Patent Application
20230357960
The present invention is directed to melt processable carbon fiber precursors that may be used to prepare carbon fibers, and more particularly, an economical (low cost) melt-processable quad-polymer precursors for carbon fibers, a preparation method of the precursors, and preparation methods of the carbon fibers thereof.
Azarova, M. T., et al., World production and consumption of carbon fibres. Fibre Chemistry, 2011. 42(5): p. 271-277 (“Azarova 2011”).
Baker, D. A., et al., Recent advances in low-cost carbon fiber manufacture from lignin. Journal of Applied Polymer Science, 2013. 130(2): p. 713-728 (“Baker 2013”).
Batchelor, B. L., et al., Plasticization for melt viscosity reduction of melt processable carbon fiber precursor, Carbon, 2016. 98: 681-688 (“Batchelor 2016”).
Bhal, O. P., et al., Carbon Fibers, Third Edition, in Carbon Fibers, J. B. Donnet, et al., Editors. 1998, Marcel Dekker Inc.: New York. p. 1-84 (“Bhal 1998”).
Bhanu, V. A., et al., Synthesis and characterization of acrylonitrile methyl acrylate statistical copolymers as melt processable carbon fiber precursors. Polymer, 2002. 43(18): p. 4841-4850 (“Bhanu 2002”).
Bortner, M. J., et al., Shear rheological properties of acrylic copolymers and terpolymers suitable for potentially melt processable carbon fiber precursors. Journal of Applied Polymer Science, 2004. 93(6): p. 2856-2865 (“Bortner 2004”).
Cantwell, W. J., et al., The impact resistance of composite materials—a review. Composites, 1991. 22(5): p. 347-362 (“Cantwell 1991”).
Chand, S., Review Carbon fibers for composites. Journal of Materials Science, 2000. 35(6): p. 1303-1312 (“Chand 2000”).
Deng, W., et al., Poly (Acrylonitrile-co-1-Vinylimidazole): A New Carbon Fiber Precursor: Melt Processable and Thermally Crosslinkable Carbon Fiber Precursor, 2012: LAP Lambert Academic Publishing (“Deng 2012”).
Deng, W., et al., Poly (acrylonitrile-co-1-vinylimidazole): A new melt processable carbon fiber precursor. Polymer, 2011. 52(3): p. 622-628 (“Deng 2011”).
Deng, W., et al., Polym Prepr (Am Chem Soc Div Polym Chem), 2009. 50: p. 237(“Deng 2009”).
Edie, D. D., The effect of processing on the structure and properties of carbon fibers Carbon, 1998. 36(4): p. 345-362 (“Edie 1998”).
Eng, F. P., et al., Fourier transform infrared studies on the thermal degradation of polyvinylimidazoles: Part I. Journal of Applied Polymer Science, 1986. 32(5): p. 5021-5034 (“Eng 1986”).
E.P.A. and D.O.T., 2017 and later model year light-duty vehicle greenhouse gas emissions and corporate average fuel economy standards, 2012, Federal Register. p. 62623 - 63200 (“EPA 2012”).
Fu, Z., et al., Structure evolution and mechanism of polyacrylonitrile and related copolymers during the stabilization. Journal of Materials Science, 2014. 49(7): p. 2864-2874 (“Fu I 2014”).
Fu, Z., et al., Effects of an itaconic acid comonomer on the structural evolution and thermal behaviors of polyacrylonitrile used for polyacrylonitrile-based carbon fibers. Journal of Applied Polymer Science, 2014. 131(19): p. n/a-n/a (“Fu II 2014”).
Godshall, D., et al., Incorporation of methyl acrylate in acrylonitrile based copolymers: effects on melting behavior. Polymer, 2003. 44(15): p. 4221-4228 (“Godshall 2003”).
Guigon, M., et al., Heat-treatment of high tensile strength PAN-based carbon fibres: Microtexture, structure and mechanical properties. Composites Science and Technology, 1986. 27(1): p. 1-23 (“Guigon 1986”).
Jain, M., et al., Conversion of acrylonitrile-based precursor fibres to carbon fibres. Journal of Materials Science, 1987. 22(1): p. 278-300 (“Jain 1987”).
Li, W., et al., Structural features of polyacrylonitrile-based carbon fibers. Journal of Materials Science, 2012. 47(2): p. 919-928 (“Li 2012”).
Mukundan, T., et al., A photocrosslinkable melt processible acrylonitrile terpolymer as carbon fiber precursor. Polymer, 2006. 47(11): p. 4163-4171 (“Mikundan 2006”).
Naskar, A. K., et al., UV assisted stabilization routes for carbon fiber precursors produced from melt-processible polyacrylonitrile terpolymer. Carbon, 2005. 43(5): p. 1065-1072 (“Naskar 2005”).
Paiva, M. C., et al., UV stabilization route for melt-processible PAN-based carbon fibers. Carbon, 2003. 41(7): p. 1399-1409 (“Paiva 2003”).
Rahaman, M. S. A., et al., A review of heat treatment on polyacrylonitrile fiber. Polymer Degradation and Stability, 2007. 92(8): p. 1421-1432 (“Rahaman 2007”).
Rangarajan, P., et al., Effect of comonomers on melt processability of polyacrylonitrile. Journal of Applied Polymer Science, 2002. 85(1): p. 69-83 (“Ramgarajan I 2002”).
Salem, D. R., Structure Formation in Polymeric Fibers. 2001: Hanser (“Salem 2001”).
Rangarajan, P., et al., Dynamic oscillatory shear properties of potentially melt processable high acrylonitrile terpolymers. Polymer, 2002. 43(9): p. 2699-2709 (“Ramgarajan II 2002”).
Yang, D. J., et al., International PCT Patent Application Publication No. WO 2015/175050, Carbon fiber compositions and methods of making, filed Feb. 14, 2015 and published Nov. 19, 2015 (“Yang '050 PCT Patent Application”).
The background art of the present disclosure will be described in reference to above mentioned works of literature.
Carbon fibers, because of their excellent mechanical properties with additional good chemical and thermal properties, have attracted interest from the aerospace, sporting goods, automotive, and defense industries [Edie 1998; Bhal 1998; Cantwell 1991; Chand 2000; Li 2012]. Majority of the carbon fibers are manufactured from a polyacrylonitrile (PAN) precursor, although small amounts are derived from other sources like pitches (mesophase), lignin, and hydrated cellulose. Pitch-based precursors have the advantages of low raw materials cost, low energy requirement for carbon fiber preparation and high carbon yield, but their mechanical properties are very poor compared to the PAN-based carbon fibers [Azarova 2011; Baker 2013; Rahaman 2007; Salem 2001]. Thus, due to excellent mechanical properties, PAN-based precursors are found to be the most appropriate [Rahaman 2007; Fu I 2014].
According to a 2012 U.S. government legislation, the average fuel economy of cars and light trucks for the model year 2017 will be 35.5 mpg and for the model year 2025, 54.5 mpg [EPA 2012]. Lowering the vehicle weight will be an effective way to achieve higher fuel economy and to reduce greenhouse gas emission. According to studies by the U.S. Department of Energy (DOE), PAN-based carbon fiber composites have the potential to reduce the weight of the automotive parts as much as 60% compared to metal parts [Baker 2013]. To use the composites for automotive parts, it requires mechanical properties such as tensile strength of 1.72 GPa and a modulus of 172 GPa [Baker 2013]. However, the current technology for the production of PAN-based carbon fibers uses solution spinning process that requires expensive and environmentally hazardous solvents recovery steps. So when the carbon fiber composite parts are used for all car manufacturing, the consumption and recovery of hazardous solvent may create enormous environmental problem as well as economic problem.
Since PAN-based precursors degrade before they melt, solution spinning (20-30 wt % solution) of the precursors using polar solvent is the typical fiber forming process [Ramgarajan I 2002]. Two thermal treatment stages are required for the conversion of the precursors into carbon fibers. In the first stage, the thermal-oxidative ‘stabilization’ forms a ladder-like structure at temperatures ranging from 200-300° C. in an oxygen-rich environment. The second stage of ‘carbonization’ is conducted in inert atmosphere usually around 1,000-1,400° C. to form carbon fibers [Cantwell 1991; Rahaman 2007; Jain 1987].
As mentioned above, the solution spinning process is associated with solvent recovery, thereby having high processing costs. The replacement of solution spinning process by melt spinning is a major benefit for a cost-effective and environmentally friendly carbon fiber production. Melt processable carbon fiber precursors were studied by different researchers. For example, co-monomers such as methyl acrylate (MA), itaconic acid (IA), methacrylic acid (MAA), acryl amide (AM), acryloyl benzophenone (ABP) were incorporated with PAN, but their thermal stabilization was always an issue [Fu I 2014; Ramgarajan I 2002; Ramgarajan II 2002; Bhanu 2002; Bortner 2004; Fu II 2014; Godshall 2003; Mikundan 2006; Naskar 2005; Paiva 2003]. In particular, Pavia 2003 et al. [Paiva 2003] and Naskar et al. [Naskar 2005] studied PAN-based melt processable precursor copolymers made with MA and ABP, where a UV-assisted stabilization was required. In 2011, Deng et al reported the potential of poly (acrylonitrile-co-N-vinylimidazole) (AN/VIM) as a new melt processable carbon fiber precursor [Deng 2012; Deng 2011]. This new AN/VIM copolymer does not need the UV treatment for thermal stabilization and may be processed for stabilization as typical PAN-based precursors. Recently, Batchelor et al. reported the melt viscosity reduction for AN/VIM precursor polymer using oligomeric plasticizer where only thermal stabilization was used [Batchelor 2016]. In Yang '050 PCT Patent Application, the present inventors disclosed and taught the preparation of automotive grade carbon fiber from melt processable AN/VIM copolymer. However, in view of the higher cost of VIM in AN/VIM copolymer, there remains a need for low cost alternative melt processable precursors that will make the technology become economically viable.
In order to solve the above-mentiond problems, an object of the present disclosure is to provide quad-polymer precursors for preparing carbon fibers, a method for preparing the same, and a use method thereof.
The present disclosure relates to a quad-polymer composition. The quad-polymer composition includes a chemical structure selected from a group consisting of
X, Y, Z, and M are wt % of the quad-polymer composition. X+Y+Z+M=100%.
Implementations of the present disclosure may include one or more of the following features:
The quad-polymer composition may have the chemical structure of
X may be in a range from 0.1 to 40.0 wt %. Y may be in a range from 50.0 to 99.0 wt %. Z may be in a range from 0.1 to 50.0 wt %. M may be in a range from 0.1 to 40.0 wt %.
X may be in a range from 0.1 to 10.0 wt %. Y may be in a range from 60.0 to 95.0 wt %. Z may be in a range from 2.5 to 30.0 wt %. M may be in a range from 0.1 to 10.0 wt %.
X may be in a range from 0.1 to 5.0 wt %. Y may be in a range from 70.0 to 92.5 wt %. Z may be in a range from 2.5 to 25.0 wt %. M may be in a range from 0.1 to 5.0 wt %.
The quad-polymer composition may have the chemical structure of
X may be in a range from 0.1 to 40.0 wt %. Y may be in a range from 50.0 to 99.0 wt %. Z may be in a range from 0.1 to 50.0 wt %. M may be in a range from 0.1 to 40.0 wt %.
X may be in a range from 0.1 to 10.0 wt %. Y may be in a range from 60.0 to 95.0 wt %. Z may be in a range from 2.5 to 30.0 wt %. M may be in a range from 0.1 to 10.0 wt %.
X may be in a range from 0.1 to 5.0 wt %. Y may be in a range from 70.0 to 92.5 wt %. Z may be in a range from 2.5 to 25.0 wt %. M may be in a range from 0.1 to 5.0 wt %.
The quad-polymer composition may have a molecular weight ranging from 18 KDa to 200 KDa. The quad-polymer composition may have a polydispersity index (PDI) ranging from 1.2 to 3.0.
In general, in another aspect, the present invention features a method of preparing a quad-polymer composition. The method includes synthesizing the quad-polymer composition from (a) acrylonitrile, (b) vinylimidazole, (c) methyl acrylate, and (d) an acid selected from a group consisting of acrylic acid and itaconic acid. The quad-polymer has a chemical structure in which:
(A) when the acid is the acrylic acid, the chemical structure is:
and
(B) when the acid is the itaconic acid, the chemical structure is:
X, Y, Z, and M are wt % of the quad-polymer composition. X+Y+Z+M=100%.
Implementations of the present invention may include one or more of the following features:
The acid may be the acrylic acid, and the chemical structure is:
The acid may be the itaconic acid, and the chemical structure is:
The wt % of the acrylonitrile, wt % of the vinylimidazole, wt % of the methyl acrylate, and wt % of the acid may be total wt % with respect to a total wt % of 100%. The wt % of the acrylonitrile may be in a range from 50.0 to 99.0 wt %. The wt % of the vinylimidazole may be in a range from 0.1 to 40.0 wt %. The wt % of the methyl acrylate may be in a range from 0.1 to 50.0 wt %. The wt % of the acid may be in a range from 0.1 to 40.0 wt %.
X may be in a range from 0.1 to 40.0 wt %. Y may be in a range from 50.0 to 99.0 wt %. Z may be in a range from 0.1 to 50.0 wt %. M may be in a range from 0.1 to 40.0 wt %.
The wt % of the acrylonitrile may be in a range from 60.0 to 95.0 wt %. The wt % of the vinylimidazole may be in a range from 0.1 to 10.0 wt %. The wt % of the methyl acrylate may be in a range from 2.5 to 30.0 wt %. The wt % of the acid may be in the range from 0.1 to 10.0 wt %.
X may be in a range from 0.1 to 10.0 wt %. Y may be in a range from 60.0 to 95.0 wt %. Z may be in a range from 2.5 to 30.0 wt %. M may be in a range from 0.1 to 10.0 wt %.
The wt % of the acrylonitrile may be in a range from 70.0 to 92.5 wt %. The wt % of the vinylimidazole may be in a range from 0.1 to 5.0 wt %. The wt % of the methyl acrylate may be in a range from 2.5 to 25.0 wt %. The wt % of the acid may be in the range from 0.1 to 10.0 wt %.
X may be in a range from 0.1 to 5.0 wt %. Y may be in a range from 70.0 to 92.5 wt %. Z may be in a range from 2.5 to 25.0 wt %. M may be in a range from 0.1 to 10.0 wt %.
In general, in another aspect, the present invention features a quad-polymer composition. The quad-polymer composition includes a first monomer, a second monomer, a third monomer, and a fourth monomer. The first monomer is acrylonitrile at a wt % of Y in the quad-polymer composition. The second monomer is selected from a group consisting of 1-vinylimidazole, 4- vinylimidazole, 2-vinylimidazole and 1-methyl-2-vinylimidazole, in which the second monomer is at a wt % of X in the quad-polymer composition. The third monomer is an acrylate at a wt % of Z in the quad-polymer composition. The acrylate is selected from a group consisting of methyl acrylate, ethyl acrylate, butyl acrylate, methyl methacrylate, and tert-butyl acrylate. The fourth monomer is an acid at a wt % of M in the quad-polymer composition. The acid is selected from a group consisting of acrylic acid, itaconic acid, and methacrylic acid. The total of the Y wt % of the first monomer, the X wt % of the second monomer, the Z wt % of the third monomer, and the M wt % of the fourth monomer equals 100%.
Implementations of the present invention may include one or more of the following features:
The second monomer may be 1-vinylimidazole. The third monomer may be methyl acrylate. The fourth monomer may be acrylic acid or itaconic acid.
In general, in another aspect, the present invention features a method for forming fibers of quad-polymers. The quad-polymer includes a first monomer that is acrylonitrile. The quad-polymer further includes a second monomer that is selected from a group consisting of 1-vinylimidazole, 4-vinylimidazole, 2-vinylimidazole, and 1-methyl-2-vinylimidazole. The quad-polymer further includes a third monomer that is selected from a group consisting of methyl acrylate, ethyl acrylate, butyl acrylate, methyl methacrylate, and tert-butyl acrylate. The quad-polymer further includes a fourth monomer that is an acid and is selected from a group consisting of acrylic acid, itaconic acid, and methacrylic acid. The method includes the steps of combining the first monomer, the second monomer, the third monomer, and the fourth monomer to form the quad-polymer composition. The method further includes the steps of melt-spinning the quad-polymer composition to form fibers of the quad-polymer composition.
Implementations of the present invention may include one or more of the following features:
The step of combining the first monomer, the second monomer, the third monomer, and the fourth monomer to form the quad-polymer composition may include utilizing a solvent. The solvent may be selected from the group consisting of dimethylformamide (DMF), dimethyl sulfoxide (DMSO), dimethylacetamide (DMAc), N-methyl-2-pyrrolidone (NMP), and mixtures thereof.
The melt-spinning of the quad-polymer may obtain thin fibers. The thin fibers may have diameters of between around 10 mm and 250 mm.
The thin fibers may be obtained by including a process selected from a group consisting of (a) using dies in capillary rheometer; (b) stretching the molten polymer under tension; and (c) combinations thereof.
The step of combining the first monomer, the second monomer, the third monomer, and the fourth monomer to form the quad-polymer composition may include using an initiator to initiate radical polymerization.
The initiator may include a thermal initiator.
The thermal initiator may be selected from a group consisting of 2,2′-azobisisobutyronitrile (AIBN), 1,1′-azobis(cyclohexanecarbonitrile), benzoyl peroxide, tert-butyl peroxide and lauroyl peroxide, and combinations thereof.
The thermal initiator may be the 2,2′-azobisisobutyronitrile (AIBN).
The step of combining the first monomer, the second monomer, the third monomer, and the fourth monomer to form the quad-polymer composition may include utilizing a chain transfer agent.
The chain transfer agent may include 1-dodecanethiol.
The step of melt spinning may be carried out, at least in part, at a temperature in the range of 100° C. and 200° C.
The step of melt spinning may be carried out, at least in part, in an atmospheric atmosphere or an inert atmosphere.
The method may further include an additional step selected from the group consisting of (i) annealing the fibers; (ii) stabilizing the fibers; (iii) carbonizing the fibers; and (iv) a combination thereof.
The additional step may include (i) annealing the fibers; (ii) stabilizing the fibers; and (iii) carbonizing the fibers.
The second monomer may be vinylimidazole. The third monomer may be methyl acrylate. The third monomer may be acrylic acid or itaconic acid.
The additional step may include the step of annealing. The step of annealing may be carried out, at least in part, at a temperature in the range of 100° C. and 190° C. while applying tension to the fiber.
The additional step may include the step of annealing. Diameters of the quad-polymer fibers may be reduced to be in the range of 1 μm and 300 μm by repeated drawing of the fibers during the step of melt spinning and the step of annealing.
The diameters of the quad-polymer fibers may be in the range of 1 μm and 40 μm.
The diameters of the quad-polymer fibers may be in the range of 1 μm and 20 μm.
The additional step may include the step of annealing and the step of stabilizing.
The step of annealing and the step of stabilizing may be performed together.
The step of annealing and the step of stabilizing may be performed separately. The step of annealing and the step of stabilizing may be performed at different temperatures.
The step of stabilizing may be carried out by a process that includes heating the quad-polymer fibers to a first temperature. The step of stabilizing may be carried out by a process that further includes maintaining the quad-polymer fibers at the first temperature for a first period of time. The step of stabilizing may be carried out by a process that further includes heating the quad-polymer fibers to a second temperature. The step of stabilizing may be carried out by a process that further includes maintaining the quad-polymer fibers at the second temperature for a second period of time.
The step of annealing may include heating the quad-polymer fibers to a third temperature. The step of annealing may further include maintaining the quad-polymer fibers at the third temperature for a first period of time. The step of annealing may further include cooling the quad-polymer fibers to room temperature, in which the step of annealing occurs before the step of stabilizing.
The step of stabilizing may further include heating the quad-polymer fibers to 190° C. at a rate of 3° C. per minute. The step of stabilizing may further include maintaining the quad-polymer fibers at 190° C. during a first period of 180 minutes. The step of stabilizing may further include heating the quad-polymer fibers to 240° C. at a rate of 1° C. per minute. The step of stabilizing may further include maintaining the quad-polymer fibers at 190° C. during a second period of 180 minutes. The step of stabilizing may further include cooling the quad-polymer fibers to room temperature.
The step of annealing may include heating the quad-polymer fibers to 130° C. The step of annealing may further include maintaining the quad-polymer fibers at 190° C. during a third period of 48 hours. The step of annealing may further include cooling the quad-polymer fibers to room temperature. The step of annealing may occur before the step of stabilizing.
The step of carbonizing may be performed by heating the stabilized fibers to a temperature between 900° C. and 1400° C. under an inert atmosphere.
The quad-polymer composition may have a molecular weight ranging from 18 KDa to 200 KDa. The quad-polymer composition may have a polydispersity index (PDI) ranging from 1.2 to 3.0.
In general, in another aspect, the present invention features a carbon fiber composition made from a quad-polymer that includes between 70 and 92.5 wt % of an acrylonitrile monomer. The quad-polymer further includes between 0.1 and 5.0 wt % of a vinylimidazole monomer. The quad-polymer further includes between 2.5 and 25.0 wt % of a methyl acrylate monomer. The quad-polymer further includes between 0.1 and 5.0 wt % of an acid monomer. The acid monomer is an acrylic acid monomer or an itaconic acid monomer. The carbon fiber composition is prepared by melt spinning, stabilizing and carbonizing. The carbon fiber composition has a diameter ranging between 0.5 μm and 150 μm.
Implementations of the present invention may include one or more of the following features:
The carbon fiber composition may have a diameter ranging from 0.5 μm to 30 μm.
The carbon fiber composition may have a diameter ranging from 0.5 μm to 15 μm.
In general, in another aspect, the present invention features a device that includes the quad-polymer composition described above.
Implementations of the present invention may include one or more of the following features:
The device is selected from a group consisting of supercapacitors, lithium battery electrodes, wound healing fibers, fabrics, coatings, and films, and anti-bacterial/microbial fibers, fabrics, coatings, and films.
In general, in another aspect, the present invention features a device that includes a fiber that includes the quad-polymer composition described above.
Implementations of the present invention may include one or more of the following features:
The fiber is made by the process described above.
The device is selected from a group consisting of automobile, aerospace structures, marine structures, military equipment/parts, sporting goods, robotics, furniture, and electronic parts.
The foregoing has outlined rather broadly the features and technical advantages of the present invention in order that the detailed description of the present invention that follows may be better understood. Additional features and advantages of the present invention will be described hereinafter that form the subject of the claims of the present invention. It should be appreciated by those skilled in the art that the conception and the specific embodiments disclosed may be readily utilized as a basis for modifying or designing other structures for carrying out the same purposes of the present invention. It should also be realized by those skilled in the art that such equivalent constructions do not depart from the spirit and scope of the present invention as set forth in the appended claims.
It is also to be understood that the present invention is not limited in its application to the details of construction and arrangements of the components set forth in the following description or illustrated in the drawings. The present invention is capable of other embodiments and of being practiced and carried out in various ways. Also, it is to be understood that the phraseology and terminology employed herein are for the purpose of the description and should not be regarded as limiting.
The present invention describes the synthesis of new melt processable carbon fiber precursors. Free radical solution polymerization technique is used to the precursor polymers which are chemically and thermally characterized. Use of low cost raw materials makes them cost effective compared to the current technology. Suitable thermal properties enable the polymers to be melt processable. Thin fibers are prepared by melt-extrusion of the precursor polymers. These melt-extruded precursor fibers have the ability to undergo thermal stabilization in atmospheric condition. Thermally stabilized fibers are used to make high strength carbon fibers by carbonization process at inert conditions. Both single precursor fibers and tow of the precursor fibers are thermally stabilized and carbonized to yield carbon fibers.
The present invention provides a method for preparing lower cost carbon fibers via the use of a four-component system of less expensive monomers. Each monomer has a specific purpose and use for the development of melt processable carbon fibers. The acrylonitrile is the main component that is required for the development of carbon fibers. It is the nitrile groups that cyclize to form the network of carbon fiber. When vinylimidazole (VIM) is incorporated into PAN, it allows for melt processing by disrupting the crystallinity, while the unsaturated pendant imidazole groups assist the thermal crosslink ability at elevated temperatures. The microstructure and the mechanical properties of the carbon fibers are further affected by the VIM that helps balancing the atomic ratio of nitrogen to carbon (N/C) [Guigon 1986; Deng 2009; Eng 1986], while the third component methyl acrylate is also incorporated to enhance the melt property of the system. The use of methyl acrylate (a low cost monomer) alleviates the higher cost of N-vinylimidazole. Then the fourth components, acrylic acid or itaconic acid are used for the advancement of the initiation of stabilization in a thermal environment. Purposes of the development of a quad-polymer system are (1) for the lowering of the raw material cost associated with the higher price of the AN/VIM copolymer and (2) for enhancing polymer's thermal stability during melt-spinning process and polymer fiber's thermal stabilization.
The present invention provides a method for preparing a carbon fiber via the use of a four-component system of monomers. Each monomer has a specific purpose and use for the development of melt processable carbon fiber. The acrylonitrile (AN) is the main component that is required for the development of carbon fiber. It is a nitrile group that is cyclized to form the network of carbon fibers. The N-vinylimidazole (VIM) is the component that allows for the melt processability while keeping the carbon-to-nitrogen (C/N) ratios at the proper level for development of high strength fibers. While the third component methyl acrylate (MA) is also a melt processable monomer unit, the main purpose is for the lowering of costs which offsets the higher costs of N-vinylimidazole. Then the fourth components, acrylic acid (AA) or itaconic acid (IA), are used for the advancement of the initiation of stabilization in a thermal environment. The main purpose of the development of a quad-polymer system is for (1) the lowering of the developmental costs associated with the high price of the original copolymer, while also (2) enhancing the stabilization of the polymer fibers.
Yang '050 PCT Patent Application discloses and teaches various synthesis of AN-based copolymers, including the synthesis of acrylonitrile (AN) and N-vinylimidazole (VIM) to form a copolymer (See, e.g.,
In an embodiment of the present invention, the free radical solution polymerization of AN, VIM, MA, and AA monomers was carried out in 250-2,000 mL flasks fitted with a thermocouple probe, a condenser, an addition funnel and a nitrogen inlet. The flask was charged with DMF and purged with nitrogen for 30 minutes. Then the monomers, AIBN, and chain transfer agent, 1-dodecanethiol were added drop wise into the flask over a period of 2-8 hours. The polymerization reactions were carried out at 70° C. with continuous stirring over-night. The polymer was precipitated in de-ionized water, filtered and washed with methanol and hexane to remove residual monomers and then dried in a vacuum oven for two days till constant weight was obtained.
The co-monomers in the AN-VIM-MA-AA quad-polymer may be present in any suitable ratio in the quad-polymer. For example, if four monomers AN, VIM, MA, and AA are used, the resulting quad-polymer may have a range of weight ratios of AN: VIM:MA:AA, such that the total of the monomers adds up to 100% in wt %.
In certain embodiments of the present invention, the amount of each monomer in the feed and product of a quad-polymer varies as shown in
Feed ratios (wt %): AN+VIM+MA+AA=100%, where
In certain embodiments, more preferably, the amount of each monomer in the feed and product of a quad-polymer varies as shown in
In certain embodiments, most preferably, the amount of each monomer in the feed and product of a quad-polymer varies as shown in
For example, in an embodiment of the present invention (“Example A”), the free radical polymerization of 28.80 gm of a mixture of AN, VIM, MA and AA monomers (AN: 79.0 parts, VIM: 2.5 parts, MA: 16.0 parts and AA: 2.5 parts by weight) was carried out in a 500 mL flask fitted with a thermocouple probe, a condenser, an addition funnel, and a nitrogen inlet. The flask was charged with 33 gm of DMF and purged with nitrogen for 30 minutes. Then the monomers, DMF (33.6 gm), AIBN (0.123 gm), and chain transfer agent, 1-dodecanethiol (0.016 gm) were added drop wise into the flask over a period of 2 hours. The polymerization reactions were carried out at 70° C. with continuous stirring over-night. The polymers were precipitated in de-ionized water, filtered and washed with methanol and hexane to remove residual monomers and then dried in a vacuum oven for two days till constant weight was obtained. Polymer yield was in between 95 and 85%. This resulting product is referred to as “Example A” herein and in
Further, for example, in another embodiment of the present invention (“Example B”), the free radical polymerization of 281.0 gm of a mixture of AN, VIM, MA and AA monomers (AN: 85.0 parts, VIM: 2.5 parts, MA: 10.0 parts and AA: 2.5 parts by weight) was carried out in a 2000 mL flask fitted with a thermocouple probe, a condenser, an addition funnel and a nitrogen inlet. The flask was charged with 330.0 gm of DMF and purged with nitrogen for 30 minutes. Then the monomers, DMF (336 gm), AIBN (1.232 gm) and chain transfer agent, 1-dodecanethiol (0.16 gm) were added drop wise into the flask over a period of 8 hours. The polymerization reactions were carried out at 70° C. with continuous stirring over-night. The polymers were precipitated in de-ionized water, filtered and washed with methanol and hexane to remove residual monomers and then dried in a vacuum oven for two days till constant weight was obtained. Polymer yield was in between 93 and 88%. This resulting product is referred to as “Example B” herein and in
The success of polymerization was evaluated by ATR-FTIR spectroscopy and 1H-NMR spectroscopy as shown in
The monomer ratios in the feed and the polymer were in accordance with the ratios set forth in
Generally, higher molecular weight polymers will produce higher strength fibers. However, extremely high molecular weight polymers adversely may affect the ability of melt-processing because a high molecular weight polymer yields higher melt viscosity. When the viscosity is too high, the resulting compositions may be difficult to extrude.
In embodiments of the present invention, the molecular weight of the quad-polymers ranged from 18 KDa-300 KDa with a polydispersity index (PDI) of 1.2-4.0. In certain embodiments of the present invention, the molecular weight of the quad-polymers ranged from 40 KDa-120 KDa with a PDI of 1.2-2.0.
The polymer samples from both Example A and Example B showed excellent thermal stability, as evident from their high degradation temperature (˜250° C.) evident from thermo-gravimetric analysis (TGA). High char yield (˜52%) for both Examples A and Example B were also observed from char yield analysis. The summary of the DSC, TGA, and char yield analysis are shown below in Table 2.
Further, for example, in another embodiment of the present invention (“Example C”), a quad-polymer precursor was prepared that demonstrated excellent extrude ability, thermal stabilization, and carbonization capability. Example C is an AN-VIM-MA-AA quad-polymer with a feed composition of AN:VIM:MA:AA=79:2.5:16:2.5 wt %. This new precursor polymer has low Tg of 97° C. and may be extruded into thin fiber. One major advantage is its capability of thermal stabilization. Similar to the AN-VIM copolymer precursor (disclosed and taught in Yang '050 PCT Patent Application), this new quad-polymer precursor is thermally stabilizable so it does not require any UV treatment. The raw material cost for this quad-polymer precursor will be ˜1.45 $/lb which is ˜22% lower than the threshold value of 1.85 $/lb for the AN-VIM copolymer precursor. Mechanical testing results also showed excellent properties for these precursors. The carbonized fiber with 77 μm diameter showed a tensile strength (TS) of 894 MPa and Young's modulus (YM) of 220 GPa while the stabilized fiber showed a TS of 294 MPa and a modulus of 7004 MPa. The TSs of neat and annealed fibers were 109 MPa and 163 MPa, respectively. Also upon optimized extrusion condition, very thin fiber may be made. Such a fiber with 25 μm diameter showed high mechanical strength as TS of 369 MPa and YM of 7.4 GPa.
As noted above, the thermal properties render the quad-polymers suitable to be melt-processable. For example, an AN-VIM-MA-AA quad-polymer precursor as described above was ground into coarse granules in a grinder. A Rosaland RH-7 capillary rheometer was used to extrude the fibers. In a typical trial, 11 g of copolymer was loaded in preheated rheometer in between 100 and 200° C. in atmospheric condition and left there to heat up for 10 minutes. Melted polymers passed through a die having a diameter within a range of 0.01-1.0 mm. A continuous fiber 901 was made by this method, where the fiber 901 is shown in
Annealing or drawing is the step to align the polymer chains parallel to the fiber axis. This process is important to increase the fiber strength. Annealing and stabilization steps are done either together or separately.
In heating program, HP1 (as shown in
Stabilization is the step of cyclization of the acrylonitrile groups. Heating programs of the stabilization step are shown in
As shown in
As shown in
In another embodiment of the present invention, the stabilization of multi-filament in a tow of fiber is carried out without any melting or fusing of the fiber.
Such multi-fiber stabilization was a significant achievement. Previously, with the AN-VIM precursor (disclosed and taught in Yang '050 PCT Patent Application), this was not possible. However, with the quad-polymer precursors of the present invention, multi-fiber thermal stabilization has been successfully performed.
Thermally stabilized fibers may be used to make high strength carbon fiber by carbonization process under inert conditions. Both single precursor fiber and tow of the precursor fibers may be thermally stabilized and carbonized to yield carbon fibers.
For example, a heating program of the carbonization step is shown in FIG. 16A (CP1). Carbonization is the last step in the formation of carbon fiber (which is carried out under inert condition), where the stabilized fiber is subjected to further heating. A typical heating program involves multiple steps (such as in CP1, which is shown in
Alternative heating programs of the carbonization step are shown in
An AN-VIM-MA-AA quad-polymer was synthesized (using processes discussed and described above) and was extruded by using a single fiber extruder (rheometer), and the extruded fiber was then stabilized at 190° C. for 180 min followed by heating 240° C. at a step of 3° C. per minute, applying tension followed by a carbonization to produce a carbon fiber. The carbonization condition used was to heat the stabilized fiber in an oven under nitrogen atmosphere to reach the temperature at 900° C. in multiple steps (as shown in
A carbon fiber of approximately 6 cm or 2.25 inch long was successfully prepared by carbonization of the stabilized fiber made from an AN-VIM-MA-AA copolymer.
In an embodiment of the present invention, for example, for a melt-extruded fiber with diameter within 338 mm when annealed and stabilized by following heating program HP2 (
In an embodiment of the present invention, for example, for a melt-extruded fiber with a diameter within 168 mm when annealed and stabilized by following heating program HP1 (
As noted above, in embodiments of the present invention, the fourth components may be itaconic acid (IA) instead of acrylic acid (AA). The free radical solution polymerization of AN, VIM, MA and IA monomers was carried out in 250-2000 mL flasks fitted with a thermocouple probe, a condenser, an addition funnel and a nitrogen inlet. The flask was charged with DMF and purged with nitrogen for 30 minutes. Then, the monomers, AIBN and chain transfer agent, 1-dodecanethiol were added drop wise into the flask over a period of 2-8 hours. The polymerization reactions were carried out at 70° C. with continuous stirring over-night. The polymers were precipitated in de-ionized water, filtered and washed with methanol and hexane to remove residual monomers and then dried in a vacuum oven for two days till constant weight was obtained.
The monomers in the AN-VIM-MA-IA quad-polymer may be present in any suitable ratio in the quad-polymer. For example, if four monomers AN, VIM, MA and IA are used, the resulting quad-polymer may have a range of weight ratios of AN:VIM:MA:IA, such that the total amount of the monomers adds up to 100% in wt %. In certain embodiments of the present invention, the amount of each monomer in the feed and product of a quad-polymer varies from as shown in
In certain embodiments, more preferably, the amount of each monomer in the feed and product of a quad-polymer varies as follows:
In certain embodiments, most preferably, the amount of each monomer in the feed and product of a quad-polymer varies as follows:
In additional embodiments: the second monomer (N-vinylimidazole) may be, alternatively, 4-vinylimidazole, 2-vinylimidazole or 1-methyl-2-vinylimidazole; the third monomer (methyl acrylate) may be, alternatively, ethyl acrylate, butyl acrylate, methyl methacrylate, or tert-butyl acrylate; and the fourth monomer (acrylic acid or itaconic acid) may be, alternatively, methacrylic acid.
| Number | Date | Country | |
|---|---|---|---|
| 62504409 | May 2017 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16611214 | Nov 2019 | US |
| Child | 18217822 | US |