Claims
- 1. A process for purification of wet-process phosphoric acid by use of urea and oxalic acid with coproduction of oxamide which comprises the steps of:
- (a) mixing wet-process phosphoric acid with about stoichiometric amounts of urea to effect the preparation of urea phosphate, said resulting urea phosphate containing less than about 50 percent of the congeneric impurities originally present in said wet-process acid;
- (b) mixing said resulting urea phosphate with oxalic acid and with water in the mole ratios 1.9 to 2.1 and 3 to 6, respectively, at a temperature in the range from about 15.degree. C. to about 100.degree. C.;
- (c) cooling the resulting slurry, separating the product phosphoric acid from the urea oxalate; and
- (d) heating the urea oxalate with a catalytic amount of an acidic phosphate (3 to 15 weight percent) at temperatures ranging from about 150.degree. C. to about 200.degree. C. to form a mixture of urea and oxamide.
- 2. The process of claim 1 wherein step (b) thereof the mole ratios of urea phosphate with oxalic acid and with water is about 2 and about 3 to 4, respectively, wherein the mixing of same is effected at a temperature in the range from about 60.degree. to about 80.degree. C., and wherein step (d) thereof the temperature of heating of the urea oxalate with the acidic phosphate ranges from about 160.degree. C. to about 185.degree. C.
- 3. A process according to claims 1 or 2 wherein the urea oxalate is contacted with ammonia at a temperature in the range from about 25.degree. C. to about 132.degree. C. to form a mixture of urea and ammonium oxalate.
- 4. A process according to claims 1 or 2 wherein the urea oxalate is contacted with ammonia at a temperature in the range from about 75.degree. C. to about 100.degree. C. to form a mixture of urea and ammonium oxalate.
Government Interests
The invention herein described may be manufactured and used by or for the Government for governmental purposes without the payment to me of any royalty therefor.
US Referenced Citations (1)
Number |
Name |
Date |
Kind |
3967948 |
McCullough |
Jul 1976 |
|
Foreign Referenced Citations (1)
Number |
Date |
Country |
2511345 |
Sep 1975 |
DEX |