Claims
- 1. A process for the preparation of a prosthetic device comprised of a load-bearing functional component and over at least a portion thereof, a porous coating of an engineering thermoplastic material which is biocompatible with, and conducive for, the ingrowth of bone spicules, said process comprising contacting at least a portion of the surface of said load-bearing functional component with a particulate bioengineering thermoplastic material selected from the group consisting of polysulfones, polyphenylenesulfides, polyacetals, thermoplastic polyesters, polycarbonates, aromatic polyamides, aromatic polyamideimides, thermoplastic polyimides, polyaryletherketones, polyarylethernitriles and aromatic polyhydroxyethers, said thermoplastic material having at least one fraction of a biomodal distribution of average particle diameters within the range from about 7:1 to about 5:1, by heating said particulate thermoplastic material at a temperature and time sufficient to sinter said material to provide a porous coating having a porosity, pore diameter and pore interconnections which enables such device to become firmly and permanently anchored into a musculosketal system in which it is employed by tissue ingrowth into the coating.
- 2. The process of claim 1 wherein the porous coating has an average pore diameter of from about 90 to about 600 microns.
- 3. The process of claim 1 wherein the porous coating has pore interconnections having average diameters of greater than about 50 microns.
- 4. The process of claim 1 wherein the porous coating has a modulus of elasticity of from about 250,000 to about 300,000 pounds per square inch.
- 5. The process of claim 1 wherein the porous coating has a total creep strain of less than one percent at a constant stress of 1,000 pounds per square inch at ambient temperature.
- 6. The process of claim 1 wherein said bimodal distribution of particle sizes is present within the range of from about 40:60 to about 60:40.
- 7. The process of claim 1 wherein the temperature sufficient to sinter said particulate bioengineering thermoplastic material is between the glass transition temperature and melt temperature of said material.
- 8. The process of claim 1 wherein a sintering additive is present in an amount to lower said temperature and/or time sufficient to sinter said material.
- 9. The process of claim 8 wherein said sintering additive is present in an amount of up to about 1 weight percent based on said bioengineering thermoplastic material.
- 10. The process of claim 8 wherein said sintering additive is a low molecular weight sulfone.
- 11. The process of claim 10 wherein said sintering additive is diphenylsulfone.
- 12. The process of claim 1 wherein said material is sintered directly to said load-bearing functioning component.
- 13. The process of claim 1 wherein said material is sintered independently of said load-bearing functional component and thereafter affixed thereto.
- 14. The process of claim 1 wherein said sintered material is affixed to said load-bearing functional component by heat shrinking a conformal coating of said material which is slightly larger than said component.
- 15. A process for the preparation of a prosthetic device comprised of a porous engineering thermoplastic material which is biocompatible with, and conducive for, the ingrowth of bone spicules, said process comprising fabricating said device from a particulate bioengineering thermoplastic material selected from the group consisting of polysulfones, polyphenylenesulfides, polyacetals, thermoplastic polyesters, polycarbonates, aromatic polyamides, aromatic polyamideimides, thermoplastic polyimides, polyaryletherketones, polyarylethernitriles and aromatic polyhydroxyethers, said thermoplastic material having at least one fraction of a biomodal distribution of average particle diameters within the range from about 7:1 to about 5:1, by heating said particulate thermoplastic material at a temperature and time sufficient to sinter said material to provide a porous device having a porosity, pore diameter and pore interconnections which enables such device to become firmly and permanently anchored into a musculoskeletal system in which it is employed by tissue ingrowth into the porous device,
- and shaping the surface of said sintered device to form an anatomically shaped prosthetic device.
Parent Case Info
This application is a continuation of Ser. No. 000,377 filed Dec. 29, 1978, now abandoned. Ser. No. 000,377 is itself a divisional application of Ser. No. 787,531 filed Apr. 14, 1977, now U.S. Pat. No. 4,164,794.
US Referenced Citations (7)
Divisions (1)
|
Number |
Date |
Country |
Parent |
787531 |
Apr 1977 |
|
Continuations (1)
|
Number |
Date |
Country |
Parent |
377 |
Dec 1978 |
|