This invention relates to protective covers for equipment typically stored outdoors such as airplanes, vehicles, munitions, weapons and weapons systems, electrical equipment and the like, as well as fabrics for such protective covers.
Protective covers are often used to protect equipment and parts in a wide range of environmental conditions. Corrosion and oxidation are of particular concern, especially in connection with vehicles, airplanes, munitions, weapons and weapons systems and equipment with metal and/or electronic components and the like.
Prior protective covers that address the problem of corrosion are described in U.S. Pat. Nos. 6,794,317 and 6,444,595. There remains a need, however, for more effective covers that provide protection and resistance to penetration of water, wind and sand, and that are especially effective with respect to the prevention or at least minimization of oxidation and/or corrosion due to humidity build-up around the covered objects.
In accordance with an exemplary embodiment of this invention, an air permeable protective cover is provided that is designed to prevent the ingress of moisture but, at the same time, to allow moisture vapor underneath the cover to readily pass through to the outer environment, thereby preventing humidity buildup and thus helping to prevent or at least minimize oxidation and corrosion of the covered object.
In the exemplary embodiment, the cover is composed of a plurality of laminated layers of different materials. The multiple layers include at least an outer textile layer, an intermediate film or membrane of ePTFE or other similar hydrophobic material having good air permeability and moisture-vapor-transmission properties, and an inner textile layer that faces toward the object being covered. For specific applications, the ePTFE membrane may be an air permeable, breathable, treated membrane such as an eVENT® membrane available from BHA Technologies. An optional fourth fabric layer between the outer layer and the film or membrane may incorporate Super Absorbing Polymers (SAPs) to prevent reabsorption of moisture back through the cover. Corrosion or other inhibitors, such as an anti-microbial to inhibit mold, may also be included in either the textile layers or the membrane itself. All of the various embodiments preferably take advantage of moisture-wicking materials as the laminate layers to help remove moisture vapor from the covered equipment. The various layers or laminations are held together by adhesive or any other acceptable method in order to achieve the required durability of the final product.
The protective covers described herein preferably have a Moisture Vapor Transmission Rating (MVTR) of at least 4000 g/m2/day or more.
In all cases, the inner textile layer may have material such as silicone dots applied to the inner face thereof, so that contact between the cover and the object to be protected is minimized if not eliminated, and to thereby enhance the moisture vapor transmission away from the object.
Textiles suitable for the outer layer include woven, knit and non-woven fabrics such as nylon plain weave and ripstop-fabrics, warp knit fabrics, woven Cordura®, a registered trademark of Invista, fabric, Nomex® and Kevlar® (both registered trademarks of Dupont) fabrics, including blends Taslan fabrics (70-160D) and equivalents.
Textiles suitable for the inner layer include woven, knit and non-woven fabrics such as lightweight warp or circular knit fabrics using nylon, polyester, Nomex® and equivalent fabrics, spunbond nylon and equivalents.
Accordingly, in one aspect, the invention relates to a protective cover comprising a textile layer and an air permeable, moisture-vapor-transmissive, expanded polytetrafluoroethylene membrane layer attached to the textile layer, the cover having an MVTR of at least 4000 g/m2/day.
In another aspect, the invention relates to a fabric for use in protective covers, the fabric comprising at least three layers including an outer woven, knit or non-woven fabric layer and an inner woven, knit or non-woven fabric layer, and a moisture-vapor-transmissive, air permeable and oleophobic expanded polytetrafluoroethylene membrane layer between the outer and inner layers; the fabric having an MVTR of at least 4000 g/m2/day.
The invention will now be described in detail in connection with the single drawing figure described below.
Referring to
The outer fabric layer may be treated to be durably water-resistant, with available treatments including, for example, a Teflon® finish from Dupont or other similar finish from Invista or other known suppliers.
An interior intermediate layer 14 is in the form of a hydrophobic film or membrane with good air permeability and moisture-vapor-transmission properties. In the exemplary embodiment, layer 14 is an expanded polytetrafluoroethylene (ePTFE). The expansion of polytetrafluroethylene opens billions of microscopic pores in the resulting film or membrane to enhance air permeability and water vapor transmission rate. The ePTFE layer or membrane is also treated to render it permanently oleophobic, waterproof and hydrophobic. A treated membrane of this type is commercially available from BHA Technologies under the trade name eVENT® Fabric. The oleophobic property of this membrane is particularly beneficial in that equipment, particularly military equipment, is often sprayed with oil to minimize corrosion. The ePTFE may also be rendered resistant to hydraulic fluid, diesel fuel, weapon lubricants and similar field chemicals.
It is believed that the unique value that eVENT® Fabric offers is its ability to eliminate moisture condensation on the article covered while providing a completely waterproof protection (resists liquid water penetration at pressure as high as 10 meters of hydrostatic head). Moisture condenses on the surfaces if the protective cover cannot “breathe.” This happens due to environmental temperature swings during the storage. For example, if an object is covered with a non-breathable protective cover and the environmental conditions are 25 dg C temperature and 50% relative humidity, then a drop of ambient temperature by 12 dg C would drive the relative humidity inside to over 100% and hence lead to condensation. Utilizing an eVENT® membrane would keep the relative humidity inside equilibrated to the ambient conditions by allowing the moisture vapors to escape out.
The inner textile layer 16 faces the object to be covered, and it is therefore preferable that the exposed surface be smooth so as not to scratch covered equipment. This textile fabric layer may be composed of woven, knits, and non-woven fabrics such as lightweight tricot warp knits of polyester or nylon. Such materials include Style 1158 manufactured by Hornwood and available from K-Tex of Wayne N.J., or Style #0862, a 100% semi-dull nylon 6,6 with 52 courses and 42 wales and a weight of 0.9 oz. per sq.yd., available from Somerset Industries of Gloversville, N.Y. Also suitable are non-woven spunbond nylon fabrics such as Cerex Advanced Fabrics Orion style #70 having a weight of 0.7 oz./sq. yd. and a thickness of 6-7 mil. Another suitable fabric is yellow Nexus® non-woven polyester having a weight of 1-1.2 oz./yd2, and a thickness of 0.008-0.012 in., also available from Precision Fabrics Group. The inner layer may also be hydrophilic, either by treatment or choice of fibers and construction, helping to wick moisture away from the covered object and to spread the moisture laterally, facilitating the vapor transmission through the cover to the outside. The inner layer may also be rendered electrically conductive by either weaving in of inherently conductive fibers or by topical treatment.
Referring now to
With the above configurations, the laminated protective cover allows moisture to be expelled readily from the interior covered area through the laminated cover itself to the outside environment. In this regard, the cover fabric and cover itself preferably have an MVTR of at least 4000 to about 8000 g/m2/day and as high as 14000 g/m2/day or more, per ISO 15496 (inverted cup method). The cover thus provides environmental protection and resistance to penetration of water, wind and sand. The cover may be especially useful in the prevention of corrosion during transportation of military vehicles or other equipment, and protection from contamination by chemical and biological warfare agents.
In the specific comparative example below an ePTFE laminate cover in accordance with the invention is constructed of three layers including:
(a) Nylon 6,6 Ripstop face fabric available from Mitsui Textiles, Japan;
(b) ePTFE membrane;
(c) Nexus® polyester spunlace, 30 g/m2, available from Precision Fabrics Group.
The ePTFE laminate is available from BHA Technologies, Inc. under the name eV5004-3L.
The following commonly used protective cover materials were compared against the above ePTFE laminate
(1) Herculite® 90 Coated Cover Fabric available from Manart-Hirsch Co., Inc., NY
(2) Sunbrella® Marine Canvas Cover Fabric available from Great Lakes Fabrics Inc., MI as their product number 4630
(3) Polyethylene shrink wrap (Marine Boat cover) available from Shrinkwrap International Inc., MI
Mild Steel corrosion coupons were obtained from Metal Samples Company, AL. Each coupon was 2″×1″× 1/16″ in dimensions. Ten such coupons were wrapped in each of the four cover materials and left in an open parking lot for a period of two weeks. At the end of two weeks, the condition of the coupons was evaluated for signs of rusting. They were graded on a scale of 1 to 5, with 1 indicating that none of the tens coupons were visually rusted and 5 indicating that all ten coupons were visually rusted.
The results from this evaluation are given in the table below. Also listed is the moisture vapor transmission rate of each of the four laminates.
It is also within the scope of this invention to add a layer of air (gas) permeable insulation such as Primaloft® within the laminate, specifically under the membrane, to retain heat under the cover. In addition, a metal (e.g., aluminum) reflective coating may be applied to the exposed inner face of the inner layer for reflecting heat and/or for its electrostatic dissipative properties.
Another variation includes the addition of a durable water repellant coating on the exposed face of the outer textile layer.
Some of the applications for these laminate fabrics are protective covers that are particularly useful in situations where there is need for protection against dust, rain, microbes, UV light exposure, while minimizing corrosion. For example:
(a) Protective covers for military and civilian helicopters and other aircraft;
(b) Protective covers for military ground vehicles;
(c) Protective covers for ground aviation equipment;
(d) Protective covers for shipboard equipment;
(e) Boat covers;
(f) Vehicle covers (e.g., motorcycles, automobiles, etc.);
(g) Military Tank hatch covers; and
(h) Personal arms protective covers.
While the invention has been described in connection with what is presently considered to be the most practical and preferred embodiment, it is to be understood that the invention is not to be limited to the disclosed embodiment, but on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims.
This is a continuation-in-part of application Ser. No. 11/123,076, filed May 6, 2005.