 2731 2971______________________________________
While a preferred embodiment of the invention has been disclosed in detail, it should be understood by those skilled in the art that various other modifications may be made to the illustrated embodiments without departing from the scope of the invention as described in the specification and defined in the appended claims.
Claims
  • 1. A method of preparing a metallic surface comprised of a biocompatible metal or alloy for reception thereon of a ceramic coating comprising the steps of:
  • depositing on the metallic surface to a thickness of up to 200 microns a layer of aspherical metallic powder of the biocompatible metal or alloy and having a size range of approximately -80 mesh to +635 mesh;
  • performing a heat treating process on the metallic surface with the layer of metallic powder deposited thereon to thereby yield a substantially non-porous surface which exhibits a surface roughness defined by a peak to valley variation up to approximately 200 microns.
  • 2. A method as set forth in claim 1 wherein the step of performing a heat treating process includes sintering the metallic surface.
  • 3. A method of preparing a surface of a metallic prosthetic implant comprised of a biocompatible metal or alloy comprising the steps of:
  • depositing on the surface of the implant to a thickness of up to 200 microns a layer of aspherical metallic powder composed of the biocompatible metal or alloy and having a size range of approximately -80 mesh to +635 mesh; and
  • performing a heat treating process on the metallic surface with the layer of metallic powder deposited thereon to thereby yield a substantially non-porous surface which exhibits a surface roughness defined by a peak to valley variation up to approximately 200 microns.
  • 4. A method as set forth in claim 3, wherein the step of performing a heat treating process includes sintering the metallic surface.
  • 5. A method as set forth in claim 4 wherein the composition of the implant is the same as that of the metallic powder.
  • 6. A method as set forth in claim 4 wherein the composition of the implant is different from that of the metallic powder.
  • 7. A method as set forth in claim 1 wherein the composition of the metallic surface is the same as that of the metallic powder.
  • 8. A method as set forth in claim 1 wherein the composition of the metallic surface is different from that of the metallic powder.
US Referenced Citations (18)
Number Name Date Kind
3855638 Pilliar Dec 1974
4145764 Suzuki et al. Mar 1979
4156943 Collier Jun 1979
4206516 Pilliar Jun 1980
4309488 Heide et al. Jan 1982
4434211 Shoher et al. Feb 1984
4483678 Nishio et al. Nov 1984
4542539 Rowe, Jr. et al. Sep 1985
4612160 Donlevy et al. Sep 1986
4689197 Groll et al. Aug 1987
4793968 Mosser Dec 1988
4813965 Roberts Mar 1989
4846837 Kurze et al. Jul 1989
4855101 Mohs et al. Aug 1989
4889685 Shimamune et al. Dec 1989
4911720 Collier Mar 1990
5034186 Shimamune et al. Jul 1991
5263986 Noiles et al. Nov 1993
Foreign Referenced Citations (1)
Number Date Country
3027473 Feb 1982 DEX
Non-Patent Literature Citations (2)
Entry
Derwent Abstract 48910 of J 0 1265954, Oct. 1989, Kobe Steel KK.
Derwent Abstract 48612 of JA 0279249, Dec. 1986, Sumitomo Elec. Ind. KK.