This application claims the priority benefit of Korean Patent Application No. 10-2020-0022331 filed on Feb. 24, 2020, in the Korean Intellectual Property Office, the disclosure of which is incorporated herein by reference for all purposes.
One or more example embodiments relate to a pseudo-ternary thermoelectric material, a method of manufacturing the pseudo-ternary thermoelectric material, a thermoelectric element, and a thermoelectric module.
A thermoelectric effect refers to a reversible direct conversion between heat energy and electric energy and is generated by a movement of electrons and holes in a material. The thermoelectric effect encompasses a Peltier effect which is applied to a cooling field using a temperature difference between both ends formed by a current applied from outside, and a Seebeck effect which is applied to a generation field using an electromotive force (EMF) generated from a temperature difference between both ends of a material.
A level of performance of a thermoelectric material may be referred to as a dimensionless thermoelectric figure of merit, or a ZT value, defined as represented by Equation 1 below.
In Equation 1 above, Z denotes a figure of merit. S denotes a Seebeck coefficient. σ denotes an electrical conductivity. T denotes an absolute temperature. κ denotes a thermal conductivity.
However, the electrical conductivity and the Seebeck coefficient have a trade-off relationship such that, when one of them increases, the other decreases. Thus, for approximately 50 years from the late 1950s to the early 2000s, the ZT value remained at approximately 1, which is a value of a bulk bismuth telluride (Bi2Te3)-based alloy, and was equivalent to merely about 10% of the efficiency of a Carnot engine. Thus, to increase the thermoelectric figure of merit, or the ZT value, as represented by Equation 1 above, there has been ongoing research on a method of increasing the Seebeck coefficient and the electrical conductivity, or a power factor (S2σ), and decreasing the thermal conductivity.
A currently commercialized thermoelectric material is manufactured through a single-crystal method, such as, for example, zone melting, a Czochralski process, a Bridgman process, and the like, and the performance thereof hovers at ZT 0.7 to 0.8 levels. In addition, it may have a cleavage surface along a base surface and thus be easily cracked, and thus be ineffective in terms of durability of a thermoelectric module manufactured and commercialized using the thermoelectric material.
A bismuth telluride (BiTe) alloy is known as a thermoelectric material having an optimal level of performance in a temperature range from approximately 300 degrees Celsius (° C.) to 500° C. However, it has a low thermoelectric property at room temperature, and it is only used for limited applications.
For a thermoelectric module for thermoelectric generation, it is required to develop a thermoelectric material having a relatively high thermoelectric property in a wide temperature range because there may be an environment where the temperature of a heat source is not consistent but varying. In related arts, a single thermoelectric material may not be used in an environment where there are various heat sources or the temperature of a heat source varies, and various thermoelectric materials having optimal thermoelectric properties at different temperatures may be combined to be used. However, when such different materials are combined, the mechanical and thermal stability of a thermoelectric module may be degraded due to the diffusion of heterogeneous materials and a difference in thermal expansion coefficient, and thus the long-term stability of the thermoelectric module may be degraded.
An aspect provides a pseudo-ternary thermoelectric material, a method of manufacturing the pseudo-ternary thermoelectric material, a thermoelectric element, and a thermoelectric module that may enable the achievement of a high-density and uniform Seebeck coefficient without hindering a movement of electrons, and enable the increase in production through the mass-production.
However, aspects or tasks to be achieved by the present disclosure are not limited to the aspect described in the foregoing, and thus other aspects or tasks not described above may also be clearly understood by those skilled in the art from the following description.
According to an example embodiment, there is provided a pseudo-ternary thermoelectric material including bismuth (Bi), antimony (Sb), tellurium (Te), and selenium (Se). A composition ratio of the pseudo-ternary thermoelectric material may be BixSb2-xTe3 in which 0.3≤x≤0.6, or (Bi2Te3)1-x-y(Sb2Te3)x(Sb2Se3)y in which 0<x<1 and 0.001≤y≤0.05.
A sintered density may be greater than or equal to 99%, and a density deviation may be 99.8±0.01%.
A difference in Seebeck coefficient between a center portion and an edge portion may be 2 millivolts per Kelvin (mV/K) to 4 mV/K.
A particle size in the center portion may be less than or equal to 6 micrometers (μm), and a particle size in the edge portion may be less than or equal to 10 μm. An average particle size in the center portion may be greater than an average particle size in the edge portion.
A degree of hardness of the center portion may be greater than or equal to 30 Vickers hardness (HV) and less than 50 HV, and a degree of hardness of the edge portion may be greater than or equal to 50 HV and less than or equal to 80 HV.
The pseudo-ternary thermoelectric material may be a p-type semiconductor.
The pseudo-ternary thermoelectric material may be large with a length of 50 millimeters (mm) to 70 mm, a thickness of 30T to 50T, and a weight of 1 kilogram (kg).
According to another example embodiment, there is provided a method of manufacturing a pseudo-ternary thermoelectric material, the method including melting bismuth (Bi), antimony (Sb), tellurium (Te), and selenium (Se), preparing an ingot by quenching a molten raw material obtained by the melting, preparing raw powder by pulverizing the ingot, and preparing a thermoelectric material specimen by performing spark plasma sintering (SPS) on the raw powder.
The melting of Bi, Sb, Te, and Se may include weighing such that a composition ratio is BixSb2-xTe3 in which 0.3≤x≤0.6, or (Bi2Te3)1-x-y(Sb2Te3)x(Sb2Se3)y in which 0<x<1 and 0.001≤y≤0.05.
The melting of Bi, Sb, Te, and Se may include melting Bi, Sb, Te, and Se in a temperature range between 650 degrees Celsius (° C.) and 750° C.
The preparing of the raw powder by pulverizing the ingot may be performed through one of blade milling, ball milling, attrition milling, gyro ball milling, and jet milling.
A powder size of the raw powder may be 0.1 μm to 50 μm.
The SPS may be performed for 10 minutes to 2 hours under a pressure of 10 megapascals (MPa) to 60 MPa and at a temperature of 200° C. to 500° C. in a vacuum atmosphere.
The thermoelectric material specimen may be cut in a direction perpendicular to a direction of the SPS.
According to still another example embodiment, there is provided a thermoelectric element including the pseudo-ternary thermoelectric material described above, or a pseudo-ternary thermoelectric material manufactured by the method described above.
According to yet another example embodiment, there is provided a thermoelectric module including a first electrode, a second electrode, and the thermoelectric element described above that is interposed between the first electrode and the second electrode.
Additional aspects of example embodiments will be set forth in part in the description which follows and, in part, will be apparent from the description, or may be learned by practice of the disclosure.
These and/or other aspects, features, and advantages of the present disclosure will become apparent and more readily appreciated from the following description of example embodiments, taken in conjunction with the accompanying drawings of which:
The following detailed description is provided to assist the reader in gaining a comprehensive understanding of the methods, apparatuses, and/or systems described herein. However, various changes, modifications, and equivalents of the methods, apparatuses, and/or systems described herein will be apparent after an understanding of the disclosure of this application. For example, the sequences of operations described herein are merely examples, and are not limited to those set forth herein, but may be changed as will be apparent after an understanding of the disclosure of this application, with the exception of operations necessarily occurring in a certain order. Also, descriptions of features that are known in the art may be omitted for increased clarity and conciseness. The features described herein may be embodied in different forms, and are not to be construed as being limited to the examples described herein. Rather, the examples described herein have been provided merely to illustrate some of the many possible ways of implementing the methods, apparatuses, and/or systems described herein that will be apparent after an understanding of the disclosure of this application.
The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting. As used herein, the singular forms “a,” “an,” and “the,” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprises,” “comprising,” “includes,” and/or “including,” when used herein, specify the presence of stated features, integers, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, operations, elements, components, and/or groups thereof. In addition, terms such as first, second, A, B, (a), (b), and the like may be used herein to describe components. Each of these terminologies is not used to define an essence, order, or sequence of a corresponding component but used merely to distinguish the corresponding component from other component(s).
It should be noted that if it is described in the specification that one component is “connected,” “coupled,” or “joined” to another component, a third component may be “connected,” “coupled,” and “joined” between the first and second components, although the first component may be directly connected, coupled or joined to the second component. In addition, it should be noted that if it is described in the specification that one component is “on” another component, the two components may be in contact with each other, and also a third component may be present therebetween.
Unless otherwise defined, all terms, including technical and scientific terms, used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure pertains based on an understanding of the present disclosure. Terms, such as those defined in commonly used dictionaries, are to be interpreted as having a meaning that is consistent with their meaning in the context of the relevant art and the present disclosure, and are not to be interpreted in an idealized or overly formal sense unless expressly so defined herein.
Hereinafter, example embodiments will be described in detail with reference to the accompanying drawings. Regarding the reference numerals assigned to the elements in the drawings, it should be noted that the same elements will be designated by the same reference numerals, wherever possible, even though they are shown in different drawings.
Hereinafter, a pseudo-ternary thermoelectric material, a method of manufacturing the pseudo-ternary thermoelectric material, a thermoelectric element, and a thermoelectric module will be described in detail with reference to examples and accompanying drawings. However, the present disclosure is not limited to the examples and accompanying drawings.
According to an example embodiment, a pseudo-ternary thermoelectric material includes bismuth (Bi), antimony (Sb), tellurium (Te) and selenium (Se). A composition ratio of the pseudo-ternary thermoelectric material may be BixSb2-xTe3 BixSb2-xTe3 in which 0.3≤x≤0.6, or (Bi2Te3)1-x-y(Sb2Te3)x(Sb2Se3)y in which 0<x<1 and 0.001≤y≤0.05. When a BiSbTe-based material is used as the thermoelectric material, it may have a relatively great level of performance in a temperature range including a room temperature, and may be used to radiate heat of highly integrated elements, various sensors, or the like.
The pseudo-ternary thermoelectric material may have a sintered density of 99% or greater and have a density deviation of 99.8±0.01%. The pseudo-ternary thermoelectric material may be manufactured by a melting and alloying method, and it is possible to manufacture a high-density and uniform BiSbTe-based thermoelectric material.
According to an example embodiment, the pseudo-ternary thermoelectric material may have a Seebeck coefficient difference between the center portion and the edge portion thereof, which may be 2 millivolts per Kelvin (mV/K) to 4 mV/K. Although a Seebeck coefficient of the edge portion may be greater than that of the center portion, a standard deviation may not be great, and it may be thus even or smooth as a whole.
A particle size in the center portion may be less than or equal to 6 micrometers (μm) and a particle size in the edge portion may be less than or equal to 10 μm. An average particle size in the center portion may be greater than an average particle size in the edge portion. Here, the smaller the particle size, the better. Currently, hundreds to tens nano-level thermoelectric powder may not be manufactured in large quantities, and only a few μm average particle size may be considered very fine powder.
A higher joule of heat may be generated at the center portion of the pseudo-ternary thermoelectric material, and grain growth may occur.
A degree of hardness of the center portion may be greater than or equal to 30 Vickers hardness (HV) and less than 50 HV, and a degree of hardness of the edge portion may be greater than or equal to 50 HV and less than or equal to 80 HV. A degree of hardness may gradually increase from the center portion to the edge portion.
The pseudo-ternary thermoelectric material may be a p-type semiconductor.
The pseudo-ternary thermoelectric material may be large in scale with a length of 50 millimeters (mm) to 70 mm, a thickness of 30T to 50T, and a weight of 1 kilogram (kg).
The pseudo-ternary thermoelectric material may be provided on a large scale without impurities or lattice defects, and have a single-phase, and high-density and uniform thermoelectric property.
According to another example embodiment, a method of manufacturing a pseudo-ternary thermoelectric material may include melting bismuth (Bi), antimony (Sb), tellurium (Te), and selenium (Se), preparing an ingot by quenching a molten raw material obtained by the melting, preparing raw powder by pulverizing the ingot, and preparing a thermoelectric material specimen by performing spark plasma sintering (SPS) on the raw powder.
The method of manufacturing the pseudo-ternary thermoelectric material may be performed through a melting and alloying method which may be effective in improving a thermal property.
Operation 110 may include melting bismuth (Bi), antimony (Sb), tellurium (Te), and selenium (Se).
The melting of bismuth (Bi), antimony (Sb), tellurium (Te), and selenium (Se) may include melting them by weighing such that a composition ratio is BixSb2-xTe3 in which 0.3≤x≤0.6, or (Bi2Te3)1-x-y(Sb2Te3)x(Sb2Se3)y in which 0<x<1 and 0.001≤y≤0.05.
A raw material of bismuth (Bi) may include at least one selected from a group consisting of, for example, Bi, BiF3, BiF5, BiCl3, BiBr3, BiI3, Bi2O3, Bi(OH)3, BiOCl, BiOI, BiONO3, Bi(NO3)3, Bi(NO3)3·xH2O (x is a natural number), BiPO4, and (BiO)2CO3. A raw material of antimony (Sb) may include at least one selected from a group consisting of, for example, Sb, SbOCl, SbCl3, SbCl5, Sb2O3, Sb2O5, Sb2O4, SbBr3, SbF3, and SbF5. A raw material of tellurium (Te) may include at least one selected from a group consisting of, for example, Te, TeO2, TeO3, Te(OH)6, Na2TeO3, K2TeO3, TeI4, TeBr4, and TeCl4.
For the melting of the raw material, there is no limit to a method. For example, the melting may be performed in a rocking furnace. In this example, it may be desirable to insert the weighted Pb, Te, and Bi into a vacuum ampoule, and then input and melt it in the rocking furnace.
The melting of bismuth (Bi), antimony (Sb), tellurium (Te), and selenium (Se) may be performed in a temperature range between 650 degrees Celsius (° C.) and 750° C. When the temperature for the melting is less than 650° C., the melting may not be performed evenly. In addition, when the temperature for the melting exceeds 750° C., a chemical composition amount may be inconsistent and a thermoelectric performance may be degraded, due to Te which is a volatile element.
Operation 120 may include preparing the ingot by quenching a molten raw material obtained by the melting.
Operation 130 may include preparing the raw powder by pulverizing the ingot. Here, the pulverizing may also include grinding or milling.
The preparing of the raw powder by pulverizing the ingot may be performed through one of blade milling, ball milling, attrition milling, gyro ball milling, and jet milling.
For the pulverizing, there is no limit to a method, and a general pulverizer may be used. The blade milling may be desirably used. Through the blade milling, coarse particles may be pulverized or milled by blades continuously until a sample passes through a separation screen disposed inside while the sample is moving along a flow of air by a blower. A portion of the sample that is not pulverized or milled may be captured or collected based on the transport of air. The pulverizing or milling may be performed in an inert state with oxygen being less than or equal to 0.10%.
A powder size of the raw powder may be 0.1 μm to 50 μm. The smaller the size of the raw powder, the better. Currently, hundreds to tens nano-level thermoelectric powder may not be manufactured in large quantities, and only a few μm average particle size may be considered very fine powder.
Operation 140 may include manufacturing a bar-shaped thermoelectric material specimen having a certain diameter and height by performing SPS on the raw powder. In addition, it is possible to manufacture a thermoelectric material pellet of a predetermined size by cutting the bar-shaped thermoelectric material specimen in a direction perpendicular to a direction of the SPS using an electric spark machine. Through the SPS, it is possible to obtain a robust sintered body of a thermoelectric material with little or least microcracks.
The SPS may be performed for 10 minutes to 2 hours, or desirably 10 to 30 minutes, under a pressure of 10 megapascals (MPa) to 100 MPa, or desirably 10 MPa to 60 MPa, and at a temperature of 200° C. to 500° C., or desirably 300° C. to 420° C., in a vacuum atmosphere. At a temperature less than 200° C., physical thermoelectric performance including, for example, a density and hardness of the sintered body may be degraded. At a temperature exceeding 500° C., a stable phase may not be obtained due to the volatilization of Te. In addition, under a pressure less than 10 MPa, a desired phase may not be obtained. Under a pressure exceeding 100 MPa, there may be no significant change in the property. Here, 10 minutes may be a minimum amount of time for sintering. However, the time exceeding 2 hours may not change the property.
Only when a temperature and a pressure for the SPS are greater than or equal to predetermined conditions, a high-purity thermoelectric material may be formed to have improved thermoelectric properties. However, under other conditions, a very small amount of components of the thermoelectric material may remain in a structure at the time of the manufacturing, which may hinder charge transfer and increase electric resistivity. Thus, when the temperature and pressure do not satisfy the predetermined conditions, the electric resistivity may increase and the thermoelectric property may thus be degraded. In addition, at a high temperature, a component of the thermoelectric material may be volatilized, and thus the thermoelectric property may change greatly according to a degree of volatilization of the component when it is repeatedly exposed to a thermal environment.
Through such an SPS, and an annealing process as needed, it is possible to induce an interfacial reaction between nanoparticles and the thermoelectric material. When a previous state is maintained before the reaction is completed, a nanocomposite phase formed by the reaction and nanoparticles that are not reacted may coexist, and thus a density may increase. Here, the newly generated interface may act as a scattering center that induces phonons (mainly mid/long-wavelength phonons) to be scattered, along with a surface of the nanoparticles. Thus, an additional reduction in lattice thermal conductivity may be expected.
The method of manufacturing the pseudo-ternary thermoelectric material may reduce the energy used to manufacture a thermoelectric element and reduce a production cost. Thus, the method may enable the mass-production of a large pseudo-ternary thermoelectric material.
According to still another example embodiment, a thermoelectric element may include a pseudo-ternary thermoelectric material according to an example embodiment, or a pseudo-ternary thermoelectric material manufactured by a method of manufacturing a pseudo-ternary thermoelectric material according to another example embodiment.
The thermoelectric element may be obtained by molding the pseudo-ternary thermoelectric material through a method such as, for example, a cutting process. For example, when the pseudo-ternary thermoelectric material has a single-crystal structure, a cutting direction for the pseudo-ternary thermoelectric material may be, for example, a direction perpendicular to a growth direction.
The thermoelectric element may be a p-type thermoelectric element. Such a thermoelectric element may be provided in a predetermined shape, for example, a rectangular parallelepiped. In addition, the thermoelectric element may be combined with an electrode, and exhibit a cooling effect by a current applied and exhibit a power generation effect by a device or a temperature difference.
According to yet another example embodiment, a thermoelectric module may include a first electrode, a second electrode, and a thermoelectric element interposed between the first electrode and the second electrode.
The insulators 210 and 220 may include at least one selected from a group consisting of, for example, gallium arsenide (GaAs), sapphire, silicon, pyrex, and quartz substrate. A material of the electrodes 212 and 222 may include at least one selected from a group consisting of aluminum, nickel, gold, and titanium. In addition, sizes thereof may be selected in various ways. For patterning the electrodes 212 and 222, any patterning method that is already known in related application fields may be used without a restriction. The patterning method may include at least one selected from a group consisting of a lift-off semiconductor process, a deposition method, and a photolithography.
According to an example, a p-type thermoelectric element and an n-type thermoelectric element may be alternately arranged, and at least one of the p-type thermoelectric element or the n-type thermoelectric element may include a thermoelectric material according to an example embodiment.
The thermoelectric module 200 may be a thermoelectric cooling system and a thermoelectric generation system, for example. The thermoelectric cooling system may include, for example, a micro cooling system, a general-purpose cooling device, an air conditioner, a waste heat generation system, or the like.
The example embodiments described herein will be described in greater detail with reference to examples below. However, they are not limited to the following examples.
In the following examples, thermoelectric material specimens having different values of x and y in a composition ratio of (Bi2Te3)1-x-y(Sb2Te3)x(Sb2Se3)y (x=0.76-0.79 and y=0.03) were prepared.
A thermoelectric material specimen was prepared using a Bi—Te based alloy as a raw thermoelectric material and a melting and alloying method. To prepare the Bi—Te based alloy, powder of each of raw materials Bi, Sb, and Te was weighed to be at a mole ratio (x=0.79 and y=0.03) of the composition ratio (Bi2Te3)1-x-y(Sb2Te3)x(Sb2Se3)y, and then inserted into a vacuum quartz tube and an argon (Ar) gas was injected. Subsequently, the quartz tube was inserted into a rocking or shaking furnace to melt the raw powder. Here, the melting was performed at a melting temperature of 960° C. for 10 hours.
An ingot was formed by taking out the melted raw powder from the rocking furnace, and then rapidly cooling it in air.
The ingot was milled and pulverized in an inert state with oxygen being less than or equal to 0.1% using a blade mill such that a powder size of the ingot is less than or equal to 45 μm. The blade mill may pulverize again coarse particles by blades continuously until a sample passes through a separation screen inside while the sample is being transported through a flow of air by a blower. Here, an unpulverized sample was captured or collected as the air flows.
The pulverized powder was prepared as a bar-type specimen using SPS. Here, conditions for the SPS included an atmosphere of a vacuum of 10−2 to 10−5 torr, a pressure of 30 to 60 MPa, a temperature of 250 to 400° C., and 30 minutes.
The prepared bar-type specimen was cut in a direction perpendicular to a direction of the SPS to have a coin shape having a diameter of 50 mm and a thickness of 37T.
Through the process described above, a specimen (Bi2Te3)0.18(Sb2Te3)0.79(Sb2Se3)0.03 was prepared.
A specimen (Bi2Te3)0.2(Sb2Te3)0.77(Sb2Se3)0.03 was prepared through the same process as Example 1, except that the raw powder of each of Pb, Bi, and Te was weighed to have certain x and y values (x=0.77 and y=0.03) of the ratio (Bi2Te3)1-x-y(Sb2Te3)x(Sb2Se3)y.
A specimen (Bi2Te3)0.21(Sb2Te3)0.76(Sb2Se3)0.03 was prepared through the same process as Example 1, except that the raw powder of each of Pb, Bi, and Te was weighed to have certain x and y values (x=0.76 and y=0.03) of the ratio (Bi2Te3)1-x-y(Sb2Te3)x(Sb2Se3)y.
Referring to
Table 1 below indicates results of measuring amounts of oxygen of powder of Example 1.
It was verified that a result of measuring an amount of oxygen of powder is 0.07%.
Referring to
Referring to
Leg Production Verification
A leg production was verified by slicing-plating-dicing a polycrystal material of 4 kg (production per day).
Manufacturing a Thermoelectric Device
A 40×40 thin copper sheet-type thermoelectric device (Tesbi metal substrate applied) for a vehicle was produced by applying a developed polycrystal p-type thermoelectric material and a single-crystal n-type material.
Referring to
According to an example embodiment described herein, it is possible to provide a large-scale pseudo-ternary thermoelectric material without impurities or lattice defects, and having a single-phase, and a high-density and uniform thermoelectric property.
According to an example embodiment described herein, it is possible to reduce energy and a production cost to be used to manufacture a thermoelectric element, and mass-produce a large pseudo-ternary thermoelectric material, by employing a method of manufacturing a pseudo-ternary thermoelectric material described herein.
According to an example embodiment described herein, it is possible to manufacture a thermoelectric element and a thermoelectric module using a pseudo-ternary thermoelectric material described herein.
While this disclosure includes specific examples, it will be apparent to one of ordinary skill in the art that various changes in form and details may be made in these examples without departing from the spirit and scope of the claims and their equivalents. The examples described herein are to be considered in a descriptive sense only, and not for purposes of limitation. Descriptions of features or aspects in each example are to be considered as being applicable to similar features or aspects in other examples. Suitable results may be achieved if the described techniques are performed in a different order, and/or if components in a described system, architecture, device, or circuit are combined in a different manner, and/or replaced or supplemented by other components or their equivalents. Therefore, the scope of the disclosure is defined not by the detailed description, but by the claims and their equivalents, and all variations within the scope of the claims and their equivalents are to be construed as being included in the disclosure.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2020-0022331 | Feb 2020 | KR | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 20070095383 | Tajima | May 2007 | A1 |
| 20130164165 | Yeh | Jun 2013 | A1 |
| 20160035954 | Salvador | Feb 2016 | A1 |
| 20200227609 | Tsurumi | Jul 2020 | A1 |
| Number | Date | Country |
|---|---|---|
| 2002111086 | Apr 2002 | JP |
| 10-1367719 | Feb 2014 | KR |
| 20180023765 | Mar 2018 | KR |
| 1020190009341 | Jan 2019 | KR |
| 20190012456 | Feb 2019 | KR |
| WO-2019039320 | Feb 2019 | WO |
| Entry |
|---|
| Choi, Jong-Il et al. Chromosome 4q25 variants and biomarkers of myocardial fibrosis in patients with atrial fibrillation, Journal of Cardiovascular Electrophysiology, 2019; 30: 1904-1913. |
| Number | Date | Country | |
|---|---|---|---|
| 20210265548 A1 | Aug 2021 | US |