Patent Application
20160362483
The present invention relates to sustained-release pharmaceutical formulations for administering proteins to the eye. In particular, the invention relates to formulations comprising single chain antibodies and hydrophobic polyester hexylsubstituted poly(lactic acid) (hexPLA). The invention further relates to processes for the production of sustained-release pharmaceutical formulations and medical uses thereof.
A number of intravitreal sustained-release pharmaceuticals for small molecules have been investigated and marketed in the past years. Early implants delivering Ganciclovir (Vitrasert®) and Fluocinolone (Retisert®) showed long release periods but were non-biodegradable (Musch et al., 1997, New England Journal of Medicine 337:83; Jaffe et al., 2005, Ophthalmology 112:119). A number of adverse effects, material problems, and surgical problems were reported when removing the implants from the eye (Martin et al., 1997, Arch Ophthalmol-Chic 115:1389; Boyer et al., 1999, Am J Ophthalmol 127:349). Thus, interest shifted toward biodegradable implants.
The currently approved degradable implants for intravitreal application (Ozurdex®) are based on poly(lactic-co-glycolic acid) (PLGA) and release dexamethasone for around 6 months (Kuppermann et al., 2007, Arch Ophthalmol-Chic 2007, 125:309). For the preparation of the PLGA-implants, pressure, heat, solvents or a combination thereof is used to incorporate the active substance and to form the implant (Kimura et al., 2001, Ophthalmologica 215:143). This implies problems for the formulation of proteins due to their intrinsically lower stability as compared to many small molecules.
A possible solution to the formulation problem of proteins for sustained-release could be the use of viscous excipients instead of solid implants. These can simply be mixed with the lyophilized protein to form the final formulation. Poly(ortho esters) (POEs) of the third generation were the first viscous, polymeric liquids investigated toward sustained intravitreal release (Einmahl et al., 2000, J Biomed Mater Res 50:566). But due to the lack of storage stability (Merkli et al., 1996, Biomaterials 17:897), difficulties with sterilizability (Sintzel et al., 1998, International Journal of Pharmaceutics 175:165) and difficulties in synthesis and upscaling (Behar-Cohen et al., 2006, Advanced Drug Delivery Reviews 58:1182), they were soon followed by a new generation of POEs.
Fourth generation POEs (POEs IV) were easier to synthesize, and a control of the degradation rate was possible by adjusting the ratio of the used monomers (Gurny et al., 1998, Biomaterials 19:791). POEs IV were evaluated up to a clinical phase II study and showed good biocompatibility in the human eye (Behar-Cohen et al., 2006, Advanced Drug Delivery Reviews 58:1182). However, their period of degradation in vivo was much longer than the period of drug release, shifting interest toward new liquid polymer entities for sustained-release delivery in the eye. Consequently, there is a need for improved sustained-release delivery systems and formulations for administering proteins to treat ocular diseases.
The invention provides sustained-release pharmaceutical formulations, comprising a single chain antibody Fv fragment (scFv) and hydrophobic polyester hexylsubstituted poly(lactic acid) (hexPLA). In one aspect, a formulation of the invention is for ocular administration to a subject in need thereof.
In certain aspects, a formulation of the invention comprises a scFv present in a final molecular weight of at least about 1.25% (w/w).
In other aspects, a formulation of the invention comprises hexPLA present at a concentration of at least about 1500 g/mol.
In one aspect, an intravitreal sustained-release depot comprising the formulation of the invention is provided.
In another aspect, the invention provides a delivery system comprising the sustained-release pharmaceutical formulation of a scFv and hexPLA and a syringe.
The invention further provides a process for the preparation of a sustained-release pharmaceutical formulation, the process comprising cryo-milling a scFv and hydrophobic polyester hexylsubstituted poly(lactic acid) (hexPLA). In certain aspects, the process further comprises warming the formulation to room temperature under vacuum.
The invention also provides methods of treating an ocular disorder in a patient, comprising administering to the patient an effective amount of the sustained-release pharmaceutical formulation of a scFv and hexPLA.
In addition, the invention provides a stable single chain antibody formulation, comprising a single chain antibody and hexylsubstituted poly(lactic acid) (hexPLA), wherein the single chain antibody is stable at 37° C.
Specific preferred embodiments of the invention will become evident from the following more detailed description of certain preferred embodiments and the claims.
The invention provides a stable single chain antibody formulation, comprising a single chain antibody and hexylsubstituted poly(lactic acid) (hexPLA), wherein the single chain antibody is stable at 37° C. The invention also provides sustained-release pharmaceutical formulations of single chain antibodies and hexPLA. The formulations are stable, with high protein concentration and a low viscosity. As described herein, surprisingly single chain antibodies are stable in matrices of hexPLA, and can be released from the matrices in a sustained manner.
A “stable” formulation within the meaning of the invention is one in which the antibody therein essentially retains its physical and chemical stability and integrity upon storage. Various analytical techniques for measuring protein stability are available in the art. Stability can be measured at a selected temperature for a selected time period. Chemical stability may, for example, be measured by reversed-phase chromatography (RP), for example by RP-HPLC after trypsin digestion. For example, after storage of at least 1 year at about 4° C., the peak representing unmodified single chain antibody in RP-HPLC after trypsin digestion decreases no more than 20%, preferably no more than 10%, more preferably no more than 5% or even no more than 1%, as compared to the single chain antibody suspension prior to storage. As the person skilled in the art will readily appreciate, there are other methods suitable to measure the stability of the suspensions of the invention. For example, chemical stability may also be measured by capillary electrophoresis.
Certain techniques for measuring stability are described in the Examples herein.
The viscosity of a stable formulation of the invention at room temperature is low enough to allow the application through narrow needles (e.g., a 27 G needle). Preferably, the viscosity is about 100 Pa x s or lower. More preferably, the viscosity is about 38 Pa x s or lower. A formulation of the invention is suitable for injection at room temperature or at slightly warmer (e.g, 25° C.) temperatures. No further excipients (e.g., solvents or plasticizers) are necessary for application of a formulation of the invention, but can be included if desired.
A “sustained-release” pharmaceutical formulation within the meaning of the invention is one in which the single chain antibody therein is protected over an extended period from degradation or elimination, and is delivered locally to a particular site or body compartment thereby lowering overall systemic exposure. Preferably, the extended period is at least 6 weeks and up to 14 weeks or more (i.e., 6, 7, 8, 9, 10, 11, 12, 13, 14, or more weeks). Upon exposure to an aqueous environment, as described herein, the single-chain antibody is slowly released from the formulation of the invention.
In one embodiment, a formulation of the invention is administered by intraocular injection, such as intravitreal injection, to a patient in need thereof. In the eye, a formulation of the invention forms a slow-release intravitreal depot, from which the single chain antibody is slowly released over an extended period of time.
The concentration (i.e., drug loading) of the single chain antibody in a formulation of the invention is at least about 1.0% (w/w), and preferably higher than 1.0% (one of skill in art can readily determine a desired concentration, which may be up to about 15% or higher, e.g., 1.0%, 1.25%, 1.50%, 1.75%, 2.0%, 2.25%, 2.5%, 2.75%, 3.0%, 3.25%, 3.5%, 3.75%, 4.0%, 4.25%, 4.5%, 4.75%, 5.0%, 7.5%, 10%, 12.5%, 15%, or higher), with hexPLA having molecular weight of at least about 1500 g/mol, (e.g., 1500 g/mol, 2000 g/mol, 2500 g/mol, 3000 g/mol, 3500 g/mol, 4000 g/mol, 4500 g/mol, 5000 g/mol, or higher). Preferably, the polymer weight is sufficient to maintain a formulation of the invention in a stable form (e.g., a spherical shape) when mixed with a single chain antibody, such that the formulation will settle at the bottom of an eye upon injection to the eye, thereby not influencing the path of sight. In certain embodiments, platicizers as known in the art may be included in a formulation of the invention. In certain embodiments, plasticizers may be included in a formulation of the invention. In such situations, one of skill in the art will recognize that the molecular weight of the hexPLA for use in a formulation of the invention has no specific limit (e.g., the hexPLA may have a molecular weight much higher than 5000 g/mol).
For administration to a subject, different sizes of formulation droplets can be selected, depending on the amount of single chain antibody desired for a particular use. In certain embodiments, the formulation mass for administration to a subject is 1.0 mg to about 100 mg. In a preferred embodiment, the formulation mass is about 10 mg to about 100 mg.
The term “antibody”, “single chain antibody”, or “scFv” as used herein is intended to refer to a molecule comprising an antibody heavy chain variable domain (or region; VH) and an antibody light chain variable domain (or region; VL) connected by a linker. Such scFv molecules can have the general structures: NH2-VL-linker-VH-COOH or NH2-VH-linker-VL-COOH.
In one embodiment, the single chain antibody is ESBA903, (as defined in WO 2009/155724, the entire contents of which are incorporated herein by reference), which comprises the sequence of SEQ ID NO: 1:
The formulation of the invention may, for example, be used with standard ampoules, vials, pre-filled syringes or multiple administration systems. In certain embodiments, a formulation of the invention is administered by ocular tissue injection such as periocular, conjunctival, subtenon, intracameral, intravitreal, intraocular, subretinal, subconjunctival, retrobulbar, or intracanalicular injections. In a preferred embodiment, the formulation is administered to the patient by intravitreal administration. For example, for such purposes, the formulation may be injected using a syringe. Accordingly, in one aspect the present invention also provides a delivery system which contains the liquid formulation selected from the group of single use injection syringes.
In certain embodiments, a delivery system comprises a container. Suitable containers include, for example, bottles, vials (e.g. dual chamber vials), syringes (such as dual chamber syringes) and test tubes. The container may be formed from a variety of materials such as glass or plastic. The container holds the formulation and the label on, or associated with, the container may indicate directions for use. The label may for example indicate that the formulation is useful or intended for intravitreal administration. The container holding the formulation may be a multi-use vial, which allows for repeat administrations (e.g. 2-6 administrations) of the formulation.
Accordingly, also provided is the use of the formulation according to the invention for the production of a delivery system for use in the treatment of a disease.
In another embodiment of the invention, an article of manufacture is provided which contains the formulation of the present invention and provides instructions for its use. Thus, an article of manufacture is provided herein which comprises: a) container which holds a concentrated formulation of a single chain antibody and hexPLA; and b) instructions for use.
The article of manufacture may further include other materials desirable from a commercial and user standpoint, including other buffers, diluents, filters, needles, syringes, and package inserts with instructions for use.
The invention also provides a process for preparing a sustained-release formulation comprising a single chain antibody and hexPLA.
The poly(lactic acid) (PLA) derivative hexylsubstituted poly(lactic acid) (hexPLA; poly(2-hydroxyoctanoic acid)), wherein all methyl groups along the PLA-backbone are substituted by hexyl groups, is a viscous liquid at room-temperature. It can be synthesized by ring-opening polymerization (Trimaille et al., 2004, Journal of Polymer Science Part A-Polymer Chemistry 42:4379) as well as by a green-chemistry polycondensation (Asmus et al., 2011, European Journal of Pharmaceutics and Biopharmaceutics 79:584). Preparation of hexPLA is described in the Examples herein. HexPLA is stable under dry heat sterilization conditions and formulations with small, lipophilic molecules released the active compound over several weeks.
Prior to formulation, the single chain antibody for formulation is preferably lyophilized as described herein. Lyophilization can be accomplished using well-known techniques in the art.
In certain embodiments, a formulation of the invention is prepared by cryo-milling. For example, lyophilized single chain antibody protein and the hexPLA polymer are slowly frozen to −80° C. and milled together in a SPEX 6700 Freezer/Mill (SPEX Industries, Edison, USA) under liquid nitrogen for 5 minutes. This cryo-milling procedure simultaneously reduces the particle size of the solid compound and homogeneously disperses it in the polymer matrix to form a suspension formulation. In certain embodiments, after milling, the formulation is slowly warmed to room-temperature under conditions suitable to avoid water condensation on the product (e.g., vacuum, inert gas, or hermetically closed cylinders). In other embodiments, mixing of a single chain antibody and hexPLA is carried out at a temperature at which the lyophilized single-chain protein is stable, preferably at temperatures below room-temperature, preferably at cooled conditions, preferably at temperatures below the glass transition point of the hexPLA polymer, preferably under cryo-milling.
Further provided is a process for preparing a sustained-release formulation comprising a single chain antibody and hexPLA for therapeutic applications, wherein: a single chain antibody is lyophilized, and the lyophilized antibody and hex-PLA are frozen and milled together to form a suspension.
In certain embodiments, the freezing step is carried out slowly to a temperature of −80° C., and the milling step is carried out under liquid nitrogen for about 5 minutes.
In another embodiment, the process further comprises warming the resulting suspension to room temperature or a slightly warmer temperature (e.g., 25° C.).
The present invention also provides the formulation of the invention for use in medicine. In particular, the use of the formulation for the manufacture of a medicament for the treatment of disease, such as an ocular disease, is provided.
In certain embodiments, the ocular disease is a retinal disease, such as a disease associated with ocular neovascularization. In certain embodiments, the ocular disease is macular degeneration, diabetic retinopathy, sequela associated with retinal ischemia, and posterior segment neovascularization, retinal edema, geographic atrophy, diabetic macular edema, and the like.
The appropriate dosage of the antibody will depend, for example, on the condition to be treated, the severity and course of the condition, whether the protein is administered for preventive or therapeutic purposes, previous therapy, the patient's clinical history and response to the protein, the type of antibody used, and the discretion of the attending physician. The antibody is suitably administered to the patient at one time or over a series of treatments and may be administered to the patient at any time from diagnosis onwards. The antibody may be administered as the sole treatment or in conjunction with other drugs or therapies useful in treating the condition in question.
Depending on the disease or disorder to be treated, a therapeutically effective amount of the antibody may be administered to the patient.
The contents of any patents, patent applications, and references cited throughout this specification are hereby incorporated by reference in their entireties.
Unless otherwise required by context, singular terms used herein shall include pluralities and plural terms shall include the singular.
The present disclosure is further illustrated by the following examples, which should not be construed as further limiting. The contents of all Figures and all references, patents and published patent applications cited throughout this application are expressly incorporated herein by reference in their entireties.
The humanized antibody-fragment ESBA903 was produced and lyophilized in-house by ESBATech, an Alcon Biomedical Research Unit (Schlieren, Switzerland). Three mL ESBA903 (10 mg/ml in 20 mM Na-citrate, pH 6.25) were added to 10 mL tubular-type vials, covered with bromobutyl stoppers that are suitable for lyophilization. Lyophilization was performed using a VirTis AdVantage Plus freeze dryer (Wizard 2.0 process controller, SP Scientific, Warminster, USA), equipped with an intergrated stoppering mechanism and a Leybold Trivac B high-performance vacuum pump (D4B/D6B, Oerlikon Corporate, Switzerland). The process was controlled using the actual shelf-temperature, and process data were recorded (Mentor/Wizard Synoptic 6.0, SP Scientific, Warminster, USA). Product temperature was recorded using thermocouples that had been placed in lyophilization vials. Vials were frozen to −55° C.; after evacuation of the lyophilization chamber (0.15 mbar), the shelf temperature was ramped to −10° C. in the course of several hours. Secondary drying was performed at 25° C. under full vacuum. The freeze dryer was floated with nitrogen gas before stoppering to avoid re-introduction of humidity and to minimize potential oxidative degradation processes. After reconstitution the protein proved fully monomeric.
Hexylsubstituted poly(lactic acid) (hexPLA) was synthesized by polycondensation of 2-hydroxyoctanoic acid as published (Asmus et al., 2011, European Journal of Pharmaceutics and Biopharmaceutics 79:584). Briefly, the polymers of 2500 g/mol and 5000 g/mol were synthesized by heating the monomer to 120° C. using 0.5 mol % sulfuric acid (Acros Organics, New Jersey, USA) as polycondensation catalyst. The reactions were performed under an oil-pump vacuum of 0.001 bar until the appropriate molecular weight was obtained. The polymers were purified by precipitation from acetone into aqueous 0.1 M NaHCO3, then dissolved in acetone, filtered over Celite® 545 coarse and the solvent removed under vacuum. The hexPLA polymers of 1500 g/mol and 3500 g/mol were prepared by an improved method, without the use of a catalyst. The monomer was simply heated to 150° C. and the melt was stirred under a vacuum of 0.001 bar. No additional synthesis steps or purifications were performed on these hexPLA polymers due to the absence of any additional substances like catalysts or solvents. All four polymers were sterilized using a standard European Pharmacopoeia dry heat sterilization method by heating them to 180° C. for 30 min. The molecular weight was determined by gel permeation chromatographie (GPC) using a Waters 515 HPLC pump, Waters 410 injector, Styragel HR 1-4 columns and Waters 717 GPC-detector (Waters Corporation, Milford, USA). The continuous phase was THF. Polystyrene standards (PSS, Mainz, Germany) were used for calibration. All chemicals and solvents were used as received.
The lyophilized ESBA903 protein and the hexPLA polymer were slowly frozen to −80° C. and milled together in a SPEX 6700 Freezer/Mill (SPEX Industries, Edison, USA) under liquid nitrogen for 5 min. This cryo-milling procedure simultaneously reduced the particle size of the solid compound and homogeneously dispersed it in the polymer matrix to form a suspension formulation. After milling, the formulation was slowly warmed to room-temperature under vacuum to avoid water condensation on the product.
In total, seven formulations were prepared with drug loadings in the range between 1.25% and 5.0% (w/w) protein in polymer, with weight average molecular weights from 1500 g/mol to 5000 g/mol (Table 1). The particle size of the incorporated lyophilisate and the homogeneous distribution inside the hexPLA were verified by optical microscopy using an Optiphot-2 microscope (Nikon, Tokyo, Japan).
Lyophilized ESBA903 formed suspensions with the viscous, lipophilic polymer hexyl-substituted poly(lactic acid) (hexPLA). Accordingly, the particle size of the incorporated protein lyophilisate was a key factor for the suitability of ESBA903-hexPLA formulations as injectables for an ophthalmic application, as the solid lyophilisate particles need to be small enough and homogenously dispersed to allow good injectability through narrow needles, physical suspension stability and controlled release from the matrix. For proteins, the formulation process is critical because shear stress and warming of the active compound can alter the protein structure and thus its activity. Therefore, a preparation method limiting these influences is necessary. Cryo-milling of the ESBA903 lyophilisate together with the polymer matrix was the method of choice because it allowed simultaneous milling of the solid particles and distribution in the polymer. The liquid nitrogen prevented the formation of heat spots during the milling process, reducing the risk of protein denaturation.
Seven ESBA903-hexPLA formulations (Table 1) were prepared to investigate the influence of the drug loading and polymer molecular weight on the rheology and injectability characteristics. The rheological behavior of the protein formulations is important for the injectability and the suspension stability. Two inherent factors influencing the viscosity, the hexPLA molecular weight and the ratio of incorporated drug, were separately studied in dependence of the formulation temperature.
The rheological behavior of the formulations was investigated using a RheoStress 1 Haake stress rheometer (Vreden, Germany), a cone-plate set-up with 0.10 mm gap spacing, 2° angle and a plate diameter of 35 mm. The measurements were performed at a shear rate of 0.1 s−1 and a heating cycle of 10 min ranging from 15° C. to 37° C.
However, the ease of injection was highly dependent on the polymer molecular weight, an important factor influencing the viscosity of the formulation, as can be seen in
As expected, higher drug loadings resulted in an increase in viscosity of the formulations because the incorporated particles hinder the free flow of the liquid hexPLA polymer. As displayed in
In the investigated range between 15 and 37° C. the correlation between temperature and viscosity can be expressed by a simple exponential equation for all formulations with correlation coefficients higher than 0.99 in the form: y=m×e(n×x).
The exponential factor (n) is determined by the type of polymer and thus, by the molecular weight, while the multiplication factor (m) depends on the rate of drug loading. Therefore, the viscosity of an ESBA903-hexPLA formulation can be calculated for a certain drug loading and defined temperature if the pure polymer was previously characterized for its rheology.
Injectability of parenteral formulations was examined with the needle length set to 12 mm as generally used for intraocular injections and the inner diameter to 0.210 mm, corresponding to a 27 G needle. Depending on the drug loading, an amount of 50 μL of formulation should be sufficient for a treatment period of 3 to 6 months. To allow a fast and practical injection by the ophthalmologist, the application process should last less than 15 seconds. A 0.5 mL syringe suitable for the application of 50 μL of ESBA903-hexPLA has a typical inner plunger diameter of around 4.0 mm. Finally, the maximal applicable force for good injectability was fixed at 50 N. Using these parameters, viscosity below 38 Pa×s allows easy injection, according to the law of Hagen-Poiseuille. As displayed in
The influence of the formulation process on the protein conformation was analyzed by size exclusion chromatography (SEC), with which ESBA903 monomers could be separated from dimers and other oligomers and quantified. Therefore, the protein was extracted from two formulations containing 5.0% protein in hexPLA of 2500 g/mol and 5000 g/mol immediately after the cryo-milling preparation process, and the extracts were compared to the pure single chain antibody fragment of the original lyophilisate.
The humanized VEGF-antibody fragment ESBA903 was quantified and the monomer ratio of the protein was assessed using size exclusion chromatography (SEC). The analyses were performed on a Dionex Ultimate 3000 HPLC system (Sunnyvale, Calif., USA) equipped with a TSK-Gel Super SW2000, 4.6 mm×30 cm columns (Tosoh Bioscience, Yamaguchi, Japan). An isocratic method was used with a flow rate of 0.35 mL/min of PBS running buffer (25 mM Na2HPO4, 0.1 M NaCl, pH 6.5). The column temperature was maintained at 30° C., and the protein was detected by UV absorption at 214 nm. Calibration standard solutions of ESBA903 were prepared in citrate buffer (20 mM sodium citrate, 125 mM NaCl, pH-value 6.25), and the sample solutions were analyzed as such. The applied method allowed separation of ESBA903 monomers from lower-order oligomers and soluble aggregates.
10 mg of the two formulations containing 5.0% ESBA903 in hexPLA of 2500 g/mol and 5000 g/mol, respectively were dispersed in three Eppendorf cups each. 0.7 mL citrate buffer (20 mM sodium citrate, 125 mM NaCl, pH 6.25) was added and the protein was extracted for 1.5 hours. Three different extraction methods were used to eliminate an influence of the handling during the extraction process on the protein conformation: i) gentle agitation, ii) incubation at 37° C. and shaking at 60 rpm (in vitro release conditions), iii) intense vortexing. Afterwards, the supernatant samples were analyzed regarding the monomer to multimer ratio by SEC-HPLC.
As displayed in
The storage stability of ESBA903 in the hexPLA matrix was assessed with suspension formulations containing 5.0% ESBA903 in hexPLA of 2500 g/mol and 5000 g/mol. 50 mg were filled into Eppendorf cups and stored at 4° C. and 37° C., respectively under light protection. After 4 weeks and 10 weeks, the protein was extracted from 10 mg of the sample formulations by vortexing with citrate buffer, as described above. The supernatant was analyzed by SEC-HPLC regarding the percentage of the ESBA903 monomer peak area relative to the total peak area.
Stability over long time periods is an issue for protein formulations. They are generally stored under refrigerated conditions to prevent denaturation even as lyophilisates. Therefore, a stability study of ESBA903-hexPLA formulations was performed. Samples containing 5.0% ESBA903 in hexPLA of 2500 g/mol and 5000 g/mol were stored at 4° C. After 4 and 10 weeks the protein was extracted from the polymer and analyzed by SEC-HPLC.
Table 2 summarizes the relative peak areas of the ESBA903 monomer compared to the peak area of the total extracted protein. Both formulations showed similar results under equal storage conditions, independent of the hexPLA molecular weight. Since the molecular weight determined the number of present polymer chains and thus of the polymer end groups, a considerable influence of the hydroxy- and carboxy-moieties on the protein was minimal, if not excludable. At 4° C. the rate of the protein monomer remained above 97% during the entire study period, proving that ESBA903 was not only compatible with hexPLA but also stable inside the polymer. Thus, the application-ready ESBA903-hexPLA formulations could be stored under standard refrigerator conditions as defined by the ICH. Since the monomer values remained above 97% without exhibiting a negative trend, storage times exceeding 10 weeks seem feasible as would be needed for convenient handling.
To investigate the stability of ESBA903 at body temperature, formulations were stored at 37° C. and analyzed after 4 and 10 weeks by SEC-HPLC (Table 2).
Both formulations with hexPLA of 2500 g/mol and 5000 g/mol, respectively displayed a slight trend of decreasing monomer, while dimers and multimers of ESBA903 were formed in the matrix. Nevertheless, the monomeric fraction remained above 90% after 10 weeks, suggesting that ESBA903-hexPLA suspensions were rather stable at 37° C., and that apparently no significant alterations in protein conformation took place. Most interestingly, with over 90% active monomer content, the protein was more stable in lyophilized state in the hexPLA polymer matrix at this temperature than in the buffer solution, from which only 71% of active protein were recovered after 10 weeks. The lyophilized protein was protected by the hydrophobic matrix, which prevented contact with the aqueous environment until its release.
Samples in citrate buffer solution containing 0.12 mg/mL ESBA903 were stored at 37° C. for 10 weeks. In a second approach under the same storage conditions, 2.2 mg/mL 2-hydroxyoctanoic acid were added as the final degradation product to investigate the influence of the degrading polymer on the protein stability. All experiments were done in duplicates. The amounts of the ESBA903 monomer were determined by SE-HPLC after 2 and 10 weeks.
A prescreening of different buffer systems revealed the citrate buffer with a pH of 6.5 as the best choice for this antibody fragment. In this work, the stability in this buffer solution was evaluated by SEC-HPLC, quantifying the ESBA903 monomer concentration, in the presence and absence of 2-hydroxyoctanoic acid as the final degradation product of hexPLA. In the pure buffer solution under release conditions, the ESBA903 monomer concentration decreased to 84% of its initial value after 10 weeks due to aggregation. In the buffer solution with added polymer degradation product, the monomer content was slightly lower with 71% after 10 weeks, assumingly related to the decrease in the pH-value. For the intended feasibility study of the sustained-release characteristics, the monomer stability above 70% was rated sufficient for a release test covering several weeks. However, the time dependent decreasing amount of monomer antibody fragments resulted in an underestimation of the released ESBA903 concentration in in vitro release experiments, especially for later time points.
After placing the ESBA903-hexPLA formulations into the aqueous buffer solution, the formulations formed single droplets of spherical shape (
To verify first the suitability of the release system, the behavior of the formulation and the protein in the aqueous release environment were tested. Afterwards, an in vitro study covering the influence on the release characteristics of the drug loading, the polymer molecular weight, and the amount of applied formulation was performed to identify good formulation candidates for ophthalmic sustained-release applications.
50±0.5 mg of the formulations were weighed into 20 mL sealable glass vials. The formulation containing 5.0% drug in hexPLA of 2500 g/mol was additionally investigated with 25±0.5 mg of formulation. 20 mL of citrate buffer (50 mM sodium citrate, 72 mM NaCl, 8 mM NaN3, pH-value 6.25) as the release medium were added. The samples were incubated at 37° C. and shaking at 60 rpm. 1 mL of the release-solution was taken from each vial after 1 and 3 days, after 1, 2, 3 and 4 weeks, followed by sampling every second week until week 14. Each time, the same volume of fresh citrate buffer was refilled to maintain the buffer volume constant. The ESBA903 concentration in the release samples was determined by SEC-HPLC.
To investigate the influence of the formulation drug loading on the release behavior, three formulations were prepared using the same hexPLA polymer of 2500 g/mol and ESBA903 loadings of 1.25%, 2.5%, and 5.0%.
Viewing the release curves in more detail, the fast release in the first 3 weeks can be explained by the release of protein molecules close to the surface of the depot. Most interestingly, no pronounced burst release was observed for the ESBA903-hexPLA formulations as it is known for many sustained-release formulations, e.g. with poly(lactic acid) (Maincent et al., 2009, European Journal of Pharmaceutics and Biopharmaceutics 73:337). Presumably, the liquid hexPLA polymer entirely covered the incorporated lyophilized protein preparation, shielding it from immediate dissolution. After 3 weeks the release rate decreased, presumably because the active compound was less accessible by the aqueous solution.
A difference in the relative release rate between the three drug loading formulations was only detectable during the first 2 to 3 weeks. With higher drug loadings the protein monomer release increased in the range between 1.25% and 5.0%. Since less of the polymer needs to be degraded in the beginning and the dissolution of the lyophilized drug preparation facilitates additional infiltration of water, the formulation with 5.0% ESBA903 released fastest in the initial phase.
In these classical in vitro tests a sustained-release was detectable for 6 weeks for the ESBA903-hexPLA formulations. This long duration is a significant improvement compared to the immediate release formulations currently marketed.
The 3500 g/mol and 2500 g/mol suspensions liberated the protein as expected, showing slower release for the formulation with the higher molecular weight. Furthermore, the period of pronounced release was longer for the formulation with 3500 g/mol reaching 4 weeks. In the later stage at 6 weeks both formulations resulted in a similar rate of release.
The ESBA903-hexPLA formulation with the polymer of 1500 g/mol showed a faster release compared to the 2500 g/mol and 3500 g/mol polymer during the first day, but then the daily release slowed down faster. The higher concentrations in the beginning were due to the lower viscosity and faster dissolution of accessible water soluble hexPLA oligomers, what might lead to an easier intrusion of water and release of active compound. Then presumably, a layer of protein free polymer formed out on the surface of the depot, rapidly decreasing the release rate. Nevertheless, also this formulation showed a release period of at least 6 weeks.
In
A general problem for the in vitro sustained-release tests of proteins is their limited stability in aqueous buffer solution, potentially resulting in degradation, oligomerization and precipitation of the released active substance. For ESBA903, the decline in the monomer concentration in the citrate buffer during 10 weeks is shown in
Table 3 summarizes the ESBA903 monomer concentrations in the release medium of the seven release samples between week 6 and 14. All samples showed almost constant concentrations, despite the known limited stability of the protein monomer in the buffer solution after release. The constant monomer concentrations can be explained by the fact that the protein monomer aggregation in the buffer solution comes to equilibrium with its further release from the polymer matrix. Thus, the overall release period of these formulations is probably much longer than 6 and 8 weeks, respectively.
The sample with 25 mg of the formulation containing 5.0% ESBA903 in hexPLA of 2500 g/mol released the protein continuously over the whole period of 14 weeks, showing steadily increasing ESBA903 monomer concentrations. The more pronounced release from the 25 mg of formulation was probably due to the higher surface to volume ratio, facilitating polymer degradation and resulting in a predominance of protein release. Nevertheless, small amounts of ESBA903-hexPLA formulation may be advantageous regarding ease of application and their release profile.
Next to the sustained-release profiles, the stability and the activity of the released single chain antibody fragment were assessed to evaluate the quality of the released protein. Therefore, samples from the release experiments were analyzed using sodium dodecyl sulfate polyacrylamide gel electrophoresis (SDS-PAGE) to control the integrity of the released protein monomer, and surface plasmon resonance analysis to investigate its activity. The in vitro release samples of the final time point at week 14 were compared to a freshly prepared ESBA903 reference. Protein species were separated on a NuPAGE Novex 12% Bis-Tris gel (Life Technologies Corporation, Grand Island, USA) using the buffers and reagents provided by the manufacturer. The protein bands were then stained using Coomassie Blue.
The resulting SDS-PAGE gel is displayed in
The affinity of the released ESBA903 monomer toward human VEGF was measured using surface plasmon resonance analysis in comparison to a fresh ESBA903 reference. For evaluation of the binding kinetics, surface plasmon resonance measurements using a BIAcore T100 were performed. Carboxymethylated dextran biosensor chips (CM4, GE HealthCare, Uppsala, Sweden) were activated with N-ethyl-N′-(3-dimethylaminopropyl) carbodiimide hydrochloride and N-hydroxysuccinimide according to the supplier's instructions. Recombinant human VEGF165 (Pep roTech EC Ltd., London, UK) was immobilized on a CM4 sensor chip using a standard amine-coupling procedure to achieve a response of approximately 500 resonance units. 2-fold serial dilutions (2.5-20 nM) of ESBA903 standard and formulation samples in HBS-EP buffer (10 mM HEPES, 150 mM NaCl, 3 mM EDTA, and 0.05% surfactant P20, pH 7.4) were injected into the flow cells at a flow rate of 30 μL/min for 5 minutes. Dissociation of the anti-VEGF scFv from the VEGF on the CM4 chip was allowed to proceed for 10 minutes. After each injection cycle, surfaces were regenerated with 2 injections of 100 mM NaOH.
The apparent dissociation (kd) and association (ka) rate constants and the apparent dissociation equilibrium constant (KD) were calculated with BIAcore T100 evaluation Software version 2.0.1 using a one-to-one Langmuir binding model (Biacore Inc., Uppsala, Sweden).
Three formulations were analyzed, including the formulations with 2.5% and 5.0% ESBA903 in hexPLA of 2500 g/mol and 2.5% in the 3500 g/mol polymer. Table 4 summarizes the obtained affinity data for the investigated time points after 3 days, 4, and the final 14 weeks.
All samples, independent of the formulation and time point, showed similar results for the association and dissociation rate constant and thus also for the equilibrium dissociation constant. The release samples showed comparable constants to the scFv reference.
Together with the low dissociation constant, the high association constants of more than 105 M−1 s−1 reflect the high affinity of the antibody fragment monomer to human VEGF, emphasizing its potency to scavenge the growth factor molecule. The slightly lower association constants of the samples compared to the reference were most probably due to imprecision in the protein monomer quantification. This assumption was supported by the fact of similar dissociation rate constants between samples and reference, which are independent of the concentration. The measured dissociation rate constants resulted in low equilibrium dissociation constants for the release samples at all time points up to 14 weeks. Thus, the antibody fragment monomers released from the hexPLA matrix were in their biologically active form over the whole sustained-release period of more than 3 months. Neither the drug loading nor the polymer molecular weight had a significant influence on the equilibrium dissociation constant, therefore they do not affect the protein structure, which otherwise would have resulted in an activity decrease. This further proved that hexPLA showed in vitro suitability as a parenteral sustained-release excipient for ESBA903, because it preserved and released the pharmaceutically active monomer of the antibody fragment.
It should be understood that the foregoing disclosure emphasizes certain specific embodiments of the invention and that all modifications or alternatives equivalent thereto are within the spirit and scope of the invention as set forth in the appended claims.
| Number | Date | Country | |
|---|---|---|---|
| 61594099 | Feb 2012 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14462065 | Aug 2014 | US |
| Child | 15245767 | US | |
| Parent | 13756932 | Feb 2013 | US |
| Child | 14462065 | US |