Embodiments of the present invention generally relate to punch tooling utilized in forming metallic containers, and more specifically to punch tooling with surface texturing utilized in forming metallic food and beverage containers.
Light-weight metal containers, including food and beverage containers, and the tooling employed to manufacture and form the metal food and beverage containers are generally known in the art. Typically, it is desired to manufacture metal food and beverage containers with as little material and the highest rates of production as possible, while maintaining desired quality characteristics. In typical metal forming processes used in metal container manufacturing, the metal is sized through various stages of tooling, which forms the desired shape and size of the container. The process often starts cutting a circular metal “blank” out of a sheet of metal. Then the metal blank (typically aluminum) placed into a cupping press, where the blank is “drawn” or pulled up into the shape of a cup, which has a diameter of about 3.5 inches to 4.0 inches and a height of about 1.3 inches for traditional 12 oz. cans. The following steps and processes typically work the cup (e.g., in a bodymaker machine) through numerous ironing and redrawing operations. This process reduces the wall thicknesses of the starting material and elongates the container into the desired final container shape. Here, a sleeve holds the cup in place and a punch is lowered swiftly into the cup and redraws the cup to a diameter of about 2.6 inches and a height of 2.25 inches for traditional 12 oz. cans. The punch (also called a punch sleeve) then pushes the cup against multiple ironing rings (typically three, also called ironing die), which stretch and thin the cup walls such that the cup for a traditional 12 oz. can is 5 inches tall. This entire process (the redrawing and ironing) is done in one continuous punch stroke.
The typical process of ironing deforms the metal between an ironing die and a punch sleeve. The metal is deformed under ultra-high forming pressures and loads, where the metal climbs or elongates up the punch surface as the container wall thickness is reduced and the container height is increased. The friction of the tools in the ironing process often determines the resultant quality of the ironing process.
Punch tooling (punch and die) is often made of hardened steel or tungsten carbide. A die is located on the opposite side of the workpiece and supports the material around the perimeter of the container. There is a small amount of clearance between the punch and the die to prevent the punch from sticking in the die. The amount of clearance needed depends on the thickness of the workpiece (i.e., the metallic container), with thicker materials requiring more clearance, but the clearance is always less than the thickness of the workpiece.
Traditional treatments of the punch surface finish have been consistently monolithic applications to amend the surface finish in an effort to control friction and removability of the can from the tooling once ironed. The friction of the punch, the ironing load, and the speed of the punch often determines the defect rates. Such defects are known as tearoffs. “Tearoffs” are a primary defect observed in the normal ironing process, where metal containers that experience excessive tensile loads have a portion of the container which breaks away from the remainder of the cylindrical container. The punch finish has a direct effect on the tear off frequency. Traditional treatments of the punch surface include polished surfaces or crosshatched surfaces that are applied to the entire surface of the punch such that the punch has a single surface treatment. Punch surface texture supports and improves container “stripability,” i.e., removal from the punch and ironing die. Thus, punch surface finishes are used to facilitate and improve stripability and, as a result, reduce the defect rates of tear-offs during the manufacturing process.
Common treatments of the punch surface include scoring the sidewall of the punch sleeve in crosshatching patterns. The angle and the coarseness of the crosshatching patterns may vary from punch to punch.
All ductile materials stretch to some extent during punching, which often causes the punch to stick in the container. If this happens, the punch must be physically pulled back out of the container and the container must be pulled off of the punch. This process is known as “stripping” because you are stripping the can from the punch and the defect is called “removability.” Additionally, the finer the finish on the punch, the more difficult the stripability (i.e., the ability to easily remove the can from the punch sleeve without excessive damage).
A third defect common in metal container manufacturing is due to the interaction of the punch's normal surface treatments in relationship to ironing forces and the actual releasing of ironing pressure during discharge of metal from the ironing dies. These defects are often described as “ears,” “pinch points,” or “feathered edges.” Ears are ripples at the top of the metal container after the drawing and ironing process. Additionally, ears are elongated regions with an irregular area that causes unequal loading of the ironing die and the resultant defects multiply creating feathered edges, pulled ears, or pinch points.
The material of the punch is often a very durable material, such as carbides, ceramics, and/or tool steel. However, due to millions and millions of cycles these finished surfaces degrade over time due to friction. The degradations cause deformation inconsistencies and changes to the sidewall characteristics of the metal container. Numerous defects can occur and the container walls may contain defects that require removal from the production stream and ultimately reduce the efficiency of the production process.
Various embodiments and configurations of the present invention relate to a novel system, device, and method for providing surface texturing on a punch used to make metal food and beverage containers. The novel punch surface texture provided herein reduces the defect rate during the punching process. Features of the present invention may be employed in a wide range of food and beverage container manufacturing, including metallic cans and metallic bottles.
It is one aspect of various embodiments of the present invention to provide a punch sleeve with specific surface texturing to facilitate the manufacture of metallic containers, including cans and bottles. The metal of the container is ironed over the surface of the punch sleeve with significant force and pressure as the metal walls of the container are forced through dies and are compressed and placed into tension. Therefore, deformations of the metal occur as a result of the surface treatment of the punch.
Thus, it is one aspect of various embodiments of the present invention to provide a punch surface treatment that addresses and resolves specific quality defects. For example, the present invention can reduce and eliminate the quality defects caused by the ironing processes by uniquely designing the surface texture coarseness, finish treatment, and placement of textured regions on the exterior surface of the punch.
It is a further aspect of various embodiments of the present invention to provide punch surface texturing that improves container quality, reduces spoilage rates, and substantially eliminates the quality defect of slivers. Slivers are created with normal crosshatch patterns as metal flakes and particles (i.e., “slivers”) become trapped in the grooves of the crosshatch texture. These metal particles then become ironed into the container walls during post-ironing operations. For example, a particle or multiple particles are created in the first or second ironing operations, then are deposited on or attached to the container walls during the third or fourth ironing operations. Embodiments of the present invention reduce slivers by reducing the intensity of the debris fields created during the container manufacturing process, which reduces the number of defects. For example, using a punch sleeve according to embodiments of the present invention reduces the number of defective containers from 50 defects an hour using traditional punch sleeves to zero defects an hour using a punch sleeve according to embodiments of the present invention.
Another aspect of various embodiments of the present invention is to provide punch surface texturing with a crosshatch pattern having a specific angle and roughness (micron level) that is designed to reduce the tear off rates and optimize production quality and throughput while maintaining stripability.
The ability of the container to be removed from the punch efficiently at high speeds without damage is critical to lightweight metal container manufacturing. Thus, one aspect of various embodiments of the present invention is to provide punch surface texturing that improves and enables better stripping on lower wall thicknesses and lighter containers at higher rates of production (i.e., speeds).
One aspect of various embodiments of the present invention is to provide a punch with various surface textures that also uses at least one normal crosshatch pattern to retain the stripability of the surface finish. Therefore, the speed and integrity of the lightweight metal container is retained, while the quality defects are eliminated or minimized.
It is one aspect of various embodiments of the present invention to provide a metal can punch with various surface textures. It is another aspect of various embodiments of the present invention to provide a punch surface treatment with specific positional and regionalization of the texturing. Thus, in some embodiments, various surface textures are applied to the punch surface at critical regions to optimize and improve metal container manufacturing quality, reliability, speed, and throughput. Additionally, embodiments of the present invention retain the draw and iron process bandwidth, retain the capability for stripping, improve sliver suppression, and improve optimal edge quality. In one embodiment of the present invention, the food or beverage container punch comprises two or more surface textures. Further, the food or beverage container punch can comprise of three distinct surface finishes. Alternatively, the punch can comprise four distinct surface finishes.
It is another aspect of various embodiments of the present invention to provide a metal bottle punch with various surface textures. The threaded and neck areas of bottles are hyper sensitive to deep crosshatch patterns. Therefore, a polished or control surface finish in the neck and thread regions of the bottle can be optimized as needed for the desired results. Specifically, in some embodiments, the punch is smooth in the bottle's threaded area to reduce the occurrence of false positive curl cracks during machine vision inspections. Further, having a smooth punch surface in the bottle's threaded area improves the ability to form threads on the bottle during later steps in the bottle manufacturing process.
In one embodiment of the present invention, the punch surface contains two or more regions and each region contains a different predetermined texture. The surface texture is often described herein using the “Ra” value for the surface. Ra is a common roughness (also called surface roughness) parameter used in the art. Ra is the arithmetic average of the roughness profile of the surface, meaning that Ra is calculated using an arithmetic average of absolute values from a two-dimensional roughness profile. Further, specific finishes and Ra ranges are designed into interactional regions of the punch to improve the container quality during the ironing process. The application of surface finishes in specific regions allows the container walls to be less tapered, less oval, and less feathered and it also reduces or eliminates slivers.
For example, in one embodiment, the punch outer surface comprises polished regions or surfaces less than 8 Ra positioned at the corresponding heights of the container during the redraw process through the second container progressions such that the cut edge movements during ironing are optimized. The specific heights of these regions depend on the size of the finished container, which can be anywhere from 3 oz. to 32 oz. to 750 mL.
In some embodiments, the punch sleeve is made of carbide. In other embodiments, the punch sleeve is made of steel or other metal alloy. In still other embodiments, the punch sleeve is made of a ceramic material.
In various embodiments of the present invention, a metal container punch is provided that is manufactured with conventional manufacturing equipment. Alternatively, in some embodiments, the punch surface treatments are applied with a custom machine. In other embodiments, the custom surface treatments are applied by hand with skilled workmanship. However, the best application of treating/texturing multiple regions of the punch surface must remove and maintain constant material thickness and resultant diameters of each of the textured regions. Thus, the machine is designed to remove the material of the base carbide, tool steel, or ceramic punch such that the entire surface of the punch is concentric, linear, and parallel. The resultant metal container manufacturing process requires a consistent punch surface (meaning, for example, concentric, linear, and parallel) to produce consistent wall thickness and container weights.
As appreciated by one skilled in the art, the present invention could be used to manufacture 12 oz. cans, smaller metallic containers between about 3-11.5 oz., and larger metallic containers between about 13 oz. and 32 oz. Embodiments of the present invention can also be used to manufacture 500 mL, 587 mL, and 750 mL metallic containers. In one embodiment of the present invention, a punch used in a process to form metal containers is provided, the punch comprises a nose positioned on one end of the punch; a trailing edge positioned opposite the nose on a second end; a cylindrical portion positioned between the nose and the trailing edge; and an outer surface comprising: a first region proximate the nose and having a first length and a first surface finish; a second region proximate to the first region and having a second length and a second surface finish, wherein the second surface finish is different than the first surface finish; and a third region positioned proximate to the second region and to the trailing edge, the third region having a third length and a third surface finish, wherein the third surface finish is different than the second surface finish.
In additional embodiments, the first surface finish comprises a crosshatch pattern and the second surface finish is polished between an Ra 2 and an Ra 8 finish. The third surface finish can also comprise a crosshatch pattern. In various embodiments, the first length of the first region is between about 1.0 inches and 2.0 inches, the second length of the second region is between about 1.0 inches and 2.0 inches, and the third length of the third region is about 1.0 and 2.5 inches.
In one embodiment of the present invention, a method of texturing an exterior surface of a punch sleeve used in metallic container manufacturing is provided, comprising (a) providing the punch sleeve comprising a nose positioned on one end of the punch; a trailing edge positioned opposite the nose on a second end; a cylindrical portion positioned between the nose and the trailing edge; and an outer surface comprising a first region proximate the nose; a second region positioned proximate to the first region; and a third region position proximate to the second region and positioned proximate the trailing edge; (b) applying a first crosshatch pattern to the first region using a first diamond impregnated tab with a first micron finish; (c) applying a second crosshatch pattern to the third region using a second diamond impregnated tab with a second micron finish; and (d) polishing the first region, the second region, and the third region.
In a further embodiment of the present invention, the method further comprises using an air pressure of about 30 psi when applying the first crosshatch pattern; and positioning the first crosshatch pattern at an angle between about 30 degrees and 60 degrees relative to a longitudinal axis of the punch sleeve. In various embodiments of the present invention, at least one of the first crosshatch pattern and the second crosshatch pattern is applied by rotating the punch at a first speed while simultaneously contacting an exterior surface of the punch with at least one of the first diamond impregnated tab and the second diamond impregnated tab operating at a second speed.
In one embodiment, a punch used in a manufacturing process to form metal containers is provided comprising: a nose positioned on one end of the punch; a trailing edge positioned opposite the nose on a second end of the punch; a cylindrical portion positioned between the nose and the trailing edge; and an outer surface comprising: a first region positioned proximate to the nose and having a first length and a first surface finish; a second region positioned proximate to the trailing edge and having a second length and a second surface finish, wherein the second surface finish is different than the first surface finish; and a third region positioned proximate to at least one of the first region and the second region and having a third length and a third surface finish, wherein the third surface finish is different than the second surface finish. In a further embodiment, the first surface finish comprises a first crosshatch pattern, and wherein the second surface finish comprises a second crosshatch pattern, the second crosshatch pattern is a 10-60 micron level crosshatch pattern and the first crosshatch pattern is a coarser crosshatch pattern than the second crosshatch pattern, and the third surface finish is polished between an Ra 2 and an Ra 8 finish. In some embodiments, the first region extends from a first point on the punch proximate the nose to a second point on the punch, and wherein the first length is between about 15 percent and about 35 percent of a total length of the punch, the third region extends from the second point on the punch to a third point on the punch, and wherein the third length is between about 15 percent and about 35 percent of the total length of the punch, and the second region extends from the third point on the punch to a fourth point on the punch, and wherein the second length is between about 15 percent and about 35 percent of the total length of the punch. In still further embodiments, the first length of the first region is between about 1.0 inches and about 2.0 inches, the second length of the second region is between about 1.0 inches and about 2.5 inches, and the third length of the third region is between about 1.0 inches and about 2.0 inches. In some embodiments, the punch has a fourth region positioned between the first region and the third region and having a fourth length and a fourth surface finish.
In one embodiment, a method of texturing an exterior surface of a punch sleeve used in a metallic container manufacturing process is provided comprising: providing the punch sleeve, comprising: a nose positioned on one end of the punch sleeve; a trailing edge positioned opposite the nose on a second end; a cylindrical portion positioned between the nose and the trailing edge; and an outer surface comprising: a first region proximate the nose; a second region positioned proximate to the trailing edge; and a third region positioned between the first region and the second region; applying a first textured pattern to at least one of the first region, the second region, and the third region using a first etching tool with a first micron finish; applying a second textured pattern to at least one of the first region, the second region, and the third region using a second etching tool with a second micron finish, wherein the second textured pattern is applied to a different region than the first textured pattern; and polishing the first region, the second region, and the third region.
In further embodiments, the method includes using a force between about 10 pounds and about 20 pounds when applying the first textured pattern, and wherein the first textured pattern is a crosshatch pattern. In a further embodiment, the method comprises positioning the first textured pattern at an angle between about 30 degrees and about 60 degrees relative to a longitudinal axis of the punch sleeve. In another embodiment, the method comprises positioning the crosshatch pattern at an angle between about 30 degrees and about 60 degrees relative to a longitudinal axis of the punch sleeve. In some embodiments, at least one of the first textured pattern and the second textured pattern is a crosshatch pattern. In one embodiment, at least one of the first textured pattern and the second textured pattern is applied by rotating the punch sleeve at a first speed while simultaneously contacting an exterior surface of the punch sleeve with at least one of the first etching tool and the second etching tool, and wherein the at least one of the first etching tool and the second etching tool moves along a longitudinal axis of the punch sleeve at a second speed while simultaneously contacting the exterior surface of the punch sleeve. In one embodiment, wherein the first region has a first length between about 1.0 inches and about 2.0 inches, the second region has a second length between about 1.0 inches and about 2.5 inches, and the third region has a third length between about 1.0 inches and about 2.0 inches.
In another embodiment, an apparatus for providing surface texturing on a punch sleeve used in a metal container manufacturing process is provided comprising: a connection mechanism positioned proximate to a first end of the machine, the connection mechanism configured to interconnect to one end of the punch sleeve, and wherein the connection mechanism rotates the punch sleeve around a longitudinal axis of the punch sleeve; an arm positioned parallel to the longitudinal axis of the punch sleeve; and an etching tool for applying a first surface texture to a first region of an outer surface of the punch sleeve, said etching tool moveably interconnected to the arm such that the etching tool can slide along the arm and move along the longitudinal axis of the punch sleeve. In further embodiments, the apparatus comprises a means to apply a force on the etching tool in a direction toward the punch sleeve, wherein the connection mechanism rotates the punch sleeve while the etching tool simultaneously moves along the longitudinal axis of the punch sleeve. In various embodiments, the apparatus comprises a second etching tool for applying a second surface texture to a second region of the outer surface of the punch sleeve, and a programmable logic system which operably communicates with the machine to control the positioning of the etching tool with respect to the punch sleeve. In still further embodiments, the etching tool comprises a diamond impregnated tab with a micron finish and the second etching tool comprises a second diamond impregnated tab with a second micron finish. In various embodiments, the etching tool further comprises an etching tool holder or a tab holder, wherein the etching tool holder or the tab holder is interconnected to the arm and is configured to hold the etching tool or tab. In some embodiments, the apparatus further comprises an electronic display for displaying content, a processor, memory, and a communication interface to connect to a communication network.
The phrases “at least one,” “one or more,” and “and/or,” as used herein, are open-ended expressions that are both conjunctive and disjunctive in operation. For example, each of the expressions “at least one of A, B and C,” “at least one of A, B, or C,” “one or more of A, B, and C,” “one or more of A, B, or C,” and “A, B, and/or C” means A alone, B alone, C alone, A and B together, A and C together, B and C together, or A, B, and C together.
Unless otherwise indicated, all numbers expressing quantities, dimensions, conditions, and so forth used in the specification and claims are to be understood as being modified in all instances by the term “about”.
The term “a” or “an” entity, as used herein, refers to one or more of that entity. As such, the terms “a” (or “an”), “one or more,” and “at least one” can be used interchangeably herein.
The use of “including,” “comprising,” or “having” and variations thereof herein is meant to encompass the items listed thereafter and equivalents thereof as well as additional items. Accordingly, the terms “including,” “comprising,” or “having” and variations thereof can be used interchangeably herein.
It shall be understood that the term “means” as used herein shall be given its broadest possible interpretation in accordance with 35 U.S.C. Section 112(f). Accordingly, a claim incorporating the term “means” shall cover all structures, materials, or acts set forth herein, and all of the equivalents thereof. Further, the structures, materials, or acts and the equivalents thereof shall include all those described in the summary of the invention, brief description of the drawings, detailed description, abstract, and claims themselves.
These and other advantages will be apparent from the disclosure of the invention(s) contained herein. The above-described embodiments, objectives, and configurations are neither complete nor exhaustive. The Summary of the Invention is neither intended nor should it be construed as being representative of the full extent and scope of the present invention. Moreover, references made herein to “the present invention” or aspects thereof should be understood to mean certain embodiments of the present invention and should not necessarily be construed as limiting all embodiments to a particular description. The present invention is set forth in various levels of detail in the Summary of the Invention as well as in the attached drawings and the Detailed Description and no limitation as to the scope of the present invention is intended by either the inclusion or non-inclusion of elements, components, etc. in this Summary of the Invention. Additional aspects of the present invention will become more readily apparent from the Detailed Description, particularly when taken together with the drawings.
The accompanying drawings, which are incorporated in and constitute a part of the specification, illustrate embodiments of the invention and together with the Summary of the Invention given above and the Detailed Description of the drawings given below, serve to explain the principles of these embodiments. In certain instances, details that are not necessary for an understanding of the invention or that render other details difficult to perceive may have been omitted. It should be understood, of course, that the invention is not necessarily limited to the particular embodiments illustrated herein. Additionally, it should be understood that the drawings are not necessarily to scale.
To assist in the understanding of the embodiments of the present invention the following list of components and associated numbering found in the drawings is provided herein:
Similar components and/or features may have the same reference label. Further, various components of the same type may be distinguished by following the reference label by a letter that distinguishes among the similar components. If only the first reference label is used, the description is applicable to any one of the similar components having the same first reference label irrespective of the second reference label.
Although the following text sets forth a detailed description of numerous different embodiments, it should be understood that the legal scope of the description is defined by the words of the claims set forth at the end of this disclosure. The detailed description is to be construed as exemplary only and does not describe every possible embodiment since describing every possible embodiment would be impractical, if not impossible. Numerous alternative embodiments could be implemented, using either current technology or technology developed after the filing date of this patent, which would still fall within the scope of the claims. To the extent that any term recited in the claims at the end of this patent is referred to in this patent in a manner consistent with a single meaning, that is done for sake of clarity only so as to not confuse the reader, and it is not intended that such claim term be limited, by implication or otherwise, to that single meaning.
The accompanying drawings, which are incorporated in and constitute a part of the specification, illustrate embodiments of the invention and together with the summary of the invention given above and the detailed description of the drawings given below, serve to explain the principles of the invention.
It should be understood that the drawings are not necessarily to scale, and various dimensions may be altered. In certain instances, details that are not necessary for an understanding of the invention or that render other details difficult to perceive may have been omitted. It should be understood, of course, that the invention is not necessarily limited to the particular embodiments illustrated herein.
Various embodiments of the present invention are described herein and as depicted in the drawings. It is expressly understood that although the figures depict metal container punches, and methods and systems for using and manufacturing the same, the present invention is not limited to these embodiments. It should also be understood that the terms “container” and “container body” may be used interchangeably in some instances.
Referring to
The punch sleeve 2 has a nose 6, a trailing edge 22, an inner surface 32, an outer surface 36, and a mounting transition section 26 proximate the trailing edge 22. The mounting transition section 26 is tapered from the diameter of the third region 18 to the diameter of the ram at the trailing edge 22 of the punch 2. The ram is the part of the punch machine to which the punch 2 is mounted or interconnected at the trailing edge 22 of the punch 2. The outer surface 36 of the punch sleeve 2 comprises three (or more) regions: a first region 10, a second region 14, and a third region 18. In various embodiments, the nose 6 of the punch sleeve 2 does not have crosshatching. Further, the mounting transition section 26 also does not have crosshatching because this portion of the punch 2 is not intended to contact the metallic container. The surface of the mounting transition section 26 is “as ground.”
The first region 10 has a coarse crosshatch pattern and extends from a point above the punch nose 6 to the height of the redrawn cup in one embodiment or to about 0.5 inches below the height of the redrawn cup in a second embodiment. The redrawn cup is the first stage of the drawn and ironing process. This stage transforms the cup into a smaller diameter cylinder, which is then ready for the ironing process. It is a redrawing process, and not necessarily an ironing process, but some metal shape and transformation takes place. Elimination of wrinkles in the container during the redrawing process is key to optimize performance. The positioning of the first region 10 enables the edge of the cup to clear the first region's 10 crosshatch pattern by a sufficient amount to not hinder performance. Note that the length of the first region 10 may change slightly for each specific can size and starting metal gauge. A rougher surface Ra finish coarseness may be used in the first region 10 because this is the thickest container wall and the lowest compressive loads of the punch processes are experienced in the first region 10. Stripability is also maintained by using a surface finish coarseness that facilitates stripping.
In the embodiment shown, the second region 14 extends from the end of the first region 10 to the top edge of the last progression height, meaning the second region 14 extends to the height of the container after the last ironing progression, which may be a first ironing progression, second ironing progression, third ironing progression, etc. In one embodiment, the second region 14 has a surface pattern that is polished to below an Ra 12 finish. In another embodiment, the second region 14 has a surface pattern that is polished to between an Ra 2 and an Ra 8 finish. The second region 14's surface is relatively smooth and without scratches or grooves because scratches and grooves create slivers of small metal particles, which cause defects in later processing steps. The surface treatment of the second region 14 is designed to suppress particle fragments and sliver generation from the ironing process. Each can size has a banded region (which corresponds to the second region 14) that is located at a starting height just below the height of the redrawn cup and extends up the punch cylinder 2 to just above the height of the second ironing progression height in a normal 3-die tool pack arrangement. On multiple ironing die embodiments, the banded section would extend to just above the edge locations of the final ironing height. The surface texture and length of the second region 14 is specifically designed to eliminate debris and sliver generation.
In some embodiments, the second region 14 is broken into multiple regions for applications where distances between progression heights dictate some roughness for improved stripability. However, the top edge of each progression height would optimize sliver or debris suppression with specific surface texturing as described above. Thus, having a smooth the second region 14 eliminates or reduces the reattachment of the slivers created during the metal container manufacturing process.
The third region 18 may extend from the end of the second region 14 to a point at or above the transition from a midwall to a topwall of the container. In some embodiments, the third region 18 is interconnected to the end portion 36. The desired surface finish for the third region 18 is the lightest micron level required, which aids stripability. The surface finish of the third region 18 is generally between a 10-60 micron level crosshatch pattern. Thus, the crosshatch pattern on the third region 18 is lighter than the crosshatch pattern on the first region 10. The pattern angularity may result in some process benefit but ideally the crosshatch pattern in the third region 18 is between about 30-60 degrees relative to the longitudinal axis of the punch 2. Alternatively, the crosshatch pattern may be positioned at an angle between 20 degrees and 80 degrees relative to the longitudinal axis of the punch 2.
In some embodiments, the third region 18 is polished prior to crosshatching. Thus, a polished surface is first produced and then a crosshatch pattern is applied on top of the polished surface. In other embodiments, the order is reversed: a crosshatch pattern is applied to the third region 18 and then a polished treatment is applied to the third region 18 to smooth the surface edges and sharpness. Further, punches used to manufacture bottles can also benefit from a polished the third region 18 because the bottle drawn and ironed container requires smoothness in the neck area for optimal threading. The smooth region of the punch used to create the neck portion of the bottle may be the third region 18 in some embodiments or may be a fourth region (not shown) in other embodiments, depending on the height of the bottle and the progression-height correspondence. The region of the punch used to create the neck portion of the bottle must have a surface finish that is specially applied and designed for improved bottle necking, coating adhesion, and threading performance. Because the threaded and neck areas of bottles are hyper sensitive to deep crosshatch patterns, a polished or control surface finish in the neck and thread regions of the bottle is typically used.
In
In the embodiment shown in
In
An etching tool, which may be a diamond-impregnated tab or other tab or tool, is positioned where the marker 208 is shown in
In some embodiments, the machine comprises a processor, memory, an input device (which can be a touch-screen display surface configured to receive touch input), a display to display content, and a power source (which can be a battery). The machine can further include data storage, software, a user interface, an input device, an output device, a communication network, such as Bluetooth or WiFi, and/or a communication interface for communicating with another smart phone or computing device and/or the communication network. In further embodiments, the processor can include any processor capable of performing instructions encoded in software or firmware. Further, the processor can be provided to execute instructions contained within the memory and/or data storage. The processor can comprise a controller or application specific integrated circuit (ASIC) having or capable of performing instructions encoded in logic circuits. The memory may be used to store programs or data, including data comprising content. As examples, the memory may comprise RAM, SDRAM, or other solid state memory. Alternatively or in addition, data storage may be provided. The data storage may generally include storage for programs and data. In one embodiment, the machine comprises a programmable logic system that operably communicates with the machine to control the positioning of the etching tool with respect to the punch sleeve. As such, a user can program the machine to create any number of desired surface textures on the desired regions of the punch sleeve. The machine then will automatically texture and polish the desired portions of the punch sleeve. In some embodiments, the method of providing surface texture on the punch sleeve comprises applying a first textured pattern to the first region using a first etching tool with a first micron finish, applying a force between about 10 pounds and 20 pounds on the punch sleeve to scratch the punch sleeve, and positioning the textured pattern at between about 30 degrees and 60 degrees relative to the longitudinal axis of the punch. In one embodiment, the first etching tool is a first diamond impregnated tab. In some embodiments, the textured pattern is a crosshatch pattern. In some embodiments, the machine used to apply the textured pattern and other surface finishes to the outer surface of the punch sleeve uses a pneumatic cylinder and an adjustable air pressure to apply the force on the etching tool on the punch sleeve. In one embodiment, this force is applied by using an air pressure of about 30 psi. In other embodiments, the machine used to apply the textured pattern and other surface finishes to the outer surface of the punch sleeve uses mechanical or hydraulic means of creating pressure or force on the etching tool on the punch sleeve. Next, applying a third textured pattern to the third region using a second etching tool with a second micron finish, using an air pressure of about 30 psi, and positioning the third textured pattern at between about 30 degrees and 60 degrees relative to the longitudinal axis of the punch. In one embodiment, the second etching tool is a second diamond impregnated tab. Then polish the first, second, and third regions of the punch sleeve. Alternatively, the punch may be polished before the textured patterns or crosshatch patterns are applied to the first and third regions. To crosshatch punch sleeves according to embodiments of the present invention, the crosshatching machine will use special cams and special attachments (e.g., working heads) for different surfacing technologies.
Each food and beverage container size has specific heights and regions (i.e., locations) of greater value for maintaining stripability and optimizing performance, which reduces undesirable quality defects. The patterns of the textured area (including the crosshatched areas) are adjusted based on the number of ironing steps or die setups in the forming process.
While various embodiments of the present invention have been described in detail, it is apparent that modifications and alterations of those embodiments will occur to those skilled in the art. However, it is to be expressly understood that such modifications and alterations are within the scope and spirit of the present invention, as set forth in the following claims. Further, the invention(s) described herein is capable of other embodiments and of being practiced or of being carried out in various ways. It is to be understood that the phraseology and terminology used herein is for the purpose of description and should not be regarded as limiting.
This application claims the benefit of U.S. Provisional Patent Application Ser. No. 62/187,575, filed Jul. 1, 2015, entitled “Punch Surface Texturing for Use in the Manufacturing of Metallic Containers,” which is hereby incorporated by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 62187575 | Jul 2015 | US |