Quality management system for pre-processed workpiece

Abstract

A method and system for assessing proper pre-processing and proper welding of polymer workpieces. A visible or infrared radiation source, optionally coupled with optical filters, directs radiation at test wavelengths through a workpiece which is captured by sensors at one or more stations. The system controller determines from the sensor data whether the absorber dye was properly deposited onto the workpiece. The workpiece is then certified weld-enabled within a bandwidth range of the test wavelength. The bandwidth range is determined by absorption spectra and extinction coefficients of the dye or by utilizing multiple test wavelengths. For determining whether proper welds occurred, a further embodiment of the method and system check for spectral characteristics that the dye vehicle did not unduly interfere or occlude the weld. Further spectral data indicates fusing of reflective surfaces, increased transmission and increase photopic transmission.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

The invention relates to a pre-processed workpiece having a surface deposition of absorber dye for the express purpose of being consumed in future welding process. More particularly, it relates to a quality management system for certifying the mechanical and chemical characteristics of the workpiece.

2. Description of the Prior Art

Joining plastic parts by through transmission laser welding in known, for example, from U.S. Pat. No. 5,893,959. U.S. Pat. No. 5,893,959 utilizes pigments to increase the absorption properties along the welding zone. However, since the disclosed pigments survive the welding process, they unfavorably affect the appearance of the joint. The patent compensates for reduced aesthetics by incorporating the pigment into the entirety of both upper and lower substrates to render them opaque, both before and after joining. The upper substrate is described as having a concentration of pigment throughout of less than 1% that provides a transmission of greater than 60% at the welding laser wavelength. The lower substrate receives a pigment concentration of between 1-2% resulting in a negligible transmission.

Accordingly, it would be desirable to define the range of design criteria and engineering characteristics of a weldable workpiece that can: provide minimal occlusion at the joint, and may further include visual, even optical, clarity at the joint; selectively deposit absorber dye only onto the welding zone to eliminate absorber-induced occlusion throughout the remainder of the ensemble; incorporate dyes in such a way that they will undergo decomposition into inert, soluble, invisible by-products; utilize absorber dyes which primarily effect transmission at the 5 welding wavelength; utilize absorber dyes that minimally effect transmission at wavelengths numerically spaced from the welding wavelength; utilize absorber dyes that minimally effect transmission within the visible spectrum; and in certain embodiments, have no effect or even beneficial transmission effects within the visible spectrum.

The relationship between applications utilizing carbon black pigmentation and absorber dyes is discussed as a function of line energy in the Russek article entitled “Laser Beam Welding of Polymers with High Power Diode Lasers: Joining Innovation for Micro and Macro Technologies”. The article proposes three dimensional, volumetric thermodynamic process modeling to address concerns in gap bridging during welding. A significant drawback of such approach is that the weld must be completed and cross-sectioned to obtain the energy density distribution, as shown in FIG. 6 . Russek does not suggest the dye density on a single workpiece, nor does it suggest the range of energy per surface area that will correspond to the inherent capacity of the surface dye deposition. The published PCT application bearing International Application Number PCT/GB99/03241, discloses a process for welding parts having an infrared absorber dye sandwiched therebetween.

SUMMARY OF THE INVENTION

Accordingly, it would be desirable to manage the quality of a pre-processed polymer workpiece so that is can be flexibly welded to another freely selectable mating part.

It is therefore an object of the present invention to provide a system for monitoring the minimum mechanical and chemical requirements for such a polymer workpiece.

It is another object of the present invention to provide a system for monitoring the optical transmission properties of such workpiece under ideal conditions.

These and other related objects are achieved according to the invention by a method and system for monitoring the quality of the mechanical and chemical properties of the pre-processing stages of a workpiece.

A weldable workpiece having at least its surface made from a first polymer which softens on heating adapted for fusing to a material which softens on heating and is freely-selectable from a second polymer which is the same or similar to the first polymer or a different polymer which is at least locally mutually miscible with the surface of the first polymer, wherein the first polymer and the freely-selectable second polymer have overlapping melting temperature ranges. The workpiece has a surface extending across a bulk portion. An absorber dye possessing both strong absorption and a high extinction coefficient at a welding wavelength of a radiant energy source is deposited on or above the surface thereby defining a welding zone via a vehicle having necessary viscosity and which avoids undue interference with or occlusion of the welding zone. The deposition comprising a generally uniform density of about 5 to about 3000 nanograms of dye per mm 2 to provide predictable and consistent heating thereby rendering the workpiece weld-enabled. The welding zone has the capacity to convert inbound radiant energy at the welding wavelength over about 0.1 j/mm 2 into thermal energy via vibronic relaxation immediately followed by exothermic decomposition of at least a portion of the dye into inert, invisible by-products, the combination of which being capable of delivering (i) a first quantity of thermal energy directed in the direction of the bulk portion to elevate the surface into the melting temperature range of the surface and (ii) an approximately equal quantity of thermal energy directed in the opposite direction away from the bulk portion. The dye, the vehicle, the by-products, and the surface of the first polymer are mutually miscible. The workpiece, and any film, may be made from a thermoplastic polymer. The dye may be a visible light absorbing dye, a near infrared absorbing dye, an infrared absorbing dye, or combinations thereof. If the vehicle is a liquid solvent it must be capable of dissolving the absorber dye to provide uniform surface density. If the liquid vehicle delivers absorber dye below the surface, it should be to a depth sufficiently small to avoid foaming during welding. In liquid solvents, the absorber dye is present in a concentration of about 1×10 −2 to about 1×10 −4 grams per milliliter to deliver dye within the stated surface deposition density range following solvent evaporation.

These properties are monitored by a method wherein electromagnetic radiation is transmitted through the workpiece toward a sensor. The system controller determines if dye was properly placed, at the correct density, in the proper locations, and certifies the workpiece as being weld-enabled based on the test wavelength or wavelengths, or stored data, containing information similar to that shown in the graphs. The transmitted radiation may be at or near the anticipated welding wavelengths, in the blue or red visible spectrums, or may comprise a scan to determine the color coordinates or color profile of the workpiece. The test transmissions occur at wavelengths in which the various curves are sufficiently spaced apart from each other to allow the method to assess if the workpiece has successfully passed from one state, represented by one curve, to another state, represented by another curve.

These and other related objects are achieved according to the invention by a second embodiment thereof, relating to a method and system for monitoring the quality of the mechanical and chemical properties of the post-processing stages of a workpiece.

A transmission-enhancing formulation disposed between a first reflective surface of a first radiant energy-transmissive workpiece having a first bulk portion and a second reflective surface of a second workpiece having a second bulk portion. Both reflective surfaces are made of a polymer material which softens on heating, wherein the transmission at a welding wavelength of a radiant energy source along an optical path through the formulation and the bulk portions and the reflective surfaces is lower than the optical transmission through just the bulk portions and the reflective surfaces only. The first and second reflective surfaces are made of polymers having overlapping melting temperature ranges. The transmission-enhancing formulation includes a material system containing a radiant energy absorbing dye having an absorption band matched to the welding wavelength of the radiant energy source. The material system is capable of directing the lower optical transmission attributable to the formulation into thermal energy via successive electronic-to-thermal and chemical-to-thermal conversion activities, wherein the thermal energy is transferable into the reflective surfaces disposed within the same optical path as the material system. The thermal energy transfer is capable of welding the transmission-reducing reflective surfaces together into a transmission-enhancing region having the bulk portions optically fused together.

The transmission-enhanced region exhibits an optical transmission within the visible spectrum greater than the transmission through both portions and both reflective surfaces only. The transmission-enhanced region exhibits an optical transmission at selected wavelengths within the visible spectrum of about 10% more than, or 1.1 times greater than, the transmission through both portions and both reflective surfaces only.

The transmission-enhanced region exhibits a photopic transmission of about 10% more than, or 1.1 times greater than, the photopic transmission through both portions and both reflective surfaces only. The optical transmission along the optical path through the formulation is about 10% lower than, or 0.9 times less than, the optical transmission through the bulk portions and the reflective surfaces. The material system is mutually miscible with the reflective surfaces to avoid occluding the transmission-enhancing region. The mutual miscibility is measured by numerical proximity of the Hansen solubility parameters of the dye, the vehicle, the by-products and the reflective surfaces. The numerically proximate Hansen solubility factors provide minimal occlusion of the optical transmission within the transmission-enhancing region.

These properties are monitored by a method wherein electromagnetic radiation is transmitted through the completed weld or adjacent the completed weld toward a sensor. The system controller determines if dye was properly reacted during welding and certifies the workpiece as being welded based on the test wavelength or wavelengths, or stored data, containing information similar to that shown in the graphs. The transmitted radiation may be at or near the anticipated welding wavelengths, in the blue or red visible spectrums, or may comprise a scan to determine the color coordinates or color profile of the workpiece. The test transmissions occur at wavelengths in which the various curves are sufficiently spaced apart from each other to allow the method to assess if the workpiece has successfully passed from one state, represented by one curve, to another state, represented by another curve. Basically, the first set of steps checks if the dye was properly placed to permit welding, characterized by marked lower transmissions for absorbing the welding energy. The second set of steps then checks if the dye was properly consumed during welding, characterized by marked increase transmission due to absence of dye and elimination of one pair or refractive or reflective surfaces. These various states are each represented by a transmission curve, which are sufficiently separated from each other at selected points. Other curves indicate improper dye placement or improper welding, and these are also sufficiently separated from all others at selected points to be useful in quality management.

A method of preprocessing a workpiece made from a first polymer for the exclusive purpose of preparing it for a high-efficiency through transmission radiant energy welding operation fusing the workpiece to a mating panel made from a material which softens on heating and is freely selectable from a second polymer which is the same or similar to the first polymer or a different polymer which is at least locally miscible with the surface of the first polymer. The polymers have overlapping melting temperature ranges. In a first step, a radiant energy director is formed as a substantially laminar welding zone. Formation includes the steps of (i) selecting a first polymer which softens on heating and includes a bulk portion and a surface extending across the bulk portion, (ii) selecting a dye possessing both strong absorption and a high extinction coefficient at a welding wavelength of a radiant energy source, (iii) selecting a dye vehicle with sufficient viscosity to define the edge of the welding zone and avoid undue interference with the welding operation or occlusion of the ultimately fused portion, and (iv) depositing, via the dye vehicle, between 5 and 3000 nanograms of dye per mm 2 on or above the workpiece surface. The radiant energy director has the capacity to undergo electronic, chemical and mechanical transformations during the welding operation according to the following steps of (1) converting inbound radiant energy at said welding wavelength over about 0.1 Joule/mm 2 into thermal energy via vibronic relaxation, (2) exothermically decomposing at least a portion of said dye into inert, invisible by-products immediately following said converting step, and (3) during said converting and decomposing steps, delivering a first quantity of energy into the bulk portion to elevate the surface into the melting temperature range of the first polymer and delivering an approximately equal second quantity of energy in the opposite direction away from the bulk portion.

Other objects and features of the present invention will become apparent from the following detailed description considered in conjunction with the accompanying drawings. It is to be understood, however, that the drawings are designed solely for purposes of illustration and not as a definition of the limits of the invention, for which reference should be made to the appended claims. It should be further understood that the drawings are not necessarily drawn to scale and that, unless otherwise indicated, they are merely intended to conceptually illustrate the structures and procedures described herein.

BRIEF DESCRIPTION OF THE DRAWINGS

In the drawings wherein like reference numeral denote similar components throughout the views:

FIG. 1 is a perspective view of a pre-processed workpiece according to the 5 invention having a surface deposition of absorber dye along one side thereof;

FIG. 2A is an enlarged cross-sectional view of the surface deposition, taken along the line II—II from FIG. 1 ;

FIG. 2B is an enlarged cross-sectional view of an alternate embodiment of the surface deposition, taken along the line II—II from FIG. 1 ;

FIG. 3A is a graph showing transmission curves of various stages in the pre-processing of the workpiece along with transmission curves following electromagnetic irradiation;

FIG. 3B is a graph showing transmission curves of another pre-processed workpiece along with a transmission curve of a unitary polymer block; and

FIG. 4 is a multi-part cross-sectional view of the workpiece and mating material illustrating components of the quality assurance and quality control system.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

Referring now in detail to the drawings, and in particular FIG. 1 , there is shown a prepared workpiece 10 , designed for the express and ultimate purpose of being welded, at any future time, to a material made from a compatible polymer. In other words, workpiece 10 may be thought of as a work-in-process, wherein the workpiece has undergone some initial processing and may reside in inventory for an extended period of time awaiting further processing. This patent application shall cover the design and engineering characteristics of this workpiece which is adapted for bonding to a material via mutual heating of surface layers into their respective melting temperature ranges until the parts meld and fuse together. Though not specifically part of this patent application, the welding process consists of through transmission radiant energy welding. Such radiant energy may be provided from a number of sources including lasers operating in the visible, near infrared, and infrared spectrums along with infrared lamps and infrared emitters. While lasers generally have narrower bandwidths than infrared lamps, the phrase “welding wavelength” as used herein, shall mean one or more wavelengths that the absorber and radiant energy source have in common for delivering thermal welding energy.

Workpiece and Mating Material Compatibility

Generally workpieces according to the invention are made from thermoplastic materials or a small group of thermoset plastics. Also included are textiles made from plastic or plastic fibers, or other fibers having plastic coatings. The inventive design of the workpiece comprises its ability to fuse its surface to a mating surface, affecting several polymer layers in each direction adjacent the surface. The main characteristic is that at least the surface of the workpiece softens upon heating, rather than decomposing. Similarly, the mating surface should soften upon heating. The workpiece and the mating material that it is adapted to weld to, should be mutually miscible polymers and should have melting temperature ranges that overlap.

Workpiece, Dye, and Related Chemical Components Compatibility

While the absorber dye may be placed onto the workpiece surface in solid form as a tape or film, particular utility results from application in liquid form. While the application process is not part of this invention, the resulting workpiece should not be limited in any way by the mention of a limited number of application processes, as the characteristics imparted from the application process can result from a multitude of application processes. For example, liquid dispensing or ink jet printing each provide a different aspect of flexibility, cost-effectiveness and uniformity for applying dye to a wide variety of surfaces, shapes, workpiece types, intended uses and combinations thereof.

For applications in liquid form, a solvent which substantially dissolves the dye to form an ink is required. Engineering requirements include proper viscosity, surface tension and drying time for the ink, all of which can effect how well defined the edge of the welding zone is. Following evaporation of the solvent, the dye remains on the surface along with additives, solvent residues and contaminants. Similarly, for applications in solid form, the dye is disposed on the surface along with the other constituents that make up the film or tape. As will be discussed in greater detail below, the dye may decompose during welding. Accordingly, it is desirable that the additives, residues, contaminants, other constituents, dyes, decomposition products and other by-products of the application process, all be miscible in the surface polymers of the workpiece and mating material. Any non-miscible components should only be present in very low concentrations to avoid interference with the welding process, for example through heat sinking or mismatched melting temperature(s). Non-miscible components may also occlude, color or introduce haze into the welding zone, and their levels should be limited commensurate with the optical requirements of the workpieces.

The dyes are visible light absorbing, near infrared (NIR) absorbing or infrared (IR) absorbing dyes having high absorption and large extinction coefficients at the welding wavelength. At the same time, the dye should have low absorption and low coloration in regions other than the laser wavelength, particularly within the visible spectrum.

In one embodiment of the invention, one visible light absorbing dye is used with a matching visible light transmitting laser. Alternatively, a NIR absorbing dye is used with an NIR laser. Other sources of visible, NIR or IR radiant energy may be employed. While lasers operate at single wavelengths, IR lamps or IR emitters may operate at multiple wavelengths. Combinations of dyes may be used to absorb across a bandwidth that includes these multiple wavelengths. In addition, the exothermic energy of one dye may be used to trigger the decomposition of a second dye. Whether one or more than one dye is used, the key element is the efficient conversion of energy and low occlusion where optical transmission of the weld is an issue.

Referring again to FIGS. 1 and 2A , workpiece 10 includes a surface 16 , representing the surface layers of interaction. Workpiece 10 also has a bulk portion 14 , which is the bulk of the material below surface 16 , and represents a non-reactive portion of workpiece 10 . Workpiece 10 is designed and engineered for the exclusive and ultimate purpose of welding to a mating material 12 .

An absorber dye 20 is deposited along surface 16 . The presence of dye 20 defines a welding zone 22 . In other words, the welding zone 22 is a region of surface 16 that is weld-enabled. At any future time a weld can be obtained along the welding zone 22 by properly placing a compatible polymer 12 into contact with surface 16 and exposing welding zone 22 to an amount of laser energy within the range according to the invention. FIG. 2A shows absorber dye present on surface 16 in the form of individual molecules, several molecular layers thick. The absorber dye is dissolved in an appropriate, compatible solvent and applied to surface 16 . The solvent may cause the infusion of dye several molecular layers deep into surface 16 , depending on the aggressiveness of the solvent with respect to the workpiece material. As these surface layers melt during welding the infused dye will encounter the melt flow in the joint region. Surprisingly, applicants discovered that slight infusion of dye is acceptable as long as the melt flow region subsequently reaches those infused dye molecules. However, if the dye infuses further into the surface, its heating remote from the melt flow region causes foaming that occludes the welded joint.

In the embodiment of FIG. 2B , infusion is totally avoided as the absorber dye is first incorporated into a thin film which is then placed onto surface 16 . This embodiment also avoids any problems associated with having the dye/solvent solution running along the surface thereby diminishing the sharpness of the edge of the welding zone. The edge of the welding zone represents the boundary between weld-enabled portions of surface 16 and non weld-enabled portions.

Pre-Processing Examples

FIG. 3 shows a series of transmission graphs wherein curve 40 is the transmission through a sample mating material 12 laid on top of a sample workpiece 10 . Both samples were made of polycarbonate. Next a solution containing 1 gram per liter of absorber dye was applied to workpiece 10 forming a welding zone thereon. Curve 50 is the transmission through mating material 12 laid on top of workpiece 10 containing the absorber dye.

FIG. 4 shows the cross-sectional relationship of the panels with mating material 12 on the left and workpiece 10 on the right. Section 44 corresponds to curve 40 . Section 55 corresponds to curve 50 , where workpiece 10 is weld-enabled, and represents the lowest transmission values in the near infrared (NIR) and infrared (IR).

Post Processing Examples

Referring again to FIG. 3 , curve 60 is the transmission through both panels following laser irradiation where the panels were not clamped together resulting in no weld. Curve 70 is the transmission through both panels following laser irradiation where the welding zone was facing out resulting in no weld. Curve 80 is the transmission through both panels following laser irradiation with the panels properly oriented and clamped, resulting in a successful weld.

In FIG. 4 , section 66 corresponds to curve 60 and section 77 corresponds to curve 70 . Note that the absorber dye 20 is partially or completely decomposed, but that no weld occurred. The test data indicates that a workpiece improperly clamped to the mating material 66 is equivalent to an improper orientation of the workpiece 77 . In another test a Cyrolite acrylic was prepared for welding to a polyolefin. The workpiece failed to weld to the mating material as the melting temperature range of the polymers did not overlap, thereby preventing mutual miscibility from occurring. Section 88 corresponds to curve 80 , wherein the dye has been decomposed and the reflective boundaries between workpiece 10 and mating material 12 have been fused together. The elimination of the transmission detracting reflective boundaries, results in the highest transmission values for the successfully welded section 88 , as shown in curve 80 . FIG. 3 B shows that the quality management and certification steps according to the invention can provide transmission values for welded parts (curve 80 b ) that are equivalent to a unitary block (curve 200 ).

In FIG. 3A , at an exemplary diode laser welding wavelength of 940 nm, the transmission through both bulk portions and both reflective surfaces is 81.9%, corresponding to curve 40 . The same measurement after introduction of the formulation is 71.8%, corresponding to curve 50 . This difference is about 10% lower or about 0.9 times lower. Mis-welds, corresponding to curves 60 and 70 , have about 78.4% transmission and a proper weld, corresponding to curve 80 possesses an 86.6% transmission.

At the exemplary Nd:YAG laser welding wavelength of 1064 nm, the transmission through both bulk portions and both reflective surfaces is 81.7%, corresponding to curve 40 . The same measurement after introduction of the formulation is 69.1%, corresponding to curve 50 . This difference is about 10% lower, and more specifically 12.6% lower. The difference is about 0.9 times lower and more specifically 0.8 times lower. Mis-welds, corresponding to curves 60 and 70 , have about 77.5% transmission and a proper weld, corresponding to curve 80 possesses a 86.1% transmission.

An exemplary VIS wavelength is 550 nm which will also serve as an approximation of the photopic. All curves 40 , 50 , 60 and 70 are grouped within 0.3% of 75.3% transmission, illustrating the minimal effect of the introduction and decomposition following mis-welds on the visible spectrum. The proper weld yields a transmission of 83.4%. This is about 10% higher and about 1.1 times higher, for both the absolute measurements at 550 nm and for the photopic approximation. These percent transmission values are summarized in the following Table 1.

TABLE 1
	Curve 40	Curve 50	Curve 60	Curve 70	Curve 80
wavelength	Section 44	Section 55	Section 66	Section 77	Section 88
1064 nm	81.7	69.1	77.5	77.5	86.1
940 nm	81.9	71.8	78.4	78.4	86.6
550 nm	75.3	75.3	75.3	75.3	83.4

The use of different polymers, different dyes, different vehicles and different dye densities, and different levels of irradiation will have varying results. In optical applications, these values are typical. IR sources, such as IR lamps, as well as other lasers, including lasers operating in the visible spectrum may also be used.

A further example with the same dye and same polymer containing a different color correction package is shown in FIG. 3 B. Curves 40 b , 50 b and 80 b correspond to curves 40 , 50 and 80 , respectively. Curve 200 represents a unitary block of polymer, equivalent in thickness to the two pieces which are welded together and illustrated in curve 80 b.

Another example at 7 times the dye concentration, as measured at the liquid vehicle state, is shown in Table 2. The presence of additional dye is confirmed by low values of section 55 at the higher wavelengths. All other factors remain the same. After welding, note the excellent transmission in section 88 at 550 nm, comparable to the same measurement in Table 1, despite the presence of dye at the other wavelengths in section 88 . Accordingly, this example illustrates partial exothermic decomposition with virtually no effect on visible or photopic transmission. At this dye concentration, additional capacity exists for use of greater amounts of thermal energy during welding, within the parameters according to the invention.

	TABLE 2
	wavelength	Section 44	Section 55	Section 88
	1064 nm	82.7	34.0	75.4
	940 nm	82.9	36.4	74.5
	550 nm	77.9	76.0	84.0

In another series of tests, a particular dye was tested at high concentrations by painting onto polyurethane for welding to polycarbonate and in another instance painted onto PVC for welding to PVC. Laser power and weld speed were varied to adjust the weld energy per surface area, but no weld occurred. It is believed that the high concentration of dye and the painting technique delivered a surface density which was non-uniform and/or beyond the range specified according to the invention. When the same dye was uniformly loaded into a film at the concentration specified according to the invention, PMMA plates were readily welded together at dye concentrations spanning a 10-fold concentration, at film thicknesses spanning a 3-fold range, at laser powers spanning a 2.5-fold range, and at weld speeds spanning a 6.6-fold range. In terms of weld energy per surface area the range extended from 0.7 J/mm 2 to 11.4 J/mm 2 , more than a 16-fold range, i.e. 2.5 times 6.6.

The transmission values as exemplified in Tables 1 and 2 may be useful in a further embodiment of the invention directed toward quality assurance and quality control (QA/QC). Such quality assurance and quality control may provide manufacturers and end-users of the pre-processed workpiece with data in some of the following exemplary categories: absence ( 44 ) or presence ( 55 ) of dye; proper placement and density of dye; dye decomposition in no weld scenarios ( 66 and 77 ); and proper welds ( 88 ). An embodiment for implementing such QA/QC system is illustrated in FIG. 4 , wherein a suitable microprocessor, PC or system controller 100 serves as the hub for data collection, data storage and data manipulation. A VIS, IR, or combination of VIS and IR sources 102 is optional combined with optical filters 104 at one or more QA/QC stations. System controller 100 is coupled to components 102 and 104 to control any variables provided therein and to receive signals as to the operational status and settings thereof.

One or more sensors 106 a - 106 e are provided at each QA/QC station. System controller 100 is coupled to sensors 106 a - 106 e to control any variables provided therein and to receive optical data from electromagnetic waves passing though the workpiece. The sensors may be selected from any suitable optical devices capable of capturing photometric or spectrophotometric data, including analog or digital cameras. A data storage device 108 stores sensed optical data and historical data for comparison via compare function block 120 . An accept/reject decision module 130 analyzes comparison data to generate either an accept signal 130 a or a reject signal 130 b.

In the examples the following symbols are used where T represents a transmission value and Δ represents a change in transmission value:

For the Workpiece:

T INIT represents the initial transmission without dye— 44 a

T PRE represents the transmission after the workpiece is weld-enabled— 55 a

Δ PRE represents the loss between T INIT and T PRE .

For the workpiece in contact with the material:

T ZONE represents the transmission through both parts and the welding zone— 50 , 50 b , 55

T REF represents the transmission through both parts remote from welding zone — 40 , 40 b , 44

T POST represents the transmission through both parts after welding— 80 , 80 b , 88

Δ POST represents the gain between T ZONE and T POST .

Note that T post corresponding to curve 80 b is equivalent to the transmission and photopic for a unitary block shown in curve 200 . While results may vary if different polymers are being welded together, the benefit in fusing their refractive boundaries will still result in enhanced transmission and photopic values.

In a pre-processing example, system controller 100 may capture sensed optical date, at 940 nm, for sections 44 and 55 . Historical data from storage 108 indicates an expected Δ PRE of a 10% transmission loss, or 0.9 times transmission loss. Module 120 compares the transmission actual transmission loss of 10.1% (i.e. 81.9-71.8) or the relative transmission loss .12 (i.e. 10.1/81.9) to historical data. If the comparison is within allowable tolerances, module 130 will generate an accept signal 130 a , thereby certifying that the workpiece is weld-enabled for 940 nm. We refer to this as testing within numerical proximity to the radiant energy welding wavelength. Otherwise, upon generation of reject signal 130 R, controller 100 may reject the part or re-test with a different source, with a different wavelength, or with a different filter, for example. When testing at 940 nm, it is possible to accept the workpiece for use at a 1064 nm welding wavelength through two methods. First, stored data on the dyes absorption spectrum reflecting it's absorption strength and extinction coefficient may be accessed to extrapolate an acceptable 1064 nm Δ PRE based on the 940 nm test. We refer to this as certifying the workpiece weld-enabled as a function of the dye's known absorption and extinction coefficient. Second, the test may occur at 940 nm and 1064 nm to certify the part for 900 nm to 1100 nm. We refer to this as testing within a bandwidth range of the radiant energy welding wavelength. Wherein a bandwidth range may span the visible spectrum, the rear infrared spectrum, the infrared spectrum or combinations thereof.

According to another method, the test may occur anywhere in the range of about 400 nm to about 450 nm to identify a dye's, or dye class', tell tale blue spectrum shift. The dye, or dye class', absorption spectrum is accessed and the workpiece may be certified for a welding wavelength remote from the test wavelength. Typically, the welding wavelength will be selected from the visible spectrum, near infrared spectrum, infrared spectrum or multiple wavelengths within one or more of the aforementioned spectrums. Alternately, the test may occur anywhere in the range of about 750 nm to about 800 nm to identify a dye's, or dye class', tell tale red spectrum shift. An advanced version of testing at one wavelength is to test the entire visible spectrum and obtain a composite color signal, for example one method utilized is capable of categorizing a composite color signal into one of 64,000 unique and identifiable colors. Even though the infrared dyes used in this experiment do not absorb readily in the visible spectrum, the small amount of absorption that does occur in the red and blue regions of the visible spectrum provides enough of a color profile to be readily identifiable by the color signal. This testing method is accurate enough to distinguish and identify individual dyes as well as combinations of dyes, from the typically green hue resulting from the suppression of red and blue regions in the visible spectrum.

Furthermore, a supplemental feature of the system may be utilized to certify that an area has not been printed. This is desirable in optical applications where stray dye outside the welding zone is likely to remain and adversely affect the transmission characteristics of the assembled parts. In certain medical applications it may also be desirable to limit the amount of stray dye present outside the welding zone for toxicological reasons.

In a post-processing example, system controller 100 may capture sensed optical date, at 940 nm, for sections 66 or 77 . Historical data from storage 108 indicates an expected Δ POST of a 6.5% transmission gain over section 55 for failed welds. Alternatively, system controller 100 may capture sensed optical date, at 940 nm, for section 88 . Historical data from storage 108 indicates an expected Δ POST of a 14.8% transmission gain over section 55 for completed welds. Module 120 compares the actual transmission gain to historical data for both failed and successful welds, generating an appropriate accept or reject signal.

Other tests conducted within the parameters according to the invention successfully welded the following pairs of materials together:

Workpiece          Mating Material
MDPE Film          LDPE coated paperboard
Polypropylene film ABA
Copolyester        PEN
Copolyester        Polypropylene

Welding workpieces to mating materials made from the same polymer was more easily accomplished and includes: polycarbonate, polypropylene, PMMA, HDPE, acetal, TPE, polyetherimide, PEEK, polystyrene, nylon, and ABS. Since certain nylons have transmissions below 50%, and even 10%, it is impractical to measure changes in transmission on a scale of 10%. Accordingly, the 1.1 times and the 0.9 times transmission changes work well at measuring performance within the parameters of the invention, because the predicted behavior still occurs, even at low transmissions with opaque parts. Successful welding was achieved, for example, It with lasers operating in the following spectrums: the visible spectrum with Nd:YAG doubled 532 nm, ruby laser 694 nm and visible diode lasers 670 nm; near infrared with GaAs lasers; and infrared with diode lasers at 808 nm, 940 nm and 980 nm; and the Nd:YAG 1064 nm.

As can be seen, a workpiece prepared according to the design and engineering parameters according to the invention provide a high tolerance and latitude for the ultimate welding process. Thus a single workpiece prepared according to the invention, can be flexibly utilized with different welding lasers at different power levels, and with different mating parts. It may be utilized in applications requiring high strength, high confidence of proper weld, and high optical or photopic transmissions values combined with low occlusion. In addition, in preparing the workpiece according the invention a wide range of dyes and delivery vehicles may be utilized as long as the solubility guidelines are followed. The inherent flexibility of the invention is in contrast to the prior art systems which typically dope parts with occluding pigments, have a single pigment or dye concentration level or treat the parts as matched pairs of the same material.

Thus, while there have shown and described and pointed out fundamental novel features of the invention as applied to preferred embodiments thereof, it will be understood that various omissions and substitutions and changes in the form and details of the methods described and devices illustrated, and in their applications, may be made by those skilled in the art without departing from the spirit of the invention. For example, it is expressly intended that all combinations of those elements and/or method steps which perform substantially the same function in substantially the same way to achieve the same results are within the scope of the invention. Moreover, it should be recognized that design and engineering criteria, their constituents and/or elements and/or method steps shown and/or described in connection with any disclosed form or embodiment of the invention may be incorporated in any other disclosed or described or suggested form or embodiment as a general matter of design choice. It is the intention, therefore, to be limited only as indicated by the scope of the claims appended hereto.

Claims

1. A method for assessing whether a workpiece having an initial transmission of TINIT has been rendered weld-enabled as defined by a transmission drop ΔPRE to a pre-processed transmission TPRE within a welding zone, the method comprising the steps of:providing a workpiece with a bulk portion and a surface extending across the bulk portion, wherein at least the surface is made from a first polymer which softens on heating; transmitting electromagnetic radiation toward the surface in the region of the expected welding zone to be tested; sensing electromagnetic radiation at a test wavelength passing through the surface of the workpiece and generating a signal representative of transmission; determining whether the sensed transmission signal is within a range of TPRE as an indication that an absorber dye possessing both strong absorption and a high extinction coefficient was deposited on or above said workpiece surface within the welding zone via a vehicle having necessary viscosity and which avoids undue interference with or occlusion of the welding zone; and certifying the workpiece weld-enabled for radiant energy welding wavelengths within a bandwidth range of the test wavelength.

2. The method of claim 1, wherein said certifying step comprises determining the bandwidth range as a function of the dye's absorption and extinction coefficient.

3. The method of claim 1, wherein said step of sensing comprises scanning across the surface of the workpiece to generate multiple signals representative of transmission; andsaid determining step comprises determining whether the multiple scanned transmission signals are within a range of TPRE as an indication that the deposition comprises a generally uniform density of about 5 to about 3000 nanograms of dye per mm2 to provide predictable and consistent heating.

4. The method of claim 1, wherein said sensing step comprises sensing electromagnetic radiation at multiple test wavelengths and said certifying step comprises determining the bandwidth range as a function of said multiple test wavelengths.

5. The method of claim 1, wherein at least one of said multiple test wavelengths is in numerical proximity to the radiant energy welding wavelength.

6. The method of claim 1, wherein the transmission drop ΔPRE within the certified bandwidth is within a range from about a 10% transmission drop to a 0.9 times transmission drop.

7. The method of claim 1, additionally comprising the steps of:transmitting electromagnetic radiation toward the surface remote from the region of the expected welding zone; sensing electromagnetic radiation at a further test wavelength passing through the remote surface of the workpiece and generating a further signal representative of transmission; determining whether the further sensed signal is withing a range of TINIT; and certifying the remote surface dye free.

8. A method for assessing whether a workpiece having an initial transmission of TINIT has been rendered weld-enabled as defined by a transmission drop ΔPRE to a pre-processed transmission TPRE within a welding zone, the method comprising the steps of:providing a workpiece with a bulk portion and a surface extending across the bulk portion, wherein at least the surface is made from a first polymer which softens on heating; transmitting electromagnetic radiation toward the surface in the region of the expected welding zone to be tested; sensing electromagnetic radiation at a test wavelength within the visible spectrum passing through the surface of the workpiece and generating a signal representative of transmission; determining whether the sensed transmission signal is within a range of TPRE as an indication that an absorber dye possessing both strong absorption and a high extinction coefficient was deposited on or above said workpiece surface within the welding zone via a vehicle having necessary viscosity and which avoids undue interference with or occlusion of the welding zone; and certifying the workpiece weld-enabled for a radiant energy welding wavelength as a function of the dye's absorption and extinction coefficient.

9. The method of claim 8, wherein said test wavelength is within the blue portion of the visible spectrum.

10. The method of claim 8, wherein said test wavelength is within the red portion of the visible spectrum.

11. The method of claim 8, wherein said signal representative of transmission comprises a composite color profile signal.

12. The method of claim 8, wherein said radiant energy welding wavelength is within one of a visible spectrum, a near infrared spectrum and an infrared spectrum.

13. A method for assessing whether a weld-enabled workpiece, having a welding zone formed by a deposition of dye via a vehicle, has been properly or improperly welded to a material evidenced by a transmission gain ΔPOST from a workpiece-material transmission TZONE passing through the welding zone, to a post-processed transmission TPOST, the method comprising the steps of:providing a workpiece and a material in contact with the workpiece; transmitting electromagnetic radiation toward the prior location of the welding zone to be tested; sensing electromagnetic radiation at a test wavelength passing through the workpiece, the prior location of the welding zone, and the material and generating a signal representative of transmission; determining whether the sensed transmission signal is within a range of TPOST as an indication that the dye has undergone vibronic relaxation followed by exothermic decomposition of at least a portion of said dye in response to inbound radiant energy at a welding wavelength over about 0.1 J/mm2; and certifying that the vehicle avoided undue interference with welding zone and that the workpiece and material are properly welded together.

14. The method of claim 13, wherein said certifying step comprises optically certifying that the vehicle avoided occlusion of the welding zone and that the dye exothermically decomposed into inert, invisible by-products and that the dye, the vehicle, the by-products and the portions of the workpiece and the material that were welded are mutually miscible.

15. The method of claim 14, wherein mutual miscibility comprises numerical proximity of the Hansen solubility parameters of the dye, the vehicle, the by-products and the portions of the workpiece and the material that were welded together.

16. The method of claim 13, wherein said providing step comprises providing a workpiece with a reflective boundary facing the material and providing a material with a reflective boundary facing the workpiece, and wherein the transmission through both reflective boundaries and the welding zone is represented by TZONE and wherein the transmission through both reflective boundaries and remote from the welding zone is represented by TREF.

17. The method of claim 16, wherein said determining step comprises determining if TPOST exceeds TREF as in indication that the reflective boundaries are fused together.

18. The method of claim 17, wherein said certifying step comprises certifying that TPOST exceeds TREF by about 10%.

19. The method of claim 17, wherein said certifying step comprises certifying that a photopic transmission through the weld exceeds a photopic transmission through both reflective surfaces.

20. The method of claim 17, wherein said certifying step comprises certifying that a photopic transmission through the weld exceeds a photopic transmission through both reflective surfaces by 10%.

21. The method of claim 13, further comprising the steps of:additionally determining whether the sensed transmission signal is within a range in between TZONE and TPOST a s an indication that at least a portion of the dye has undergone decomposition; and rejecting the workpiece and material as being improperly welded.