The present disclosure relates generally to safety glazing and, more particularly, to a protective barrier applied to the exterior of a vehicle windshield.
Currently, vehicle windshields are being manufactured to include opto-electric devices such as cameras, rain sensors, proximity sensors, heads-up displays, defrosters, and antennas. This has increased the cost of replacing a cracked windshield by a factor of 10. In addition, costly calibration procedures must be performed after the installation of a new windshield, further increasing the costs associated with replacing the windshield.
The American National Standards Institute (ANSI) Z26.1-1996 standard, entitled “Safety Glazing Materials for Glazing Motor Vehicles and Motor Vehicle Equipment Operating on Land Highways,” is a standard that specifies the durability and safety requirements to qualify materials for vehicle glazing. Among the various tests mandated by the standard are transmission, humidity, heat, impact, fracturing, penetration, distortion, weathering, haze, and abrasion resistance. Applicable standards such as the Z26.1-1996 standard currently specify sixteen categories of construction for safety glazing allowable in various locations on the vehicle. The most stringent category is for windshields because of the need for visual acuity, impact resistance, and abrasion resistance from pitting and wiper blades, as well as the need to contain glass fragments to prevent them from injuring passengers.
The two basic groups of construction materials for windshields are glass and plastics. Per applicable standards, plastics are relegated to vehicles such as motorcycles, and the windshield is only allowed to be 15 inches higher than the seat so that the rider can look over it. This is because the plastics available today are so soft that they abrade easily, reducing visual acuity of the windshield after only a short service life. Considering their limited use, the abrasion test for plastics (e.g. test 5.17 specified in the ANSI Z26.1-1996 standard) only requires 100 cycles of Taber abrasion. This is 10 times less than the requirement for glass, which is 1,000 cycles of Taber abrasion. On the other hand, plastic could be a preferred material because it does not produce the sharp fragments that glass does with impacts and is half the weight. Although glass is hard and abrasion resistant, its low tensile strength makes it subject to pitting. In addition, on impact it produces dangerous sharp fragments that can injure the passengers. To mitigate this safety issue, glass windshields may be laminated with a soft plastic core to hold the fragments together and improve penetration resistance.
There are no commercially available safety barrier films for windshields that meet applicable requirements for weathering for one year (e.g. test 5.16 specified in the ANSI Z26.1-1996 standard), abrasion of plastics (e.g. test 5.17 specified in the ANSI Z26.1-1996 standard), and abrasion of glass (e.g. test 5.18 specified in the ANSI Z26.1-1996 standard), as shown in the table below:
In today's commercial market, the existing polymer safety films for protecting glass windows are mounted to the interior of the building or vehicle. These commercial products would not last more than a few months if mounted to the exteriors, due to the embrittlement of the polyester substrate. This allows fracturing of the hard coating on the surface, and thus a failure of the film. The durability of interior mounted safety films to windows is specified in ANSI Z97.1-2015, entitled “American National Standard for Safety Glazing Materials Used in Buildings—Safety Performance Specifications and Methods of Test.” An example of such an interior mounted safety film is a 3M Scotch-shield safety and security window film Ultra Series, having a thickness of 8 mil, a peel strength of 2,000 g/in, a transmission of greater than 88%, substantially no distortion at 45 degrees angle of incidence, and an abrasion resistance of 5% haze after 100 Taber cycles. While such a film may have a service life of 10 years, it is not manufactured for exterior usage and the abrasion resistance does not qualify for ANSI Z26 windshield usage (e.g. less than 2% haze after 1,000 Taber cycles).
In the case of interior mounting of a safety film such as the above 3M film, the glass window itself may provide protection from portions of the UV and IR spectrum. The addition of UV inhibitors mixed into the mounting adhesive may be enough to provide a long service life (e.g. 10 years) of the film and hard coated surface facing the interior. However, the exterior glass surface remains subject to pitting due to the low tensile strength of the glass.
The only commercially available safety film for exterior use on vehicles operating on land highways is made by Clear-Plex. According to Clear-Plex's published commercial specification and related U.S. Pat. Nos. 7,992,917 and 9,023,162, the Clear-Plex safety film includes a layer of 4 mil thick PET with a hard coat and pressure sensitive adhesive for mounting and has a peel strength of 1,800 g/in, a transmission of greater than 87%, substantially no distortion at 40 degrees angle of incidence, and an abrasion resistance of 0.5% haze after 100 cycles before weathering. Clear-Plex does not claim any testing performed to ANSI Z26 standards. The haze value may be acceptable for plastic, but the commercial specification does not include Taber testing after 1 year of weathering.
There exist other products that may be mounted onto windshield exteriors of vehicles that do not operate on land highways, such as vehicles used in stockcar racing or military vehicles. One such product, by Racing Optics, Inc., is a 4-layer×4 mil safety film (hereinafter “RO 4×4”) having a thickness of 18 mil (4 layers of 4 mil thick PET with a hard coat and pressure sensitive adhesive on each layer), a peel strength of 100 g/in for the upper layers and 400 g/in for the base layer, a transmission of greater than 88%, a Z26 haze test #5.17 result of less than 1.5% haze before weathering, a Z26 abrasion test #5.16 result of less than 5% haze after 100 Taber cycles, and a Z26 weatherability test #5.15 result of less than 4 months per layer (e.g. transmittance noticeably reduced after 3-4 months weathering, resulting in a haze of about 20-50% without Taber testing). Because the RO 4×4 product is designed for a short-term service life (which is renewed as each layer is peeled off during use), it does not have the weather durability or abrasion resistance required to meet the Z26 standard for a windshield of a vehicle operating on land highways.
The present disclosure contemplates various systems and methods for overcoming the above drawbacks accompanying the related art. According to one or more aspects of the present disclosure, an external barrier may be added to both glass and plastic windshields to improve abrasion resistance, pitting, and impact cracking. The external barrier may increase the safety of passengers as well as reduce the number one insurance cost of the national fleet of vehicles, namely windshield damage, all while reducing the carbon footprint of replacing a glass windshield.
One aspect of the embodiments of the present disclosure is a protective barrier affixable to a curved substrate. The protective barrier may comprise a stack of two or more lenses, each of the two or more lenses including a polyethylene terephthalate (PET) film, a hard coat on a first side of the PET film, and an adhesive layer on a second side of the PET film opposite the first side. The stack of two or more lenses may have a modulation transfer function that exhibits a contrast value greater than 75% for a spatial resolution of one line-pair per 0.0003 radians at 65 degrees angle of incidence.
The modulation transfer function of the stack of two or more lenses may exhibit a contrast value greater than 70% for a spatial resolution of one line-pair per 0.0003 radians at 70 degrees angle of incidence. The modulation transfer function of the stack of two or more lenses may exhibit a contrast value greater than 85% for a spatial resolution of one line-pair per 0.0003 radians at 55 degrees angle of incidence. The modulation transfer function of the stack of two or more lenses may exhibit a contrast value greater than 90% for a spatial resolution of one line-pair per 0.0003 radians at 45 degrees angle of incidence.
The PET film of each of the two or more lenses may have a modulation transfer function that exhibits a contrast value greater than 80% for a spatial resolution of one line-pair per 0.0003 radians at 65 degrees angle of incidence.
Each of the two or more lenses may be 2-4 mil thick.
The PET film of each of the two or more lenses may include UV stabilizers. The hard coat and the adhesive layer of each of the two or more lenses may include UV stabilizers.
The PET film of each of the two or more lenses may have a machine direction shrinkage of 0.6%-1.8% and a transverse direction shrinkage of 0.3%-1.1% at 150° C.
Another aspect of the embodiments of the present disclosure is a method. The method may comprise stacking two or more lenses, each of the two or more lenses including a polyethylene terephthalate (PET) film, a hard coat on a first side of the PET film, and an adhesive layer on a second side of the PET film opposite the first side. The stack of two or more lenses may have a modulation transfer function that exhibits a contrast value greater than 75% for a spatial resolution of one line-pair per 0.0003 radians at 65 degrees angle of incidence. The method may comprise placing the stack of two more lenses on a curved substrate with the adhesive of a first lens of the stack in contact with the curved substrate and applying heat and pressure to conform the stack of two or more lenses to the shape of the curved substrate.
The applying of heat and pressure may be performed at least in part prior to the adhesive layer of each of the two or more lenses being fully cured. The applying of heat and pressure may be performed at least in part prior to the adhesive layer of each of the two or more lenses exceeding a peel strength of 25 grams per inch determined as a constant load per unit width needed for peeling.
The method may comprise peeling off an outermost lens of the stack of two or more lenses after the applying of heat and pressure.
The adhesive of the first lens of the stack of two or more lenses may be stronger than the adhesive of an outermost lens of the stack of two or more lenses.
The modulation transfer function of the stack of two or more lenses may exhibit a contrast value greater than 70% for a spatial resolution of one line-pair per 0.0003 radians at 70 degrees angle of incidence.
The PET film of each of the two or more lenses may have a modulation transfer function that exhibits a contrast value greater than 80% for a spatial resolution of one line-pair per 0.0003 radians at 65 degrees angle of incidence.
Each of the two or more lenses may be 2-4 mil thick.
The PET film of each of the two or more lenses may include UV stabilizers. The hard coat and the adhesive layer of each of the two or more lenses may include UV stabilizers.
The PET film of each of the two or more lenses may have a machine direction shrinkage of 0.6%-1.8% and a transverse direction shrinkage of 0.3%-1.1% at 150° C.
These and other features and advantages of the various embodiments disclosed herein will be better understood with respect to the following description and drawings, in which like numbers refer to like parts throughout, and in which:
The present disclosure encompasses various embodiments of a protective barrier affixable to a curved substrate and methods of manufacture, installation, and use thereof. The detailed description set forth below in connection with the appended drawings is intended as a description of several currently contemplated embodiments and is not intended to represent the only form in which the disclosed invention may be developed or utilized. The description sets forth the functions and features in connection with the illustrated embodiments. It is to be understood, however, that the same or equivalent functions may be accomplished by different embodiments that are also intended to be encompassed within the scope of the present disclosure. It is further understood that relational terms such as first and second and the like are used solely to distinguish one from another entity without necessarily requiring or implying any actual such relationship in order between such entities.
Distortion is a visual acuity error caused by a displaced object in the far field (e.g. 40-1,000 feet). Safety glazing can have localized zones which cause object displacements perceived as distortion, where an object may appear to jump from one position to another when viewed from a slightly different position or angle. Conventionally, distortion is only qualitatively determined, for example, by test 5.15 specified in the ANSI Z26.1-1996 standard. This test uses a shadow graph in a long tunnel with a collimated light source and white screen. The technician places a specimen in the light path at normal angle of incidence, 15 inches from the screen. The technician then looks for dark and light artifacts caused by distortion. The test has no quantitative criteria and does not address distortion at the high angle of incidence used in modern car windshields (e.g. 60-70 degrees).
Ideally, the distortion should be minimized to the resolution of the human eye with 20/20 vision, which is about one line-pair per 0.0003 radians. If an object is displaced by 0.0006 radians, for example, then the eye will perceive the location change as distortion. Effectively, then, distortion must be reduced such that any object displacement is below the resolution capability of the human eye in order to be considered distortion-free. Meanwhile, when safety glazing is viewed at high angles of incidence (e.g. 60-70 degrees), the optical thickness increases as a function of the cosine of the angle according to Snell's law. This may cause any distortion effects to be amplified, especially for safety film thicker than around 4 mil as may be needed to resist impact damage at automobile speeds.
A test setup such as that of
For example, at any or all stages of producing the stack of lenses 110 (e.g. during the formation of the PET film 112 by melting a resin, extruding the melted resin through a die to produce a film, and cooling the film, during the applying of the hard coat 114, during the applying of the adhesive layer 116, etc.), one or more images of the test pattern 220 may be captured through the lens 110 or stack of lenses 110 being produced. The image(s) may be captured, for example, by aiming an image capturing device through a roll-to-roll processing web containing the lens 110 or stack of lenses 110 at one or more desired angles of incidence. On the basis of such image(s), a computer may calculate the MTF data and produce an output used for adjusting process parameters that are found to effect the modulation transfer function of the lens 110 or stack of lenses 110, such as a temperature setting of a heater used in melting the resin (e.g. absolute temperature or relative temperatures of a gradient or profile of a plurality of heated regions of an extruder assembly), a rotation speed of an extrusion screw (which may determine melting time as well as degree of mixing of the resin), a rotation speed of one or more rollers (which may determine cooling time and/or a degree of force acting on the polymer film during cooling), a flow speed, deposition speed, or other application speed of the hard coat 114 or adhesive layer 116, and/or a speed at which the lenses 110 are stacked. It is contemplated, for example, that the PET film 112 may in some cases be prefabricated and selected for its known MTF data, whereas the modulation transfer function of the stack of lenses 110 may be actively controlled during the application of the hard coats 114 and/or adhesive layers 116 and the stacking of the lenses 110. In other cases, the PET film 112 may also be manufactured while actively controlling the modulation transfer function thereof. The output of the computer may include, for example, a feedback signal for automatically adjusting the relevant process parameters without user input in either a continuous or batch-to-batch process. As another example, the output may include a visual representation of the data to be interpreted by an operator who will make the necessary adjustments manually.
An example of a prefabricated PET film 112 that may be selected for its known MTF data for use in the stack of lenses 110 is a PET film 112 having a modulation transfer function that itself exhibits a contrast value greater than 80% for a spatial resolution of one line-pair per 0.0003 radians at 65 degrees angle of incidence. One such material is a film sold under the name MELINEX® 454 by DuPont Teijin Films, which is represented in
In contrast, the sample labeled T-8 3×3, represented in
In general, the increased thickness needed to protect a glass windshield poses several challenges to the production of the protective barrier 100. As described above, for example, the increased thickness may amplify distortion at high angles of incidence (e.g. 60-70 degrees). This challenge may be overcome by controlling the modulation transfer function of the protective barrier 100 as described above, for example, by producing a stack of lenses 110 having a modulation transfer function that exhibits a contrast value greater than 75% for a spatial resolution of one line-pair per 0.0003 radians at 65 degrees angle of incidence. Additional challenges posed by the thickness of the protective barrier 100 include making a product that can be successfully molded to a curved substrate 10 (e.g. an automobile windshield), achieving a high degree of weatherability and abrasion resistance and reduced haze, and maintaining a reasonably long service life. Each of these challenges may be overcome by the disclosed protective battier 100 as described in more detail below.
The windshields of most cars exhibit a compound curvature, such that the protective barrier 100 will not conform to the windshield 10 without shrinking it in the upper and lower corners. Since the protective barrier 100 may be flat (e.g. having been manufactured in a roll-to-roll process), the stack of two or more lenses 110 may not initially conform to the curved shape of the windshield 10, resulting in regions of greater or less adhesion and pockets/bubbles of air between the stack of lenses 110 and the windshield. Therefore, in order to conform the stack of lenses 110 to the shape of the windshield 10, heat and pressure may be applied using a heater 30 such as a hot air source (e.g. a heat gun or blow dryer) or an infrared heater. At the same time, pressure may be applied to the stack of lenses 110 using a card or squeegee. In some cases, the protective barrier 100 may be applied using a sacrificial layer serving as a female mold cavity to sandwich the stack of lenses 110 between the sacrificial layer and the windshield 10 as described in commonly owned U.S. application Ser. No. 16/778,928, filed Jan. 31, 2020 and entitled “THERMOFORM WINDSHIELD STACK WITH INTEGRATED FORMABLE MOLD,” the entire contents of which is expressly incorporated herein by reference.
As the installer heats and presses down on the stack of lenses 110, the stack of lenses 110 may shrink and stretch to take on the contour of the curved substrate 10 (the windshield). In the case of commercial films having a thickness of only 2 mil, the necessary shrinking may be easy to achieve. On the other hand, a monolithic film of 8 mil or thicker will crease before the film conforms to the windshield, making it unusable. In light of this challenge, the protective barrier 100 described herein uses multiple thin lenses 110 (e.g. 2-4 mil thick each) that individually shrink well. The adhesive layers 116 between the lenses 110 of the stack, which may be the same acrylic adhesive for example, may be only partially cured to produce an extremely low peel strength (e.g. 15-25 g/in) and high elasticity. As such, each individual lens 110 of the stack may “float” in relationship to each other, allowing shrinking to occur without creasing any of the lenses 110. Once the protective barrier 100 is installed and exposed to sunlight, for example, the adhesive layers 116 will cure and increase the peel and bonding strength (e.g. by a factor of 3 to 5), promoting a long service life. The peel strength after initial weathering may be 100-150 g/in, for example.
In addition to improving moldability as described above, the use of multiple thin lenses 110 (e.g. 2-4 mil thick) rather than a single monolithic film may allow for a sufficiently reduced haze to be usable on automobile windshields. In general, haze in a PET film has two components: scattering of incident light at the surface and dispersion of incident light in the bulk material. The latter bulk component increases with the thickness of the PET film, for example, as shown in the table below:
However, the effect is not additive when multiple PET films are stacked, with three layers only adding about 0.1-0.2% haze in total. Meanwhile, the surface component of haze is mitigated by the addition of hard coat or adhesive. By structuring the protective barrier 100 as a stack of lenses 110 containing relatively thin PET films 112 rather than a single large PET film, a reduced haze can be achieved even while the protective barrier 100 may be thick enough to resist impact at automobile speeds (e.g. 8 mil or thicker) as described above. In particular, the protective barrier 100 described herein, comprising a stack of two or more lenses 110 each of which includes a PET film 112 with a hard coat 114 and an adhesive layer 116, may achieve an initial (pre-weathering) haze of below 1% (preferably below 0.6%), making it suitable for use on automobile windshields.
Weathering may be defined according to a standard such as the ANSI Z26.1-1996 standard at exposure of one year at around 300 MJ/m2 of ultraviolet radiation (e.g. 301 MJ/m2 or 306 MJ/m2 per applicable standards, or 280 MJ/m2 extrapolated from 70 MJ/m2 per three month period). In order to simulate exposure for one year in an outdoor Arizona climate (Arizona being selected as a weathering benchmark for its high temperatures and high-intensity sunlight), a natural sunlight concentrator may be used such as one that complies with the American Society for Testing and Materials (ASTM) G90 standard, entitled “Standard Practice for Performing Accelerated Outdoor Weathering of Materials Using Concentrated Natural Sunlight.” The haze and abrasion resistance of the protective barrier 100 may be measured before and at the end of the exposure cycle.
In the comparative example of the RO 4×4 product described above, a UV stabilizer such as a UV absorbing compound is mixed into the hard coat and the adhesive of each of the four layers. After only six months of Arizona exposure, the outermost layer becomes unusable because of loss of transmission, increased haze, and loss of hardness. Because there is so much UV inhibitor in the hard coat, the hard coat has reduced hardness and fractures, allowing the underlying PET core of the outermost layer to become yellow and brittle. The resulting haze may exceed 20%.
In contrast to the RO 4×4 product, the protective barrier 100 described herein may be produced with the PET film 112 of each of the two or more lenses 110 including UV stabilizers such as hydroxyphenyl-benzotriazole or hydroxyphenyl-triazine UV absorbers. The hard coat 114 and/or the adhesive layer 116 of each lens 110 may also include UV stabilizers. Because the UV stabilizers are mixed into the PET film 112, a reduced amount of UV stabilizers can be used in the hard coat 114 and adhesive layer 116, allowing the hard coat 114 to maintain its hardness without sacrificing UV stability. Spreading the UV stabilizers across all components allows for a highly weatherable assembly, such that the protective barrier 100 may exceed one year of ANSI G90 exposure in Arizona sun and may look very good with low haze and little if any yellowing after weathering. The protective barrier 100 may, for example, have an abrasion resistance at 1,000 Taber cycles of less than 1% haze before weathering and less than 4% (preferably less than 2%) haze after weathering.
Although the protective barrier 100 may have sufficient weatherability, eventually the outermost lens 110 (e.g. lens 110c in the 3-layer example of
During any or all of steps 810-840, the operational flow may comprise controlling the MTF of the stack of lenses 110 (step 850). The MTF of the stack of lenses 110 may be controlled, for example, so as to exhibit a contrast value greater than 75% for a spatial resolution of one line-pair per 0.0003 radians at 65 degrees angle of incidence. As explained above, such control may be achieved by selecting an appropriate pre-fabricated PET film 112 in step 810. Alternatively, or additionally, the control of the MTF may be achieved by actively monitoring and adjusting process parameters (e.g. roller speed of a roll-to-roll process, etc.) while fabricating a PET film 112 in step 810, depositing the hard coat 114 in step 820, applying the adhesive layer 116 in step 830, and/or stacking the two or more lenses 110 in step 840. It is contemplated that such active monitoring and adjusting of process parameters may include a continuous process including a feedback loop of monitored MTF data and/or a batch-to-batch process with MTF measurements manually or automatically fed back from a preceding batch.
Once the protective barrier 100 comprising the stack of lenses 110 has been assembled, the operational flow may continue with installing the protective barrier 100 on a curved substrate 10 such as the windshield of the car 20 shown in
After allowing the protective barrier 100 to cool down, the installation may conclude with performing a final trim as described in relation to
As explained above, it is contemplated that a protective barrier 100 having more than one lens 110 may allow for the outermost lens 110 to be peeled off and removed to reveal the unused surface of the lens 110 beneath. In this respect, the operational flow of
The above description is given by way of example, and not limitation. Given the above disclosure, one skilled in the art could devise variations that are within the scope and spirit of the invention disclosed herein. Further, the various features of the embodiments disclosed herein can be used alone, or in varying combinations with each other and are not intended to be limited to the specific combination described herein. Thus, the scope of the claims is not to be limited by the illustrated embodiments.
This application is a continuation of U.S. application Ser. No. 18/062,901, filed Dec. 7, 2022, which is a continuation of U.S. application Ser. No. 16/866,392, filed May 4, 2020, now U.S. Pat. No. 11,548,356, issued Jan. 10, 2023, which relates to and claims the benefit of U.S. Provisional Application No. 62/987,726, filed Mar. 10, 2020 and entitled “PROTECTIVE BARRIER FOR SAFETY GLAZING,” the entire contents of which is expressly incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| 62987726 | Mar 2020 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 18062901 | Dec 2022 | US |
| Child | 18478220 | US | |
| Parent | 16866392 | May 2020 | US |
| Child | 18062901 | US |