1. Field of the Invention
The present invention relates to a pyrotechnic composition comprising a 5-aminotetrazole salt, preferably a fireworks composition comprising a 5-aminotetrazole salt.
2. Relevant Background
Conventional colorful fireworks have the major disadvantage that they generate a lot of smoke which causes major problems in enclosed venues as for instance sport stadiums inside cities.
In U.S. Pat. No. 6,214,139 and U.S. Pat. No. 5,917,146 metal salts of several high-nitrogen, low carbon content energetic materials are presented as viable ingredients for low-smoke fireworks compositions.
The high nitrogen, low carbon content energetic materials mentioned in these documents are, however, not readily available compounds. In order to prepare these compounds multi-step syntheses are required. Furthermore, in some of these syntheses environmental unfriendly, toxic or hazardous chemical precursors are required. These two issues increase the price of the metal salts of a high-nitrogen, low-carbon content considerably.
An object of the present invention is to reduce the environmental impact of fireworks by providing low-smoke, perchlorate-free pyrotechnic compositions that can be used for large scale industrial production of fireworks.
Surprisingly, it has now been found that this object can be realized when use is made of chlorine-containing pyrotechnic compositions which comprise a metal salt of 5-aminotetrazole. The inventors found that a pyrotechnic composition, preferably a firework article, comprising a metal salt of 5-aminotetrazole generates relatively low smoke, while being able to generate colored flames upon combustion. This provides an attractive alternative to the low-smoke pyrotechnic compositions suggested in the prior art, due to the availability of the metal salts. In addition, the synthesis of the components in the pyrotechnic composition and the pyrotechnic composition itself are environmentally friendly. Moreover, even the combustion of the pyrotechnic compositions of the invention can be called environmentally friendly.
Advantageously, the metal salts of 5-aminotetrazole are easy to handle and in addition do not have the risk of self-combustion.
The present invention relates to a chlorine-containing pyrotechnic composition which comprises a binder, an oxidator, a pyrotechnic fuel, and a colorant comprising a metal salt of 5-aminotetrazole.
The metal salt can be obtained by reacting a corresponding metal compound with 5-aminotetrazole. Preferably, the metal salt is obtained by reacting the corresponding metal hydroxide, metal sulphate, metal chloride or metal nitrate with 5-aminotetrazole. More preferably, the metal salt is obtained by reacting the corresponding metal hydroxide or metal nitrate with 5-aminotetrazole. Most preferably, the metal salt is obtained by reacting the corresponding metal hydroxide with 5-aminotetrazole.
The 5-aminotetrazole can either be in anhydrous form or containing crystal water.
Suitably, the metal to be used in the metal salt is selected from the group consisting of calcium, strontium, barium, copper, potassium, iron, magnesium, lithium, boron, titanium, antimony and aluminium.
Preferably, the metal is strontium, barium or copper.
Mixtures of various metal salts can suitably be used to yield desired colors.
Suitably, the binder is present in an amount in the range of from 2-96 wt %, the oxidator is present in an amount in the range of from 1-85 wt %, the pyrotechnic fuel is present in an amount in the range of from 20-96 wt %, and the metal salt of 5-aminotetrazole is present in an amount of from 2-30 wt %, all amounts based n total pyrotechnic composition.
Preferably, the metal salt of 5-aminotetrazole is present in an amount of from 4-10 wt %, based on total pyrotechnic composition.
Suitably, the binder comprises nitrocellulose or PVC. Preferably, the binder comprises nitrocellulose.
Suitably, the nitrocellulose to be used in accordance with the present invention will have a nitrogen content of less than 14 wt %, preferably a nitrogen content in the range of from 12-13.5 wt %.
The binder to be used according to the present invention will usually be extrudable and energetic. With the term energetic is meant that the binder will decompose exothermically.
Suitably, the oxidator is selected from the group consisting of ammonium nitrate, ammonium perchlorate, barium nitrate, barium chlorate, strontium nitrate, potassium nitrate and potassium perchlorate.
Preferably, the oxidator comprises ammonium nitrate or ammonium perchlorate.
The pyrotechnic fuel is selected from the group consisting of nitrocellulose, cellulose, cellulose nitrate, guanidinium nitrate, Arabic gum, red gum and schellack.
Preferably, the pyrotechnic fuel comprises nitrocellulose or cellulose.
It will be clear to the skilled person that nitrocellulose can be used as the binder as well as the pyrotechnic fuel.
The pyrotechnic composition according to the present invention contains chlorine. Suitably, the present pyrotechnic compositions comprise chlorine in an amount in the range of from 0.2-20 wt %, preferably in the range of from 1-5 wt %., based on total pyrotechnic composition.
The chlorine can be provided by the binder, oxidator and/or colorant.
In an attractive embodiment, the metal salt of 5-aminotetrazole is protonated by means of an acid. The protonation can be established by contacting 5-aminotetrazole with hydrochloric acid in a suitable solvent and retrieving the formed crystals.
Suitably, the acid is selected from the group consisting of hydrogen chloride, hydrogen bromide, hydrogen iodide, hydrogen fluoride, nitric acid, chloric acid and perchloric acid.
Preferably, the acid is hydrogen chloride, chloric acid or perchloric acid.
The pyrotechnic composition to be used in accordance with the present invention may include other conventional components (burn rate modifier, stabilizer, processing additives, flegmatizer, etc.) which are common for those skilled in the art. If present, these components will be present in an amount of less than 10 wt %, based on total pyrotechnic composition.
The present invention also relates to a firework article comprising the pyrotechnic composition in accordance with the present invention.
In addition, the present invention relates to the use of a metal salt of 5-aminotetrazole as described hereinabove in a firework article. More in particular, the invention relates to the use of a metal salt of 5-aminotetrazole as described herein in a low-smoke pyrotechnic composition. The pyrotechnic composition of the invention, in particular when used in a firework article, can generate colored flames upon combustion while generating only very little smoke in comparison with conventional pyrotechnic compositions. Preferably pyrotechnic composition is essentially smoke-free.
The present invention further relates to a method for preparing the colorant of the pyrotechnic composition according to the present invention, which method comprises reacting for instance a metal hydroxide or a metal nitrate with 5-aminotetrazole, and recovering the colorant in the form of the metal salt of 5-aminotetrazole so obtained.
Suitably, said process is carried out in the presence of water.
The pyrotechnic composition according to the invention can suitably be made by dry mixing the respective components and pressing the composition so obtained in the desired form. In another embodiment, the respective components are mixed in the presence of a solvent, after which the mixture obtained is extruded, and the solvent is removed by means of evaporation.
The solvent can suitable be selected from the group consisting of ethanol or solvent esters such as ethyl acetate, butyl acetate, or alcohols such as isopropanol butanol. Such solvents have the advantage, when compared with conventionally used solvents such as acetone and hexane, that they have less impact on the environment and reduce the risk of safety hazards (explosions) considerably. Preferably, the solvent comprises acetone.
The solvent is suitably present in an amount in the range of from 0 to 20 wt %, based on total pyrotechnic composition. Preferably, the solvent is present in an amount in the range of from 5 to 14 wt %, based on total mixture. It will be understood by the skilled person that said solvent will in essence not be present in the pyrotechnic composition eventually obtained, due to evaporation of the solvent concerned.
A pyrotechnic composition according to the present description was prepared having the following composition: 94.8 wt % Nitrocellulose (13.5% N); 5 wt % Strontium-aminotetrazole complex; and 0.2 wt % ammonium chloride.
The pyrotechnic composition was prepared by mixing 100 gram dry NC 13.5% with 5.27 gram Strontium Amino-tetrazole complex and 0.22 gram ammonium chloride. Acetone was then added to the mixture, and the mixture thus obtained was mixed until the composition can be shape formed in a ram extrusion process in strands of 10 mm diameter. The acetone was removed at room temperature. The strands so obtained are cut in pellets of 10 mm length which pellets are further processed into a firework article. The firework article burnt with a red flame.
A pyrotechnic composition according to the present description was prepared having the following composition: 83 wt % Ammonium Nitrate; 6 wt % Barium-aminotetrazole complex with hydrochloride; 11 wt % Nitrocellulose (13.5% N2).
Said pyrotechnic composition was dry mixed in a turbulator. After mixing the composition was pressed in pellets of 15 mm diameter. The composition so prepared burnt with a green flame.
A pyrotechnic composition according to the present description was prepared having the following composition: 48 wt % Ammonium perchlorate; 17 wt % Aminotetrazole; 5 wt % Strontium-aminotetrazole complex; 30 wt % Nitrocellulose (13.5% N2. The pyrotechnic composition was dry mixed in a turbulator. After mixing, the composition was pressed in pellets of 15 mm diameter. The composition so prepared burnt with a red flame.
| Number | Date | Country | Kind |
|---|---|---|---|
| 07106234 | Apr 2007 | EP | regional |
| PCT/NL2008/050216 | Apr 2008 | WO | international |
| Number | Name | Date | Kind |
|---|---|---|---|
| 3657028 | Pannell | Apr 1972 | A |
| 4078954 | Bernardy | Mar 1978 | A |
| 5500059 | Lund et al. | Mar 1996 | A |
| 5501823 | Lund et al. | Mar 1996 | A |
| 5917146 | Hiskey et al. | Jun 1999 | A |
| 6019861 | Canterberry et al. | Feb 2000 | A |
| 6156137 | Lundstrom et al. | Dec 2000 | A |
| 6214139 | Hiskey et al. | Apr 2001 | B1 |
| 6627014 | Blomquist | Sep 2003 | B1 |
| 6779464 | Yamato | Aug 2004 | B1 |
| 20060011276 | Grix et al. | Jan 2006 | A1 |
| 20080271365 | Goldfarb et al. | Nov 2008 | A1 |
| 20080271825 | Halpin et al. | Nov 2008 | A1 |
| 20100024931 | Zevenbergen et al. | Feb 2010 | A1 |
| 20100024932 | Webb et al. | Feb 2010 | A1 |
| Number | Date | Country |
|---|---|---|
| 19505568 | Aug 1996 | DE |
| 0536916 | Apr 1993 | EP |
| 1127860 | Aug 2001 | EP |
| 2000297078 | Oct 2000 | JP |
| 02084458 | Oct 2002 | WO |
| 2006047085 | May 2006 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20100024931 A1 | Feb 2010 | US |