Patent Application
20050221979
1. Field of the Invention
The present invention relates to a purification catalyst for exhaust gas, and specifically relates to a purification catalyst for exhaust gas in which nitrogen oxides (NOx), carbon hydride (HC), and carbon monoxide (CO) contained in an exhaust gas emitted from an internal combustion engine of an automobile or the like can be simultaneously and effectively reduced so that the exhaust gas is purified.
2. Related Art
For purifying exhaust gas containing, for example, CO, HC, and NO, precious metal elements (Pt, Rh, Pd and Ir) exhibit high performance. Therefore, it is preferable to employ the above-mentioned precious metal elements in the purification catalyst for exhaust gas. These precious metals are generally used by supporting one of them on Al2O3 of high surface-to-weight ratio. On the other hand, composite oxides (for example, a perovskite oxide), made by combining various elements, have extremely varied properties. Therefore, it is preferable for a purification catalyst for exhaust gas to employ the above-mentioned composite oxides. Moreover, when the precious metal is supported on the composite oxides, the properties of precious metal are significantly changed. From this viewpoint, a preferable performance for purifying exhaust gas can be obtained in the purification catalyst for exhaust gas in which a precious metal is supported on a composite oxide.
Various catalysts mentioned above are now being developed, and for example, a technique in which a cohesion rate of the precious metal can be reduced by providing a perovskite oxide as a support, judging from deterioration of the precious metal by reduction of active sites by cohesion of the precious metal, is proposed (see Japanese Unexamined Application Publication No. 5-86259). Moreover, another technique in which reduction of PdO can be reduced by using a perovskite oxide in which the A site is defective, judging from reducing PdO which is an activated species in a NO reduction reaction when the precious metal is Pd, whereby the PdO changes to Pd which has low activity, is proposed (see Japanese Unexamined Application Publication No. 2003-175337).
However, in the conventional purification catalyst for exhaust gas for automobiles, a large content of the precious metals (Pt, Rh, and Pd) are used in order to effectively purify CO, HC, and NOx emitted from automobiles. When large amounts of the precious metals are used as described above, the cost is simultaneously increased along with increase in catalyst performance. Therefore, the above-mentioned embodiment is not always effective. Accordingly, development of a purification catalyst for exhaust gas in which production cost is not high has been requested.
Moreover, the precious metals (for example, Pt, Rh, and Pd) are generally used in a condition of supporting one of them on Al2O3 which is a support having high surface-to-weight ratio. Therefore, these precious metals can be supported on Al2O3 in a highly dispersed condition. However, Al2O3 is a stable compound, and Al2O3 therefore does not interact with a supported precious metal. Therefore, activity for each precious metal cannot be improved, whereby high performance cannot be maintained after a long period of use or after exposure to a high temperature atmosphere. Accordingly, development is desired of a support, in which high performance can be maintained after a long period of use or after exposure to a high temperature atmosphere, that is, endurance can be improved, by effectively utilizing the precious metals, in other words, by improving the activity for each precious metal.
Al2O3 has no effect in which activity for each precious metal is improved because the surface of Al2O3 is extremely stable and is electrically stable, whereby Al2O3 does not electrically interact with the precious metal. Moreover, a reason that the endurance of the Al2O3 is low is as follows. That is, deterioration patterns of the precious metal catalyst (specifically, Pd-based catalyst) are classified into a decrease in activity based on reduction of active sites by cohesion of Pd and a decrease in activity based on decomposition and reduction of PdO in an oxidation state which is highly active. Due to the quite stable surface of the Al2O3 as mentioned above, cohesive properties along with the precious metal flux in using the catalyst cannot be suppressed, and an oxidation state of PdO on the surface of Al2O3 cannot be stabilized. Therefore, when Al2O3 is used as a support, the activity is extremely decreased, whereby an excellent endurance of a purification catalyst for exhaust gas cannot be realized.
The present invention was made in light of the above various findings, and it is hence an object thereof to provide a purification catalyst for exhaust gas, specifically in which activity for each precious metal is improved by effectively utilizing the precious metal without incurring a high production cost, whereby endurance is improved.
The present inventors have intensively researched purification catalysts for exhaust gas, in which activity for each precious metal is improved at a low cost, whereby endurance can be improved. As a result, it was found that when Pd is supported on a composite oxide in which a rational formula is MXO3 (M: alkali metal element, X: an element in group 5 in periodic table) and a crystal structure is a perovskite structure, the production cost can be reduced and improvement of catalyst activity can be realized, whereby the endurance of the purification catalysts for exhaust gas can be improved. The present invention was made in light of the above findings.
That is, a purification catalyst for exhaust gas of the present invention has a composite oxide supporting Pd, the composite oxide has a rational formula MXO3 in which M is an alkali metal element and X is an element in group 5 in periodic table, and a crystal structure of the composite oxide is a perovskite structure.
According to the present invention, by supporting Pd on a composite oxide having a rational formula MXO3 in which M is an alkali metal element and X is an element in group 5 in periodic table, poisonous gases, for example, NO, CO, and HC in the exhaust gas can be effectively purified from an initial using stage to an using stage in a high temperature (980° C.). Additionally, purification performance specifically for CO and HC in the poisonous gases can be extremely improved in the purification catalyst for exhaust gas of the present invention. Hereinafter, a reason in which components in the purification catalyst for exhaust gas of the present invention are restricted will be respectively explained.
That is, in a composite oxide used in the purification catalyst for exhaust gas of the present invention, a rational formula is MXO3 in which M is an alkali metal element and X is an element in group 5 in periodic table, and elements constituting the composite oxide are a monovalent alkali metal element, a pentavalent element in group 5 in periodic table, and oxygen. A reason that X (an element in group 5 in periodic table) is used as an element constituting the purification catalyst for exhaust gas of the present invention is as follows. That is, the pentavalent state is the most stable in X. However, X can be changed in various valences from bivalent state to pentavalent state. For example, Nb is listed as an element included in X. Oxidants, for example, O2 and NOx, and reductants, for example, CO, HC, and H2 are contained in the exhaust gas. Therefore, when Nb constituting NbO3 is exposed to the exhaust gas, Nb is oxidized or reduced to change the valences thereof, whereby oxygen defects are generated. The oxygen defects make lattice oxygen mobile, whereby the oxygen can be absorbed and emitted at the surface of the catalyst. Due to the effect mentioned above, MNbO3 provides Pd supported on the surface of the MNbO3 with oxygen, or MNbO3 absorbs oxygen from PdO. Pd exists as PdO in an exhaust gas atmosphere, oxidation of Pd and reduction of PdO are repeated to purify the exhaust gas. In purification, a cycle of oxidation and reduction of PdO is promoted due to provision and absorption of oxygen by MNbO3 which is a support, whereby purification activity of the exhaust gas can be improved.
Moreover, a reason in which M (alkali metal element) is used as an element constituting the purification catalyst for exhaust gas of the present invention is as follows. That is, while M (alkali metal element) exhibits an alkaline reaction, NOx in the exhaust gas exhibits an acidic reaction. Due to strong interaction of alkaline component and acidic component, NOx in the exhaust gas atmosphere is strongly attracted to M in MXO3, whereby NOx is condensed on a surface of MXO3. Therefore, a condensed NOx exists in the vicinity of the Pd which is an active site and is supported on MXO3, whereby purification reaction of NOx is promoted. Due to high reactivity of the condensed NOx, both purification reaction of NOx, and purification reaction of CO and HC are promoted.
Furthermore, a reason that a crystal structure of a purification catalyst for exhaust gas of the present invention is a perovskite structure is as follows. That is, MXO3 having a perovskite structure is extremely thermally stable. Therefore, even after MXO3 is exposed to an atmosphere at a high temperature of about 1000° C., the perovskite structure is not destroyed and decrease in the surface-to-weight ratio is small. Therefore, a crystal structure of the MXO3 is predetermined to be a perovskite structure, whereby implant and cohesion of Pd can be suppressed along with decrease in the surface-to-weight ratio.
As mentioned above, in the purification catalyst for exhaust gas of the present invention, a promotion effect of oxidation and reduction of PdO by X (an element in group 5 in periodic table), a condense effect of NOx by M (alkali metal element), and a maintenance effect of endurance by perovskite structure can be combined, whereby activity of the purification catalyst for exhaust gas in reaction can be extremely improved in comparison with conventional catalyst. That is, according to the purification catalyst for exhaust gas of the present invention, the activity for each precious metal can be improved by effectively utilizing the precious metals, whereby endurance can be improved. Additionally, this effect can be realized after endurance running at a high temperature of about 1000° C.
Hereinafter, the present invention will be concretely explained by the following Manufacturing Examples.
Production of Composite Oxides as Support
Predetermined amounts of K2CO3 and Nb2O5 were mixed by a wet blending in a mortar to obtain a mixed material. The mixed material was moved to an aluminum crucible, and was heated to 800° C. at a rate of 5° C./min in a muffle kiln, and a heat treatment was performed at 800° C. for 10 hours. Owing to the heat treatment, a composite oxide of which the composition was KNbO3 was obtained.
A composite oxide of which the composition was NaNbO3 was obtained in a manner similar to Manufacturing Example 1.
A composite oxide of which the composition was KTaO3 was obtained in a manner similar to Manufacturing Example 1.
A commercially available Al2O3 (AF115 produced by Sumitomo Chemical Co., Ltd.) was prepared.
A composite oxide of which the composition was LiNbO3 was obtained in a manner similar to Manufacturing Example 1.
Support of a Precious Metal
The following treatment was respectively performed with the composite oxides of the Manufacturing Examples 1 to 5. That is, a predetermined amount of a palladium nitrate-dihydrate was dissolved in ion-exchanged water, whereby a palladium nitrate solution was obtained. The palladium nitrate solution and a predetermined amount of composite oxides (KNbO3, NaNbO3, KTaO3, Al2O3 and LiNbO3) powder were put in an eggplant-shaped flask, and while the flask was evacuated by a rotary evaporator, a mixture of the solution and the powder was evaporated and solidified in a hot bath at 60° C. After heating up to 250° C. at a rate of 2.5° C./min in a muffle kiln, the temperature of the mixture was further raised to 750° C. at a rate of 5° C./min, and the mixture was held at 750° C. for 3 hours. As a result, catalyst powders of Manufacturing Example 1 to 5 in which PdO is impregnated and supported on the above-mentioned composite oxides or oxide were obtained.
Differences in crystal system among catalysts powders of Manufacturing Examples 1 to 5 were investigated.
Estimation of Activity
Next, initial activities and activities after endurance running were estimated for the obtained catalyst powders. The estimation was performed by flowing model exhaust gas of an automobile into catalysts under conditions in which A/F (air-fuel ratio) was substantially 14.6 and SV (stroke volume) was 5000 h−1. Endurance running was performed for 20 hours at an endurance running temperature of 980° C. by using model exhaust gas in which A/F (air-fuel ratio) was substantially 14.6. These results are shown in Tables 1 and 2. That is, the Table 1 shows a temperature at which HC, CO, and NO are reduced by 50% in a temperature increase test of catalysts before the endurance running, and a purification rate at 400° C. of catalysts before the endurance running. Moreover, Table 2 shows a temperature at which HC, CO, and NO are reduced by 50% in a temperature increase test of catalysts after the endurance running and a purification rate at 400° C. of catalysts after the endurance running.
According to Tables 1 and 2, the purification catalysts for exhaust gas of the Manufacturing Examples 1 to 3 exhibit excellent temperatures at which HC, CO, and NO are reduced by 50% at any time before and after the endurance running, and the purification catalysts for exhaust gas of the Manufacturing Example 1 to 3 exhibit excellent purification rates at 400° C. of catalysts before and after the endurance running. The reasons for these results are that the purification catalysts for exhaust gas of the Manufacturing Examples 1 to 3 are made by supporting Pd on the KNbO3, NaNbO3, or KTaO3. Therefore, a promotion effect of oxidizing and reducing PdO by an element in group 5 in periodic table, a condense effect of NOx by an alkali metal element, and a maintenance effect of endurance by a perovskite structure are all and well demonstrated, whereby increase in activity for each precious metal by effectively utilizing the precious metal can be realized.
On the other hand, the purification catalysts for exhaust gas of the Manufacturing Examples 4 and 5 does not exhibit excellent temperatures at which HC, CO, and NO are reduced by 50% at any time before and after the endurance running, and the purification catalysts for exhaust gas of the Manufacturing Examples 4 and 5 does not exhibit excellent purification rate at 400° C. of catalysts before and after the endurance running. The reasons for these results are as follows. In the Manufacturing Example 4, Al2O3 is a stable compound which does not interact with a supported precious metal, whereby activity of Pd itself is not improved. In the Manufacturing Example 5 in which the crystal structure is an ilmenite structure, the crystal system is different from that of Manufacturing Examples 1 to 3, whereby the existence of a state of electrical charge between constituting atoms is not unstable in comparison with that of Manufacturing Examples 1 to 3 in which the crystal structure is a perovskite structure.
The purification catalyst of exhaust gas of the present invention can be applied to an internal combustion engine of an automobile or the like in which it is required to simultaneously and effectively purify and reduce nitrogen oxide (NOx), carbon hydride (HC), and carbon monoxide (CO) contained in an exhaust gas.