The viscose process is still the most important technology for producing a family of products, also called elongate cellulose members, like filaments (rayon), staple fibres, films (cellophane), sausage casings etc. The key process step is the formation of sodium-cellulose-xanthate, a cellulose derivate used as an intermediate product for dissolving the cellulose in a solvent.
The main raw material for derivatisation reactions is the so-called dissolving pulp, produced traditionally with the sulphite or the sulphate process, using different kinds of timber; for example hardwood such as eucalyptus and softwood such as spruce or pine. Dissolving pulp can be characterized by a multitude of parameters. Some important ones are:
Under special processing conditions a low grade dissolving pulp or so-called paper grade pulp can be used as a raw material. These pulps can be characterized by the following parameters:
The viscose process comprises of the following conventional steps, briefly summarized as follows:
The key quality-related issue for achieving a good viscose dope for spinning and casting is the evenness of the degree of substitution (DS) of the cellulose-xanthate across the different molecular weights of the cellulose in the AC, used for xanthation. There are three known methods to improve the evenness of the DS:
Surfactants are added to the pulp before the drying procedure in the pulp mill or during the steeping process in the viscose mill.
Despite the application of the methods mentioned above, the DS is normally still relatively uneven. For this reason the viscose dope before spinning/casting, and after dissolving, is ripened by storage at or around room temperature for some hours, during which time chemical changes, including redistribution of xanthate groups, take place.
During any alkaline treatment-steeping or extraction with aqueous sodium hydroxide-of the dissolving pulp, i.e. of the cellulose fibres in the pulp, some hemi-cellulose is extracted from the cellulose fibres and dissolved in the aqueous sodium hydroxide. The concentration of highest solubility and also highest swelling and opening of the structure is about 11% NaOH.
The more hemi-cellulose is dissolved the more holes are created in the interfibrillar spaces of the cellulose fibres. These holes have a tendency to collapse during pressing of the AC in order to remove the excess of aqueous sodium hydroxide, necessary for the subsequent AC-ageing and xanthation procedures.
Under normal conditions—using a standard dissolving pulp and normal steeping conditions with 17-19% NaOH—the collapsing of the structure of the cellulose fibres in the AC is not a major problem for the xanthation procedure. A real deterioration of the heterogeneous xanthation reaction can only be observed under two essential conditions:
This invention relates to pulp reactivity enhancement.
The invention provides according to a first aspect, a method of producing an alkali cellulose by alkaline treatment of a pulp which includes the improvement of carrying out the alkaline treatment in the presence of a spacer capable of entering the holes in the interfibrillar spaces of the cellulose fibres.
Further according to the invention, a method of producing an alkali cellulose which includes steps of providing a pulp and subjecting the pulp to an alkaline treatment to produce the alkali cellulose in the presence of a spacer capable of entering the holes in the interfibrillar spaces of the cellulose fibres.
The spacer enters the holes in the interfibrillar spaces of the cellulose fibres, particularly those created by the removal of hemi-cellulose, reducing the tendency for collapse to occur, for example during the subsequent pressing step. The spacer will have a molecular size suitable to be accommodated by the holes or spaces.
The spacer is typically a hydrophilic polymer which is soluble or dispersable in an aqueous solution (typically water or aqueous sodium hydroxide) with a molecular weight of 1000 to 2500, preferably 1250 to 1750, more preferably 1400 to 1600, most preferably about 1500.
Preferably, the spacer is capable of forming hydrogen bridges or ether linkages with the cellulose molecules. Chemical groups which allow for the formation of such bridges are hydrophilic groups such as carboxyl, carbonyl and hydroxide groups.
Examples of suitable spacers are polyethylene glycols, polyvinyl alcohols and polyacrylates, particularly as the sodium salt.
The amount of spacer used will vary according to the nature of the spacer. Typically, the amount of spacer used is 0.5% to 2% (m/m) based on the cellulose.
The spacer can be added during the alkaline treatment or before, e.g. to the dissolving pulp and before drying.
In many methods of producing alkali cellulose, hemi-cellulose is extracted or removed from the cellulose fibres leading to collapse of the holes or spaces created and hence collapse of the fibres on to themselves. This invention provides a method of reducing this tendency by introducing a spacer in the holes or spaces left by the extracted or removed hemi-cellulose. Thus, this invention relates to pulp reactivity enhancement and has particular application in the following methods.
The special requirements of the viscose filament process, i.e. low hemi-cellulose levels in steeping and therefore also in the AC for xanthation, necessitate the use of high purity cellulose (dissolving) pulps, for example, a 96-alpha dissolving pulp from a sulphite process. In order to achieve such a high alpha grade of 96%, the Eo stage of the bleaching sequence must use a sodium hydroxide concentration in the range of 8-9% (compared to 1-3.5% for 90-92-alpha pulps), in order to be able to extract sufficient hemi-cellulose with the aqueous sodium hydroxide to achieve a high alpha-level.
This concentration is just in the range of the abovementioned 11±3% NaOH for causing a subsequent collapsing during AC-pressing.
With a typical commercial surfactant (Berol 388 which is an ethoxylated alcohol) only inferior and unacceptable viscose dope qualities were achieved. With the addition of PEG (polyethylene glycol) as a spacer during steeping in a quantity of 0.5% (m/m) on cellulose, good viscose dope qualities can be obtained. The spacer can also be added to the dissolving pulp before drying in the pulp mill.
In order to take out as much as possible hemi-cellulose from the cellulose fibres (as cotton linters or dissolving pulp) during steeping some viscose mills employ when using cotton linters as the main raw material source, a double steeping procedure: about 18% sodium hydroxide in a first steeping and 14% NaOH in a second steeping. The last concentration is also just in the aforementioned range of 11±3% causing a subsequent collapsing. The viscose dope quality recovers fully working under these conditions with 0.5% PEG on cellulose as a spacer, if dissolving pulp is used. Again, the spacer can be added to the pulp before drying in the pulp mill.
As described above, the opening of the structure of the cellulose fibres in the pulp by activation treatments like e-beaming causes more or less a subsequent collapsing after any alkaline treatment-extraction or steeping—at any NaOH concentration, because of the excellent accessibility of the hemi-cellulose molecules in the interfibriller spaces, where they work as an inner spacer.
In the case of e-beaming the collapsing of the created holes can directly be measured after AC pressing by determining the so-called bulk density of the AC in comparison to an untreated normal pulp; or the same pulp before e-beaming.
The presence of a spacer during the alkaline treatment reduces the tendency for collapse to occur.
B.1) E-Beaming with Extraction
The principal idea of this method is the activation of the dissolving pulp with e-beaming, in-line or off-line, combined with a subsequent extraction of hemi-cellulose with an aqueous sodium hydroxide of 1-2% NaOH at 40-60° C.
The extraction has the aim not only to extract from the dissolving pulp the already available hemi-cellulose before e-beaming, but also to dissolve and extract most of the hemi-cellulose formed during e-beaming because of the DP degradation associated with the pulp activation.
The lower hemi-cellulose content improves the quality of the pulp for derivatisation reactions, especially viscose making: lower hemi-cellulose content in the aqueous sodium hydroxide for steeping which results in lower hemi-cellulose content in AC which results in a more even degree of substitution (DS).
Laboratory trials have demonstrated, that this method only produces a suitable dissolving pulp for achieving the aforementioned aim, if a spacer like PEG is added during the alkaline extraction procedure in an amount of 0.5-2% (m/m) on cellulose.
Normally the dissolving pulp is directly used in steeping after an in-line or off-line e-beaming. The traditional sodium hydroxide concentration for steeping an e-beam pulp is 16% NaOH. Because of the collapsing of the structure of the cellulose fibres during AC-pressing a very dense AC is obtained and responsible for an inferior viscose dope quality.
Laboratory trials have demonstrated, that in the presence of the spacer like PEG during steeping in a concentration of 0.5-2% (m/m) on cellulose excellent viscoses dopes can be obtained, also in comparison with the addition of a typical commercial surfactant (e.g. Berol 388) instead of a spacer.
Under these conditions the advantages of the e-beam technology can be used:
The spacer can also be added to the pulp after an in-line e-beaming.
The invention will now be described in more detail with reference to the following non-limiting Examples.
In the Examples, the following abbreviations are used:
CiA: Cellulose in alkcell
SiA: Soda in alkcell
CiV: Cellulose in viscose
AR:alkali ratio
Kw*: viscosity corrected value for filterability.
In the Examples, the Berol, PEG, PAS and PVA were added during the steeping step.
Conditions for making viscose:
Mercerisation:
Steep soda: 220 g/l
Steeping: 30 min at 50° C.
alternative additives
Pressing:
CiA: 33%
SiA: 16%
Alkcell ageing:
Temperature: 54° C.
Time: 150 to 180 min
Xanthation:
33% CS2
Temperature: 30° C.
Time: 90 min
Viscose:
CiV: 9%
AR: 0.6
Influence of 0.5% PEG 1500 and 0.5% Berol 388 on filterability (Kw*-value)
Filterability describes how much of viscose passes through a certain filter area in a certain time and allows therefore a qualification of viscose. The relation between filterability and viscose dope quality can be described as follows provided that comparable viscose making conditions were used:
Conditions for making viscose:
Influence of PEG on filterability (Kw*-value)
3.1 E-Beaming of Dissolving Pulp without Pre-Extraction
Conditions for making viscose:
Pre-treatment:
Degradation of pulps by electron beam irradiation up to a DP of 300 to 350
Mercerisation:
Steep soda: 180 g/l
Steeping: 30 min at 50° C.
Alternative additives
Pressing:
CiA: 33%
SiA: 14%
Xanthation:
26% CS2
Temperature: 30° C.
Time: 90 min
Viscose:
CiV: 9%
AR: 0.52
Influence of 0.5% PEG and 0.5% Berol on filterability (Kw*-value)
3.2 E-Beaming of Dissolving Pulp with Pre-Extraction
Conditions for making viscose:
Pre-treatment:
Degradation of pulps by electron beam irradiation up to a DP of 300 to 350
Pre-extraction:
Soda: 1% NaOH
Temperature: 6° C.
Time: 60 min
Mercerisation:
Steep soda: 180 g/l
Steeping: 30 min at 50° C.
Alternative Additives
Pressing:
CiA: 33%
SiA: 14%
Xanthation:
24% CS2
Temperature: 30° C.
Time: 90 min
Viscose:
CiV: 9%
AR: 0.53
Influence of PEG on filterability (Kw*-value)
Conditions for making viscose:
Mercerisation:
Steep soda: 220 g/l
Steeping: 30 min at 50° C.
alternative additives
Pressing:
CiA: 33%
SiA: 16%
Alkcell ageing:
Temperature: 54° C.
Time: 210 to 220 min
Xanthation:
33% CS2
Temperature: 30° C.
Time: 90 min
Viscose:
CiV: 9%
AR: 0.6
Influence of 0.5% PEG, PAS, PVA (all 1500) and Berol 388 on filterability (Kw*-value)
| Number | Date | Country | Kind |
|---|---|---|---|
| 2006/04915 | Jun 2006 | ZA | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/IB2007/052212 | 6/12/2007 | WO | 00 | 2/26/2009 |