Protective tip for a titanium blade and a method of brazing such a tip

Information

  • Patent Grant
  • 4795313
  • Patent Number
    4,795,313
  • Date Filed
    Thursday, May 28, 1987
    37 years ago
  • Date Issued
    Tuesday, January 3, 1989
    35 years ago
  • Inventors
  • Original Assignees
  • Examiners
    • Garrett; Robert E.
    • Pitko; Joseph M.
    Agents
    • Sughrue, Mion, Zinn, Macpeak & Seas
Abstract
A protective tip (5) for a titanium steam-turbine blade (1), comprises 28% to 40% TiC, 12% to 26% Cr+Co, 1% to 6% Mo, 3% to 8% Ni 0.3% to 1.5% Cu and a balance of Fe. The tip (5) is brazed to the blade (1) by interposing a copper-based strip (6) having a thickness lying between 7/100 mm and 15/100 mm therebetween, then raising the temperature of the blade (1) and its tip (5) to between 900.degree. C. and 950.degree. C. in a vacuum or inert atmosphere oven. This temperature is maintained for a period of between thirty minutes and seventy-five minutes, and the oven is allowed to cool to ambient temperature. Optimal brazing also serves to harden the tip (5) possesses very good resistance to abrasion by water droplets.
Description

The present invention relates to a protective tip for a turbine blade made of titanium alloy.
BACKGROUND OF THE INVENTION
Titanium alloy blades for steam turbines are particularly advantageous for the last, low-pressure stages where the blades must be of large size. However, in such last stages, the steam includes water droplets which strike the moving blades whose peripheral speeds are high.
SUMMARY OF THE INVENTION
In order to protect the leading edges of the blades, tips are welded or brazed to said leading edges, said tips comprising the following constituents:
TiC: 28% to 40%
Cr+Co: 12% to 26%
Mo: 1% to 6%
Ni: 3% to 8%
Cu: 0.3% to 1.5%
Fe: balance
Titanium carbide has the same coefficient of expansion and the same shear modulus as titanium. The binder is constituted by cobalt and chromium which have high intrinsic resistance to erosion and by nickel which improves the ductility of the assembly.
The iron provides the base matrix in which titanium carbide is integrated without difficulty.
The structure of the tip is a nickel martensite having high resistance to wear by virtue of the presence of chromium and cobalt, and relatively high toughness by virtue of the presence of nickel.
The invention also relates to a method of brazing the tip characterized in that it comprises the following steps:
the tip is placed on the blade and a copper-based strip having a thickness lying between 7/100 mm and 15/100 mm is interposed therebetween;
the temperature of the blade and its tip is raised to between 900.degree. C. and 950.degree. C. in a vacuum or inert atmosphere oven and this temperature is maintained for a period of between thirty minutes and seventy-five minutes; and
the temperature is cooled to ambient.
By virtue of this method, the brazing between the blade, the copper-based strip, and the tip is simultaneous and optimum. Further, the titanium carbide is at least partially put into solution, thereby conferring a hardness of greater than 50 HRC to the tip.
If the tip is to have a hardness greater than 60 HRC then the temperature is raised, after cooling down to ambient, to 450.degree. C. to 500.degree. C. and maintained for four to six hours prior to being lowered back to ambient. This additional stage puts substantially all of the titanium carbide into solution and simultaneously provides stress-relieving heat treatment.





BRIEF DESCRIPTION OF THE DRAWING
An embodiment of the invention is described by way of example with reference to the accompanying drawing, in which:
FIG. 1 shows a titanium carbide tip in accordance with the invention fixed to a blade;
FIG. 2 is a plan view of the FIG. 1 blade; and
FIG. 3 is a section through the FIG. 1 blade.





MORE DETAILED DESCRIPTION
The steam turbine blade shown in FIG. 1 comprises a root 1 and a twisted vane 2 having a leading edge 3 and a trailing edge 4. A tip 5 is placed along the leading edge 3 of the blade near its top and over its convex surface. This tip extends over about one-third of the width of the blade 2. A copper-based strip 6 is placed between the blade and the tip (see FIGS. 2 and 3).
The blade is made of titanium alloy and the tip 5 has the following composition:
TiC: 28% to 40%
Cr+Co: 12% to 26%
Mo: 1% to 6%
Ni: 3% to 8%
Cu: 0.3% to 1.5%
Fe: balance
Two specific compositions have given good results.
______________________________________ TiC Cr Co Mo Ni Cu Fe______________________________________Composition 1 32% 20% 0% 2% 3% 1% BalanceComposition 2 33% 14% 9% 5% 6% 0.8% Balance______________________________________
The tip is obtained by sintering and mechanically compacting powder followed by machining. The length of the tip is equal to the length of the blade portion to be protected (up to 500 mm), its width is adequate, it is plane or curved in shape, with or without angles or rounding, in order to fit the shape of the leading edge of the blade.
The machining must be performed with sufficient accuracy for the residual play between the blade 2 and the tip 5 to be never greater than 1/10 mm.
The blade 2 is then prepared and the tip 5 is brazed onto the blade 2 by interposing a copper-based strip 6 therebetween, said strip having a thickness lying in the range 7/100 mm to 15/100 mm.
In order to perform the brazing operation, the blade 2 is placed in an oven together with the tip 5 which is held in place by two or three molybdenum clamps.
The temperature is raised to a temperature between 900.degree. C. and 950.degree. C. This temperature is maintained for thirty minutes to seventy-five minutes depending on the thickness of the leading edge of the blade, and then the oven is allowed to cool to ambient temperature.
In addition to brazing, this treatment structurally hardens the tip 5 by putting a considerable portion of the titanium carbide into solution. The tip 5 then has a hardness lying in the range 50 HRC to 55 HRC.
In order to further increase the hardness of the tip 5 it is subjected to the following additional treatment.
The temperature of the oven is raised to the range 450.degree. C. to 500.degree. C. and this is maintained for four hours to six hours, thereby putting substantially all of the titanium carbide into solution. This simultaneously performs stress-relieving treatment.
Claims
  • 1. A protective tip for a titanium turbine blade, said tip comprising the following constituents:
  • TiC: 28% to 40%
  • Cr+Co: 12% to 26%
  • Mo: 1% to 6%
  • Ni: 3% to 8%
  • Cu: 0.3% to 1.5%
  • Fe: balance
  • 2. A method of brazing a tip according to claim 1 onto a titanium blade, the method comprising the following steps:
  • the tip is placed on the blade and a copper-based strip having a thickness lying between 7/100 mm and 15/100 mm is interposed therebetween;
  • the temperature of the blade and its tip is raised to between 900.degree. C. and 950.degree. C. in a vacuum or inert atmosphere oven and this temperature is maintained for a period of between thirty minutes and seventy-five minutes; and
  • the temperature is cooled to ambient.
  • 3. A method according to claim 2, wherein after cooling down to ambient, the temperature is raised to 450.degree. C. to 500.degree. C. and is maintained for four to six hours prior to being brought back down to ambient.
Priority Claims (1)
Number Date Country Kind
86 07661 May 1986 FRX
US Referenced Citations (8)
Number Name Date Kind
2661286 Swazy et al. Dec 1953
2664355 Craighead Dec 1953
2714245 Goetzel Aug 1955
2903785 Hanink et al. Sep 1959
3561886 Kreischer et al. Feb 1971
4010530 Degrosso et al. Mar 1977
4342542 Tan et al. Aug 1982
4626295 Sasaki et al. Dec 1986
Foreign Referenced Citations (9)
Number Date Country
2004724 Sep 1970 DEX
1146511 Nov 1957 FRX
2482627 Nov 1981 FRX
55-60605 May 1980 JPX
0692867 Jun 1953 GBX
833758 Apr 1960 GBX
1096294 Dec 1967 GBX
1479855 Jul 1977 GBX
2076019 Nov 1981 GBX